Hot corrosion behavior of YSZ/ZrW2O8 composites exposed to V2O5 at 700 °C and 850 °C in air

The hot corrosion behavior of YSZ/ZrW₂O₈ composites as a promising thermal barrier coating system exposed to V₂O₅ at 700 °C and 850 °C was investigated in order to better understand the influence of the incorporated ZrW₂O₈ with isotropic negative thermal expansion performance on the corrosion resistance. Results indicate that the ZrW₂O₈ incorporation could retard the degradation of YSZ from V₂O₅ attack and the corrosion process is significantly related to the inclusion content and the temperature. The corrosion resistance could be determined by the incorporation content, while the reaction products are only temperature dependent. At 700 °C, ZrV₂O₇, YVO₄ and m-ZrO₂ were the main corrosion products, while ZrW₂O₈ recrystallized under the acidic environment provided by V₂O₅. At 850 °C, ZrW₂O₈ decomposed and only WO₃, YVO₄ and m-ZrO₂ could be detected as final corrosion products. The corrosion mechanisms of YSZ/ZrW₂O₈ composites at 700 °C and 850 °C were discussed based on the phase diagrams and Lewis acid-base rule as well as the volume compensation of the positive and negative expansion ceramics.