Effect of Al2O3 on the microstructure and mechanical properties of Ti3AlC2/Al2O3 in situ composites synthesized by reactive hot pressing

Ti₃AlC₂/Al₂O₃ in situ composites with different Al₂O₃ contents were successfully synthesized from the powder mixture of Ti, TiC, Al and TiO₂ by a reactive hot-pressing method at 1350 °C. The effect of Al₂O₃ on the microstructure and mechanical properties of the composites was investigated in detail. The results indicate that the as-fabricated products mainly consist of Ti₃AlC₂, Al₂O₃ and a small amount of TiC. With increasing the Al₂O₃ content, the flexural strength of Ti₃AlC₂/Al₂O₃ composites increase gradually, the fracture toughness reaches the peak value of 8.21 MPa m^1/2 as the Al₂O₃ content increasing to 9 wt%, the hardness attains the maximum value of 10.16 GPa for 12 wt% Al₂O_3. The strengthening mechanism of the composites was also discussed.