Scheelite coatings on SiC fiber: Effect of coating temperature and atmosphere

Scheelite coating was deposited on SiC fiber tows from various liquid-phase precursors followed by heat treatments between 900 °C and 1100 °C in different atmospheres. The tensile strength was fully retained for the coated fibers treated at 900 °C in vacuum. Subsequent heat treatment at 1100 °C in Ar had little effect on the fiber strength, which is explained by the excepted good thermal stability between the scheelite coating and SiC fiber. However, larger strength degradation and poor spool ability of coated fibers prepared in Ar/air were found. Assisted oxidation of SiC fiber by calcium salts is suggested to be responsible for the much larger strength degradation of fibers prepared in Ar/air.