Al2(SO4)3复合CPB-膨润土处理垃圾渗滤液

用溴代十六烷基吡啶对天然膨润土进行改性，制得CPB-膨润土，然后与Al2(SO4)，复合制得复合CPB-膨润土。研究复合CPB-膨润土去除垃圾渗滤液中CODCr和色度的适宜条件。实验结果表明：与原土比较，复合CPB-膨润土对垃圾渗滤液中CODCr和色度的去除效果有显著提高，CODCr和色度去除率分别可达到91．6％和95．2％。为膨润土的改性及其在垃圾渗滤液处理中的应用提供了有价值的参考数据。     

复合HDTMAB-膨润土处理垃圾渗滤液

用溴化十六烷基三甲铵（HDTMAB）对天然膨润土进行改性,制得HDTMAB-膨润土,然后与Al2（SO4）3复合制得复合HDTMAB-膨润土.研究复合HDTMAB-膨润土在聚丙烯酰胺（PAM）辅助下去除垃圾渗滤液中COD和色度的效果及适宜条件.实验结果表明：与原土比较,复合HDTMAB-膨润土对垃圾渗滤液中COD和色度的去除效果有显著提高,在适宜的实验条件下,COD和色度去除率分别可达到92.6%和97.5%.为天然膨润土的改性及其在垃圾渗滤液处理中的应用提供了有价值的参考数据.     

加碳焙烧膨润土处理活性黑染料废水

用加碳焙烧法对膨润土进行活化改性,并用加碳焙烧膨润土处理活性黑染料废水,探讨其去除活性黑染料废水中CODCr和色度的能力。通过实验,确定了最佳活化改性条件：焙烧时间3.5h,加碳量3%,焙烧温度550℃。实验结果表明,加碳焙烧膨润土对活性黑染料废水的处理效果较之原土有较大程度提高,CODCr和色度的去除率分别达到88.2%和96.5%。     

微波柱撑膨润土预处理垃圾渗滤液氨氮的研究

利用微波辐照强化制备铝柱撑膨润土吸附剂,并对其进行了性能表征。将其应用于氨氮浓度1200mg/L的垃圾渗滤液预处理。通过柱撑膨润土吸附实验,研究了微波柱撑膨润土在不同条件下对垃圾渗滤液中氨氮的去除效果。实验结果表明,在微波柱撑膨润土投加量为10g/L,pH值为6,反应时间20min,沉降时间30min时,能够使垃圾渗滤液中氨氮的去除效率达到76.8%,CODcr去除率85.5%,减轻了后续生物处理的负荷。     

钙基膨润土的组合改性及对垃圾渗滤液的处理

钙基膨润土的钠化改型工艺简单、实用性强 ;酸改性后的膨润土对于金属离子具有较强的吸附能力 ;有机改性后的膨润土对有机物具有较强的吸附能力 ;而“组合”改性后的膨润土 ,对金属离子和有机物都具有较强的吸附能力。利用“组合”改性后的膨润土作吸附剂 ,处理垃圾渗滤液 ,效果比较理想 ,CODCr的去除率可达 79%、重金属离子的去除率 5 3 %～ 98%、氨氮去除率达 46%。     

改性膨润土吸附处理含Gr(Ⅵ)废水的研究

用阳离子表面活性剂十六烷基三甲基溴化铵(CTMAB)对钙基膨润土进行活化改性,并用制备的改性膨润土对含Cr(Ⅵ)模拟废水进行吸附实验,研究了改性膨润土去除模拟水样中重金属Cr(Ⅵ)的适宜条件.结果表明,用质量分数为5%的CTMAB溶液改性后的膨润土去除Cr(Ⅵ)效果较好,当改性膨润土用量为10g/L,搅拌时间30min、pH值为3～5时、有机膨润土对含Cr(Ⅵ)废水的去除率超过85%.     

微波有机改性膨润土处理活性染料废水研究

以十六烷基三甲基溴化铵为改性剂,在微波加热条件下制备了微波有机改性膨润土,并研究了该改性膨润土对主要含活性翠绿KN（蒽醌类）和活性嫩黄K（醌类）、色度和COD_Cr分别为2 000倍和620 mg/L的染料废水的处理效果。试验结果表明,在pH=6.0,微波有机改性膨润土投加量为2 g/L,反应温度为60 ℃,反应时间为15 min的条件下,染料废水的脱色率和COD_Cr去除率可分别达到97.5%和92.8%,处理效果不仅优于传统有机改性膨润土,而且优于活性炭。     

改性膨润土预处理垃圾渗滤液的试验研究

垃圾渗滤液成分复杂,较难处理。膨润土具有较强的吸附性能和阳离子交换能力,价廉易得且可再生利用,所以可应用于污水处理中。通过对改性膨润土处理渗滤液的试验,发现:改性高效钠基土的处理效果最好,当渗滤液pH=6.5、投土量为4g/L时,对COD平均去除率为72%,对BOD平均去除率为70%,对NH3-N的平均去除率为41%,显著减轻了后续处理的负担。     

鄂州钙基膨润土有机改性研究

以湖北鄂州钙基膨润土为原料,研究了将提纯、钠化改型和有机插层改性结合在一起的制备有机膨润土的联合处理工艺.通过L9(34)正交实验和调优实验,确定了最佳的工艺条件:插层剂用量40%,反应温度95℃,钠化剂用量6%,反应时间5h.4种有机改性剂实验结果表明:1831的改性效果最佳,有机膨润土中蒙脱石的d001为4.1639nm.     

用改性膨润土去除水中四氯化碳的试验研究

为完善地下水中氯代烃污染物的处理技术,进行了用改性膨润土吸附模拟水样中四氯化碳的试验研究。试验结果表明：天然钙基膨润土经十六烷基三甲基溴化铵改性后,颗粒间间距明显增大,颗粒表面由亲水性变为疏水性,可有效吸附去除水中的四氯化碳,其适宜的吸附条件为膨润土投加量5 g/L、吸附时间2 h、吸附温度30 ℃。按此条件用改性膨润土处理某CCl₄含量为1.60 mg/L的实际四氯化碳污染地下水,CCl₄的去除率可达70%～80%。     

矿化垃圾生物反应床处理垃圾渗滤液

介绍了矿化垃圾的概念、性质（物理、化学、生物）及矿化垃圾生物反应床去除有机物的机理。通过工程实例说明矿化垃圾生物反应床对渗滤液中COD_Cr、BOD₅、NH₃-N及悬浮物具有较好的降低效果。此外,还具有抗冲击负荷性能优越,投资运行成本低,且在国内存在数量多,具有充足的资源与开发利用前景。其在垃圾渗滤液处理中的推广与应用具有较好的生态化意义,必将带来良好的环境效益和经济效益。     

水泥混凝处理垃圾渗滤液研究

针对水泥较强的混凝特性,探讨了水泥处理垃圾渗滤液的可行性。试验结果表明,水泥对垃圾渗滤液的浊度、六价铬、铜离子和COD均有较好的去除效果。在最佳条件下,水泥对垃圾渗滤液中浊度的去除率达97.5%,六价铬去除率达72.2%,铜离子去除率达79.0%,COD去除率达81.6%。     

微波改性沸石后处理垃圾渗滤液中氨氮的实验研究

采用微波技术和NaCl对天然沸石进行活化改性,研究了改性沸石对预处理后的垃圾渗滤液中氨氮的去除效果,结果表明:沸石最佳的改性条件是微波功率60%,微波改性时间5min,NaCl溶液浓度8%,沸石粒径100目;在100mL水样的氨氮含量为32mg/L的前提下,实验对垃圾渗滤液中氨氮去除在水样pH值为6,改性沸石投加量为7g,吸附时间为20min时效果最佳,氨氮去除率可达92.11%。     

Use of landfill leachate as a carbon source in a sulfidogenic fluidized-bed reactor for the treatment of synthetic acid mine drainage

High rate sulfate reducing bioreactors can be effectively used in the treatment of acid mine drainage (AMD). The main disadvantage of sulfate reducing bioreactors is the requirement of a suitable carbon source and electron donor as the dissolved organic carbon content of AMD is usually quite low. In this study, a landfill leachate was used as a low-cost carbon source for sulfate reducing bacteria in a fluidized-bed (FBR) reactor for the treatment of synthetic AMD. Ethanol was replaced with leachate in the feed of FBR operated longer than 150 days at 35 °C. Although sulfate reduction rates decreased appreciably when ethanol (3.44 g sulfate/L/d) was replaced with leachate (0.90 g sulfate/L/d), leachate-fed FBR still performed well as the pH increased to neutral values, soluble metal removals were 82–99.9%, and total metal removals were 80–99.9%. In the case of leachate, electron flow to sulfate reduction decreased significantly. Higher performance may be achieved at chemical oxygen demand (COD)/sulfate ratios higher than 1.0. This study showed that leachate may be used as a low-cost soluble substrate for sulfate reducing bacteria in high rate bioreactors for AMD treatment.     

Feasibility analysis of remedial scheme of Qilongcun landfill

Based on hydro-geological of Qilongcun landfill, the transportation mathematical model of leachat was established. The boundaries conditions and replenishment of model were determined, The leachate COD density and the water level were simulated, and the model was identified, and then the right model was defined. The right model was used to simulate leachate COD density in the interior, exterior, and peripheral of landfill. The results show that the COD densities are not high. The pollution is slight in the interior of landfill and is little in the exterior of landfill. They are proving the overburden on top of landfill and drain around the landfill is right. The max. density on the south of landfill shows it is scientific that the cisterns are building on the south of landfill. The paper shows the remediation scheme is feasible.     

改性沸石处理高岭土洗选废水的实验研究

采用改性沸石处理高岭土洗选废水.研究表明:时于200ml洗选废水,当改性沸石用量为5g、振荡反应20min后,改性沸石对洗选废水中CODcr的最大去除率可达94%,出水值达到国家一级排放标准;吸附脱色率达到79%,出水值可达国家二级排放标准;对铁的最佳去除率超过70%.改性沸石对CODcr的去除,主要依靠其极化表面与有机分子的极性官能团发生的强吸附反应;而对色度的去除,为其对铁和CODcr去除作用的综合结果.改性沸石对有机质的吸附选择性,要大于铁.     

改性膨润土载体复混肥对玉米的增产效应

改性膨润土载体玉米专用复混肥是由膨润土分别与尿素、硫酸铵、磷酸一氨、氯化钾等按一定的比例混合，经过特殊的生产工艺制成。三年的田间试验表明，改性膨润土载体玉米专用复混肥具有显著的增产效果，比施用普通肥料增产6．9％；改性膨润土载体玉米专用复混肥利用率51．1％，等养分量普通肥料利用率35．6％。施用改性膨润土载体玉米专用复混肥比等养分量普通肥料利用率提高15．5％。