自催化乙醇麦草浆热置换洗涤工艺的研究

对麦草乙醇浆快速热置换洗涤工艺进行了研究,探讨了洗涤温度、乙醇质量分数、液比、洗涤段数、洗涤时间对纸浆卡伯值及得率的影响。结果表明,洗涤温度对降低麦草乙醇浆卡伯值的贡献最显著,卡伯值从122降低到36.3;乙醇质量分数、液比和洗涤段数也有一定影响,而洗涤时间对降低卡伯值的作用不明显。麦草乙醇浆最佳洗涤条件为:乙醇质量分数70%,液比1∶30,每段洗涤时间30min,洗涤温度145℃,洗涤段数3。该洗涤条件下麦草乙醇浆卡伯值为38.1,得率47.5%。     

利用预处理技术对三倍体毛白杨进行深度脱木素的研究

利用120℃预汽蒸、120℃黑液预浸以及120℃黑液预浸与螺旋挤压相结合三种预处理技术对三倍体毛白杨NaOH-AQ法和KP法进行改良蒸煮,纸浆卡伯值降至1 5以下,达到了深度脱木素的目的.与常规的NaOHAQ法蒸煮相比,120℃汽蒸预处理三倍体毛白杨NaOH-AQ法蒸煮,在相同用碱量和相近细浆得率下,纸浆卡伯值从16.7降至14.3;高温黑液预浸与挤压预处理三倍体毛白杨NaOH-AQ法蒸煮,在相近细浆得率和纸浆强度下,用碱量降低4%,纸浆卡伯值降至15.0.与常规KP法蒸煮细浆得率相近的情况下,高温黑液预浸处理三倍体毛白杨KP法蒸煮,用碱量降低2%,纸浆卡伯值降至14.1.     

可见光光谱技术在亚硫酸盐浆卡伯值在线测量中的应用

卡伯值是纸浆质量的重要指标,而红浆中的木素含量决定了纸浆的卡伯值。本研究是用可见分光光谱技术在线测量酸法制浆过程蒸煮液中木素的浓度,通过蒸煮液中溶出的木素含量去推算纸浆中木素含量和纸浆的卡伯值。本文确定了合适的可见分光光谱测量波段,并建立了纸浆卡伯值与蒸煮液吸光度之间的数学模型,为实现蒸煮过程卡伯值的在线测量提供了依据。     

基于SVM和遗传算法的纸浆间歇蒸煮参数优化方法

为降低纸浆间歇蒸煮过程的能耗,提出了一种基于支持向量机(SVM)和遗传算法的蒸煮参数优化方法。该方法先根据生产数据,采用SVM建立了间歇蒸煮纸浆卡伯值模型,描述了白液浓度、硫化度、白液量、黑液量、蒸煮时间和蒸煮温度等参数与纸浆卡伯值之间的数学关系;再针对基于SVM的纸浆卡伯值模型较难用于常规优化方法的问题,提出了一种改进的自适应小生境遗传算法,用于间歇蒸煮的参数优化,使纸浆满足质量要求的前提下尽量降低蒸煮过程能耗;最后进行仿真,与实际生产数据相比,实验结果节约蒸汽3.52%,节约白液用量17.18%,硫化度减少0.37%。实验结果表明,该方法模型泛化性好,优化效果明显,很大程度上实现了节能降耗。     

大液比药液循环蒸煮对蔗渣烧碱法制浆的影响

本实验以蔗渣为原料,采用烧碱法蒸煮制浆,研究了大液比药液循环蒸煮中用碱量的影响,并讨论了加大液比对蔗渣制浆性能的影响。结果表明,与传统烧碱-蒽醌法蒸煮工艺相比,大液比药液循环蒸煮的碱耗略高,但处于合理范围,并且能够深度脱除木质素,获得纸浆卡伯值较低（8.9~13.5）、黏度较高（973~1134 mL/g）,有利于提高纸浆的滤水性能。同时,大液比药液循环蒸煮后,蔗渣浆纤维形态的主要分布同桉木浆一致,数均纤维平均长度约1.00 mm,数均纤维平均宽度约26.0 μm。     

纸浆卡伯值计算的Basic语言程序和综合计算式

纸浆卡伯值测定目前已在造纸科研和工厂生产控制中得到广泛应用。卡伯值测定适用范围比较广,不仅可用于化学浆,也可以用于得率在70%以下的半化学浆的硬度分析。而且纸浆卡伯值和木素含量之间呈良好的线性关系.国外对木浆的研究表明,对亚硫酸盐纸浆,木素=卡伯值×0.17;对硫酸盐纸浆,木素=卡伯值×0.15;对木素含量达15～16％的半化学浆,木素=卡伯值×0.16。国内对非木材纸浆的卡伯值与木素含量的关系也进行了很多研究。因而,用纸浆卡伯值可以相对表示纸浆中木素的含量。     

硫酸盐桉木浆蒸煮卡伯值对氧脱木索效果的影响

提高纸浆总得率的传统方法是提高纸浆蒸煮卡伯值,并在氧脱木素和漂白段增加木素的脱除,由此降低漂白成本。但是对硫酸盐针叶木浆,在氧脱木素段延长氧脱木素时间也很难达到木素脱除率60％～65％的程度。本研究旨在阐明提高硫酸盐桉木浆蒸煮卡伯值对蒸煮得率、纸浆黏度以及氧脱木素效果的影响;为增强对氧脱木素机理的认识,分析了蒸煮后和氧脱木素后纸浆卡伯值的组成,探讨了提高工艺选择性的途径。研究结果表明,蒸煮卡伯值为22时,比蒸煮卡伯值为17的纸浆的总得率提高1．5个百分点,且无木素纸浆得率和无筛渣纸浆得率达到最大值。在本实验的卡伯值范围内,纸浆得率的损失归因于纤维素,而非半纤维素。为降低纸浆卡伯值而强化氧脱木素在一定程度上降低了纸浆得率。     

硫酸盐桉木浆蒸煮卡伯值对氧脱木素效果的影响

提高纸浆总得率的传统方法是提高纸浆蒸煮卡伯值,并在氧脱木素和漂白段增加木素的脱除,由此降低漂白成本。但是对硫酸盐针叶木浆,在氧脱木素段延长氧脱木素时间也很难达到木素脱除率60%～65%的程度。本研究旨在阐明提高硫酸盐桉木浆蒸煮卡伯值对蒸煮得率、纸浆黏度以及氧脱木素效果的影响;为增强对氧脱木素机理的认识,分析了蒸煮后和氧脱木素后纸浆卡伯值的组成,探讨了提高工艺选择性的途径。研究结果表明,蒸煮卡伯值为22时,比蒸煮卡伯值为17的纸浆的总得率提高1.5个百分点,且无木素纸浆得率和无筛渣纸浆得率达到最大值。在本实验的卡伯值范围内,纸浆得率的损失归因于纤维素,而非半纤维素。为降低纸浆卡伯值而强化氧脱木素在一定程度上降低了纸浆得率。     

高卡伯值尾叶桉硫酸盐浆的蒸煮及其性能研究

本文研究了不同条件下尾叶桉硫酸盐法蒸煮的纸浆卡伯值和H因子,纸浆得率、HexA含量和黏度及基于总固形物的残碱含量与卡伯值的关系.结果表明,尾叶桉高卡伯值硫酸盐法蒸煮的特征卡伯值为40,其对应的H因子和较优的活性碱用量分别约为297和19%～20%,此时的细浆得率为52%.当纸浆卡伯值随蒸煮条件的加剧低于该特征值而又大于16时,继续蒸煮不但会导致纸浆得率和黏度的下降以及有效碱消耗的增加,同时纸浆中HexA含量也逐渐增大.     

阔叶木碱-蒽醌制浆的改进

介绍了糖槭木硫酸盐、碱-蒽醌、碱-α-甲基蒽醌法制浆,虽然碱-蒽醌蒸煮过程中脱木素作用明显低于硫酸盐蒸煮,但是,当用α-甲基蒽醌代替蒽醌,蒸煮过程中脱木素速率稍低于硫酸盐蒸煮。当有效碱用量相同时,由糖槭木生产碱-α-甲基蒽醌法浆,在纸浆卡伯值相同(约20)情况下,比硫酸盐浆得率增加1.2%(对绝干木片重量计),而这两种纸浆强度基本相同。采用AlCl3催化Friedel-crafts反应是一种工业生产蒽醌方法,用甲苯代替苯可以生产α-甲基蒽醌,而甲苯价格比苯便宜,因此,碱-α-甲基蒽醌法适合于生产阔叶木化学浆。     

液比对尾叶桉硫酸盐法制浆过程中脱木素的影响

本文以尾叶桉为原料,研究了液比对其在硫酸盐法蒸煮过程中脱木素的影响;在此基础上,建立了基于蒸煮液比、纸浆修正卡伯值预测溶解木素量的数学方程,即CLS=1.94(45-KappaM)(L-1.8)+136。结果表明:在蒸煮前期(保温15min前),相同卡伯值条件下,液比变化对溶解木素的扩散几乎无影响;在蒸煮后期(保温15min后),相同卡伯值下,液比越小木素溶出量随之减少。     

Sulfite-Formaldehyde Pulping and Oxygen Delignification of Wheat Straw

In this study,wheat straw pulp was prepared by sulfiteformaldehyde(SF) pulping combined with oxygen delignification to develop a sustainable methodology for chemical pulping of straw materials.The bleachability of oxygen-delignified SF pulp was also evaluated by hypochlorite bleaching.The results indicated that the Na_2SO_3 charge played an important role in lignin removal during SF pulping as well as oxygen delignification.The efficiency of oxygen delignification of wheat straw SF pulp was markedly high.After the oxygenation stage,the Kappa number decreased by over 50%(the original Kappa number of SF pulp was lower than 30) when the Na OH charge was in the range of 3%~5%.The optimal conditions for preparing bleached pulp via combined SF pulping and oxygen delignification involved the use of 12% of Na_2SO_3 and 3% of Na OH,respectively.Pulp with relatively high brightness,a low Kappa number,as well as an acceptable viscosity could be obtained when oxygen-delignified SF pulp was bleached with hypochlorite under a low active chlorine dosage.     

竹材热水预抽提对硫酸盐法制浆的影响

以绿竹为原料,采用不同热水预抽提时间以及蒸煮前将热水预抽提液与竹片分离的方法,通过对比KP法制浆黑液残碱含量以及KP浆的卡伯值、得率、黏度含量等探讨了对硫酸盐法制浆性能的影响。结果表明：热水预抽提可以提高竹片蒸煮脱木素效率,达到相同的脱木素程度（相同卡伯值20）可节省约52%的有效碱用量。在预抽提时间80 min时,浆料的最低卡伯值为7.03。另外,预抽提工艺有利于提高纸浆的黏度,同时纸浆的得率也产生了较大的下降。     

碱—蒽醌化学浆漂白性能的研究

对加拿大一枝黄花碱-蒽醌化学浆D／CEpD和D／CEpD1EpD2漂白条件、漂白浆特性和D／CEpD漂白浆的打浆性能进行了研究。确定了较佳的D／CEpD和D／OEpD1EpD2漂白工艺。D／CFpD漂白较佳工艺条件：总用氟量为10％（D／C、D段用氯量比6．5：3．5），Ep段H2O2用量1．0％。漂白浆指标：AP＋AQ浆得率89．61％，卡伯值1．9，白度79．6％ISO，返黄值5．6，粘度718mL／g；KP＋AQ浆得率91．00％，卡伯值1．3，白度82．3％ISO，返黄值4．7，粘度711mL／g。D／CEpD1EpD2漂白较佳工艺条件：总用氟量10％（D／C、D1和D2段用氯量比为6：3：1），EP段H2O2用量1．5％。漂白浆指标为：AP＋AQ浆得率88．11％，卡伯值1．2，白度83．8％ISO，返黄值4．0，粘度710mL／g；KP＋AQ浆得率88．96％，卡伯值1．1，白度84．7％ISO，返黄值3．9，粘度709mL／g。     

加拿大一枝黄花制浆研究(系列报道之三)碱-蒽醌法蒸煮性能的研究

对加拿大一枝黄花碱-蒽醌法蒸煮性能进行了研究。结果表明：适宜的AP（烧碱）＋AQ（蒽醌）法蒸煮工艺条件是：用碱量17％（以Na2O计），AQ用量0．1％，蒸煮最高温度160℃，保温90min。液比1：4。此蒸煮条件下浆料的得率47．16％，卡伯值25．1，残碱15．98g／L（以Na2O计）。适宜的KP（硫酸盐）＋AQ法蒸煮工艺是：用碱量17％（以Na2O计），硫化度20％，AQ用0．1％，液比1：4，蒸煮最高温度160℃，保温时间90min。此工艺条件下浆料的得率48．44％，卡伯值21．8，残碱8．74g／L（以Na2O计）。AP＋AQ法和KP＋AQ法能显著降低浆料硬度，是生产可漂浆适合的蒸煮工艺。在相似的蒸煮条件下，AP＋AQ法和KP＋AQ（硫化度20％）法浆料性能差异不大。     

杨木NS-AQ法高得率化学浆氧脱木素前的DTPA预处理

对杨木NS AQ法高得率化学浆氧脱木素前的DTPA预处理进行了研究。结果表明 ,DTPA预处理对浆的性质有一定影响 ,在pH值 1～ 9范围内 ,随着 pH值的提高 ,浆的白度逐渐下降 ,卡伯值和黏度也有一定变化 ,并在pH值 7处有峰值。DTPA预处理的适宜条件是 :pH值 3,时间 30min ,温度 4 0℃ ,浆浓 15 % ,用量 2 .5 %。预处理使氧脱木素的反应选择性提高 ,卡伯值下降 12 % ,黏度提高 4 .7% ,白度提高 5 .4 %。     

漂白废水中EOX含量的测定

本文分析了用两种相似的溶剂萃取漂白废水测定EOX含量的差别，对酸性和碱性条件下的萃取样分别进行了分析，并测定了三种纸浆漂白废水中EOX的含量。结果表明，EOX的生成与浆种关系密切，而与纸浆的卡伯值关系不大，这与AOX的生成有很大的差别。     

酸性亚硫酸镁纸浆卡伯值的光学法在线测量机理的研究

制浆蒸煮过程中纸浆的卡伯值无法在线测量一直是困扰造纸工作者的难题,本文采用光学分析法,研究了酸性亚硫酸镁纸浆卡伯值光学法在线测量的波段选择问题,并且验证了所选测量波段的合理性,为实现酸性亚硫酸镁纸浆卡伯值的在线测量提供了理论依据.     

桑枝-桉木板皮混合制浆漂白特性的研究

探究了不同桑枝替代率下桑枝-桉木板皮混合硫酸盐法制浆和ODEp漂白的特性。结果表明,桑枝的化学组分与桉木板皮存在较大差异,桑枝综纤维素含量低、木素含量高、纤维长度较长;在相同制浆漂白工艺下,桑枝较桉木难漂白,其所占比例越高,纸浆的卡伯值越高、白度越低,但桑枝替代率不超过30%时,纸浆具有较好的可漂性,氧脱木素效率在40%以上,漂白浆的白度在78%以上;另外,桑枝的加入可以提高混合浆的黏度和撕裂度,但对漂白浆的抗张强度和耐破度不利。     

不同卡伯值麦草浆臭氧-TCF漂白性能比较

在不同蒸煮条件下，得到不同卡伯值的麦草浆G-1、G-2、G-3、L-1，卡伯值分别为29、18．6、14、7．81；浆料经过酸预处理和螯合预处理，去除重金属离子对臭氧漂白的影响。然后经过臭氧-过氧化氢漂白，结果表明：卡伯值越高，脱木质素选择性越差，白度上升值越低。同时进行了四种不同卡伯值麦草浆臭氧漂白前后浆料中戊聚糖含量变化的比较。结果表明，低卡伯值麦草浆L-1有利于臭氧漂白。