感应熔覆原位合成TiC/Ti复合涂层的显微组织演变规律

以石墨和Ti粉为原料,在Ti6Al4V基体表面感应熔覆原位合成了TiC增强Ti基复合涂层,研究了预置反应物粉末中C含量和熔覆工艺参数对复合涂层微观组织演变、物相组成、增强体形态与分布、界面结合行为以及显微硬度的影响规律。结果表明,复合涂层内部原位自生TiC增强体分布均匀,与Ti基质相结合紧密、界面洁净,TiC增强体的最终形态与分布主要受涂层成分、凝固过程和自身晶体结构的影响。随着石墨含量升高,TiC增强体形态逐渐由短纤维状演变为等轴晶状,尺寸和体积分数以及涂层显微硬度逐渐增大。随着热输入量增加,Ti C尺寸逐渐增大,界面过渡区宽度及基体热影响也随之增加。     

Ti6Al4V表面激光熔覆原位自生TiC颗粒增强钛基复合材料及摩擦磨损性能

以Ti,Cr3C2混合粉末作为预置合金涂层,采用YAG固体激光器进行激光熔覆处理,在Ti6Al4V合金表面制备出原位自生TiC颗粒增强钛基复合材料涂层,实验结果表明,采用合适的合金粉末成分和激光辐照能量密度,可以获得增强相TiC弥散分布的钛基复合材料熔覆层,熔覆层结晶致密,且与复合材料基体润湿性良好,熔覆层复合材料的基体组织随预置合金粉末成分的改变而变化,摩擦磨损实验结果表明,原位自生TiC/Ti复合材料熔覆层可明显改善Ti6Al4V合金的表面硬度和摩擦磨损性能。     

Ti6Al4V表面激光熔覆NiCrBSi+B4C涂层的组织结构

选用NiCrBSi及2％民C混粉在Ti6Al4V合金表面进行激光熔覆处理，使基体中的Ti和B4C发生化学反应原位生成TiC、TiB2硬质增强相，制备出TiC与TiB2等增强相增强钛基复合材料涂层。综合运用XRD、SEM、EPMA和TEM等分析手段研究了优化熔覆工艺条件下的NiCrBSi＋B4C激光熔覆层的组织结构与相组成，并对复合涂层进行了硬度测试，结果表明：NiCrBSi＋2％B4C熔覆层的微观组织是在γ—Ni和Ni3Ti＋Ni3B共晶的基体上均匀分布着TiB2、TiC、CrB等相的多元组织，激光熔覆层的硬度比Ti6Al4V基体硬度提高到3～4倍。     

Ti6Al4V合金表面氩弧熔覆原位合成TiC-TiB2增强钛基复合涂层组织与耐磨性

以B4C和Ni60A粉末为预涂材料,采用氩弧熔覆技术,在Ti6Al4V合金表面原位合成TiC与TiB₂增强相增强钛基复合材料涂层.运用XRD,SEM等分析手段研究了复合涂层的显微组织,利用显微硬度仪测试了复合涂层的显微硬度并用磨损试验机分析了其在室温干滑动磨损条件下的耐磨性能.结果表明,熔覆层组织主要由TiC和TiB₂组成,TiC颗粒和TiB₂颗粒弥散分布在基体上,TiC颗粒的尺寸为2~3μm,而呈长条状的TiB₂颗粒尺寸为3~5μm.显微硬度和耐磨性测试结果表明,该复合涂层显微维氏硬度高达1200MPa左右,复合涂层的耐磨性能比Ti6Al4V基体提高约20倍.     

激光熔覆CoCrNiMnTix高熵合金涂层组织及耐磨性能研究

目的 针对高铁制动盘等高速强力磨损的关键件,设计激光熔覆CoCrNiMnTix高熵合金涂层,提高表面的硬度和耐磨性。方法 采用激光熔覆技术在Q235钢表面制备CoCrNiMnTix高熵合金涂层,利用XRD和SEM对涂层微观组织进行表征,通过显微硬度计和纳米压痕仪测试涂层硬度,运用摩擦磨损试验机和三维形貌仪研究涂层的摩擦磨损性能。结果 在激光熔覆CoCrNiMnTix涂层中,随着Ti含量的增加,涂层物相由单一的FCC相转变为FCC+Laves相。由于固溶强化以及Laves相含量增多,涂层的显微硬度不断提高,CoCrMnNiTi硬度达到523HV0.1,最高纳米硬度达到6.91 GPa。CoCrNiMnTix系涂层的弹性模量大小相近。随着Ti含量的增加,涂层的耐磨性呈现升高趋势,当Ti的摩尔分数增加至0.75时,涂层具有最好的耐磨性,但进一步增加Ti含量时,由于脆硬性的Laves相逐渐增多,磨损形式由低Ti含量时的粘着磨损逐渐转变为高Ti含量时的磨粒磨损,使涂层耐磨性能下降。结论 激光熔覆CoCrMnNiTix涂层可以显著提高基体的耐磨性,Ti的摩尔分数为0.75时,在FCC基体中形成了少量Laves相,既提高硬度,又实现强韧配合,涂层表现出最佳的耐磨损性能。     

钛合金表面等离子弧熔覆原位自生镍基耐磨涂层的制备及微观结构表征

目的 在钛合金表面制备陶瓷相增强复合耐磨涂层。方法 采用等离子弧熔覆技术,在Ti6Al4V钛合金表面制备了原位自生TiB2、TiC、CrB陶瓷相增强镍基耐磨涂层。采用X射线衍射仪、扫描电镜、能谱仪检测了涂层的物相组成、组织组织以及微区化学成分,采用显微硬度计测试了涂层的硬度。结果 涂层靠近熔合线区域由Ni-Ti树枝晶及枝晶间的共晶组成,在涂层的中上部,大量原位增强相分布于镍基固溶体基体之中。在熔覆过程中,钛合金基材中的Ti元素同熔覆粉末中的B、C元素发生原位冶金反应形成TiB2、TiC增强相,CrB增强相为Ni基熔覆粉末中Cr、B元素反应形成,增强相的形态由各自的晶体结构及熔池凝固热力学与动力学条件决定。涂层的显微硬度得到显著提高,最高达1037HV0.2。结论 采用等离子弧熔覆技术,利用熔池内Ni-Cr-Ti-B-C合金体系的原位冶金反应,可以在钛合金表面制备原位自生TiB2、TiC、CrB增强镍基复合耐磨涂层。同Ti6Al4V基材相比,由于涂层具有大量增强相分布于镍基固溶体的组织特征,其显微硬度得到了显著提高。     

TC4合金表面氩弧熔覆TiCp/Ti基复合涂层组织及耐磨性

利用氩弧熔覆技术在TC4合金表面制备出TiC增强的Ti基复合涂层。利用SEM、XRD和EDS分析了熔覆涂层的显微组织;利用显微硬度仪测试了复合涂层的显微硬度;利用摩擦磨损试验机测试了涂层在室温干滑动磨损条件下的耐磨性能。结果表明:氩弧熔覆涂层组织均匀致密,熔覆层与基体呈冶金结合,涂层中有大量的TiC树枝晶和条块状TiC颗粒;复合涂层明显改善了TC4合金的表面硬度,HV平均硬度可达9GPa;复合涂层室温干滑动磨损机制为磨粒磨损和轻微粘着磨损。     

La2O3含量对激光熔覆TiB/Ti涂层显微结构的影响

目的 改善钛合金表面激光熔覆复合涂层的组织结构,提高钛合金的硬度,使其在相应领域得到更广泛的应用.方法 采用激光熔覆快速非平衡合成方法 制备原位反应合成L2O3-TiB增强钛基复合涂层.用L2O3、Ti和B的混合粉末在Ti-6Al-4V基体表面激光熔覆制备L2O3-TiB/Ti复合涂层,并对其进行XRD物相分析、SEM显微结构观察及显微硬度分析.结果 添加不同含量的L2O3的激光熔覆钛合金复合涂层均与基体较好的结合,涂层中均只有α-Ti和TiB两种物相.随L2O3含量的增加,激光熔覆复合涂层中的增强相TiB的形貌越均匀细小,添加不同含量的L2O3的激光熔覆复合涂层的硬度值约为基体材料的2~3倍,添加质量分数为3%的L2O3的激光熔覆复合涂层硬度最高,其显微硬度值大约为1300HV.结论 添加稀土氧化物L2O3后制备的激光熔覆钛合金复合涂层与基体结合良好,稀土元素的添加使涂层组织细化,硬度得到了明显提高.     

TC4合金表面熔覆石墨烯增强钛基复合涂层的组织及性能

目的 通过氩弧熔覆技术在TC4合金表面制备石墨烯增强钛基复合涂层,以改善其耐磨性能.方法 将钛粉和石墨烯在球磨机中充分混合.将混合后的粉末涂覆于TC4合金表面,采用氩弧熔覆技术将预涂覆粉末熔化,制备出陶瓷颗粒增强钛基熔覆层.采用X射线衍射分析仪分析涂层的物相,利用光学显微镜、扫描电子显微镜分析熔覆层中颗粒相的组成及分布.采用显微维氏硬度仪和摩擦磨损试验机,测试熔覆层的显微硬度和磨损性能.结果 熔覆层厚度可达1 mm,且表面及横截面没有气孔、裂纹等缺陷产生,物相主要包括TiC和 α-Ti.熔覆层中不同区域的组织存在差别,涂层的中上部组织主要为树枝晶,底部组织中树枝晶逐渐减少.熔覆层与基体呈冶金结合,组织致密.增强相TiC以颗粒状和花瓣状形式存在.石墨烯增强钛基复合涂层的显微硬度高达845.4HV.在相同磨损条件下,TC4合金基体与熔覆层的磨损量分别是0.153 g和0.0123 g,熔覆层的磨损量明显降低.涂层的磨损机制主要是磨粒磨损.结论 与TC4合金基体对比,熔覆层的显微硬度提高约2.5倍,耐磨性提高12倍.氩弧熔覆原位自生TiC陶瓷颗粒增强钛基熔覆层可显著提高TC4合金表面的耐磨性.     

TC4合金氩弧熔覆Ni60+B4C复合涂层组织及耐磨性

利用氩弧熔覆技术在TC4合金表面成功制备出TiC、TiB、TiB2增强Ti基复合涂层.利用SEM、XRD和EDS分析了熔覆涂层的显微组织;利用显微硬度仪测试了复合涂层的显微硬度;利用摩擦磨损试验机测试了涂层在室温干滑动磨损条件下的耐磨性能.结果表明:氩弧熔覆涂层组织均匀致密,熔覆层与基体呈冶金结合,TC4合金表面有颗粒状TiC、粗大棒状相TiB2、细小棒状相TiB生成;复合涂层明显改善了TC4合金的表面硬度,涂层的最高显微硬度可达1300 HV0.2;复合涂层在室温干滑动磨损试验条件下具有优异的耐磨性,磨损机制主要是魔力磨损,其耐磨性较TC4合金基体提高近10倍.     

Effects of Post-weld Heat Treatment on Microstructure,Mechanical Properties and the Role of Weld Reinforcement in 2219 Aluminum Alloy TIG-Welded Joints

In as-welded state, each region of 2219 aluminum alloy TIG-welded joint shows diff erent microstructure and microhardness due to the diff erent welding heat cycles and the resulting evolution of second phases. After the post-weld heat treatment, both the amount and the size of the eutectic structure or θ phases decreased. Correspondingly, both the Cu content in α-Al matrix and the microhardness increased to a similar level in each region of the joint, and the tensile strength of the entire joint was greatly improved. Post-weld heat treatment played the role of solid solution strengthening and aging strengthening. After the post-weld heat treatment, the weld performance became similar to other regions, but weld reinforcements lost their reinforcing eff ect on the weld and their existence was more of an adverse eff ect. The joint without weld reinforcements after the post-weld heat treatment had the optimal tensile properties, and the specimens randomly crack in the weld zone.     

The First Phase of the SRIF Industrialized Base in ＂West Area＂ Has Been Put into Operation

After nearly two years＇ tense construction, the first phase of industrialized base of Shenyang Research Institute of Foundry （SRIF）, located at the Tiexi Casting and Forging Industrial Park in the west of Tiexi District, has now been completed and formally put into operation.     

新型的治疗阿尔茨海默氏症药物(1-二甲基磷酰基-2,2,2-三氯)-乙基-1-醇烟酸醋对体外神经细胞的作用

目的: 观察本实验室合成的一种治疗阿尔茨海默氏症(AD)的药物(1-二甲基磷酰基-2, 2, 2 -三氯)-乙基^-1-醇烟酸醋(NMF),对体外培养的皮层神经细胞活性的影响以及对海人藻酸(KA)所致的神经损伤的保护作用。方法: 采用体外培养皮层神经元的方法,解剖分离 15 d胚胎小鼠皮层神经细胞, 接种于 96孔板,48 h 后加药并培养 72 h,以 MIT 法 观察 NMF 对小鼠皮层神经细胞活性的影响;同时将接种于 24 孔板的细胞预先给予 NMF,d 3 时加或不加KA处理后,以台盼蓝染色鉴别并计数死、活细胞,可得出细胞的存活率。结果: NMF 明显促进胎鼠皮层神经元活性,其中 NMF1、0. 1、10nmol·L^-1促进神经元活性增殖率分别高达 34.7%、37.4%、36. 7%, NMF 明显促进正常胎鼠皮层神经元存活卒,与对照组比较,10nmol·L^-1 NMF 对皮层神经元的存活率分别提高 39.3%、73.5%。 NMF能显著 对抗 KA 所致的神经元损伤,与 KA 损伤组相比, NMF0.1、10、10nmol·L^-1对损伤皮层神经元的保护率分别为 77.30%、80.10%、84.15%。结论: NMF 明 显促进胎鼠皮层神经元的洁性、提高正常皮层神经元,的存活卒,并能有效地保护KA所致的神经元损伤,提示 NMF 是一种很有潜力的治疗 AD 的药物。     

THERMODYNAMICS STUDY ON THE DECOMPOSITION OF CHROMITE WITH KOH

Institute of Process Engineering, Chinese Academy of Sciences, China, has proposed a method for oxidative leaching of chromite with potassium hydroxide. Understanding the mechanism of chromite decomposition, especially in the potassium hydroxide fusion, is important for the optimization of the operating parameters of the oxidative leaching process. A traditional thermodynamic method is proposed and the thermal decomposition and the reaction decomposition during the oxidative leaching of chromite with KOH and oxygen is discussed, which suggests that chromite is mainly destroyed by reactions with KOH and oxygen. Meanwhile, equilibrium of the main reactions of the above process was calculated at different temperatures and oxygen partial pressures. The stable zones of productions, namely, K2CrO4 and Fe2O3, increase with the decrease of temperature, which indicates that higher temperature is not beneficial to thermodynamic reactions. In addition, a comparison of the general alkali methods is carried out, and it is concluded that the KOH leaching process is thermodynamically superior to the conventional chromate production process.     

INFLUENCE OF HEAT TREATMENT ON DAMPING BEHAVIOUR OF THE MAGNESIUM WROUGHT ALLOY AZ61

The effect of isochronal heat treatments for 1h on variation of damping, hardness and microstructural change of the magnesium wrought alloy AZ61 was investigated. Damping and hardness behaviour could be attributed to the evolution of precipitation process. The influence of precipitation on damping behaviour was explained in the framework of the dislocation string model of Granato and Lücke.     

Theoretical Analysis for the Motion and Temperature of Melt Droplets in Spray Degassing Process

The motion of melt droplets in spray degassing process was analyzed theoretically. The height of the treatment tank in spray degassing process could be determined by the results of theoretical calculation of motion of melt droplets. To know whether the melt droplets would solidify during spraying process, the balance temperature of melt droplets was also theoretically analyzed. Then proof experiments for theoretical results about temperature of melt droplets were carried. In comparison, the experimental results were nearly similar to the calculation results.     

Growth Kinetics of Single Inclusion Particle in Molten Melts

On the basis of the single-particle framework, a new theory on inclusion growth in metallurgical melts is developed to study the kinetics of inclusion growth on account of reaction and collision. The studies show that the early growth of inclusion depends on reaction growth and Brawnian motion collision, and where the former is decisive, the late growth depends on turbulence collision and Stokes＇ collision, and where the former is dominant; collision growth is very quick during the smelting process, lessened in the refining process, but nearly negligible in the continuous casting process.     

An Easy Way to Quantify the Adhesion Energy of Nanostructured Cu/X(X=Cr,Ta,Mo,Nb,Zr) Multilayer Films Adherent to Polyimide Substrates

An approach based on film buckling under simple uniaxial tensile testing was utilized in this paper to quantitatively estimate the interfacial energy of the nanostructured multilayer films(NMFs) adherent to flexible substrates. The interfacial energies of polyimide-supported NMFs are determined to be *5.0 J/m2 for Cu/Cr, *4.1 J/m2 for Cu/Ta,*2.8 J/m2 for Cu/Mo, *1.1 J/m2 for Cu/Nb, and *1.2 J/m2 for Cu/Zr NMFs. Furthermore, a linear relationship between the adhesion energy and the interfacial shear strength is clearly demonstrated for the Cu-based NMFs, which is highly indicative of the applicability and reliability of the modified models.     

High-Speed Friction Stir Welding of SiC_p/Al–Mg–Si–Cu Composite

A 17 vol% SiCp/Al–Mg–Si–Cu composite plate with a thickness of 3 mm was successfully friction stir welded(FSWed) at a very high welding speed of 2000 mm/min for the first time. Microstructural observation indicated that the coarsening of the precipitates was greatly inhibited in the heat-affected zone of the FSW joint at high welding speed, due to the significantly reduced peak temperature and duration at high temperature. Therefore, prominent enhancement of the hardness was achieved at the lowest hardness zone of the FSW joint at this high welding speed, which was similar to that of the nugget zone. Furthermore, the ultimate tensile strength of the joint was as high as 369 MPa, which was much higher than that obtained at low welding speed of 100 mm/min(298 MPa). This study provides an effective method to weld aluminum matrix composite with superior quality and high welding efficiency.     

Three-Dimensional Growth of Coherent Ferrite in Austenite: A Molecular Dynamics Study

Coherent second phase often exhibits anisotropic morphology with specifi c orientations with respect to both the second and the matrix phases. As a key feature of microstructure, the morphology of the coherent particles is essential for understanding the second-phase strengthening eff ect in various industrial alloys. This letter reports anisotropic growth of coherent ferrite from austenite matrix in pure iron based on molecular dynamics simulation. We found that the ferrite grain tends to grow into an elongated plate-like shape, independent of its initial confi guration. The fi nal shape of the ferrite is closely related to the misfi t between the two phases, with the longest direction and the broad facet of the plate being, respectively, consistent with the best matching direction and the best matching plane calculated via the Burgers vector content(BVC) method. The strain energy calculation in the framework of Eshelby's inclusion theory verifi es that the simulated orientation of the coherent ferrite is energetically favorable. It is anticipated that the BVC method will be applicable in analysis of anisotropic growth and morphology of coherent second phase in other phase transformation systems.