高硫精矿配比对烧结矿性能的影响

 相比进口富矿粉,精矿品位较高,可广泛应用于铁矿石烧结工序。为了探究高硫精矿对烧结矿产质量的影响以及精矿中硫元素对烧结过程的影响,利用烧结杯试验装置进行了高硫精矿配比在25%~45%范围内的烧结杯试验。并通过微观结构、技术指标及冶金性能等方面表征了高硫精矿配比对烧结矿性能的影响。试验结果表明,精矿配比为25%时,烧结矿还原的界面反应条件较差,硅酸盐相阻碍了还原气体的扩散,致使烧结矿还原度为77.80%,软化开始温度为1 200 ℃,软熔带透气性能恶化。精矿配比为30%时,烧结利用系数提升至1.19 t/(m2·h)、垂直烧结速度达到22.22 mm/min。精矿配比为40%时,有效改善了烧结矿还原性能,恶化了低温还原粉化性能。精矿配比为45%时,烧结利用系数最高,为1.20 t/(m2·h),还原性能和低温还原粉化性能适宜。整体而言,在试验范围内,适当增加高硫精矿配比有利于提升烧结矿的还原性能和荷重软化熔滴性能,但精矿配比为45%时烧结矿的熔滴S特性值为281.02 kPa·℃,透气性能恶化。烧结烟气方面,精矿配比为40%时,烧结烟气的CO₂和NO_x含量较高,烧结过程氧化性气氛较强,降低了烧结矿中铁橄榄石等低还原性矿物含量,恶化了低温还原性能。烟气分析结果表明,高硫精矿烧结时硫元素基本都进入烧结烟气中,并未恶化烧结矿性能。     

分流制粒协同燃料分加强化红土镍矿烧结试验

 在红土镍矿烧结生产中,为了实现资源综合利用,配料过程常常会加入烧结除尘灰、高炉重力灰、细粒返矿等物料;然而,该部分物料由于制粒性差,易对料层透气性和烧结性能产生不良影响。为了改善料层透气性,同时达到提高烧结性能的目的,对烧结除尘灰、高炉重力灰及细粒返矿等物料进行了分流制粒。另外,为防止制粒小球发生欠烧,对分流制粒物料进行了燃料分加。通过烧结杯试验,研究了分流制粒协同燃料分加对料层透气性及烧结性能的影响。通过X射线衍射和金相显微镜对烧结矿进行了工艺矿物学分析,揭示了强化红土镍矿烧结性能的相关机理。结果表明,与基准相比,分流制粒协同燃料分加30%时,混合料的平均粒度由4.18 mm提高到5.99 mm,料层透气性指数由0.233 提高到0.482;同时,烧结性能大幅提高,烧结成品率由68.69 %提高到79.37%,转鼓强度由51.73%提高到60.82%,垂直烧结速度由24.44 mm/min提高到33.48 mm/min,利用系数由0.77 t/(m2·h)提高到0.99 t/(m2·h),固体燃耗由147.10 kg/t下降到130.29 kg/t。工艺矿物学表明,与基准期相比,分流制粒烧结矿的孔洞和裂纹大量减少,微观结构更加致密;同时,烧结矿主要固相铁尖晶石与液相之间润湿程度提高,针状和交织状SFCA增多,因此烧结矿固结条件大幅改善。     

提高钒钛磁铁精矿配比对烧结的影响

为了探索钒钛磁铁精矿配比变化对烧结的影响,研究了不同钒钛磁铁精矿配比对混合料制粒、混合料液相生成特性、烧结性能、烧结矿矿物组成、烧结矿冶金性能的影响,结果表明:钒钛磁铁精矿配比在46%~67%时,随着精矿配比的升高,烧结矿中TiO2含量增加,混合料的透气性指数略有降低,烧结速度明显减慢,利用系数降低,转鼓强度略有降低;总体上液相量逐渐变少,矿物结构的粘结性与结晶性变差;滴落温度明显升高,软熔区间变宽,软化温度和熔融温度在一定范围内有所波动;混合料液相生成温度升高,生成量降低,成矿性能变差。     

梅钢4号烧结改善混合料制粒效果的生产实践

2021年梅钢4号烧结使用梅山精矿的比例高达19%,高梅山精矿配比造成混匀制粒效果差,混合料透气性差,烧结利用系数低。为改善制粒效果,从配料管理、制粒设备、加水控制方式、混合料水分等方面进行改进。改进后,4号烧结混合料的粒度组成改善明显,其中混合料<1 mm比例下降7.82%,>3 mm比例提高13.13%,平均粒度从3.39 mm提高至3.94 mm;利用系数为1.275 t/(m²·h),比2020年提高了0.134 t/(m²·h)。     

高配比镜铁矿粉混合料烧结性能改善

镜铁矿铁品位高、杂质含量低,是优质炼铁原料,但其制粒性能差,导致透气性差,烧结矿产量和质量下降,因此在烧结生产中的配比(质量分数)一般不超过20%。为了增加镜铁矿在烧结生产中的使用比例,使用烧结杯实验对添加粘结剂改善高配比镜铁矿粉混合料烧结性能进行了研究。结果表明,在镜铁矿粉配比为36%时,添加质量分数为0.65%的膨润土或0.55%的BF复合粘结剂,可使烧结混合料层冷态透气性指数分别提高19.05%和27.98%,热态透气性分别提高21.48%和18.19%,烧结机利用系数分别提高11.67%和7.50%;固体燃耗则分别降低2.82和4.01 kg/t。烧结矿转鼓强度、化学成分和冶金性能均满足高炉冶炼要求。因此,2种粘结剂均能显著改善高配比镜铁矿粉混合料制粒及烧结性能,是提高镜铁矿粉配比的有效措施之一。     

粘结剂强化高配比镜铁精矿烧结研究

就添加不同种类粘结剂,以强化镜铁精矿制粒,从而提高镜铁精矿在烧结料中的配比进行了试验研究。结果表明:在镜铁精矿配比为36%时,添加有机、无机或有机无机复合粘结剂均可改善烧结料层透气性,垂直烧结速度可提高1.08~2.62 mm/min,利用系数增加了0.03~0.14 t/(m~2·h),烧结矿转鼓强度达到67%~72%,固体燃耗则降低2.82~4.01 kg/t。其中,有机无机复合粘结剂综合效果最佳。     

攀钢钒高钛型钒钛磁铁矿烧结技术进步

攀枝花钒钛磁铁矿矿物组成复杂,其精矿产品含铁品位低、TiO2含量高,采用阶磨阶选工艺可使精矿品位达到54%,但TiO2仍高达13%左右;该精矿具有"低铁、低硅、高钛、高铝、高亚铁、高硫"的特点,同时精矿粒度粗,制粒性能差,影响烧结透气性;该精矿初始熔点高,生成液相量少,烧结矿矿物组成复杂,严重影响强度与冶金性能。近十多年来,通过采取使用生石灰,提高烧结矿碱度,燃料分加,配加普通矿粉,烧结机技术升级,采取高负压大风量烧结等一系列强化技术,烧结取得了重大技术突破,利用系数达到1.4 t/(m2.h)以上,转鼓指数达到73%以上,改变了钒钛精矿烧结多年的落后状况,满足了高炉精料要求,高钛型钒钛磁铁矿烧结技术处于世界先进水平。     

分流预成型强化制粒改善镜铁矿粉烧结性能

针对镜铁矿精粉成球性及可烧性差的特点,采用分流预成型强化制粒工艺对进口镜铁矿精粉制粒及烧结性能开展研究.与常规制粒工艺烧结指标相比,采用分流造球强化制粒烧结工艺,焦粉配比从4.85%降至4.20%,利用系数从1.44 t·m-2·h-1提高至1.71 t·m-2·h-1,转鼓强度从57.60%提高至63.80%,固体燃耗从76.46 kg·t-1降至65.24 kg·t-1;采用分流辊压预成型强化制粒烧结工艺,焦粉配加量从4.85%降至4.70%,利用系数从1.44 t·m-2·h-1提高至1.64 t·m-2·h-1,转鼓强度及固体燃耗基本不变.因此,分流预成型强化制粒工艺较常规制粒工艺能显著改善镜铁矿烧结性能.其作用机理为:镜铁精矿经分流预成型后能改善混合料的透气性,降低焦粉配比,提高烧结料层氧位,生成更多的铁酸钙及赤铁矿,所得成品烧结矿结晶完善,矿物之间胶结紧密,内部气孔由不规则大孔变为总体分布较为均匀且大小适中的规则球形,改善了烧结矿的强度和还原性.      

强化制粒对含铬型钒钛混合料烧结的影响

 含铬型钒钛混合料制粒效率低,料层透气性差,严重影响了其发展低温高料层烧结。在基准方案基础上,通过烧结杯试验研究了生石灰配比、混合料水分、润湿时间和制粒时间对含铬型钒钛混合料烧结的影响,并对强化制粒效果进行了观察。试验结果表明：在碱度为2.15、配碳量为3.2%(质量分数)、混合料配加生石灰为5%、水分为7.5%、消化时间为10 min,制粒时间为8 min时,平均粒径[d]、拟似粒化指数[GI0]、制粒效率[E]、抗粉化指数[B]分别由2.26 mm、66.30%、54.11%、48.15%提高到2.58 mm、80.43%、90.82%、73.53%,烧结速度、成品率、利用系数、转鼓强度分别由16.54 mm/min、70.39%、1.22 t/(m2·h)、55.36%提高到19.70 mm/min、77.94%、1.64 t/(m2·h)、59.36%。含铬型钒钛混合料对水分敏感度高,应严格控制水分波动。采用强化制粒措施,提高料层透气性,增加氧势,可提高烧结矿中铁酸钙质量分数改善其矿物组成与结构,提高产质量。     

富氧条件下高精粉配比对烧结指标及冶金性能的影响

为了深入研究富氧条件下磁铁矿配比对烧结矿烧结指标和冶金性能的影响,采用烧结杯试验、还原和软熔设备研究了不同磁铁矿配比下的烧结指标、还原性、低温还原粉化与软熔特性。试验结果表明,随着磁铁矿粉配比由0提升到56.4%,小于10 mm粒级烧结矿所占比例下降,大于40 mm粒级烧结矿所占比例有较大的波动,烧结料面富氧后成品烧结矿所占比例增加;垂烧速度由22.35 mm/min下降到15.87 mm/min,成品率先由73.88%升高到79.08%,后又下降到77.49%,利用系数在矿粉A配比为32.4%时达到最高,转鼓指数由59.26%上升到76.09%,收缩率和烧损随着矿粉A配比提高显著降低;富氧和增加磁铁矿配比共同导致烧结时间延长和转鼓指数的提升,随着矿粉A配比由0增加到56.4%,烧结矿的还原性由88.51%下降到82.13%,烧结矿的低温还原粉化指数由74.70%升高到了80.75%,软熔温度上升,软熔区间有下移趋势,且软熔区间变窄,滴落速度整体上呈现出下降趋势,熔滴滴落量降低,熔滴特性的变化主要是由于烧结矿中w(MgO)/w(Al₂O₃)提...     

Improvement of Sinter Properties With Ultra Fine-Sized Iron Concentrate by HPRG

The experiments were conducted on the changes of sintering performance of one kind of ultra fine-sized iron concentrate with or without being processed by high pressure roll grinding (HPRG). The experimental results indicate that the specific surface area increases from 1723. 0 to 2201. 6 cm²/g when the iron concentrate is processed by HPRG. The permeability of sintering mix increases and the iron concentrate becomes easy to react with CaO reagent at high temperature. The effect gets intensified when iron concentrate and lime are processed together by HPRG. The further studies indicate that compared with the base case, the sinter quality also gets improved, in which the yield of sinter increases from 67.24% to 69. 52% and further to 71. 68%, the tumble index (TD increases from 60. 38% to 62. 13% and further to 64. 45%, and the productivity increases from 1. 42 to 1. 57 t/(m² · h) and further to 1. 62 t/(m² · h) when the iron concentrate is processed by HPRG or is processed with lime together. The metallurgical properties of sinter also get improved when the iron concentrate is pretreated by high pressure roll. The results indicate that it is conducive to the increase of sinter quality and productivity when the iron concentrates are processed by HPRG.     

强力混合对高比例精矿烧结的影响及机制

通过混合试验、制粒试验以及烧结杯试验研究了强力混合技术对高比例精矿烧结的影响,包括混合效果、制粒效果以及烧结指标,阐明了强力混合影响高比例精矿烧结的作用机制.结果表明,与圆筒混合机相比,采用强力混合机时混合料中水分、生石灰和核颗粒分布更为均匀;制粒效果得到改善,制粒小球中粒度大于3 mm含量提高了8.25％(质量分数)...     

武钢常用含铁原料特性及配矿实践

从化学成分、粒度组成、成球性能和烧结性能等方面研究了武钢常用含铁原料的烧结特性。结果表明:非粉和纽粉烧结性能较好,巴粉、委粉和MAC粉烧结性能中等,精矿、FMG和加粉烧结性能较差。在此基础上提出了优化配矿方案,从而改善了混匀矿的烧结性能,促进了烧结经济技术指标的改善。2011年1~4月烧结台时产量达到440.22 t/(台·h),转鼓指数达到79.8%,分别较上年同期提高了30.8t/(台·h)和0.59%。     

Improvement of sintering performance of sinter mixtures containing high ratio of specularite fines

Although specularite fines possess high iron grade and low impurities, their granulation performance was poor so that the ratio of specularite fines is kept below 20% in sinter ore blends because of low permeability and productivity and weak strength. In order to increase its ratio in sintering, binders were used to improve the granulation performance of sinter blends containing high ratio of specularite fines in sintering pot test. Results show that cold permeability of the sintering bed increases by 19. 05% by adding 0. 65mass% bentonite or by 27. 98% by 0. 55mass% BF composite binder respectively when 36 mass% specularite fines are proportioned in sinter blends. In addition, the hot permeability is also improved by adding bentonite or BF composite binder, respectively, resulting in an increase in the productivity of 11. 67% and 7. 50% as well as an decrease in solid fuel consumption of 2. 82kg/t and 4. 01kg/t, respectively, while the tumble index, chemical composition and metallurgical performance meet the requirement of blast furnace. So using suitable binders is one of effective ways to improve the granulation and sintering performance of sinter ore blends comprising high ratio of specularite fines.     

钒钛铁精矿配比对钒钛烧结矿冶金性能的影响

就提高钒钛铁精矿配比对攀钢钒钛烧结矿冶金性能的影响进行了研究。结果表明:钒钛铁精矿配比从46%提高到52%,钒钛烧结矿的FeO含量升高,低温还原粉化率降低,中温还原度降低,软化开始、压差陡升和滴落温度均升高,最大压差升高。本结果可为钒钛铁精矿烧结合理配矿提供指导。     

焦粉粒度分布对铁矿石烧结指标的影响

焦粉粒度对烧结生产指标具有重要的影响。通过烧结杯试验开展焦粉粒度最佳组成的试验研究。结果表明，焦粉粒度从小于1 mm增加到5~8 mm时，烧结矿强度、烧结利用系数、固体燃耗、产量、垂直烧结速度及粒度分布均变差；烧结生产所使用的焦粉粒度组成可根据生产目标进行调整，当要求烧结矿转鼓强度达到最高值时，焦粉的粒度分布应当是57.20%的小于1 mm、25.63%的1~3 mm、11.17%的3~5 mm和6.00%的5~8 mm。当焦粉由鞍钢实际生产的粒度分布调整为最佳粒度分布时，烧结原料矿化过程合理，烧结矿转鼓强度增加1.48%，产量增加1.73%，10~40 mm的烧结矿增加2.16%，固体燃耗降低0.69 kg/t，冶金性能指标明显改善。研究结果对烧结生产中合理控制焦粉粒度分布具有一定的理论指导作用。     

红土镍矿烧结节能降耗技术研究及应用

褐铁矿型红土镍矿具有较低的铁品位和丰富的结晶水及高熔点矿物,这导致其烧结矿产质量低、固体燃耗高。通过开发加压致密化烧结技术、热废气循环烧结技术及多力场协同强化烧结技术,显著改善了其烧结矿产质量指标,有力地促进了节能减排。相对于常规烧结工艺,采用多力场协同强化技术后,烧结矿转鼓强度由45.87%增至56.93%,利用系数由0.97增至1.15 t/(m2·h),固体燃耗从140.52减至107.91 kg/t,废气中CO₂、NO_x及SO₂最高体积分数分别由27.42%、0.019 8%和0.261 5%降至19.89%、0.015 4%及0.203 0%,有害气体排放明显减少。这在相关工业应用中得到进一步验证。为更好地实现褐铁矿型红土镍矿烧结的清洁生产,可开发球团烧结技术,以进一步改善烧结矿产质量指标和降低生产能耗,值得大力推广应用。