稀土对高Nb钢奥氏体晶粒长大行为影响

钢中奥氏体晶粒越细小,经过组织转变后组织的力学性能越好.利用Gleeble-1500D热模拟机模拟稀土高Nb钢热处理过程,并对试样进行TEM观察与分析,研究稀土对加热时不同保温时间奥氏体晶粒大小的影响.结果表明:稀土能有效抑制加热过程中奥氏体晶粒长大,具有调整晶粒稳定性的作用,并且稀土降低沉淀相溶解的温度,促进第二相粒子在奥氏体中的溶解.     

均匀化退火对纯铝系负极箔坯料显微组织的影响

铸轧纯铝系负极箔坯料存在粗大且分布不均匀的第二相,均匀化退火对坯料中第二相尺寸和分布有重要影响.通过均匀化退火实验研究了退火温度和保温时间对纯铝系负极箔冷轧坯料中第二相尺寸和分布的影响.结果表明:在保温时间为10 h时,随着退火温度升高,弯曲带状Fe Al共晶相逐渐溶解球化,条状β(Fe Al Si)相分解为短棒状,当温度升高至550℃时,针状相Fe Al~3开始析出;在退火温度为520℃时,随退火时间的延长,粗大第二相的比例不断减小,而后趋于稳定;冷轧变形率为38.5%的铸轧纯铝系负极箔冷轧坯料经520℃保温10 h退火后可获得较均匀的组织.     

热处理对铸态双相不锈钢中δ-铁素体的影响

研究了不同热处理温度和保温时间对双相不锈钢0Crl7Mnl4Mo2N(A4钢的)铸态组织中δ-铁素体含量及形态的影响．发现在l050-l150℃之间加热时，奥氏体基体上分布着球状的及长条形的δ-铁素体，且加热温度越高保温时间越长，铁素体的球化率越高．在l250℃加热保温时间小于8h时，组织全部由等轴状的δ-铁素体组成；当保温时间大于8h或加热温度高于l250℃时，组织由δ-铁素体和奥氏体两相组成，铁素体为尖角网状分布．     

低合金奥—贝球铁焊接峰值温度（Tm）对热影响区组织与力学性？…

利用Ｇｌｅｅｂｌｅ－１５００焊接热模拟的试验机，在固定的加热速度，峰值温度保温时间与８００－５００℃冷却时间为７ｓ的条件下，研究了峰值温度在１０５０－８５０℃内变化对低合金奥－贝球墨铸铁热影响区组织及力学性能的影响。     

Fe-3%Si电工钢的相图计算及组织分析

使用热力学软件分析了碳含量对Fe-3%Si的电工钢相图的影响,考察了奥氏体和铁素体两相区内两相相对量随温度的变化.结合金相法观察了不同加热温度及不同保温时间的淬火组织,初步确定了不同温度及不同保温时间下电工钢组织的形貌特征.     

亚临界热处理对含V高铬铸铁组织和硬度的影响

研究了不同的亚临界热处理温度和保温时间对含V高铬铸铁组织和硬度的影响,结果表明,通过亚临界热处理可使高铬铸铁产生二次硬化现象.在500～620℃进行亚临界热处理时,随着亚临界处理温度的升高和保温时间的延长,开始析出细小、弥散分布的二次碳化物.当热处理温度为540℃和保温时间为4 h时硬度达到62.4HRC,从而使材料的综合性能得到改善,温度太高或保温时间太长,都会使高铬铸铁的硬度下降.     

低碳微合金钢高温快速回火的热模拟实验研究

通过低碳微合金淬火钢在620℃回火温度下不同回火时间的组织和低温冲击性能对比研究,结果表明,利用热模拟机快速回火保温40 s时,析出物颗粒更细小、弥散地分布于基体铁素体之上,其夏比V口低温冲击值比传统回火保温70 min、快速回火保温80和120 s的较高.实现快速回火达到传统回火的性能,从而节约时间和能耗.     

锰含量对15MnV钢钒化合物溶解析出的影响

研究了锰含量对15MnV钢中钒化合物溶解析出的影响。用中途淬火．萃取物化学相分析等方法，测定了加热时钒化合物的溶解量，980—500℃等温过程中钒化合物的析出量．用应力松弛法测定了奥氏体中钒化合物的析出动力学．讨论了锰含量与[V][C]固溶度积的关系，得到了锰含量与奥氏体中析出温度--时间(PTT)曲线的关系，分析了锰含量对等温过程中钒化合物析出峰值温度、最大析出量的影响。     

新型镍基合金静态再结晶规律研究

为了研究形变量和加热温度对新型镍基合金晶粒尺寸的影响规律,对该合金进行了静态再结晶实验,并用光学显微镜观察了其微观组织变化.合金静态再结晶实验结果表明,冷变形试样在γ′相完全熔解温度以下时,延长保温时间对晶粒尺寸的影响不大;在γ′相完全熔解温度以上时,随保温时间的延长晶粒长大效果显著.     

熔体热历史对Al-11.6%Si合金组织及性能的影响

本文研究了熔体加热温度和保温时间对Al-11.6%Si合金显微组织及性能的影响.研究发现,合金液的加热温度和保温时间不仅影响合金凝固的组织,而且也影响其力学性能.将合金液温度从720℃升到900℃,共晶硅由粗大的针片状变为点状或短棒状、合金抗拉强度提高了6.33%、延伸率提高了10.83%.升温后的保温时间对合金组织和力学性能的影响时间不同于降温后的保温时间,随升温后保温时间的延长,合金的组织变细、抗拉强度和延伸率提高;随降温后保温时间的延长,合金的组织变粗、抗拉强度和延伸率降低.     

Influence of secondary carbide precipitation and transformation on abrasion resistance of a 3Cr15Mo1V1.5 white iron

The relationship between the secondary carbide precipitation and transformation of the 3Cr15Mo1V1.5 white iron and abrasion resistance was investigated by using optical microscope （OM）, transmission electron microscopy （TEM） and X-ray diffrac- tion （XRD）. The results show that the properties of secondary carbides precipitated at holding stage play an important role in the abrasion resistance. After certain holding time at 833 K subcritical treatment, the grainy （Fe, Cr）23C6 carbide precipitated and the fresh martensite transformed at the holding stage for 3Cr15Mo1V1.5 white iron improve the bulk hardness and abrasion resistance of the alloy. Prolonging holding time, MoC and （Cr, V）2C precipitations cause the secondary hardening peak and the corresponding better abrasion resistance. Finally, granular （Fe, Cr）23C6 carbide in situ transforms into laminar M3C carbide and the matrix structure transforms into pearlitic matrix. These changes weaken hardness and abrasion resistance of the alloy sharply.     

Behavior of precipitation in bainitic steel during relaxation processing of RPC technique

Thermal simulation test, TEM (Transmission Electron Microscope) and nanobeam EDS (Energy Dispersed x-ray Spectrum) techniques were used to investigate the precipitation behavior of Nb, Ti, Mo etc. in HSLA (High Strength Low Alloy) steel. The strain induced precipitation occurred during the isothermal relaxation stage after deformed in the non-recrystallization temperature region. After 30% predeformation at 850 and 900~C, there are two kinds of particles, (Ti,Nb)(C,N) and a few Nb(C,N), to precipitate during holding. The content of Nb in particles rises with the relaxation time increasing. During the final holding stage, some Nb and Ti atoms in the lattice sites of the precipitates would be replaced by Mo atoms, and the Mo content in the precipitates increases with the relaxation time. The results were compared with the refinement effect of microstructures caused by relaxationprecipitation controlling transformation (RPC) processing.     

Influences of heat treatments on crystallization in SiO<Subscript>2</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-MgO-K<Subscript>2</Subscript>O-F glass-ceramics

Five kinds of heating treatment processing were chosen according to the experiment result of differential scanning calorimeter to prepare SiO2-Al2O3-MgO-K2O-F glass ceramics samples.The effects of heat treatment processing on the crystallization of these samples were explored by X-ray diffraction and scanning electron microscopy techniques.The results indicate that phase separations can occur in the bulk regions of the glass sample when holding at 670 ℃ for 3 h.The phase separation can accelerate the precip...     

分段加热对废旧线路板熔焊影响的数值模拟

近年来电子产业发展正存在着消耗量大、消耗快速、浪费严重等不利情况。在电子废弃物中,废旧手机芯片仍具有一定的剩余寿命,拥有较高的再利用价值。因此在废旧手机的拆解过程中提高拆解效率以及降低对芯片的损害是十分有必要的。针对废旧手机线路板上电子元器件拆解过程中常见的熔焊问题,以空气为加热介质, BGA返修台为加热工具,并采用FLUENT软件进行模拟研究。分析对比了不同预热温度、保温时间和高温加热条件下焊点熔化对于芯片拆卸效果的影响。研究结果表明,当预热温度为433 K,保温时间为40 s,高温加热温度为513 K时,拆卸效果最好。     

用LD_1钢制造冷冲模的热处理工艺及应用研究

通通 Formastor 全自动相变仪研究了高强韧性冷作模具钢(LD_1钢即7Cr7MO3V2Si)的加热转变临界点和 Ms 点,研究了加热温度对碳化物溶解及 Ms 点的影响;通过金相及热力学性能测试研究了 LD_1钢淬火温度对奥氏体晶粒度和淬火硬度的影响.淬火—回火温度对硬度和冲击韧性的影响.以此为判据制定出不同模具的热处理工艺,并进行了实际生产考核.     

化学沉淀法分离回收碱性溶液中V、Mo、Al的研究

采用化学沉淀法对碱性V⁃Mo⁃Al溶液进行分离以逐步回收其中的有价金属V、Mo、Al。通过热力学理论分析与条件实验相结合的方法分别考察了沉淀剂物质的量、温度、pH、反应时间等因素对碱性液中V、Mo沉淀分离的影响。结果表明,以CaCl2沉淀V,当反应温度为80 ℃,CaCl2物质的量为理论物质的量的1.1倍,反应时间为1 h,pH为12.9时,V的沉淀回收率约为95.3%;以Ba(OH)2沉淀Mo,当温度为80 ℃,Ba(OH)2物质的量为理论物质的量的2.5倍,反应时间为60 min时,Mo的沉淀回收率达到99.6%。     

合金元素Mo对冷轧双相钢组织的影响

分析Mo微合金冷轧双相钢和普通C-Mn冷轧双相钢在不同双相热处理工艺下微观结构,讨论Mo对冷轧双相钢组织变化规律的影响。实验结果表明：当两种双相钢以1700℃／s冷却时,均获得了铁素体、马氏体双相组织,马氏体均匀分布在铁素体基体上,随着加热温度的升高,普通C-Mn双相钢得到的马氏体体积分数多。当以5．4℃／s冷却时,Mo微合金双相钢得到的马氏体体积分数多;当加热到820℃保温结束后以5．4℃／s的速率冷却时,普通C-Mn钢的组织组成相为铁素体、珠光体、马氏体;Mo微合金钢的组织组成相为铁素体、贝氏体、马氏体;Mo对铁素体晶粒的细化作用不明显。     

Influence of isothermal aging onσprecipitation in super duplex stainless steel

The time-temperature-transformation (TTT) curve of the 00Cr25Ni7Mo4N duplex stainless steel was obtained with a Formastot-digital thermal dilatometer,and the influence of isothermal aging on σ precipitation was studied by metallographic observation,X-ray diffraction (XRD),and transmission electron microscopy (TEM).The results show that the decomposition of ferrite phase is accompanied by the formation of σ phase at 750-1000℃,especially in the range of 800-900℃.The longer the aging time,the higher the amount of σ precipitation.The area fraction of various phases remains at a certain value upon the completion of ferrite deformation.The temperature of 850℃ is the most sensitive transaction temperature,the incubation time for the formation of o precipitation is less than 1 min,and aging for 20 min leads to the complete transformation of ferrite.The o phase is formed preferentially at the α/α/γ junction,and then grows along the α/α boundary in the matrix.     

钢锭退火工艺现状及工艺参数的合理制订

调查分析了一些特殊钢厂的钢锭退火工艺规范。发现许多工厂中钢锭退火工艺陈旧,加热温度过高,保温时间太长,造成耗能、费时,生产率低。文中从加热温度,升温速度,保温时间,冷却速度等方面进行了分析研究,指出了退火工艺参数合理制订的方向。     

AZ31B镁合金应变诱发半固态组织观察

采用AZ31B镁合金挤出材,在573K进行28％-30％预变形加工,然后在863—893K经过不同保温时间进行等温球化处理,观察了试样不同区域的组织,考察了温度及保温时间对组织的影响,得到了具有圆整固相颗粒的半固态组织．实验结果表明：适当提高球化处理温度,有利于加速球化过程,以获得细小圆整半固态组织;延长保温时间固相分数降低,但幅度不大,并发生颗粒不规则化;在同一个试样上,由于部位不同,变形程度不同,所得半固态材料的固相率不同．讨论了半固态组织的形成机理,分析认为预变形后,半固态组织形成过程包括再结晶、晶粒长大阶段,受溶质、空位扩散控制的半固态组织形成阶段,受液-固界面张力作用的固相颗粒圆整化阶段．开始形成半固态组织阶段,扩散占主导地位,在进一步球化过程中,界面张力占主导地位．