Fracture toughness,strength and creep of transparent ceramics at high temperature

Fracture toughness, four-point bending strength of transparent spinel, Y₂O₃ and YAG ceramics in function of temperature (from room temperature up to 1500° C) were measured. Creep resistance at 1500–1550° C was studied too. Grain size distribution was determined on polished and etched surfaces of samples. Fracture surfaces after tests were examined by scanning electron microscopy. The obtained results showed that: in the case of spinel ceramics fracture toughness and strength decreased from 20 to 800° C, increased from 800 to 1200° C and decreased at higher temperature; in the case of Y₂O₃ ceramics they increased from 400 to 800° C, and next kept constant up to 1500° C; in the case of YAG ceramics they kept constant from 20 to 1200° C and then decreased. The creep strain rate was measured for spinel and YAG but not for Y₂O₃ ceramics which appeared creep resistant. The hypotheses concerning toughening and creep mechanisms were proposed.