PP无纺布预辐射法固相接枝4-VP的研究

以预辐射聚丙烯无纺布为基材,4-乙烯基吡啶为单体,二乙烯基苯为交联剂,采用固相接枝聚合的方法制备接枝共聚物。讨论了反应温度、反应时间、阻聚剂、单体浓度和交联剂等对接枝率的影响。结果表明,接枝反应的最佳条件为:温度50℃,时间3 h,单体浓度10%,交联剂5%,阻聚剂(FeSO4.7H2O)0.08%,最佳条件下的接枝率为7.5%。     

PP无纺布预辐射法固相接枝MA的研究

本论文研究了以预辐射聚丙烯无纺布为基材,丙烯酸甲酯为单体,采用固相接枝聚合的方法制备接枝共聚物的接枝反应过程。详细讨论了反应温度、反应时间、阻聚剂、单体浓度和交联剂等对接枝率的影响,结果表明,该接枝反应的最佳条件为:温度:80℃、时间:2h、单体浓度:25%、交联剂:6%、阻聚剂(FeSO4·7H2O):0.25g。     

PP无纺布辐射接枝MMA的研究

采用聚丙烯(PP)无纺布为基材,甲基丙烯酸甲酯(MMA)为单体,~(60)Co-γ射线预辐射接枝共聚的方法制备接枝共聚物,讨论了辐射剂量、反应温度、反应时间、单体浓度、阻聚剂和交联剂的用量等对接枝率的影响。结果表明,接枝反应的最佳条件为:辐射剂量60 kGy以上、接枝温度65℃、接枝时间2 h、MMA质量分数20%、交联剂质量分数5%、阻聚剂用量0．3g,该条件下PP的接枝率为6．5%。     

聚丙烯无纺布预辐射固相接枝丙烯酸的研究

以聚丙烯(PP)无纺布为基材,以丙烯酸为单体,进行预辐射固相接枝聚合,考察了外部环境、辐射剂量、温度、反应时间、单体用量、介质、阻聚剂、交联剂对接枝率的影响。结果表明,通过预辐射固相接枝聚合方法,可将丙烯酸单体接枝在PP无纺布上,辐射剂量增大可提高接枝率;反应时间对接枝率的影响在低、高温阶段有所不同。最佳反应条件为:氮气环境,辐射剂量大于50 kGy,反应温度65℃,反应时间3 h,单体浓度30%,反应介质为水,阻聚剂0.8 g,交联剂用量为5 mL。     

聚丙烯无纺布接枝改性研究

采用Co射线辐射后的聚丙烯(PP)无纺布为原料,通过接枝改性制备PP接枝共聚物。研究了接枝条件对接枝率的影响。结果表明:选择丙烯酸为接枝单体,其质量分数为30%,交联剂质量分数5%,阻聚剂用量0.30 g,接枝反应温度65℃,反应时间3 h,PP无纺布的接枝改性效果显著,接枝率达84.95%。     

甘蔗渣纤维素均相接枝制备阴离子吸附剂

在离子液体均相体系下,在甘蔗渣纤维素表面上接枝功能单体甲基丙烯酸二甲氨基乙酯(DMAEMA)制备一种阴离子吸附材料,研究了引发剂浓度、温度、单体用量、交联剂浓度和时间对产物接枝率的影响。结果表明,甘蔗渣纤维素与单体DMAEMA质量比为1:5,引发剂浓度为2%,交联剂浓度为3%,温度为50℃和反应时间为4 h,产物的接枝率最大为330%,在含有较低浓度的氟离子溶液中,其吸附能力为2.6 mg/g,为高效阴离子吸附剂的制备提供了理论依据。     

玉米淀粉接枝丙烯酸高吸水性树脂的制备及性能研究

以玉米淀粉为主要原料、丙烯酸(AA)为改性单体、过硫酸铵为引发剂和N,N-亚甲基双丙烯酰胺为交联剂,采用接枝共聚法制备淀粉接枝型高吸水性树脂。研究了糊化温度、糊化时间、引发剂和交联剂用量、单体浓度、接枝反应温度和反应时间等对树脂吸水性能的影响。确定其最佳工艺条件为:糊化温度为85℃、糊化时间为60min,w(引发剂)=3%(相对于淀粉而言)、w(交联剂)=0.8%(相对于淀粉而言)、AA单体浓度为4.5mol/L、反应温度为60℃和反应时间为4h。在最佳工艺条件下制备的树脂,其吸水性能最佳,吸水率达到730g/g。     

机械活化淀粉与丙烯酰胺反相乳液接枝共聚反应的研究

淀粉接枝共聚物是一种新型功能性材料.研究了经机械活化预处理后的玉米淀粉与丙烯酰胺在反相乳液体系中的接枝共聚反应规律,分别考察了机械活化时间、反应时间、反应温度、油水比、引发剂浓度和淀粉单体比对单体转化率、接枝率和接枝效率的影响.实验结果表明,在本实验考察范围内的最佳反应条件是淀粉活化30 min、反应温度50℃、反应时间2 h、m(单体):m(淀粉)=1.6:1、V(油):V(水)=1.2:1、引发剂浓度1.46 mmol·L-1;在该反应条件下,单体转化率96%,接枝率56.7%,接枝效率85.3%.而原淀粉在类似条件下,单体转化率为72.5%,接枝率和接枝效率分别为46.9%和66.5%.机械活化作用破坏玉米淀粉的结晶区,与丙烯酰胺反应几率增大,有效地提高了玉米淀粉的化学反应活性.     

聚丙烯固相接枝马来酸酐的研究

用固相接枝法在聚丙烯(PP)分子链上接枝马来酸酐(MAH),制备功能化聚丙烯。重点讨论了反应时间和反应温度以及单体浓度和引发剂浓度对接枝产物PP-g-MAH接枝率的影响。在其他条件不变的情况下,当反应时间为2h,反应温度为120℃,单体与PP的质量比为1∶1,引发剂用量为2.5%时,最大接枝率可达到1.6%。采用红外光谱表征了PP-g-MAH。     

两种不同引发剂在木薯淀粉接枝丙烯酸反应的研究

详细地研究了淀粉接枝丙烯酸反应过程中 ,两种不同的引发剂过硫酸钾 -亚硫酸氢钠和硝酸铈铵在淀粉接枝丙烯酸共聚反应的影响 ,对一些反应条件如引发剂浓度、反应的温度、单体的浓度、单体的中和度、反应的时间等进行了单因素试验 ,以接枝率 ,单体转化率 ,接枝效率为主要考查目标 ,从而得出试验的最佳条件。在过硫酸钾-亚硫酸氢钠的引发下 ,最佳的反应条件是 :反应温度 35℃ ,引发剂的浓度是 2 .8m mol/· L- 1 ,丙烯酸的浓度是1.1mol· L- 1 ,反应时间 3h,中和度为 80 %     

聚丙烯纤维接枝苯乙烯的研究

采用化学接枝法以苯乙烯(St)为接枝单体、过氧化苯甲酰(BPO)为引发剂,1,2-二乙烯苯(DVB)为交联剂、甲醇和正辛醇为溶剂,对聚丙烯(PP)纤维进行接枝改性。研究了原料配比和反应条件对其接枝的影响。结果表明,PP纤维上接枝St,适宜的原料配比和操作条件为:St质量与PP体积比(St/PP)为4,BPO质量与St体积比(BPO/St)为0.025,DVB与St体积比(DVB/St)为0.025,溶剂与St体积比为5,浸渍24～30h,在85℃恒温水浴中反应6～8h。在较佳条件下可得到导入率为110%-160%的接枝纤维。     

微波辐射下淀粉-丙烯酰胺接枝共聚物的合成

以硝酸铈铵作为引发剂、丙烯酰胺为单体,用微波辐射法合成了淀粉接枝丙烯酰胺共聚物。探讨了反应时间、引发剂浓度、单体和淀粉质量比和反应温度等因素对接枝反应的影响。正交实验确定的最优工艺条件为:反应时间20 m in,引发剂浓度4 mmol/L,丙烯酰胺和淀粉质量比2.5∶1,反应温度55℃,最高接枝率和接枝效率分别达到211.6%和74.3%。     

Preparation of crosslinked polystyrene-grafted PFA films by a simultaneous irradiation method

A series of polystyrene (PS)/divinylbenzene (DVB)-grafted poly(tetrafluoroethylene-co-perfluorovinyl vinyl ether) (PFA) films with various DVB contents were prepared by a simultaneous radiation grafting method. The degree of grafting was found to be strongly dependent on the grafting conditions, such as the monomer concentration, irradiation dose, dose rate, and crosslinker concentration. The results show that the highest degree of grafting was achieved at a 10% DVB content at the same irradiation conditions. The prepared PFA-g-PS/DVB films were characterized using FTIR, TGA, and a mechanical strength test.     

Plasma‐induced graft polymerization of acrylic acid onto poly(ethylene terephthalate) films

The graft polymerization of acrylic acid was carried out onto poly(ethylene terephthalate) films that had been pretreated with argon plasma and subsequently exposed to oxygen to create peroxides. The influence of synthesis conditions, such as plasma treatment time, plasma power, monomer concentration, temperature, and the presence of Mohr's salt, on the degree of grafting was investigated. The observed initial increase in grafting with monomer concentration accelerated at about 20% monomer. The grafting reached a maximum at 40% monomer and subsequently decreased with further increases in monomer concentration. The reaction temperature had a pronounced effect on the degree of grafting. The initial rate of grafting increased with increasing temperature, but the degree of grafting showed a maximum at 50°C. The activation energy of the grafting obtained from an Arrhenius plot was 29.1 kJ/mol. The addition of Mohr's salt to the reaction medium not only led to a homopolymer‐free grafting reaction but also diminished the degree of grafting. The degree of grafting increased with increasing plasma power and plasma treatment time. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 81: 2993–3001, 2001     

Radiation‐induced graft copolymerization of α‐methyl styrene and butyl acrylate mixture into polyetheretherketone films

Radiation‐induced graft copolymerization of α‐methyl styrene (AMS), butyl acrylate (BA) monomers, and their mixture was investigated on poly(etheretherketone) films. The graft polymerization was carried out using ethyl methyl ketone as the medium for the copolymerization and the maximum degree of grafting of 27% was achieved. It was observed that the grafting is significantly influenced by the reaction conditions, such as reaction time, preirrradiation dose, monomer concentration, monomer ratio, and the reaction temperature. The degree of grafting increases as the monomer concentration increases up to 30%, beyond which a decrease in the grafting was observed. The degree of grafting showed a maximum at 40% BA content in the monomer mixture. The temperature dependence of the grafting process shows decreasing grafting with the increase in the reaction temperature. The presence of AMS and BA grafts in the film was confirmed by FTIR spectra. The relative change in the PBA/PAMS fraction with respect to the reaction temperature has been found in this study. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

S-DMDAAC-AM阳离子型高分子絮凝剂的合成及性能研究

以淀粉(S)、二甲基二烯丙基氯化铵(DMDAAC)、丙烯酰胺(AM)为原料,采用氧化还原引发体系,合成r接枝共聚物S-DMDAAC-AM.考察了反应温度、反应时间、引发剂浓度、单体配比等因素对接枝共聚体系的接枝率、接枝效率和絮凝效果等因素的影响.试验结果表明,最优条件为淀粉(S):单体总量=3.5 g∶10.5 g,反...     

微波辐射下壳聚糖-丙烯酰胺接枝物的合成及其絮凝性能研究

以硝酸铈铵作为引发剂、丙烯酰胺为单体,用微波辐射法合成了壳聚糖-丙烯酰胺接枝共聚物。通过正交试验考察反应条件对接枝率和接枝效率的影响,得出最佳工艺条件为:反应时间12 min,引发剂浓度5 mmol/L,丙烯酰胺和壳聚糖质量比5:1,反应温度40℃。最佳条件下接枝率和接枝效率分别达到148.6%和44.0%。壳聚糖接枝物与聚丙烯酰胺(PAM)对高岭土悬浮液的絮凝对比试验表明:在酸性条件下接枝物与PAM的絮凝效果相近;在中性和碱性条件下接枝物的絮凝性能优于PAM。     

纤维素与MBA接枝共聚物在离子液体中的制备

以N,N’-亚甲基双丙烯酰胺(MBA)为单体,过硫酸钾为引发剂,研究了MBA与纤维素在离子液体中的接枝共聚反应。通过正交单因素实验,研究了反应时间、单体用量、反应温度、引发剂用量对接枝效果的影响。实验结果表明:当反应时间为2 h,单体与纤维素质量比为3∶1,反应温度为50℃,引发剂用量为0.05 g时,接枝效果最好。此条件下,MBA与纤维素的接枝率可达38.06%。