废旧聚丙烯编织袋回收料改性应用研究

废旧聚丙烯(PP)编织袋回收料分别与回收聚乙烯(PE)、回收橡胶粉、木粉共混,制备了增韧PP材料、热塑性弹性体和木塑复合材料,采用力学性能测试、SEM和DSC分析等手段对其性能和结构进行了表征。结果表明:随着回收聚乙烯(PE)含量的增加,回收PP/PE共混物的拉伸强度和冲击强度迅速提高;回收PP/橡胶粉共混物中加入聚丙烯接枝马来酸酐(PP-g-MAH)能起到增容的效果,随PP-g-MAH含量的增加,共混物的拉伸强度上升,永久变形减小;在回收PP/木粉复合材料中加入PP-g-MAH后,复合材料的冲击强度明显提高。     

聚丙烯/木粉复合材料的制备及其力学性能的研究

以聚丙烯为基体,木粉为填料,采用机械共混、二次挤出共混和注塑成型方法制备不同木粉含量的PP/木粉复合材料,并且测定了PP/木粉复合材料的力学性能。实验结果表明:随着木粉用量的增加,复合材料拉伸强度逐渐增大;木粉用量为60%时,复合材料拉伸强度达到最大值36.04 MPa;木粉用量为80%时,复合材料拉伸强度降低到34.60 MPa。木粉的含量由20%增加到80%,复合材料弹性模量由579.12 MPa增加到869.80MPa,断裂伸长率从18.92%降低到7.39%,冲击强度由9.33 kJ/m2降低到7.76 kJ/m2。这是因为PP/木粉复合材料体系中随着木粉含量的增加,木粉起到了应力集中的作用,使材料变脆,冲击强度降低。     

木粉含量对连续固态挤出自增强PP性能的影响

采用单螺杆挤出机连续固态挤出制备自增强聚丙烯(PP)复合材料试样,对不同木粉含量的试样性能进行表征和综合分析。结果表明,PP复合材料试样密度随着木粉含量的增加呈线性上升趋势;拉伸强度和弯曲强度呈现先上升后下降的趋势,而在木粉含量为50%时达到最大;拉伸弹性模量和弯曲弹性模量随着木粉含量的增加一直增大,但断裂伸长率下降;木粉含量的增加能够提高试样的耐热性,但结晶度有所下降;木粉含量过多会造成复合材料界面结合减弱,影响最终复合材料的性能。     

聚丙烯／木粉复合材料的加工成型及其力学性能研究

采用混炼工艺制备了聚丙烯／木粉复合材料（WPC）。研究了木粉、界面增溶剂-马来酸酐接枝聚丙烯（MAPP）的用量对WPC力学性能的影响。采用红外光谱仪对PP、MAPP、木粉及WPC的结构进行了表征和分析。结果表明，聚丙烯中加入木粉后，复合材料的拉伸强度及弯曲强度均比纯PP的要低，拉伸模量和弯曲模量逐渐升高，但复合材料的拉伸断裂伸长率随木粉用量的增加而逐渐下降。随着MAPP用量的增加，木粉用量较低（10％、20％）的WPC的拉伸强度和弯曲强度均先增加，然后逐渐减少，而木粉用量较高的WPC的强度值却在不断增高。当MAPP的质量分数为2％-4％时，复合材料的冲击强度值一般达到最高。红外谱图研究表明，偶联剂的加入可以把木纤维中的羟基酯化，改善木塑界面之间的相容性。     

汽车内饰用PP/黄麻纤维复合材料力学性能

采用转矩流变仪混合造粒,通过注射成型方法制备了聚丙烯(PP)/黄麻纤维复合材料,研究了对纤维表面进行处理的NaOH浓度、纤维含量和相容剂的含量对PP/黄麻纤维复合材料力学性能的影响,采用扫描电镜对纤维表面及复合材料的断面形貌进行分析。结果表明:黄麻纤维经过碱处理后PP/黄麻纤维复合材料的力学性能优于纤维未处理的复合材料的力学性能,随着NaOH浓度的提高,PP/黄麻纤维复合材料的拉伸强度和冲击强度增加,在NaOH浓度为16%时,其拉伸强度和冲击强度最佳;其弯曲强度随着NaOH浓度的提高先增加而后下降,在8%浓度时,弯曲强度最大。随着纤维含量的提高,PP/黄麻纤维复合材料的拉伸强度和弯曲强度先增加后下降,在纤维含量达到20%时,PP/黄麻纤维合材料的拉伸强度和弯曲强度达到最大。随着纤维含量的提高,PP/黄麻纤维复合材料的冲击强度降低。相容剂的加入使得PP/黄麻纤维复合材料的拉伸强度和弯曲强度明显增加。     

PP/POE-g-MAH/MF微孔发泡复合材料的制备及性能研究

采用POE-g-MAH作为聚丙烯和密胺树脂的增容剂,用化学发泡法制备了PP/POE-g-MAH/MF微孔复合材料,并探讨密胺树脂含量对微孔聚丙烯复合材料综合性能的影响。研究结果表明,密胺树脂粉末使复合材料结晶提前,对聚丙烯发泡过程起异相成核作用,导致微孔孔径变小并致密。随着密胺树脂含量的增加,微孔复合材料的拉伸强度、断裂伸长率和冲击强度先增大后减小。当密胺树脂的含量为2%时,微孔复合材料的强度和冲击韧性最佳。     

聚丙烯/废旧玻璃钢粉复合材料的结构与性能研究

采用熔融共混法制备了聚丙烯/废旧玻璃钢粉(PP/WFRP)复合材料,探讨了WFRP含量对复合材料力学性能、结晶行为及热性能的影响。力学性能测试结果表明,随着WFRP用量的增加,复合材料的弯曲强度和邵氏硬度明显升高,而拉伸强度逐渐下降。X射线衍射实验表明,加入WFRP能够诱导β晶生成,降低PP的结晶度。热重分析表明,WFRP的加入可以有效提高PP的热稳定性。     

聚丙烯/高密度聚乙烯混炼对竹木塑复合材料性能的影响

用聚丙烯(PP)、高密度聚乙烯(HDPE)共混制备竹木塑复合材料,研究其对复合材料力学性能和微观结构的影响,同时对比竹粉与木粉对材料性能的影响.结果表明:竹塑复合材料的拉伸强度较高;加入一定量的高密度聚乙烯可以提高聚丙烯/竹粉复合材料的冲击和弯曲强度;竹粉与塑料的相容性比木粉好,木塑复合材料的主要破坏形式是木粉与塑料的...     

无水硫酸钙晶须对PP复合材料的熔融结晶和力学性能的影响

制备了无水硫酸钙晶须(ACSW)填充聚丙烯(PP)复合材料,通过差示扫描量热仪、X射线衍射仪、偏光显微镜、力学性能测试等手段研究了ACSW对PP复合材料的熔融结晶和力学性能的影响。结果表明,ACSW的加入会细化聚丙烯的晶粒,质量分数低于20%的ACSW提高了PP的结晶温度、熔融温度和结晶速率,降低复合材料的拉伸强度;质量分数大于20%的ACSW能提高PP复合材料β晶成核效率和PP的结晶速率,降低复合材料的拉伸强度。当ACSW质量分数为25%时,复合材料的缺口冲击强度较纯PP增加了66%。随着ACSW的含量的增加,复合材料的弯曲强度先增加后降低,并在ACSW质量分数为10%时达到了最大值。     

聚丙烯基木塑复合材料力学性能的研究

研究了聚丙烯(PP)基木塑复合材料的界面形态,采用两种不同的偶联剂对木粉进行表面处理,考察了混炼时间和木粉用量对复合材料力学性能的影响,并通过扫描电子显微镜(SEM)对试样的断口形貌进行了观察。结果表明:在木粉用量相同的情况下,钛酸酯偶联剂对木粉的处理效果要优于铝酸酯偶联剂,偶联剂处理使木粉与PP的界面相容性得到了改善,复合材料的性能得到提高;在偶联剂不变的情况下,随着木粉含量的增加,木塑复合材料的冲击强度和拉伸强度均下降;随着混炼时间的增加,木塑复合材料的冲击强度和拉伸强度呈先升后降的趋势。     

PP-g-MAH增容改性木粉/PP复合材料的性能研究

以马来酸酐接枝聚丙烯 (PP-g-MAH) 为相容剂,聚丙烯 (PP) 为基体,通过熔融共混法制备了木粉/PP复合材料。研究了 PP-g-MAH 用量对复合材料力学性能及吸水性能的影响; 采用扫描电镜 (SEM) 观察了复合体系的冲击断面形貌。结果表明: 当 PP-g-MAH 的质量分数为 4%时,可以提高添加 35 份木粉复合材料体系的拉伸强度及弯曲强度,比未添加相容剂的分别提高了 49.4%和 16%,而缺口冲击强度仅下降了 9%。SEM 观察证实: PP-g-MAH 的加入有利于提高木粉与 PP 基体的界面相互作用。从吸水率来看,木粉/PP 复合材料的吸水率保持在 0.22% 以下,远低于纯木材。     

HDPE/木粉复合材料的性能研究

研究了不同种类的增容剂对高密度聚乙烯(HDPE)木/粉复合材料性能的影响,并研究了增容剂含量、木粉含量对复合材料力学性能及形态结构的影响。结果表明,HDPE木/粉复合材料的拉伸强度、弯曲强度均随马来酸酐接枝HDPE(HDPE-g-MAH)含量的增加而增大;复合材料的缺口冲击强度随甲基丙烯酸缩水甘油酯接枝低密度聚乙烯的增加而提高;复合材料的拉伸强度、弯曲强度随木粉含量的增加而增大;而缺口冲击强度则随木粉含量的增加呈降低趋势。     

Mechanical properties and morphology of impact modified polypropylene–wood flour composites

The mechanical properties and morphology of polypropylene/wood flour (PP/WF) composites with different impact modifiers and maleated polypropylene (MAPP) as a compatibilizer have been studied. Two different ethylene/propylene/diene terpolymers (EPDM) and one maleated styrene–ethylene/butylene–styrene triblock copolymer (SEBS–MA) have been used as impact modifiers in the PP/WF systems. All three elastomers increased the impact strength of the PP/WF composites but the addition of maleated EPDM and SEBS gave the greatest improvements in impact strength. Addition of MAPP did not affect the impact properties of the composites but had a positive effect on the composite unnotched impact strength when used together with elastomers. Tensile tests showed that MAPP had a negative effect on the elongation at break and a positive effect on tensile strength. The impact modifiers were found to decrease the stiffness of the composites. Scanning electron microscopy showed that maleated EPDM and SEBS had a stronger affinity for the wood surfaces than did the unmodified EPDM. The maleated elastomers are, therefore, expected to form a flexible interphase around the wood particles giving the composites better impact strength. MAPP further enhanced adhesion between WF and impact-modified PP systems. EPDM and EPDM–MA rubber domains were homogeneously dispersed in the PP matrix, the diameter of domains being between 0.1–1 μm. © 1998 John Wiley & Sons, Inc. J Appl Polym Sci 67:1503–1513, 1998     

甲基化木粉与PE-g-MAH对木粉/HDPE复合材料力学性能的协同作用研究

主要研究了木粉表面甲基化改性和增容剂马来酸酐接枝聚乙烯(PE-g-MAH)对木粉/高密度聚乙烯(HDPE)复合材料力学性能的协同作用。木粉经表面甲基化处理后,与10%PE-g-MAH协同使用,甲基化木粉/PE-g-MAH/HDPE复合材料的拉伸强度、弯曲强度和冲击强度均明显高于未改性木粉/PE-g-MAH/HDPE复合材料,其原因在于在PE-g-MAH的作用下,甲基化木粉在聚合物基体中分布更加均匀,两者的界面作用力更高,即甲基化木粉和PE-g-MAH对提升木粉/HDPE复合材料的力学性能具有良好的协同作用。     

聚丙烯/木粉/纳米凹凸棒土复合材料性能研究

采用双螺杆挤出机制备了一系列聚丙烯(PP)/木粉/纳米凹凸棒土(AT)木塑复合材料(WPC.研究了AT用量对复合材料力学性能、热性能、加工性能的影响.结果表明,随着AT用量的增加,复合材料拉伸强度逐渐增加、冲击强度逐渐减小,硬度先增加后减小,AT用量为5份时复合材料硬度最大;复合材料维卡软化点不断提高;熔体流动速率(M...     

The effect of epoxy‐polyester hybrid resin on mechanical properties,rheological behavior,and water absorption of polypropylene wood flour composites

The effect of epoxy resin on mechanical and Rheological properties, and moisture absorption of wood flour polypropylene composites (WPCs) were investigated. The reactive mixing of epoxy resin with 30, and 40 wt% wood flour and polypropylene (PP) was carried out in twin screw extruder with a special screw elements arrangement. PP grafted maleic anhydrides (MPP) were used as coupling agent to improve the interfacial interactions of wood flour, epoxy resin, and PP. The tensile strength of composites decreased, and elastic modulus and moisture absorption increased with increasing epoxy resin content. The complex viscosity η* increased with increasing epoxy resin content of composites, and a synergistic effect in increasing the η* was observed at 3 wt% resin. The epoxy resin modified wood‐PP composites that chemically coupled by MPP showed minimum water absorption with highest elastic modulus. The experimental oscillation rheologyical data were used to drive a model to predict the flow behavior of WPCs, in a wide range of frequencies. POLYM. ENG. SCI., 47:2041–2048, 2007. © 2007 Society of Plastics Engineers     

Water absorption and mechanical properties of PP/HIPS hybrid composites filled with wood flour

Water absorption and mechanical performance of the injection‐molded hybrid composites prepared from different ratios of two polymer blends (57 wt%), two compatibilizers (3 wt%), and two wood species (40 wt%) were investigated. The ratio of polypropylene and high‐impact polystyrene (HIPS) gradually increased in the blend (from 10 to 30 wt%). Styrene–ethylene–butylene–styreneblock copolymer and maleic anhydride‐grafted PP (MAPP) were used as compatibilizer (3 wt%). The shore D hardness of the PP/wood composites was improved by the incorporation of the HIPS. The HIPS/wood flour composites showed higher tensile modulus but lower tensile strength than the PP/wood composites. The water resistance of the PP/wood composites decreased with increasing HIPS content. POLYM. COMPOS., 38:863–869, 2017. © 2015 Society of Plastics Engineers     

回收聚丙烯/木粉复合材料性能研究

采用双螺杆挤出机制备了回收聚丙烯(PP)/木粉复合材料,研究了木粉用量时复合材料拉伸性能、冲击性能、加工流动性及耐热性的影响,并对加工工艺进行了探讨.结果表明,随着木粉用量的增加,复合材料的拉伸强度先升高后降低,冲击强度、断裂伸长率、熔体流动速率均不断降低,维卡软化点温度则呈上升趋势,木粉用量为80份时复合材料的综合性能最佳.