基于MCzHQZn的有机电致发光器件

通过结构为ITO/2T-NATA(20nm/NPBx(20nm)/MCzHQZn(30nm)/BCP(10nm)/Alq3(20nm)/LiF(0.5nm)/Al、ITO/2T-NATA(30nm/MCzHQZn(30nm)/BCP(10nm)/Alq3(30nm)/LiF(0.5nm)/Al和ITO/2T-NATA(20nm/MCzHQZn(30nm)/NPBx(16nm)/BCP(10nm)/Alq3(25nm)/LiF(0.5nm)/Al的3组有机电致发光器件(OLED),证明了MCzHQZn既具有空穴传输特性,又具有较好的发光特性。MCzHQZn在器件1中作发光层,器件最大亮度在电压16V时达到3692cd/m2,电压13V时的最大效率为0.90cd/A,发光的峰值波长为564nm;MCzHQZn在器件2中既作发光层又作空穴传输层,器件最大亮度在电压为13V时达到1929cd/m2,电压12V时的最大效率为0.57cd/A,发光的峰值波长也为564nm;MCzHQZn在器件3中作空穴传输层,由NPBx作发光层,器件最大亮度在电压为14V时达到3556cd/m2,电压9V时的最大效率为1.08cd/A,...     

空穴传输层厚度对OLED性能的影响

该文采用聚乙烯基咔唑(PVK)作为空穴传输层,8-羟基喹啉铝(Alq3)作为发光层,制备了结构为ITO/PVK (0~60nm)/Alq3(60 nm)/Mg:Ag/Al的有机发光二极管。通过测试器件的电流-电压-发光亮度特性,研究了空穴传输层厚度对有机发光二极管器件性能的影响,优化了器件功能层的厚度匹配。实验结果表明,有机发光二极管的光电性能与空穴传输层的厚度密切相关,当空穴传输层厚度为15 nm时,有机发光二极管器件具有最低的起亮电压、最高的发光亮度和最大的发光效率。     

未掺杂条件下载流子平衡提高有机电致发光器件效率的研究

用具有高电子迁移率(5×10-4cm2 V-1 s-1)的材料4,7-diphenyl-1,10-phenanthroline(BPhen)作为电子传输层(ETL),N,N-his-[1-naphthy(-N,Ndiphenyl-1,1'-biphenyl-4,4'-diamine)](NPB)作空穴传输层(HTL),tris(8-hy-droxyquinoline) aluminum(Alq3)作发光层(EML),使有机薄膜电致发光器件的效率得到显著改善.器件基本结构为:ITO/NPB/Alq3/BPhen/LiF/A1.通过对HTL和ETL的厚度进行优化,在电流密度为20mA/cm2时,器件的电流效率达到6.80cd/A,亮度达到1361 cd/m2.为了探索发光器件的效率得以改善的原因,制备了结构为ITO/A1q3/BPhen/Al的electron-only器件和结构为ITO/NPB/AI的hole-only器件.通过调整hole-only器件中空穴传输层(HTL)和electron-only器件中电子传输层(ETL)之间的厚度匹配并比较它们之间的J-V曲线,发现当电子和空穴达到栽流子平衡时,发光器件获得最佳效率和亮度.     

Spiro发光双层结构有机电致发光器件

为了研究简单结构有机电致发光器件的发光性能，采用PEDOT：PSS作为空穴输运层，Spire作为电子输运层和发光层，以金属Ba覆盖以金属AI作阴极，制备双层结构有机电致发光器件，得到性能稳定的蓝色发光。测量器件的电流密度-电压特性、发光亮度-电压特性和电致发光谱，计算了器件的外量子效率。结果表明，器件电流以陷阱电荷限制电流为主，最大发光亮度为3544cd/m2，最大外量子效率达2．40％。     

Spiro发光双层结构有机电致发光器件

为了研究简单结构有机电致发光器件的发光性能,采用PEDOT∶PSS作为空穴输运层,Spiro作为电子输运层和发光层,以金属Ba覆盖以金属Al作阴极,制备双层结构有机电致发光器件,得到性能稳定的蓝色发光。测量器件的电流密度-电压特性、发光亮度-电压特性和电致发光谱,计算了器件的外量子效率。结果表明,器件电流以陷阱电荷限制电流为主,最大发光亮度为3544cd/m2,最大外量子效率达2.40%。     

利用Ir(ppy)_3敏化CzHQZn提高OLED的性能

用CzHQZn作为受主,利用磷光敏化的方法制备了有机电致黄光和白光器件。黄光器件采用Ir(ppy)3掺杂4,4-N,N′-=咔唑基联苯(CBP),敏化新的黄光材料CzHQZn作为发光层,当发光层厚度为18nm时器件性能最好,最大发光效率为3.26cd/A(at10V),最大发光亮度为17560cd/m2(at10V);白光器件采用多发光层结构,结合ADN的蓝光复合发光,同时加入了电子阻挡层(NPBX)和空穴阻挡层(BCP),获得的白光器件最大发光效率为2.94cd/A(at8V),最大亮度为11089cd/m2(at13V)。     

NPB层嵌入MgF_2超薄层对OLED性能的影响

将MgF2超薄层嵌入有机电致发光器件(OLED)的空穴传输层NPB中,制备了结构为ITO/NPB(10nm)/MgF2(xnm)/NPB(20nm)/Alq3(30nm)/Al(30nm)的一系列OLED。测试结果表明,合适厚度的MgF2可有效降低器件启亮电压,提高器件的发光效率。MgF2厚度为0.5nm的器件启亮电压只有2.3V,较未嵌入MgF2器件降低2V;MgF2厚度为1.0nm的器件最大电流效率达到3.93cd/A,最大光功率效率达到1.58lm/W,较未嵌入MgF2器件分别提高95%和110%。     

载流子平衡的低压高效有机白光器件

研究了结构为ITO/m-MTDATA:x%4F-TCNQ/NPB/TBADN:EBDP:DCJTB/Bphen:Liq/LiF/Al的有机白光电致发光器件(WOLED)。分别在ITO与NPB间加入高迁移率的m-MTDATA:4F-TCNQ来增强器件的空穴注入,在阴极和发光层间加入高迁移率的Bphen:Liq层增强器件的电子注入,降低驱动电压,提高器件效率。同时,由于注入的电子和空穴数量偏离平衡,器件的效率也会受到影响。实验中,通过调节4F-TCNQ的掺杂浓度来调控空穴的注入和传输,使载流子达到高度平衡。器件的最大电流效率和流明效率分别达到了9.3cd/A和4.6 lm/W。     

NaCl修饰SnO_2/钙钛矿界面的高效钙钛矿太阳能电池

钛矿太阳能电池(PSC)通常由电子传输层(ETL)、钙钛矿光吸收层和空穴传输层组成,而电子传输层/钙钛矿层和钙钛矿层/空穴传输层的界面对钙钛矿薄膜的性质及太阳能电池的性能有较大影响。通过简单的旋涂法,在SnO_2电子传输层上旋涂一层NaCl层,来修饰SnO_2电子传输层与MAPbI_3钙钛矿光吸收层之间的界面。结果表明:NaCl修饰层不仅能提供部分Na~+和Cl~-溶解在钙钛矿前驱体中,辅助钙钛矿结晶,增大钙钛矿晶粒尺寸,而且NaCl能同时与MAPbI_3钙钛矿层和SnO_2电子传输层作用形成Pb—Cl和Sn—Cl键,使界面的化学结合增强,降低界面缺陷态,增强载流子的寿命和传输效率。此外,NaCl修饰层显著降低了电子传输层的功函数,使制得的器件开路电压高达1.141V,太阳能电池最终获得了高达19.49%的光电转换效率。     

基于TADF共掺杂的蓝光OLED器件性能研究

为提升蓝光OLED的发光性能,采用DPEPO和DMAC-DPS两种热活化延迟荧光(TADF)材料构成的主客体掺杂结构作为蓝光OLED器件的发光层,研究器件结构、客体掺杂浓度等因素对器件性能的影响。实验结果表明:采用MoO3薄膜作为空穴注入层有助于增强空穴注入和传输能力,进而提升器件性能。当DMAC-DPS掺杂浓度为30%时,器件性能是最优的,最大亮度为5650cd/m2,最大外量子效率(EQE)为8.63%。掺杂浓度进一步增大会导致器件性能的衰退,可能是因为高浓度导致的激子淬灭导致的。TADF有助于提升蓝光OLED器件的性能并有望应用于商业化的蓝光OLED器件中。     

High efficiency blue phosphorescent organic lighting-emitting diodes with novel anode structure

High-efficiency blue electrophosphorescent organic light-emitting devices employing MoO3 used as hole injection layer （HIL） and MoO3 doped N,N-dicarbazoly-3,5-benzene （mCP） as hole transport layer （HTL） were demonstrated. The blue OLED with the novel anode structure and TAPC used as electron blocking layer show a low turn-on voltage of 2.4 V, a maximum power efficiency of 33.6 lm/W at 3.1 V and 25 lrn/W with 1 000 cd/m2 at 3.8 V. It is also found that the efficiency of the devices is dependent on the different EBL materials. This is may because of relationship with the charge mobility and the triplet energy level of EBL materials. The device efficiency is determined by the charge balance which plays an important role.     

Performance of a combined capacitor based on ultrafine nickel oxide／carbon nanotubes composite electrodes

A new sol-gel process for the preparation of ultrafine nickel hydroxide electrode materials was developed. The composite electrodes consisting of carbon nanotubes and Ni(OH)2 were developed by mixing the hydroxide and carbon nanotubes together in different mass ratios. In order to enhance energy density, a combined type pseudocapacitor/electric double layer capacitor was considered and its electrochemical properties were characterized by cyclic voltammetry and dc charge/discharge test. The combined capacitor shows excellent capacitor behavior with an operating voltage up to 1.6 V in KOH aqueous electrolyte. Stable charge/discharge behaviors were observed with much higher specific capacitance values of 24 F/g compared with that of EDLC (12 F/g) by introducing 60% Ni(OH)2 in the anode material. By using the modified anode of a Ni(OH)E/Carbon nanotubes composite electrode, the specific capacitance of the cell was less sensitive to discharge current density compared with that of the capacitor employing pure nickel hydroxide as anode. The combined capacitor in this study exhibits high energy density and stable power characteristics.     

高亮度高分辨率YAG投影显示管

介绍了一种HDTV显示用的7.6cmYAG (钇铝石榴石)投影阴极射线管(CRT),采用离心沉屏法将荧光粉沉积在YAG面板上制作高密度荧光屏,该荧光屏上制作有多层干涉过滤膜。管壳采用能与YAG进行匹配封接的玻璃材料。经过优化设计的预聚焦透镜和主聚焦透镜满足显示HDTV图像的要求。测试结果表明,在阴极电流为1.0mA和阳极电压为29kV条件下,红、绿、蓝管的亮度分别可达1.4×105 cd/m2、6.2×104 cd/m2和8×103 cd/m2,绿色管子50%图像线宽为85μm。采用该管的122cm背投和183cm前投电视机的水平分辨率为1000电视线,平均白场亮度分别为624cd/m2和890cd/m2.     

非对称型门极换流晶闸管的优化设计

根据半导体器件的设计特点和设计原则,对600 A/3 000 V非对称型门极换流晶闸管进行了结构参数的优化设计,得到了材料参数与结构参数的关系.阴极采用条状同心环单元发射极排列结构,不仅可以提高单元承受应力的能力,而且可使单元均匀性得到改善.应用数值分析,使器件的透明阳极和缓冲层等关键结构的掺杂分布、区域宽度以及少子寿命得到优化,计算结果满足设计的要求.     

Highly efficient stacked organic light-emitting devices employing a novel intermediate layer

Highly efficient stacked organic light-emitting devices (OLEDs) have been fabricated using Mg:Alq3:BCP/ WO3 as a novel intermediate layer, which connects two identical emissive units. The stacked OLEDs consisting of NPB/Alq3 exhibited high current efficiency and brightness characteristics over conven- tional single-unit device. At 200 mA/cm2, the current efficiency of the stacked OLEDs using the inter- mediate layers of Mg:Alq3:BCP/WO3 were about 6.85 cd/A, doubling that of the conventional device. The results may prove the method to be effective to enhance the current efficiency and brightness of OLEDs.     

MoO3源漏电极缓冲层对有机薄膜晶体管性能的影响

以并五苯(pentacene)作为有机薄膜晶体管(OTFTs)的载流子传输层,采用比常用金电极(Au)廉价的Ag作为源漏电极,在pentacene与Ag之间添加MoO3超薄层作为缓冲层,制备了具有较高场效应迁移率(μ)的晶体管器件。结果表明,器件在栅极电压VG为40 V时,传输电流IDS超过了50 μA,空穴迁移率达到0.26 cm2/Vs。同时,从器件的输出特性与物理机制分析了MoO3缓冲层在器件中的作用。     

高亮度LCD平板背光源的制备及性能研究

为进一步提高内部无电极型LCD平板背光源的发光亮度及其使用寿命,制备了一种利用固体ITO导电薄膜为导电介质的等离子体激发发光平板背光源.这种电光源由两片平板玻璃中间充入纯氙气(气压2.66 104Pa)密封而成,光源内表面上均匀涂敷一层荧光粉,在玻璃板的外表面上用透明导电胶粘上一层ITO(氧化铟锡)导电薄膜作为导电介质,以1.1mm厚的玻璃板作为介质阻挡放电层,在高频交变电压的作用下产生等离子体,激发荧光粉发光.最大发光亮度可达5 000 cd/m2,可持续发光5 000 h,最佳激发频率10.0 kHz,发光均匀度大于92%.     

反转结构有机发光二极管的电子注入层研究

将薄层金属Al和含磷氧基团的有机材料DPSF依次蒸镀在ITO阴极上作为电子注入层,成功制备了具有反转结构的底发光有机发光二极管（IBOLED）。结果表明,Al/DPSF作为电子注入层可以有效降低ITO与发光层Alq3之间的注入势垒,大大降低了器件的工作电压,显著提高了器件的发光效率。反转器件的最大电流效率达到了4.9 cd A^-1,最大亮度为17000 cd m^-2,与正置器件的发光性能相当。