In situ preparation of SiC/Si3N4-NW composite powders by combustion synthesis

Large-scale composite powders containing silicon carbide (SiC) particles and silicon nitride nanowires (Si₃N₄-NWs) were synthesized in situ by combustion synthesis (CS). In this process, a mixture of silicon, carbon black, polytetrafluoroethylene (PTFE) and a small amount of iron powders was used as the precursor. The products were characterized by XRD, SEM, EDS and TEM. The particles are equiaxed with diameters in the micron range, and the in situ formed nanowires are straight with uniform diameters of 20-350 nm and lengths of tens of microns. The Si₃N₄-NWs are characterized to be α-phase single crystals grown along the [1 0 1] or [1 0 0] direction. VLS and SLGS processes are proposed as the growth mechanisms of the nanowires. The as-synthesized powders have great potential for use in the preparation of high-performance SiC/Si₃N₄-NW composites.     

Biomorphic silicon/silicon carbide ceramics from birch powder

A novel process has been developed for the fabrication of biomorphic silicon/silicon carbide (Si/SiC) ceramics from birch powder. Fine birch powder was hot-pressed to obtain pre-templates, which were subsequently carbonized to acquire carbon templates, and these were then converted into biomorphic Si/SiC ceramics by liquid silicon infiltration at 1550 °C. The prepared ceramics are characterized by homogeneous microstructure, high density, and superior mechanical properties compared to biomorphic Si/SiC ceramics from birch blocks. Their maximum density has been measured as 3.01 g/cm³. The microstructure is similar to that of conventional reaction-bonded silicon carbide. The Vicker's hardness, flexural strength, elastic modulus, and fracture toughness of the biomorphic Si/SiC were 19.6 ± 2.2 GPa, 388 ± 36 MPa, 364 ± 22 GPa, and 3.5 ± 0.3 MPa m^1/2, respectively. The outstanding mechanical properties of the biomorphic Si/SiC ceramics are assessed to derive from the improved uniform microstructure of the pre-templates made from birch powder.     

Reaction sintering of colloidal processed mixtures of sub-micrometric alumina and nano-titania

The fabrication of composites formed by alumina grains (95 vol%) in the micrometer size range and aluminium titanate nanoparticles (5 vol%) by reaction sintering of alumina (Al₂O₃) and titania (TiO₂) is investigated. The green bodies were constituted by mixtures of sub-micrometric alumina and nano-titania obtained from freeze-drying homogeneous water based suspensions, and pressing the powders. The optimization of the colloidal processing variables was performed using the viscosity of the suspensions as control parameter. Different one step and two step sintering schedules using as maximum dwell temperatures 1300 and 1400 °C were established from dynamic sintering experiments. Specimens cooled at 5 °C/min as well as quenched specimens were prepared and characterized in terms of crystalline phases, by X-ray diffraction, and microstructure by scanning electron microscopy of fracture surfaces.Even though homogeneous final materials were obtained in all cases, full reaction was obtained only in materials treated at 1400 °C. The microstructure of the composites obtained by quenching was formed by an alumina matrix with bimodal grain size distribution and submicrometric aluminium titanate grains located inside the largest alumina grains and at triple points. However a cooling rate of 5 °C/min led to significant decomposition of aluminium titanate. This fact is attributed to the small size of the particles and the effect of the alumina surrounding matrix.     

Erosion behavior of SiC–WC composites

Dense silicon carbide (SiC) ceramics were prepared with 0, 10, 30 or 50 wt% WC particles by hot pressing powder mixtures of SiC, WC and oxide additives at 1800 °C for 1 h under a pressure of 40 MPa in an Ar atmosphere. Effects of alumina or SiC erodent particles and the WC content on the erosion performance of sintered SiC–WC composites were assessed. Microstructures of the sintered composites consisted of WC particles distributed in the equi-axed grain structure of SiC. Fracture surfaces showed a mixed mode of fracture, with a large extent of transgranular fracture observed in SiC ceramics prepared with 30 wt% WC. Crack bridging by WC enhanced toughening of the SiC ceramics. A maximum fracture toughness of 6.7 MPa*m^1/2 was observed for the SiC ceramics with 50 wt% WC, whereas a high hardness of 26 GPa was obtained for the SiC ceramics with 30 wt% WC. When eroded at normal incidence, two orders of magnitude less erosion occurred when SiC–WC composites were eroded by alumina particles than that eroded by SiC particles. The erosion rate of the composites increased with increasing angle of SiC particle impingement from 30° to 90°, and decreased with WC reinforcement up to 30 wt%. A minimum erosion wear rate of 6.6 mm³/kg was obtained for SiC–30 wt% WC composites. Effects of mechanical properties and microstructure on erosion of the sintered SiC–WC composites are discussed, and the dominant wear mechanisms are also elucidated.     

Pressureless sintered Al2O3–SiC nanocomposites

Al₂O₃ + 5 vol% SiC composite ceramics were prepared via a conventional powder processing route followed by pressureless sintering. Commercially available Al₂O₃ and SiC powders were milled together in an aqueous suspension. The slurry was freeze granulated, and green bodies were obtained by cold isostatic pressing of the granules. Pressureless sintering was carried out in a nitrogen atmosphere at 1750 and 1780 °C. Near full density (>99%) was achieved at 1780 °C. Densification at the lower sintering temperature was promoted by smaller additions of MgO. Vickers hardness and indentation fracture toughness varied around 18 GPa and 2.3 MPa m^1/2 after sintering at 1780 °C. Transmission electron microscopy revealed that the SiC particles were located predominantly to the interior of the matrix grains and well distributed throughout the composite microstructures. The intragranular particles had sizes in the range 50–200 nm while the intergranular particles were larger, typically 200–500 nm in diameter.     

Sintering of Al2O3-SiC composite from sol-gel method with MgO, TiO2 and Y2O3 addition

Al₂O₃-SiC composite ceramics were prepared by pressureless sintering with and without the addition of MgO, TiO₂ and Y₂O₃ as sintering aids. The effects of these compositional variables on final density and hardness were investigated. In the present article at first α-Al₂O₃ and β-SiC nano powders have been synthesized by sol-gel method separately by using AlCl₃, TEOS and saccharose as precursors. Pressureless sintering was carried out in nitrogen atmosphere at 1600 °C and 1630 °C. The addition of 5 vol.% SiC to Al₂O₃ hindered densification. In contrast, the addition of nano MgO and nano TiO₂ to Al₂O₃-5 vol.% SiC composites improved densification but Y₂O₃ did not have positive effect on sintering. Maximum density (97%) was achieved at 1630 °C. Vickers hardness was 17.7 GPa after sintering at 1630 °C. SEM revealed that the SiC particles were well distributed throughout the composite microstructures. The precursors and the resultant powders were characterized by XRD, STA and SEM.     

Investigation of the effect of ZrO2 and ZrO2/Al2O3 additions on the hot-pressing and properties of equimolecular mixtures of α- and β-Si3N4

In this work, hot-pressing of equimolecular mixtures of α- and β-Si₃N₄ was performed with addition of different amounts of sintering additives selected in the ZrO₂–Al₂O₃ system. Phase composition and microstructure of the hot-pressed samples was investigated. Densification behavior, mechanical and thermal properties were studied and explained based on the microstructure and phase composition. The optimum mixture from the ZrO₂–Al₂O₃ system for hot-pressing of silicon nitride to give high density materials was determined. Near fully dense silicon nitride materials were obtained only with the additions of zirconia and alumina. The liquid phase formed in the zirconia and alumina mixtures is important for effective hot-pressing. Based on these results, we conclude that pure zirconia is not an effective sintering additive. Selected mechanical and thermal properties of these materials are also presented. Hot-pressed Si₃N₄ ceramics, using mixtures from of ZrO₂/Al₂O₃ as additives, gave fracture toughness, K_IC, in the range of 3.7–6.2 MPa m^1/2 and Vicker hardness values in the range of 6–12 GPa. These properties compare well with currently available high performance silicon nitride ceramics. We also report on interesting thermal expansion behavior of these materials including negative thermal expansion coefficients for a few compositions.     

Mechanical properties of SiCp/Al2O3 ceramic matrix composites prepared by directed oxidation of an aluminum alloy

Silicon carbide particulate reinforced alumina matrix composites were fabricated using DIrected Metal OXidation (DIMOX) process. Continuous oxidation of an Al-Si-Mg-Zn alloy with appropriate dopants along with a preform of silicon carbide has led to the formation of alumina matrix surrounding silicon carbide particulates. SiC_p/Al₂O₃ ceramic matrix composites fabricated by the DIMOX process, possess enhanced mechanical properties such as flexural strength, fracture toughness and wear resistance, all at an affordable cost of fabrication. SiC_p/Al₂O₃ matrix composites were investigated for mechanical properties such as flexural strength, fracture toughness and hardness; the composite specimens were evaluated using standard procedures recommended by the ASTM. The SiC_p/Al₂O₃ ceramic matrix composites with SiC volume fractions from 0.35 to 0.43 were found to possess average bend strength in range 158-230 MPa and fracture toughness was found to be in range of 5.61-4.01 MPa√m. The specimen fractured under three-point loading as observed under scanning electron microscope was found to fail in brittle manner being the dominant mode. Further the composites were found to possess lower levels of porosity, among those prepared by DIMOX process.     

Refined measurements of indentation fracture resistance of alumina using powerful optical microscopy

A round-robin of the indentation fracture (IF) method using two alumina ceramics was performed in 12 laboratories to confirm the significantly improved reproducibility of indentation fracture resistance K_IFR, using powerful optical microscopy. Powerful optical microscopy with both an objective lens of 40× or 50× and a traveling stage was employed to reduce the error in reading crack length. Indentations at 98 N for the two samples had moderate between-laboratory standard deviations of 0.3 and 0.2 MPa m^1/2 for K_IFR of 4.3 and 3.6 MPa m^1/2, respectively, which indicates the effectiveness of this measurement technique to improve the reliability of the IF method. The deviations of the grand average K_IFR reported by the laboratories from those re-measured by the authors using the returned samples were only ca. 0.4 MPa m^1/2, which was attributed to the slight misreading of the crack length by the participant laboratories. Thus, the reliability of the IF method seems reasonable by this advanced approach because our recent round-robins, together with this study, have confirmed that the precision for the three major structural ceramics, SiC, Si₃N₄ and alumina, could meet the necessary condition of reproducibility.     

Microstructure and mechanical properties of silicon carbide processed by Spark Plasma Sintering (SPS)

The unique combination of SiC properties opens the ways for a wide range of SiC-based industrial applications. Dense silicon carbide bodies (3.18±0.01 g/cm³) were obtained by an SPS treatment at 2050 °C for 10 min using a heating rate of 400 °C/min, under an applied pressure of 69 MPa. The microstructure consists of fine, equiaxed grains with an average grain size of 1.29±0.65 μm. TEM analysis showed the presence of nano-size particles at the grain boundaries and at the triple-junctions, formed mainly from the impurities present in the starting silicon carbide powder. The HRTEM examination revealed high angle and clean grain boundaries. The measured static mechanical properties (H_V=32 GPa, E=440 GPa, σ_b=490 MPa and K_C 6.8 MPa m^0.5) and the Hugoniot Elastic Limit (HEL=18 GPa) are higher than those of hot-pressed silicon carbide samples.     

Silicon carbide particle reinforced mullite composite foams

Silicon carbide particle reinforced mullite composite foams were produced by the polymer replica method using alumina and kaolin to form in situ mullite matrix. Up to 20 wt.% silicon carbide particles (SiCp) were added to aqueous ceramic slurry to explore its effect on the rheological behaviour of ceramic slurries and also properties of as sintered products. By means of solid loading optimisation and sintering enhancement by silicon carbide, mullite based ceramic composite foams of higher strength were obtained. The strength of the as sintered foams was found to depend greatly on the phase composition, relative density of the structures and the amount of SiCp addition. By studying the effect of the additive concentration, on the mechanical properties of the ceramic matrix, it is found that the optimal silicon carbide addition is 20 wt.%.     

Microstructure and phase evolution of alumina-spinel self-flowing refractory castables containing nano-alumina particles

The microstructure and phase composition of alumina-spinel self-flowing refractory castables added with nano-alumina particles at different temperatures are investigated. The physical and mechanical properties of these refractory castables are studied. The results show that the addition of nano-alumina has a great effect on the physical and mechanical properties of these refractory castables. With the increase of nano-alumina content in the castable composition, the mechanical strength is considerably increased at various temperatures. It is shown that nano-alumina particles can affect formed phases after firing. The platy crystals of CA₆ are detected inside the grain boundaries of tabular alumina and spinel grains in samples fired at 1500 °C. CA₆ phase can be formed at lower temperatures (1300 °C) with the addition of nano-alumina particles. As a result of using nanometer-sized alumina particles with high surface area, the solid phase sintering of the nano-sized particles and CA₆ formation can occur at lower temperatures.     

Diffusion bonding of alumina using interlayer of mixed hydride nano powders

In this study, mixed hydride/alanate nano powders in the Al–Mg system were used as the interlayer for low temperature diffusion bonding of dense alumina parts. Decomposition of hydride nanopowders at bonding temperatures in-situ formed metals and alloys nano particles with oxide free surfaces and high sinter-ability in the interlayer. Nano powders sintering behavior in the interlayer and formation of compounds in the reaction layer during diffusion bonding were studied. Mixture of 50–50 M ratio of AlH₃ and Mg(AlH₄)₂, as the interlayer improved bond strength of the joints. Diffusion bonding products were formed in the MgO–Al₂O₃ spinel system with different stoichiometries. Bond strength improved up to 202 MPa by induction hot pressing alumina parts at low bonding temperature of 400 °C under pressure of 20 MPa during 30 min bonding period.     

Fabrication and characteristic of non-oxide fiber tow reinforced silicon nitride matrix composites by low temperature CVI process

Non-oxide fiber tow reinforced silicon nitride matrix composite was fabricated by low temperature CVI process with PyC as interphase. The tensile strength of the C and SiC fiber tow composites were 547 MPa and 740 MPa, respectively. The difference in tensile strength was analyzed based on the length, amount of pull-out fiber and also interface bonding. The infiltration uniformity of CVI silicon nitride (SiN) matrix within SiC fiber tow was comparable with that of CVI SiC matrix. These results suggested that the low temperature CVI process is suitable for the fabrication of fiber reinforced SiN matrix composites with proper interface bonding and high strength.     

Paper derived SiC–Si3N4 ceramics for high temperature applications

Biomorphic Si₃N₄–SiC ceramics have been produced by chemical vapour infiltration and reaction technique (CVI-R) using paper preforms as template. The paper consisting mainly of cellulose fibres was first carbonized by pyrolysis in inert atmosphere to obtain carbon bio-template, which was infiltrated with methyltrichlorosilane (MTS) in excess of hydrogen depositing a silicon rich silicon carbide (Si/SiC) layer onto the carbon fibres. Finally, after thermal treatment of this Si/SiC precursor ceramic in nitrogen-containing atmosphere (N₂ or N₂/H₂), in the temperature range of 1300–1450 °C SiC–Si₃N₄ ceramics were obtained by reaction bonding silicon nitride (RBSN) process. They were mainly composed of SiC containing α-Si₃N₄ and/or β-Si₃N₄ phases depending on the nitridation conditions. The SiC–Si₃N₄ ceramics have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and Raman spectroscopy. Thermal gravimetric analysis (TGA) was applied for the determination of the residual carbon as well as for the evaluation of the oxidation behaviour of the ceramics under cyclic conditions. The bending strength of the biomorphic ceramics was related to their different microstructures depending on the nitridation conditions.     

Combustion synthesis of (Ti1−xNbx)2AlC solid solutions from elemental and Nb2O5/Al4C3-containing powder compacts

Preparation of the (Ti_1−xNb_x)₂AlC solid solution (formed from the M_n+1AX_n or MAX carbides, where n = 1, 2, or 3, M is an early transition metal, A is an A-group element, and X is C) with x = 0.2-0.8 was investigated by self-propagating high-temperature synthesis (SHS). Nearly single-phase (Ti,Nb)₂AlC was produced through direct combustion of constituent elements. Due to the decrease of reaction exothermicity, the combustion temperature and reaction front velocity decreased with increasing Nb content of (Ti_1−xNb_x)₂AlC formed from the elemental powder compacts. In addition, the samples composed of Ti, Al, Nb₂O₅, and Al₄C₃ were adopted for the in situ formation of Al₂O₃-added (Ti,Nb)₂AlC. The SHS process of the Nb₂O₅/Al₄C₃-containing sample involved aluminothermic reduction of Nb₂O₅, which not only enhanced the reaction exothermicity but also facilitated the evolution of (Ti,Nb)₂AlC. Based upon the XRD analysis, two intermediates, TiC and Nb₂Al, were detected in the (Ti,Nb)₂AlC/Al₂O₃ composite and their amounts were reduced by increasing the extent of thermite reduction involved in the SHS process. The laminated microstructure characteristic of the MAX carbide was observed for both monolithic and Al₂O₃-added (Ti,Nb)₂AlC solid solutions synthesized in this study.     

Preparation and characterization of SiO2/polydopamine/Ag nanocomposites with long-term antibacterial activity

Silver nanoparticles (Ag NPs) with diameter of approximately 10 nm were prepared by the reduction of silver nitrate using green synthesis, an eco-friendly approach. The synthesized Ag NPs were homogeneously deposited on silicon dioxide (SiO₂) particles modified with dopamine, leading to the formation of SiO₂/polydopamine (PD)/Ag nanocomposites (NCs) with a core–shell–satellite structure investigated by transmission electron microscopy. The Ag content of SiO₂/PD/Ag NCs determined by inductively coupled plasma optical emission spectrometry was approximately 5.92 wt%. The antibacterial properties of both Ag NPs and SiO₂/PD/Ag NCs against Vibrio natriegens (V. natriegens) and Erythrobacter pelagi sp. nov. (E. pelagi) were investigated by bacterial growth curves and inhibition zone. Compared to Ag NPs, the SiO₂/PD/Ag NCs exhibited superior long-term antibacterial activity, attributed to its controlled release of Ag⁺ ions.     

The wetting behaviour and reaction kinetics in diamond–silicon carbide systems

The wetting behaviour of silicon on diamond and the interaction of diamond with molten silicon were investigated. It was found that diamond is well wetted by molten silicon reaching a contact angle of about 20° after melting. The wetting is caused by the rapid formation of a SiC interlayer by nucleation of silicon carbide grains on the surface of the diamond. Investigations of the interaction of silicon with CVD diamond, using SEM, showed that the initial rate of SiC formation is very fast and is significantly reduced after the formation of a 4–6 μm thick dense SiC interlayer. At that stage further growth is likely to be controlled by the diffusion of Si and C through the grain boundaries of the silicon carbide interlayer. The results were compared with the interaction of silicon with glassy carbon.     

Effect of SiC ceramics on thermoelectric properties of SiC/SnSe composites for solid-state thermoelectric applications

Tin selenide (SnSe) based thermoelectric materials with varying amounts of embedded silicon carbide (SiC) particles were fabricated, and their thermoelectric properties were investigated. The SiC particles were evenly distributed in the SnSe matrix, thereby leading to the formation of the SiC/SnSe composite samples. The introduction of SiC into the SnSe matrix improved the power factors, owing mainly to an increase in the Seebeck coefficient, and a decrease in the thermal conductivity arising from the formation of phonon-scattering centers. Consequently, a ZT of 0.125 (at 300 K) was obtained for the SiC/SnSe composite with a SiC content of 1 wt%; this value was larger than that of the pristine SnSe. The results of this study indicate that the introduction of SiC particles into the SnSe matrix constitutes an efficient strategy for achieving thermoelectric enhancement for solid-state applications.     

Investigations of SiC aggregates oxidation: Influence on SiC castables refractories life time at high temperature

This paper reports results concerning the oxidation of silicon carbide of pure SiC powder (98% of SiC) and the oxidation of two silicon carbide castables, used in waste-to-energy plants (WTE), and containing 60% and 85% of SiC, respectively. The investigated temperature range (800-1200 °C) corresponds to typical service conditions in WTE. Thanks to thermogravimetric and thermal expansion tests, kinetics of oxidation of the powder of SiC and of the castables has been investigated. According to these tests, several important points have been underlined. Firstly, the oxidation of SiC aggregates has a high influence on the thermal expansion and on the weight gain of SiC castables. Secondly, the grain size distribution of SiC aggregates within castables plays a dominating role (especially enhanced for the fine particles) in castable expansion behaviour induced by oxidation. This is a key point according to the evolution of thermal expansion of such materials.