巯基烯烃点击反应制备超疏水聚偏氟乙烯中空纤维膜及其加湿性能

为更好地发挥中空纤维膜加湿器的加湿作用,提高加湿性能,提出对中空纤维膜进行超疏水改性.利用溶胶凝胶法制备二氧化硅(SiO2),八乙烯基笼型倍半硅氧烷(OV-POSS)与巯基-聚二甲基硅氧烷(PDMS-SH)通过巯基烯烃点击反应形成POSS-S-PDMS聚合物,利用涂覆法将其涂覆在聚偏氟乙烯(PVDF)中空纤维膜表面.在膜表面与涂层、涂层与涂层之间均利用化学键连接以提高涂层的牢固度,制备了一种具有SiO2-PDMS-POSS稳定性涂层的超疏水复合膜.研究了光引发剂的质量分数、二氧化硅粒径影响因素对复合膜的影响,并对复合膜进行了表征.最终制备的复合膜接触角达到156°,加湿效率由48％提高为58.32％.     

脱硫用PVDF膜的结构调控与性能研究

以聚偏氟乙烯(PVDF)为膜材料,二甲基乙酰胺(DMAc)为溶剂,采用浸没沉淀相转化法制膜,研究了亲/疏水性的添加剂对PVDF膜结构、接触角及气通量的影响;采用含氟表面活性剂 Zonyl 8740对PVDF膜进行疏水改性,通过ATR-FTIR、FE-SEM、接触角等对膜表征,并进行脱硫性能评价.结果表明,疏水性添加剂使PVDF膜表面水接触角提高,添加剂种类对膜气通量有明显影响,在20℃、0.01 MPa实验条件下,PVDF膜最大气通量为85.6 m3/(m2·h),Zonyl 8740涂覆改性后PVDF膜表面疏水性提高,水接触角可达到133.5°,二氧化硫脱除率可达到81.3％.     

聚偏氟乙烯超疏水分离膜的制备

采用溶液涂覆-浸没相分离法对聚偏氟乙烯膜(PVDF)进行表面复合改性,制备了超疏水分离膜。初步考察了涂覆液中PVDF固含量和涂覆条件(浸泡时间、预蒸发时间、凝固浴组成和凝固浴温度)对复合膜疏水性能的影响。实验结果表明,当涂覆液中PVDF含量为1.88%(质量分数)时,膜丝有最大接触角136°;复合膜的接触角随浸泡时间的延长呈现先增大后减小的趋势,当浸泡时间为40s时,接触角最大,达到133°;在较短时间内(0～5s),预蒸发时间对复合膜的接触角影响不大;复合膜的接触角随着凝固浴中DMAc含量的增加而逐渐减小,随着凝固浴温度的增大而增大,当凝固浴温度为65℃时,膜表面的接触角增至153°。     

聚偏氟乙烯膜的超疏水改性研究

为提高疏水膜的疏水性能,使其可在膜蒸馏、膜吸收等领域有更广泛的应用.采用溶液相转移法制备超疏水性聚偏氟乙烯(PVDF)分离膜,考察了铸膜液中PVDF和非溶剂(低分子二醇类化合物PG)的浓度对膜润湿性能的影响.结果表明,通过改变铸膜液中PVDF、PG的浓度,能使PVDF膜的表面静态接触角从75.1°提高到161.7°,滚动角仅为15.8°.还研究了PVDF复合膜的制备条件对膜润湿性能的影响,结果表明,在一定的非溶剂浓度范围,增加复合膜涂覆液中非溶剂PG的加入量,有利于得到较高的复合膜表面接触角,但膜丝在涂覆液中的浸泡时间也需要相应延长.当非溶剂PG的质量分数为39.1%、浸泡时间为50 s时,复合膜表面接触角达到了155°.     

高选择性PDMSP/VDF复合膜渗透汽化分离乙醇/水混合物

以聚偏氟乙烯( PVDF)为基膜、聚二甲基硅氧烷(PDMS)为选择层制备了PDMS/PVDF复合膜,应用于渗透汽化分离乙醇/水混合物.系统研究了膜交联温度、操作温度、物料浓度和膜下侧压力对乙醇/水混合物的渗透汽化分离性能的影响,发现经130℃交联的复合膜在温度为60℃时,对乙醇的分离因子为8.23,可将乙醇浓度从体积分...     

硅橡胶/PVDF中空纤维复合膜制备与膜蒸馏性能研究

采用溶液涂覆-固化法制备了硅橡胶/聚偏氟乙烯(PVDF)中空纤维复合膜,实验研究了涂覆次数、硅橡胶溶液浓度、涂覆温度和固化温度等对膜结构与性能的影响。初步探讨了复合膜在处理包含表面活性剂水体过程中膜蒸馏(MD)性能的稳定性。结果表明,利用溶液涂覆-固化的方法,涂覆3次可制得均匀、稳定的复合膜,膜表面的纯水接触角由78°(PVDF膜)提升到149°。在针对含有表面活性剂十二烷基苯磺酸钠(SDBS)料液的膜蒸馏处理过程中,原始PVDF膜在实验进行约20min发生亲水化泄漏;该复合膜在连续2h持续运行实验内,膜蒸馏通量保持在约36.6kg/(m~2·h),产水电导率约为16.0μS/cm。     

四乙基氢氧化铵改性聚偏氟乙烯接枝二氧化硅油水分离膜的研制

利用四乙基氢氧化铵(TEAH)和酸性高锰酸钾对聚偏氟乙烯(PVDF)粉体进行改性,得到含有羟基改性的PVDF,再将四氯化硅(Si Cl4)水解后的原硅酸通过分子内脱水缩合的方法接枝到改性PVDF骨架上,通过浸没沉淀相转移法制得聚偏氟乙烯接枝二氧化硅(PVDF-g-SiO_2)油水分离膜。研究了TEAH含量对PVDF粉体接枝二氧化硅(SiO_2)的接枝率和油水分离膜性能的影响,同时采用傅里叶变换红外光谱、扫描电镜-X射线能谱和视频光学接触角测量仪测试了膜的结构和表面接触角。结果表明,TEAH使PVDF脱去部分氟化氢(HF)产生碳碳双键,双键经酸性高锰酸钾(KMnO_4)氧化生成羟基,SiO_2接枝到改性的PVDF粉体,硅元素均匀地分散在分离膜中。PVDF粉体接枝SiO_2的接枝率随着TEAH的含量增加而升高,分离膜的水通量随接枝率的升高先增加后降低。TEAH质量分数为1.4%,分离膜的接触角降低到62.8°,膜中SiO_2的接枝率和水通量分别为6.25%、889.5 L/(m2·h),截留率和水通量恢复率分别达到94.3%和90.4%,衰减率为9.6%。     

四乙基氢氧化铵改性聚偏氟乙烯接枝二氧化硅油水分离膜的研制EI北大核心CSCD

利用四乙基氢氧化铵(TEAH)和酸性高锰酸钾对聚偏氟乙烯(PVDF)粉体进行改性,得到含有羟基改性的PVDF,再将四氯化硅(Si Cl4)水解后的原硅酸通过分子内脱水缩合的方法接枝到改性PVDF骨架上,通过浸没沉淀相转移法制得聚偏氟乙烯接枝二氧化硅(PVDF-g-SiO_2)油水分离膜。研究了TEAH含量对PVDF粉体接枝二氧化硅(SiO_2)的接枝率和油水分离膜性能的影响,同时采用傅里叶变换红外光谱、扫描电镜-X射线能谱和视频光学接触角测量仪测试了膜的结构和表面接触角。结果表明,TEAH使PVDF脱去部分氟化氢(HF)产生碳碳双键,双键经酸性高锰酸钾(KMnO_4)氧化生成羟基,SiO_2接枝到改性的PVDF粉体,硅元素均匀地分散在分离膜中。PVDF粉体接枝SiO_2的接枝率随着TEAH的含量增加而升高,分离膜的水通量随接枝率的升高先增加后降低。TEAH质量分数为1.4%,分离膜的接触角降低到62.8°,膜中SiO_2的接枝率和水通量分别为6.25%、889.5 L/(m2·h),截留率和水通量恢复率分别达到94.3%和90.4%,衰减率为9.6%。     

纳米粒子超疏水改性聚偏氟乙烯膜的研究

利用喷涂沉淀法对聚偏氟乙烯(PVDF)膜进行表面改性,考察了喷涂液中纳米粒子(NP)的浓度和纳米粒子与胶粘剂(PDMS)的质量比对聚偏氟乙烯改性膜性能的影响.测定了改性前后聚偏氟乙烯膜的表面接触角以及膜的结构变化,并研究了膜的抗润湿和抗污染性能.结果表明,当喷涂液中纳米粒子的质量浓度为1%,纳米粒子与胶粘剂的质量比为4:5时,膜表面接触角从102°提高到156°.在直接接触式膜蒸馏实验中,改性膜的抗润湿性能和抗污染性能均较改性前有较大的提高.     

填充纳米SiO2对聚偏氟乙烯膜性能的影响

聚偏氟乙烯(PVDF)是一种性能优良的膜材料,被广泛用于溶液的净化、分离、浓缩过程.但由于它的疏水性,膜在分离过程中极容易受到蛋白质等有机物的污染,会导致膜通量下降,使用寿命缩短.为提高膜的性能,将经过γ-氨丙基三乙氧基硅烷改性的纳米SiO2粒子填充到聚偏氟乙烯铸膜液中,通过溶胶-凝胶法制得复合膜,并对该膜的形貌、韧性、亲水性和中水处理的性能进行了表征.结果表明,改性的纳米SiO2能够在膜内均匀分散,使复合膜的韧性显著提高,在处理中水过程中纳米SiO2粒子与PVDF结合良好;膜的接触角由83°下降到41°,通量相对稳定,在0.1 MPa操作压力下通量维持在280 L/(m2.h),表明复合膜的耐污染能力大大增强.     

Production of calcium nitrate crystals via membrane distillation crystallization using polyvinylidene fluoride/sorbitan trioleate membranes

As an alternative to the energy-intensive evaporation-crystallization method, membrane distillation crystallization (MDC) was applied for the first time to obtain calcium nitrate crystals from its aqueous solution. Calcium nitrate solution was obtained through the reaction between calcium carbonate and nitric acid, and then it was concentrated in the membrane distillation (MD) process and further crystallized. The MD step was conducted using hydrophobic polyvinylidene fluoride (PVDF)/sorbitan trioleate (Span 85) membranes. Span 85 was incorporated into the membrane structure in various concentrations to improve the hydrophobicity of membranes, and the resultant membranes were characterized via different methods. In addition, the resultant calcium nitrate crystals were characterized by X-ray fluorescence (XRF) spectroscopy. The MDC results showed that the optimum amount of Span 85 in the polymeric solution was 4%, which led to the formation of a membrane with higher porosity (67.2%) and water contact angle (95.7°) compared to the neat PVDF membrane. The mentioned membrane exhibited the highest water flux in the MD process compared to the other membranes, and also it produced the highest amount of crystals due to its remarkably better performance in the MD step in terms of feed concentration.     

电纺制备聚丙烯腈/聚偏氟乙烯复合纤维膜及其空气过滤性能

以聚偏氟乙烯(PVDF)为芯层,聚丙烯腈(PAN)为皮层,通过同轴法静电纺丝技术制备PAN/PVDF纳米复合纤维膜。通过向纤维膜的皮层中加入纳米硅粉、气相白炭黑、硅溶胶三种不同的纳米粒子和改变皮芯层溶液挤出速度对PAN/PVDF纳米纤维膜进行结构优化。同时,采用BET、SEM、水接触角、纤维强度仪等对纤维膜的孔结构参数、表面形貌、亲水性、力学性能等进行研究。结果表明:在皮层中加入硅溶胶后的溶液导电能力达到32.90 μL/cm,PAN/PVDF纤维膜力学性能最好,纵向断裂强度达到13.02 MPa。含有硅溶胶的口罩布的品质因子达到0.0236,远大于纯聚丙烯(PP)无纺布的品质因子(0.0127),过滤性显著提高。      

新型五孔PVDF共混改性膜抗污染性能研究

观察新型五孔PVDF共混改性纤维膜SEM形貌特征,测量改性膜的接触角和临界通量,1#(PVDF/PMMA/TPU)、2#(PVDF/PMMA/PVC)共混改性膜分别在次临界和超临界通量下进行过滤实验.结果表明:PVDF共混改性膜具有优良的微观结构,且1#共混膜性能较好;1#共混膜的接触角比2#共混膜小;1#、2#共混膜的临界通量分别为10和14L/(m2.h);1#共混膜比2#共混膜抗污染性能好;次临界通量下共混膜的运行比超临界通量下的稳定.两种共混膜分别在次临界通量下采用单独超滤和混凝+超滤工艺处理某市地表水,得出混凝+超滤工艺处理效果较好,且1#共混膜比2#共混膜处理效果好.     

膜法海水提溴用PVDF中空纤维膜的研制

采用相转化法制备海水提溴用疏水性聚偏氟乙烯中空纤维膜,考察聚合物浓度、无机复合添加剂浓度、膜干燥方式及后处理方法对膜结构和性能的影响.结果表明,无机复合添加剂能有效提高膜机械性能,同时不影响膜疏水性;溶剂置换法不能完全避免膜收缩,从而直接影响膜孔结构和透气性能.物理后处理方法可显著提高膜透气性能,氮气通量为8.62 m3/(m2.h),孔隙率为63.31%,膜断裂强度可达到1.64 cN/Tex,膜断裂伸长率为79.10%.     

聚偏氟乙烯杂化微孔膜的疏水性研究

采用改进的水蒸气(或称水雾蒸气)诱导成膜的方法制备强疏水性的聚偏氟乙烯(PVDF)微孔膜.在制膜液中添加了正硅酸乙酯(TEOS),水蒸气中添加了碱后,制备的PVDF/Si杂化微孔膜的疏水性更强,水接触角得到较大提高.实验初步考察了TEOS的浓度、环境相对湿度、蒸汽中凝胶时间和蒸汽中碱的浓度对膜表面接触角的影响.结果表明,在一定范围内,膜上表面的接触角随TEOS的浓度、相对湿度和蒸汽中凝胶时间的增加而增大.扫描电镜(SEM)和原子力显微镜(AFM)照片显示,改进的蒸汽诱导法形成的杂化膜上表面无致密皮层,呈网状多孔结构并附着微米级的球形颗粒,且蒸汽中适宜的碱浓度有利于球状颗粒的形成和长大;断面呈对称的海绵状结构.     

添加剂对聚丙烯腈膜结构和性能的影响

采用相转化法制备聚丙烯腈膜,分别以高分子聚乙烯吡咯烷酮(PVP-K30和PVP-K90)、聚乙二醇(PEG-2000和PEG-6000)和有机小分子乙二醇、无机盐氯化锂(LiCl)等六种物质作为制备聚丙烯腈膜的添加剂,含量均为3%(质量分数)。并对聚丙烯腈膜的表面和断面结构、水通量、孔隙率、水接触角及对牛血清蛋白(BSA)的截留率等进行了测试及表征。结果表明:以PEG-2000作为添加剂制得的膜的微孔较多,孔径较大,断面为指状结构,具有最大的水通量和孔隙率,达到436L/(m~2·h)和86%;有机小分子乙二醇作为添加剂制得的膜的水通量较低,但对BSA的截留率最高,为93%;聚乙烯吡咯烷酮(PVP)和聚乙二醇(PEG)制得的膜的水接触角较低,最小达到68°,亲水性较好。     

轮胎模具DLC涂层的制备及性能

为探究高性能轮胎模具类金刚石(DLC)涂层的应用前景,提高模具花纹块内表面的疏水性及耐磨减摩性,采用等离子体增强化学气相沉积法在35钢基体上制备DLC涂层,并对所制备的DLC涂层的表面形貌、粗糙度、疏水性、表面元素组成、纳米硬度、摩擦系数等关键指标进行了测定.结果表明:DLC涂层具有优良的表面完整性,水接触角可达19.62°,乙醇接触角达20.37°,纳米硬度可达19.62 GPa,摩擦系数低至0.405 8,DLC涂层有望替代Teflon涂层,用于高性能轮胎模具.     

化学浴沉积法制备防污自洁聚偏氟乙烯膜

基于"荷叶效应"原理,利用聚偏氟乙烯(PVDF)涂膜构筑微米结构,氧等离子体诱导化学沉积法构筑纳米结构。采用接触角测量仪、原子力显微镜及X光电子能谱仪等研究了PVDF膜表面的微结构及化学组成与疏水性能的关系。结果显示,PVDF溶液涂膜后可形成直径8μm的微球,甲基三氯硅烷修饰的PVDF膜与水的接触角为157°;二甲基二氯硅烷/甲基三氯硅烷混合液修饰的PVDF膜的表面接触角为155°,滚动角2°;集灰实验证明,两种修饰方法制备的PVDF膜均具有良好的防污自洁性能。     

KH-570修饰的SiO2膜制备及CH4/CO2的分离

采用KH-570代替部分TEOS为前驱物,共水解缩聚反应制得疏水性SiO2膜,通过IR、DTG、SEM、接触角测试仪等手段对KH-570修饰后的SiO2膜进行表征,并对CH4和CO2渗透和分离进行研究。实验结果表明,修饰后(0.8KH-570)SiO2膜接触角达到94.2°,红外光谱分析表明修饰后SiO2膜疏水性增强;(0.8KH-570)SiO2膜具有完整性及在400℃水热稳定性;压差30kPa,分离因子随涂膜次数增加先增大后减小,涂膜5次达最大值2.13,超越了努森扩散理论分离因子1.66,此时分离效果好;对于涂膜5次的SiO2膜,CH4渗透通量随压差增加呈现非线性微增趋势,CH4/CO2分离因子几乎不变。     

聚偏氟乙烯微孔膜一步法亲水化改性研究