Power factor of La1−xSrxFeO3 and LaFe1−yNiyO3

The electrical conductivity (σ), Seebeck coefficient (S), and power factor (σS²) of perovskite-type LaFeO₃, La_1−xSr_xFeO₃ [0.1 ≤ x ≤ 0.4] and LaFe_1−yNi_yO₃ [0.1 ≤ y ≤ 0.6] were investigated in the temperature range of 300–1100 K to explore their possibility as thermoelectric materials. The electrical conductivity of LaFeO₃ showed semiconducting behavior, and its Seebeck coefficient changed from positive to negative around 650 K with increasing temperature. The electrical conductivity of LaFeO₃ increased with the substitutions of Sr and Ni atoms, while its Seebeck coefficient decreased. The Seebeck coefficient of La_1−xSr_xFeO₃ was positive, whereas that of LaFe_1−yNi_yO₃ changed from positive to negative with increasing Ni content. The substitutions of Sr and Ni were effective in increasing the power factor of LaFeO₃; 0.0053 × 10⁻⁴ Wm⁻¹ K⁻² for LaFeO₃ (1050 K), 1.1 × 10⁻⁴ Wm⁻¹ K⁻² for La_1−xSr_xFeO₃ (x = 0.1 at 1100 K) and 0.63 × 10⁻⁴ Wm⁻¹ K⁻² for LaFe_1−yNi_yO₃ (y = 0.1 at 1100 K).     

HfFe6Ge6-type YbMn6Ge6−xGax compounds (0.07≤x<0.72) with large magnetocrystalline anisotropy

The HfFe₆Ge₆-type YbMn₆Ge_6−xGa_x solid solution (0.07≤x≤0.72) has been studied by X-ray diffraction, microprobe analysis and powder magnetization measurements. All the compounds order antiferromagnetically between T_N=481 K for x=0.07 and T_N=349 K for x=0.72 and display more or less pronounced spontaneous magnetization at lower temperature. The corresponding Curie points increase from 40 K for x=0.07 to 319 K for x=0.72. The maximum magnetization values of the Ga-rich compounds (M≈5 μ_B/f.u. at 6 K) is compatible with a ferrimagnetic order of the Mn and Yb sublattices whereas the smaller values measured in the Ga-poor compounds suggest the stabilization of non-colinear magnetic structures. All the studied compounds are characterized by rather large coercive fields at low temperature (4.0≤H_c≤8.2 kOe).     

On the crystal structure of new series of compounds, RPt2+xSb2−y (x = 0.125, y = 0.25; R = La, Ce, Pr)

A new compound CePt_2+xSb_2−y (x = 0.125, y = 0.25) was synthesized by arc-melting of the elements. The chemical and structural characterizations were carried out at room temperature on as-cast samples using X-ray diffractometry, metallographic analysis and EDS-microanalysis. According to the results of X-ray single crystal diffraction this antimonide crystallizes in I4cm space group (no. 108), Z = 32, ρ = 12.19 Mg/m³, μ = 89.05 mm⁻¹ (a = 12.5386(3) Å, c = 21.4692(6) Å (crystal I) and a = 12.5455(2) Å, c = 21.4791(5) Å (crystal II)). The structure and composition were confirmed by powder X-ray diffraction (a = 12.4901(2) Å, c = 21.3620(4) Å) and EDS-microanalysis respectively. Isotypic compounds were observed with La and Pr from X-ray powder diffraction of as-cast alloys at room temperature (a = 12.6266(4) Å, c = 21.4589(6) Å for LaPt_2+xSb_2−y and a = 12.5184(5) Å, c = 21.4178(7) Å for PrPt_2+xSb_2−y). The CePt_2+xSb_2−y structure is derived from CaBe₂Ge₂ (a = 2a₀ − 2b₀, b = 2a₀ + 2b₀, c = 2c₀) and comprises a new atomic arrangement with both vacancy on 4(b) pyramidal site and substitution of antimony atoms (X) by platinum (B) in the B–XX–B layers (referring to the subcell structure) forming two B––1/2B1/2XX–3/4B and two X–BB–X layers per cell. The structure of CePt_2+xSb_2−y is compared with those reported before for URh_1.6As_1.9 and CeNi_1.91As_1.94.     

Phase behavior and some properties of LaMn1−xRhxO3 solid solution

Structure and magnetic and electrical properties of the polycrystalline compounds LaMn_1−xRh_xO₃ (0 < x ≤ 1) have been investigated. The samples were characterized by X-ray diffraction and Rietveld refinement which confirmed the space group Pnma (No. 62) for all compositions at room temperature. A transformation from O′- to O-type orthorhombic structure is seen near x = 0.6 tending to make the phase unstable. The electrical conductivity measurement shows semiconducting property above room temperature with a rather low activation energy for Mn-rich compositions. Compounds in the region 0.1 ≤ x ≤ 0.9 show ferromagnetic property but the substitution of Rh³⁺ ion for Mn³⁺ ion suppresses the ferromagnetism that results in reducing the Curie temperature, T_C.     

Characterization and hydrogenation of CeNi5−xCrx (x = 0, 1, 2) alloys

The effect of partial substitution of Ni by Cr in CeNi₅ intermetallic compound has been studied by pressure–composition isotherm measurements for different temperatures. The samples were prepared of high purity materials using the standard arc melting technique in argon atmosphere. The structure and the elemental composition of different alloys have been investigated by means of XRD, SEM and EDX techniques. The unit cell volume of the alloy was found to increase with increasing Cr content. In order to calculate the hydrogen storage capacity pressure–composition isotherm has been investigated for CeNi_5−xCr_x (x = 1, 2) alloys in the temperature and pressure ranges of 293 ≤ T ≤ 333 K and 0.5 ≤ P ≤ 35 bar, respectively. The P–C–T isotherm for different alloys clearly shows the presence of three regions ,  + β and β. The enthalpy and entropy for the systems has also been calculated using Van’t Hoff plot. The variation of enthalpy and entropy with hydrogen content has also been studied.     

Magnetocrystalline anisotropy of Nd3(Fe1−xCox)27.7Ti1.3Ny compounds

The effect of Co substitution for Fe in Nd₃(Fe_1−xCo_x)_27.7Ti_1.3N_y (0 ≤ x ≤ 0.4) compounds on the magnetocrystalline anisotropy has been investigated. The anisotropy constants K's and the anisotropy field H_A have been deduced from the magnetization curves measured on magnetically aligned powder (4–7 μm) samples. The obtained results show that at RT the anisotropy is uniaxial and H_A (about 10 T) does not change substantially upon the substitution. At 5 K the results for K's give evidence for the presence of easy-cone-type anisotropy. The cone angle as well as the anisotropy field decrease upon the substitution from 21.6° to 11.8° and from 22.8 to 18.6 T, respectively.     

Subsolidus phase relation and crystal structure of the PrBa2−xSrxCu3O7±δ system

The PrBa_2−xSr_xCu₃O_7±δ solid solution was investigated by means of X-ray powder diffraction in combination with Rietveld analysis. The Sr-doped Pr123 single phase could be synthesized at 950 °C in air. The solubility of PrBa_2−xSr_xCu₃O_7±δ solid solution is 0.2≤x≤0.6. The structure of PrBa_2−xSr_xCu₃O_7±δ is orthorhombic for x=0.2. The structure transforms into tetragonal for 0.3≤x≤0.6. In the PrBa_2−xSr_xCu₃O_7±δ structure, Sr ions can replace Ba ions, the highest value is x=0.6 under our experimental condition. But Sr ions could not replace Pr ions. Furthermore Pr ions could not occupy the sites of Ba ions in the PrBa_2−xSr_xCu₃O_7±δ system. Both ionic radii and chemical properties play an important role in the mutual substitution of Pr, Ba and Sr ions in the Pr123 structure of the PrBa_2−xSr_xCu₃O_7±δ system.     

Magnetic properties and spin-reorientation transition in DyFe10−xNixSi2 compounds

The magnetic properties of DyFe_10−xNi_xSi₂ compounds with x = 0, 1, 2, 3, 4, 6, 9 and 10 have been investigated by means of X-ray diffraction and magnetic measurements. Substitution of Ni for Fe leads to a decrease in the lattice constants a, c and the unit-cell volume V. The Curie temperature reaches a maximum of 590 K at x = 2, then decreases strongly for x ≥ 2. The spin reorientations are observed for the compounds with x = 0, 1, 2 and 3. The spin reorientation temperature decreases strongly from 255 to 60 K as the Ni content is increased from x = 0 to 3. Below the spin reorientation temperature, the compounds exhibit ferrimagnetic ordering. For the Ni-rich compounds with x = 9 and 10, the magnetization of the Dy sublattice decreases strongly since the magnetization of the Dy sublattice is strongly affected by the molecular field produced by the 3d sublattice.     

Magnetic phase transition in Ti-doped ErCo2 alloys

The homogeneity range of U₂Co_17−xSi_x system with the hexagonal Th₂Ni₁₇-type crystal structure extends from x = 1 to 3.4. The variation of the magnetic properties within the homogeneity range was studied on single crystals. All the compounds are ferromagnetic, M_s and T_C decrease monotonously with increasing Si content. The strongly modified magnetic anisotropy of U₂Co_17−xSi_x, as compared to isostructural Lu₂Co_17−xSi_x with the non-magnetic Lu, points to a magnetic state of U up to x = 3.0. The U contribution to K₁ decreases with increasing Si content and vanishes at x = 3.4 that can be treated as a transition from magnetic to non-magnetic state of U. Spin reorientation was observed with varying temperature in compounds with x ≤ 3 due to a competition of the U and Co sublattices anisotropies which occurs as two second-order phase transitions of the “plane–cone” and the “cone–axis” type.     

Ce(Au,Sb)2 with UHg2 structure type, a new member of the AlB2 family

A new ternary compound Ce(Au,Sb)₂, with a homogeneity range has been observed from X-ray powder diffraction of as cast alloys, a = 4.743–4.712 Å, c = 3.567–3.768 Å. Its crystal structure was investigated by X-ray diffraction from Ce(Au_1−xSb_x)₂ (x = 0.266) single crystal: CAD-4 automatic diffractometer, Mo K radiation, a = 4.7256(6) Å, c = 3.6711(6) Å, P6/mmm space group, V = 70.997(17) Å³, Z = 1, ρ = 10.732 Mg/m³, μ = 76.369 mm⁻¹, R₁ = 0.0415, wR₂ = 0.0793 for 99 reflections with I > 2σ(I₀). The coordination polyhedron of X (X = 0.734Au + 0.266Sb) atom is a full-capped trigonal prism [XCe₆X₃X₂]. Ce atom is coordinated by 14 atoms: [CeX₁₂Ce₂]. The compound is isotypic with UHg₂ structure, a deformation derivative of AlB₂ structure type. It forms isostructural compounds with La and Pr.     

Synthesis and characterization of LiGaxMn2−xO4 (0 ≤ x ≤ 0.05) by triethanolamine-assisted sol–gel method

Spinel LiGa_xMn_2−xO₄ (0 ≤ x ≤ 0.05) cathode materials with phase-pure particles and nano-sized distribution were synthesized by sol–gel method using triethanolamine as the chelating agent. The effects of heat treatment on the physicochemical properties of the spinel LiGa_xMn_2−xO₄ powders were examined with thermogravimetric and differential thermal analysis (TG/DTA), powder X-ray diffraction (XRD) and scanning electron micrograph (SEM). The LiGa_xMn_2−xO₄ (0 ≤ x ≤ 0.05) electrodes were characterized electrochemically by charge/discharge experiments under a current rate of 0.5C at 55 °C. Although the Ga-doped spinel electrode showed smaller initial discharge capacity, it exhibited better cycling performance than the undoped-LiMn₂O₄ electrode. The dQ/dV versus potential plots at 55 °C revealed that the improvement in cycling performance of the Ga-doped spinel electrode is attributed to stabilization of the spinel structure by the presence of gallium ion.     

Dependency of c-lattice parameter, activation energy and its magnetic power constant on x in Y1−xYbx/2Gdx/2Ba2Cu3O7−y superconductors

To investigate the effect of x on c-lattice parameter, the activation energy, and the magnetic power constant of activation energy, the nominal composition of Y_1−xYb_x/2Gd_x/2Ba₂Cu₃O_7−y superconducting samples for x = 0.0, 0.2, 0.4, 0.6, 0.8 and 1.0 were prepared by solid-state reaction technique. c-Lattice parameters of the samples were calculated using XRD data. From the resistivity curves which were obtained under 11 different magnetic fields from 0 up to 5 T in the temperature range from 70 to 100 K steps by 0.25 K in zero field cooling regime, the activation energies of the samples were determined using Arrhenius activation energy law. The magnetic power constants of activation energy of the samples were calculated from the slopes of the plots ln U versus ln H. The results showed that the value of c-lattice parameters of samples x = 0 (Y123), and x = 1.0 (YbGd123) are in good agreement with the reported works. It was found that c-lattice parameter decreased with the increasing the content x except samples of x = 0.4 and 1.0. It was thought that the origin of the separation from the linearity comes from the lack of Y in nominal composition for x = 1.0. As for the sample x = 0.4, it was thought to be due to the fact that Y, Yb and Gd atoms affect the superconductivity properties dominantly. On the other hand, there is a similarity among U(0 T), U(1 T), its magnetic power constant and the c-lattice parameter with increasing content x. The desired activation energy and its magnetic field dependency constant can be controlled with x and then this can be useful for the superconducting applications.     

Composition-dependent electrical transport properties of Pb50Te52 doped with PbI2 prepared by HPHT

Cubic (Pb₅₀Te₅₂)_100−x(PbI₂)_x (0 ≤ x ≤ 0.065) bulk thermoelectric (TE) materials with enhanced power factor were prepared by high-pressure and high-temperature (HPHT) method. The mean grain size of the samples was about 10 μm. The dependence of electrical transport properties on composition was studied at room temperature. With an increase of x, the Seebeck coefficient in absolute value and the electrical resistivity firstly increase slightly and then decrease dramatically. The maximum power factor reaches 24.2 μW cm⁻¹ K⁻² at x = 0.015, which is much higher than that reported previously for the PbTe doped with PbI₂ prepared at normal pressure. The results indicate that HPHT combined with trace quantity doping is an effective method to enhance the thermoelectric properties for PbTe.     

Influence of stress on magneto-impedance in Co71−xFexCr7Si8B14 (x = 0, 2) amorphous ribbons

Systematic measurements of stress-impedance (SI) have been carried out using Co-rich amorphous ribbons of nominal composition Co_71−xFe_xCr₇Si₈B₁₄ (x = 0, 2) at various excitation frequencies and bias fields and at room temperature. The impedance, Z(σ) for both the samples was found to be very sensitive functions of applied tensile stresses (up to 100 MPa) exhibiting a maximum SI ratio as much as 80% at low frequency 0.1 MHz. The nature of variation of SI changes with the excitation frequency especially at higher frequencies in MHz region where it exhibits a peak. Magnetization measurements were also performed to observe the effects of applied stresses and magnetization decreased with the application of stress confirming the negative magnetostriction coefficient of both the samples. Both the samples exhibited negative magneto-impedance (MI) when the variation of Z is observed with the applied bias magnetic field, H. The impedance as functions of applied magnetic field, Z(H), decreases with the application of stress thus making the MI curves broader. Maximum MI ratio as large as 99% has been observed for both the samples at low fields 27 Oe.     

Electronic structure and magnetism of PrNixPt1−x compounds

We have studied influence of the Pt–Ni substitution on the crystal structure and magnetic behavior of the PrNi_xPt_1−x compounds. Polycrystalline samples with x = 1, 0.9, 0.75, 0 were prepared and characterized by X-ray powder diffraction (XRPD) and scanning electron microscopy (SEM). The analysis of XRPD data confirmed that the orthorhombic CrB-type structure owned by the parent binary compounds remains conserved through the entire series. The samples were subsequently investigated by specific heat (C_p), magnetization (M) and ac susceptibility measurements in the temperature range 2–350 K and in magnetic fields up to 9 T. All compounds were found to order ferromagnetically. The T_C values monotonously increase with increasing Ni content. To inspect the crystal-field (CEF) effects and magnetocaloric properties specific-heat data were analyzed in detail and the magnetic contribution to the specific heat together with the magnetic entropy have been determined. The results of first principles electronic structure calculations of the PrNi and PrPt confirmed that besides the stable Pr magnetic moments due to localized 4f-electrons only a very small magnetic moments of at most 0.2μ_B is induced at the Ni (Pt) site due to the polarized 3d-electron states (5d-electron states) hybridizing with the Pr 5d-electron states, i.e. the Ni (Pt) moment plays only minor role in the total balance of the magnetic moments in these compounds.     

Nuclear structure and magnetic properties of perovskite compounds La1−xNdxFe0.5Cr0.5O3 (x = 0.1, 0.15 and 0.2)

Perovskite oxides with the composition La_1−xNd_xFe_0.5Cr_0.5O₃ (x = 0.10, 0.15 and 0.20) have been studied. The samples have been prepared using the standard solid-state reaction method in air. The X-ray and neutron diffractograms indicates that the samples crystallize in the orthorhombic perovskite structure with space group Pnma (No. 62). The Nd-substitution causes minor changes in the cell parameters and bond lengths but the nuclear structure remains orthorhombic in the whole range of substitutions and in the temperature range of 10–700 K. The magnetic structure of the samples at room temperature and below is G-type antiferromagnetic with an average magnetic moment of the Fe/Cr ions of 3.29(3) μ_B/atom at 10 K independent of the Nd content. At room temperature the average magnetic moment of the Fe/Cr ions reduces to 1.23 μ_B/atom. At temperatures below 250 K a weak but increasing uncompensated spontaneous magnetic moment develops that reaches a magnitude of about 0.5 emu/g (or 0.02 μ_B per Fe/Cr site) at 10 K. This moment saturates rather rapidly in the magnetization versus magnetic field curve and is at higher field superposed on the response of the antiferromagnetic spin system.     

Thermoelectric properties of A-site doped perovskites (Sr0.6Ba0.4)1−xMxPbO3 (M = La, K)

La- and K-doped perovskite-type ceramics, (Sr_0.6Ba_0.4)_1−xLa_xPbO₃ with x = 0.0−0.1 and (Sr_0.6Ba_0.4)_1−xK_xPbO₃ with x = 0.00−0.15, were prepared to modify thermoelectric properties of semi-metallic Sr_0.6Ba_0.4PbO₃ via the doping of electrons and holes, respectively. The electrical conductivity σ and Seebeck coefficient S for the ceramics were measured at temperatures of 373–1073 K in air. With the La doping, electron carriers were successively doped and the material changed from a semi-metal for the undoped Sr_0.6Ba_0.4PbO₃ to a metal for the (Sr_0.6Ba_0.4)_0.9La_0.1PbO₃. With the K doping, the thermoelectric properties were essentially unchanged probably due to the carrier compensation effect by the generation of oxygen deficiencies. The thermoelectric power factor S²σ was maximized to a value of 3.1 × 10⁻⁴ Wm⁻¹ K⁻² at 773 K for the undoped Sr_0.6Ba_0.4PbO₃ ceramic.     

The characteristics of Li(CoxNi1 − x)O2 cathode powders formed from the fine-sized Co3O4/NiO precursor powders

Li(Co_xNi_1 − x)O₂ (0 ≤ x ≤ 1) cathode powders were prepared by solid state reaction method using Co₃O₄/NiO precursor powders obtained by spray pyrolysis. The effect of the ratios of cobalt and nickel components on the characteristics of Co₃O₄/NiO precursor and Li(Co_xNi_1 − x)O₂ cathode powders were investigated. The Co₃O₄/NiO precursor powders with the ratios of cobalt and nickel components as 1/0, 0.75/0.25 and 0.5/0.5 had submicron size and regular morphologies. On the other hand, the Co₃O₄/NiO powders with the high contents of nickel component had aggregated morphologies of submicron size primary powders. The fine-sized precursor powders formed the fine-sized LiCoO₂ and Li(Co_0.75Ni_0.25)O₂ cathode powders by solid state reaction with LiOH powders. However, the high contents of the nickel component of the Co₃O₄/NiO precursor powders formed the Li(Co_xNi_1 − x)O₂ (0 ≤ x ≤ 0.5) cathode powders with aggregated morphologies and large sizes. The discharge capacities of the powders increased with increasing the nickel content into the Li(Co_xNi_1 − x)O₂ cathode powders up to 188 mAh/g.     

Correlation between the synthesis conditions and the compositional and magnetic properties of Co2(Cr1−xFex)Al Heusler alloys

In this study we give evidence for the strong dependence of the compositional and magnetic properties on the synthesis conditions of polycrystalline Co₂(Cr_1−xFe_x)Al Heusler alloys (0 ≤ x ≤ 1) by comparing the properties of as-grown and annealed compounds. Strong chemical inhomogeneities are found at the micrometric level depending on the compound and the synthesis method. Moreover, we find that the Co content is homogeneous at the micrometric level in all the studied samples in sharp contrast with significant inhomogeneous distribution of (Fe/Cr) and Al at the micrometric level, especially for Cr-rich compounds (x ≤ 0.4). We have found that the magnetic properties (the Curie temperature and the saturation magnetization) are strongly depressed in the annealed compounds with respect to the corresponding as-grown compounds. For the as-grown compounds the saturation magnetization is close to the theoretically predicted one for x ≥ 0.7 whereas it is lower than the theoretically predicted one for x ≤ 0.4, which correlates with the observed chemical inhomogeneity.     

Preparation and structures of the La1−xKxCo1−xNbxO3 (x = 0–l) system

The La_1−xK_xCo_1−xNb_xO₃ system was performed by conventional solid state reaction technique using metal oxides. By DSC analysis, the activation energy of crystallization of the powders with x = 0.3 is 388.4 kJ/mol. The crystal structure of the compound reveals a transition from rhombohedral to cubic, and then to orthorhombic structure as the amount of the potassium niobate (KNbO₃) increases. It is found that the structure of the samples with x < 0.3 is similar to that of lanthanum cobaltate (LaCoO₃), while at the compositions with 0.7 ≥ x ≥ 0.3, the structure transforms to cubic. Finally, with x ≥ 0.7, the structures were similar to that of KNbO₃. According to the results of selected-area-diffraction (SAD) patterns and X-ray diffraction (XRD) identifications, the lattice parameters were calculated. The direction of superlattice structure along [2 1 0] was found for x = 0.5 as identified from SAD patterns. The dielectric constants were measured with cubic structure. Dielectric constant (K) decreases with increasing x.