超声冲击对球笼-法兰焊缝残余应力场的影响

为研究超声冲击处理对传动轴总成球笼-法兰焊缝表面残余应力的影响,采用超声冲击强化对球笼-法兰激光焊接焊缝进行了焊趾冲击和全覆盖冲击试验。分析了超声冲击前后裂纹产生原因,测试了焊趾冲击和全覆盖冲击前后残余应力值。残余应力测量结果表明,采用冲击工艺,可以在焊缝表面一定深度下产生压应力,最高测得-237MPa。全覆盖冲击后焊缝整体处于压应力状态下,焊缝中心残余压应力进一步增大;焊趾冲击后,焊缝中心应力值没有较大变化,焊趾处压应力值增大。经超声冲击后,组织发生塑性变形形成了高位错密度的包状结构,这个高位错密度的表面层能够有效阻碍表面应变层底部的晶体在交变应力作用下向表层滑移,抑制表面裂纹产生。     

超声冲击对Q460高强钢焊接接头残余应力及组织性能的影响

以Q460高强钢焊接试板为研究对象,采用超声冲击处理接头表面,研究超声冲击对焊接残余应力及组织性能的影响。研究结果表明:超声冲击可以有效降低焊接残余应力,并使拉应力转化为压应力;超声冲击消除了焊缝与母材过渡区域的凹坑与尖角,焊趾处变得圆滑;超声冲击细化了表层晶粒,细化层深度约120μm;超声冲击后表面显微硬度提高了40 HV0. 2,硬化层深度约2 mm。     

不同处理工艺对转向架横梁模拟箱体焊接残余应力的影响

采用不同的处理工艺对转向架横梁模拟箱体对接接头进行处理,并采用X射线衍射法测量处理后的对接接头残余应力,对比了不同处理工艺条件下模拟箱体某条焊缝的残余应力.结果表明:整体热处理、局部热处理和风铲振动冲击均可改善模拟箱体焊接接头的残余应力.风铲振动冲击可以使模拟箱体接头焊缝区及焊趾部位表面形成一层残余压应力;局部热处理可以改善模拟箱体接头焊后残余应力,拉应力峰值可降低约33％;而整体热处理对模拟箱体接头焊后残余应力的改善效果优于局部热处理,拉应力峰值可以降低约65％.     

超声冲击工艺对16MnR十字接头表面质量的影响

目的提高焊接接头的表面质量。方法采用超声冲击方法对16Mn R十字接头焊趾处进行冲击处理,对原始焊态及不同冲击工艺参数下的焊趾表面质量进行了对比测试及比较分析。结果冲击后,焊接接头焊趾处过渡半径增大,母材与焊缝过渡趋于平缓。焊趾表面组织得到明显细化,细化层深度及细化程度随冲击工艺参数的变化而变化。冲击后焊趾处由焊态的拉应力状态转变为压应力状态,表面显微硬度大幅提高。在1.5 A/20 min冲击工艺下,焊趾处的残余压应力最大(为269.8 MPa),表面显微硬度最高(为340.5HV)。同时,经超声冲击后,表面粗糙度有增大的趋势,而且不当的冲击会使接头表层出现不同类型的缺陷,从而影响焊接接头整体的表面质量。结论接头表面质量不仅取决于冲击时间、冲击电流,还取决于单道冲击过程中冲击点与冲击点之间及多道往复冲击过程中冲击道与冲击道之间的位置及连接的紧密程度,而且并不是所有表面质量指标都与超声冲击参数正相关或线性相关。     

Q390钢多层多道焊接接头残余应力试验分析

为了深入研究Q390钢焊接性能,掌握其在不同焊接工艺条件下焊接接头残余应力分布规律,对40 mm厚Q390低合金高强度结构钢板分别采用埋孤焊和焊条电孤焊2种焊接工艺进行焊接,采用盲孔法测量了焊态下焊接试板的表面残余应力,得到了垂直于焊缝的残余应力分布曲线.结果表明:采用埋弧焊通过施加外在约束可以有效减小焊后试板变形,在焊接接头处得到压应力;经焊条电弧焊自由焊接条件下试板变形较大,在焊缝区得到拉应力,在熔合区和热影响区得到压应力.     

随焊冲击碾压整形对低匹配等承载接头硬度与残余应力的影响

随焊冲击碾压整形(weld shaping with trailing impact rolling,WSTIR)是一种能够降低应力变形、提高承载能力的随焊整形新方法.分别对原始焊态的低匹配等承载接头与随焊冲击碾压整形的低匹配等承载接头进行了硬度试验和残余应力试验.结果表明,随焊整形等承载接头焊缝表面、焊趾处表面的硬度显著高于原始焊态等承载接头的硬度,说明随焊冲击碾压整形对接头承载的关键区域有加工硬化的效果;随焊整形低匹配等承载接头各点的纵向和横向残余应力明显低于原始焊态等承载接头相应位置的纵向和横向残余应力,甚至在随焊整形接头的焊缝中心以及焊趾附近纵向均出现了残余压应力,残余压应力的引入必然能显著地提高低匹配接头承载能力.     

超声冲击对Q370qE钢焊接接头性能的影响

采用超声冲击技术对Q370qE桥梁钢对接接头进行了全覆盖超声冲击处理(UID,并通过XRD、显微硬度计、Olympus金相显微镜等对UIT前后Q370qE焊接接头的残余应力、显微硬度、焊趾应力集中系数等性能的变化进行了测试和分析.结果表明,UIT使左焊趾附近的残余压应力由25.6 MPa增高达240.8 MPa,使右焊趾附近17.2 MPa的残余拉应力转变为196.3 MPa的残余压应力;使焊接接头300 μm深度内次表层的显微硬度由100HV0.5提高到206HV0.5,提高了1倍多;使焊趾区平均过渡半径从1.58 mm增加到2.63 mm,焊缝过渡角由38°减小到27°,这有效改善了接头的几何形状,降低了疲劳应力集中系数.这些性能的变化均有利于提高Q370qE焊接接头的抗疲劳性能.     

超声冲击改善MB8镁合金焊接接头超高周疲劳性能的机理

通过超声疲劳试验探究超声冲击对MB8镁合金焊接接头超高周疲劳性能的影响。同时,从应力集中、残余应力、晶粒细化等3个因素来探究超声冲击改善MB8镁合金焊接接头超高周疲劳性能的机理。结果表明:在1.0×108疲劳寿命下,焊态试样疲劳强度为31.62 MPa,冲击态试样疲劳强度为39.81 MPa,冲击态试样疲劳强度相较于焊态提高了26%。这说明超声冲击可以明显提高MB8镁合金焊接接头超高周疲劳性能。焊态试样焊趾处应力集中系数K_(t1)=1.95,冲击态试样焊趾处应力集中系数K_(t2)=1.67,应力集中系数降低了14.4%,所以超声冲击可以降低焊趾处的应力集中程度。超声冲击后试样焊趾处的应力由残余拉应力转变成残余压应力。超声冲击细化了焊趾表面晶粒从而改善了MB8镁合金焊接接头的超高周疲劳性能。     

超声冲击改善MB8镁合金焊接接头超高周疲劳性能机理探究

通过超声疲劳试验探究超声冲击对MB8镁合金焊接接头超高周疲劳性能的影响。同时,从应力集中、残余应力、晶粒细化等三个因素来探究超声冲击改善MB8镁合金焊接接头超高周疲劳性能的机理。结果表明：在1.0×108寿命下,焊态试样疲劳强度为31.62MPa,冲击态试样疲劳强度为39.81MPa,冲击态试样疲劳强度相较于焊态提高了26%。这说明超声冲击可以明显提高MB8镁合金焊接接头超高周疲劳性能。焊态试样焊趾处应力集中系数Kt1=1.95,冲击态试样焊趾处应力集中系数Kt2=1.67,应力集中系数降低了14.4%,所以超声冲击可以降低焊趾处的应力集中程度。超声冲击后试样焊趾处的应力由残余拉应力转变成残余压应力。超声冲击细化焊趾表面晶粒改善MB8镁合金焊接接头的超高周疲劳性能。     

超声冲击及焊缝余高对6082铝合金焊接接头疲劳性能的影响

本文对6082铝合金焊接接头分别进行超声冲击处理和磨平焊缝余高处理,研究残余应力和应力集中对焊接接头疲劳性能的影响。结果表明:经超声冲击处理后,接头焊趾及其附近区域表层晶粒明显细化;焊趾处由冲击前的残余拉应力转变为残余压应力,其疲劳寿命得到提高;超声冲击前后接头疲劳裂纹均萌生于焊趾部位,而磨平焊缝接头的疲劳裂纹大多萌生于母材圆弧过渡处。无论冲击与否,疲劳断裂机制均为准解理断裂。当超声冲击电流为1.0 A、冲击时间为2 min时,与未超声冲击试样相比,6082铝合金接头疲劳寿命提高11.18%,无余高接头相对焊接接头疲劳寿命提高30.71%。接头表层金属晶粒尺寸、残余应力以及应力集中是影响6082铝合金焊接接头疲劳性能的主要因素。     

超声冲击对SMA490BW钢焊接接头超高周疲劳性能的影响

采用超声冲击工艺对转向架用SMA490BW钢对接接头焊趾表面进行冲击处理,研究了超声冲击对接头超高周疲劳性能的影响。借助金相显微镜、SEM和TEM研究了冲击层金相组织、冲击前后焊趾处的形貌及表层金属晶粒细化程度。运用有限元软件计算焊接接头的应力分布,采用X射线应力仪对冲击前后焊趾表层的应力进行了测量和分析。结果表明,在5×10~6循环周次下,冲击态接头和焊态接头的疲劳强度分别为206 MPa和153 MPa,经冲击处理后疲劳强度提高了34.6%。在1×10~8循环周次下,冲击态接头的疲劳强度为195 MPa,与焊态接头的141 MPa相比提高了38.3%。在240 MPa的应力水平下,焊接接头经超声冲击处理后的疲劳寿命提高了7倍。经冲击处理的焊趾部位的应力集中系数下降了19.1%,其表面的残余拉应力得到消除,并转变为有益的残余压缩应力,焊趾表层组织得到明显细化,这3个方面均对提高焊接接头疲劳性能起到了积极贡献。     

Suggestion of welding procedure for compressive residual stress induction by using low transformation temperature welding materials

ABSTRACT

To understand the cause of compressive residual stress in welded joints, we analysed by numerical analysis the effect of welding pass sequence using low transformation temperature (LTT) welding materials on residual stress around the weld toe of boxing fillet welded joints. It was determined by numerical analysis that the produced compressive residual stress and the influence of the stiffeners are reduced in the equivalent position of the weld toe in a fillet welded joint because of the influence on the behaviour of the stiffener in the weld being due to residual stress distribution around the weld toe. The residual stress reduction method of extending the length of the welded bead and releasing the weld toe from the stiffener, similar to the concept of discarding a bead to reduce tensile residual stress, was effective in fillet welded joints. Numerical analysis of the relationship between residual stress around the weld toe and width of the weld bead in the bead-on-plate welding model clarified that compressive residual stress can be introduced around the weld toe by having a wide width weld bead. In addition, a fully penetrated welded joint was very effective for causing compressive residual stress around the weld toe.     

Residual stress variation in a thick welded joint after ultrasonic impact treatment

The effects of ultrasonic impact treatment (UIT) on the residual stress within a 45?mm-thick high-strength steel welded joint were investigated. The internal residual stresses after UIT was measured with contour method and compared with the as-welded stresses simulated by finite element method. The surface stresses were also measured by X-ray diffraction method and hole-drilling method to validate the simulation model. Results show that UIT introduces compressive stress layer in the weld zone and has the same effect on the longitudinal and transverse welding stresses; the interior stresses increase and demonstrate more uniform distribution after UIT; UIT would not affect the initial compressive stress presented far away from the weld zone.     

超声冲击处理对2A12铝合金焊接接头表层组织性能的影响

用手工氩弧焊(TIG)、ER5356焊丝对2A12铝合金板进行了焊接,用超声冲击处理技术对焊接接头进行了全覆盖强化处理;借助金相显微镜、X射线衍射仪、透射电镜和显微硬度计对超声冲击强化处理前后接头表层的组织和性能进行了分析。结果表明,超声冲击处理可在接头表层形成尺寸均匀、取向随机分布的细晶组织,大幅消除了气孔、缩松等焊接缺陷,接头显微硬度显著提高。讨论了超声冲击导致的晶粒细化和位错增殖对接头强度的影响。     

Stress relaxation due to ultrasonic impact treatment on multi-pass welds

Ultrasonic impact treatment (UIT) is a relatively novel technique applied to the toe of welded joints to improve the fatigue life by changing the weld geometry and the residual stress state. In this study, the stress relaxation due to ultrasonic impact treatment is investigated on a six pass welded high strength quenched and tempered steel section. Stress measurements in two orthogonal directions were conducted by energy dispersive synchrotron X-ray diffraction. Results show that the application of only ultrasound to a welded component re-distributes the residual stresses more uniformly, while mechanical impacts in combination with ultrasound is an effective way to release the residual stresses. After welding, diffraction peak broadening due to the lattice distortion, characterised by the full width at half maximum (FWHM), is observed in the region of the weld toes. Ultrasonic impact treatment reduces the FWHM at these locations.     

冷喷涂改善2219铝合金熔焊接头残余应力新方法

目的采用冷喷涂技术改善2219铝合金变极性钨极氩弧焊(VPTIG)焊接接头残余应力。方法采用冷喷涂技术在8 mm厚2219铝合金VPTIG焊接接头表面进行Cu涂层制备,分析冷喷涂前后接头微观组织、力学性能及残余应力的变化,探究冷喷涂过程中高速碰撞颗粒的"喷丸效应"与加热气体的"热效应"对接头残余应力的改善作用及内在机制。结果冷喷涂前后,接头整体的微观组织无明显变化,但在焊缝表面(Cu涂层与焊缝结合面处)观察到明显的塑性变形。冷喷涂后,焊缝区上表面显微硬度提高,作用深度约2 mm(余高处);接头抗拉强度表观上稍有降低,这是由于涂层对焊缝的拉伸应变局部化改变所致,"喷丸效应"与"热效应"单独作用下,接头抗拉强度无明显变化,所有拉伸试样均从焊趾处沿着熔合区发生断裂。焊态接头残余应力分布总体呈拉应力状态,在焊缝处最大,经过冷喷涂后,焊缝残余拉应力峰值从约200MPa降到约24MPa,大部分区域从拉应力变为压应力,且分布均匀性变好。结论冷喷涂技术可以显著改善VPTIG焊接接头残余应力分布。冷喷涂粒子的"喷丸效应"对基体残余应力的改善作用显著。高温气流的"热效应"虽未能显著降低残余应力,但使应力分布变得均匀。     

超声冲击处理对 7A52 铝合金焊接接头表层组织及性能的影响

目的研究超声冲击处理对7A52铝合金焊接接头表层组织及性能的影响。方法用双丝MIG焊接方法对7A52铝合金进行焊接,采用UIT-125型超声冲击机对其焊接接头进行全覆盖处理;通过金相显微镜,对超声冲击处理后的焊接接头组织变化规律进行观察分析;利用显微硬度计和磨擦磨损试验机测试研究其接头力学性能。结果超声冲击处理后,焊趾处形成相对连续、均匀、光滑的过渡圆弧,可以有效地缓解焊接接头的应力集中,7A52铝合金焊接接头表面得到了明显强化,形成一层致密的塑性变形层,接头表面晶粒细化,母材的表层塑性变形厚度可达15μm左右,热影响区的表层塑性变形厚度可达25μm左右,显微硬度和耐磨性显著提高。结论经超声冲击处理后,7A52铝合金焊接接头表面的塑性变形层最厚处可达20μm左右,形成了具有大致平行于焊接接头表面择优取向的形变织构。沿厚度方向1.5 mm内,热影响区的硬度最高可达162HV,焊缝区的最高硬度为113HV,相比之前提高了21.5%,表层的耐磨性得到较为明显的提高。