Enhancement of glass-ceramic performance by TiO2 doping: In vitro cell viability,proliferation, and differentiation

A new TiO₂-containing bioactive glass and glass-ceramics based on 50SiO₂-(45-X)CaO-(XTiO₂)-5P₂O₅ system was designed using a sol–gel technique (where X = 5, 7.5 and 10 wt %). The roles of the crystallization behavior and physicochemical characteristics of the designed glass and glass-ceramics which were played in the introduction of TiO₂ substitutions were investigated. Moreover, cell proliferation and differentiation were evaluated against human osteosarcoma cells (Saos-2). The TiO₂/CaO replacements led to the formation of a stronger glass structure and thus increased thermal parameters and the chemical stabilization of the designed materials. The FTIR data confirmed the existence of Ti within the glass and glass-ceramics samples, and no remarkable effect on their chemical integrity was observed. The XRD patterns indicated that calcium-containing minerals, including Ca₂SiO₄,Ca₃(PO₄)₂, Ca(Ti,Si)O₅, CaTiSiO₅, and Ca₁₅(PO₄)₂·(SiO₄)₆ phases were developed as a role of structure/texture under the applied heat-treatment. The results of the cytotoxicity test proved that a safe sample dose is 12–50 μg/ml, at which cell viability is ≥ 85%. The cell differentiation determined by ALP test proved the superiority of glass-ceramics compared with their native glasses. Therefore, the obtained materials could be safely used as novel biocompatible materials for the regeneration of bone tissue.