Q960E超高强钢焊接接头组织和性能研究

目的 对Q960E超高强钢的焊接工艺进行研究以获得高强高韧的焊接接头。方法 选择超高强钢Q960E作为母材、FK1000ER120S–G焊丝作为填充材料进行MAG焊,采用改变焊接电流的方式来研究焊接热输入对焊接接头组织和性能的影响。结果 当焊接电流为155~230 A时,均获得了全焊透无明显缺陷的焊缝。随着焊接热输入的增大,焊接接头中各亚区宽度增大,其中焊缝区变化最为显著,在最小热输入条件下焊缝宽度为3.98 mm,在最大热输入条件下焊缝宽度增至5.53 mm。对焊接接头进行组织分析发现,焊缝组织主要为针状铁素体和板条马氏体;完全相变区组织主要为板条马氏体;未完全相变区组织主要为回火马氏体和部分重结晶形成的马氏体。硬度测试表明,在热影响区的回火区发生了软化现象,最低硬度仅为290HV;在完全相变区发生了硬化现象,硬度最大值可达500HV。在不同热输入条件下,焊接接头各亚区硬度变化趋势一致,焊接接头抗拉强度为995~1 076 MPa,拉伸试验均断裂在热影响区,断后伸长率为9.33%~10.21%,断裂时存在颈缩现象,为韧性断裂。随着热输入的增加,粗晶区马氏体板条束宽度增大,未完全相变区马氏体含量上升。结论 在所选焊接工艺窗口内焊接均能获得高强高韧的焊接接头。     

Q&P980镀锌高强钢电阻点焊工艺及液态金属脆化裂纹分布EI北大核心

通过设计电阻点焊工艺的正交实验,确定了Q&P980镀锌高强钢的点焊工艺参数范围,并对其焊接接头进行显微组织表征和力学性能分析。结果表明:熔核区组织以交错分布的板条马氏体为主;热影响区组织由板条马氏体、残余奥氏体和铁素体组成,马氏体板条平均宽度在不完全淬火区最大为4.86μm。显微硬度测试发现,焊接接头硬度值呈“W”形对称分布,硬度峰值出现在细晶区,达到559HV,硬度最低值出现在不完全淬火区,为338HV,呈现明显的软化现象。对焊接接头进行室温拉伸,最大拉剪载荷的峰值为27.92 kN,其断口形貌呈现典型的韧窝状,属于韧性断裂。由于Zn的熔点较钢基体低,镀锌高强钢点焊时易发生Zn层优先熔化并沿晶界向基体渗透,在焊接接头处可观察到明显的液态金属脆化裂纹。     

7075高强铝合金激光填丝焊接组织与力学性能研究

采用光纤激光器对4mm厚的7075铝合金进行激光填丝焊接,对焊接接头的显微组织、相结构、断口形貌、力学性能进行观察和分析。结果表明:焊缝(FZ)边缘组织为柱状枝晶组织,焊缝中心为等轴晶组织;热影响区(HAZ)保留了母材(BM)的轧制长条状形态,但晶粒有所长大。母材的相组成主要为α-Al固溶体、S-Al_2CuMg强化相和η-MgZn_2强化相,焊缝无强化相析出。焊缝区硬度值为各区中最低,热影响区显微硬度呈阶梯式增长。焊接速度为2~4m/min的接头拉伸试样均在焊缝处断裂,抗拉强度最大为母材的67.5%。接头拉伸试样均出现了颈缩现象,断口由大量的等轴状韧窝构成,为韧性断裂。     

6009铝合金光纤激光-MIG电弧复合焊和光纤激光焊工艺对比研究

采用光纤激光-MIG 复合焊和光纤激光焊分别对6009铝合金进行焊接,研究两种焊接方式下焊接接头的成型性、显微组织、拉伸性能、显微硬度、断口形貌的不同。研究表明：激光电弧复合焊的焊接速度是激光焊接的3倍;相比于激光焊,激光电弧复合焊焊缝中心显微组织更加细小;接头的抗拉强度达到母材的63%以上,而激光焊接的抗拉强度仅仅只有母材的38%;显微硬度试验表明：复合焊存在软化区,而激光焊接几乎没有软化区;断口分析表明：复合焊和激光焊的拉伸断口都是典型的韧窝状态,但是复合焊接的韧窝更加均匀。     

590 MPa级高强钢双面双弧立焊焊缝组织性能

为研究590 MPa级高强钢双面双弧工艺得到的焊接接头组织与性能的关系,采用钨极氩弧焊(TIG)与熔化极气体保护焊(MAG)方法获得成型良好的焊接接头,经过拉伸、冲击、弯曲试验及光学显微镜、扫描电镜、EBSD分析,对590 MPa级高强钢双面双弧立焊打底焊与盖面焊焊接接头的组织及性能进行了研究.结果表明:打底焊缝组织主要为贝氏体,盖面焊缝组织以贝氏体与针状铁素体为主;打底焊缝经历过一次热循环后组织得到一定程度的细化;打底焊缝硬度值与盖面焊缝相近,盖面焊缝热影响区最高硬度值高于打底焊缝热影响区最高硬度;2 mm坡口间隙性能较5 mm坡口间隙有较大提高,2 mm坡口间隙断口以韧窝断裂为主,5 mm坡口间隙断口以解理断裂为主.     

690 MPa级低合金高强钢焊接接头组织性能

为探讨690 MPa级低合金高强钢焊接接头组织与性能的关系,采用手工电弧焊(SMAW)和埋弧焊(SAW)获得成形良好的焊接接头,经过拉伸、冲击、弯曲试验及光学显微镜、扫描电镜和透射电镜分析,对两种焊接方法的接头组织性能进行研究.结果表明:两种焊接方法的焊缝组织主要为板条状贝氏体和少量针状铁素体,粗晶区为粗大贝氏体和少量马氏体;焊缝中含有大量分布均匀的微小球形夹杂物;两种焊接方法所得焊接接头都具有较高力学性能,-50℃的冲击断口形貌为韧窝、准解理混合型;埋弧焊焊缝冲击韧性低于手工电弧焊,手工电弧焊熔合线处冲击吸收功小于埋弧焊,但随距熔合线距离增加其值增加更快.显微组织和夹杂物是影响接头性能的主要因素.     

煤矿机械用Q690高强钢激光-MAG复合焊可行性分析

目的研究激光-MAG复合焊在采煤机Q690高强钢板上的加工工艺,以提高8.8 m高端采煤机电控箱结构焊接接头的加工效率和质量性能。方法对激光-MAG复合焊工艺试验进行试验设计与参数设计,观察接头的显微组织,对接头进行拉伸试验和冲击试验,观察断口形貌。结果焊缝区整体组织性能优于母材,保证采煤机电控箱隔爆性能要求,拉伸断口和冲击断口均表现为韧性断口形貌,但是在冲击断口上观察到明显的气孔。焊缝内存在微量气孔,导致焊接接头结合不紧密,拉伸试验出现了脆性断裂。结论避免焊接工艺设计中出现气孔是激光-MAG复合焊焊接接头满足Q690钢在煤矿机械中使用要求的关键技术。     

不锈钢激光-MAG复合焊接头微区性能研究

激光复合焊可用于不锈钢焊接,但激光复合焊接头热影响区小,组织变化梯度大.研究接头微区性能可以确定接头薄弱环节,为焊接接头的工艺评定和断裂分析提供理论依据.为此,本文对4 mm厚SUS301L-HT不锈钢进行激光-MAG复合焊接,采用维氏硬度、微型剪切和微拉伸等试验,研究了焊接接头焊缝、热影响区及母材的微区力学性能,并结合金相、断口扫描等分析了各微区力学性能的差异.结果表明：焊缝区域组织主要为柱状奥氏体树枝晶+少量的δ铁素体;母材的剪切强度和抗拉强度最高,分别为560和1 066 MPa,其次为复合焊接头热影响区,焊缝区域最差,接头硬度分布规律与各微区强度变化趋势一致;运用数学方法,得出了接头微拉伸强度与微型剪切强度、硬度之间关系的经验公式.接头各微区剪切断口和拉伸断口SEM分析呈现典型的韧性断裂特征.     

X90钢级管线钢预精焊接头的性能研究

为综合研究X90管线钢的焊接性,选用国内某钢厂轧制的X90管线钢卷板,利用预精焊工艺制备试验钢管4根,采用金相分析、扫描电镜(SEM)断口分析、夏比V型缺口冲击试验、拉伸、弯曲、硬度等试验,研究了焊接接头各个区域的组织和性能.试验结果表明:内外焊缝区组织均为针状铁素体,热影响区(HAZ)粗晶区晶粒粗化严重,主要组织为粒状贝氏体和贝氏体铁素体,在原奥氏体晶界和贝氏体板条内部存在块状或条状的(马氏体-奥氏体)M-A组元;HAZ冲击功离散性较大,出现了单值较低(45 J)的试样,SEM断口分析呈现典型的解理断裂特征;焊接接头抗拉强度805~815 MPa,断裂位置均在HAZ;焊接接头反弯试样易在HAZ出现裂纹和脆断现象;HAZ硬度在220~250 HV之间,较母材下降30 HV左右.HAZ是X90预精焊钢管焊接接头的薄弱环节,为提高X90管线钢的焊接稳定性,应重点研究精焊内外热循环双热影响亚区的组织转变和脆化机理.     

退火处理对异种钢激光焊接头组织及性能的影响

目的 通过研究相同时间不同退火温度下304/Q345激光焊接头的组织和性能,得到优化后的退火处理制度,为制定异种钢激光焊退火工艺提供一定的理论指导和技术支撑。方法 基于前期大量试验,在激光功率和离焦量不变的情况下,调节焊接速度由15 mm/s到35 mm/s,通过改变焊接速度获得性能优异的焊接接头。由于异种钢物理化学性能差异较大,接头组织不均匀,因此还需对激光焊接头进行退火处理。结果 焊缝区显微组织由板条马氏体与残余奥氏体组成,Q345低碳钢热影响区显微组织为多面体状铁素体与黑色珠光体,其中铁素体含量更多,304奥氏体不锈钢热影响区在奥氏体晶界上析出了铁素体。不同退火温度下碳元素均由Q345低碳钢侧向焊缝迁移,在Q345低碳钢侧形成脱碳层,在焊缝中形成黑色条带状增碳层。随着退火处理温度的升高,峰值温度升高,高温停留时间变长,碳迁移强度随之增加,黑色条带状区域增碳层宽度增大。拉伸性能测试结果表明,试样均断裂于Q345母材一侧,且断口存在韧窝,属于典型韧性断裂。此外,焊缝区硬度(390HV左右)最高,热影响区硬度(300HV)次之,母材的硬度(130HV左右)最低。结论 在给定试验参数范围内,优化后的最佳退火工艺参数为550 ℃-1.5 h。     

Characterization on strength and toughness of welded joint for Q550 steel

Q550 high strength steel was welded using gas shielded arc welding and three different welding wires without pre- or post-heat treatments. The paper investigates the influence of welding wire on the microstructure, tensile strength and impact toughness of Q550 steel weld joints. Results showed that the microstructure of the weld metal of joints produced using ER50-6 wire was a mixture of acicular ferrite and grain boundary ferrite including pro-eutectoid ferrite and ferrite side plate. Acicular ferrite was mainly obtained in the weld metal of the joints produced using MK·G60-1 wire. Pro-eutectoid ferrite was present along the boundary of prior austenite. Crack initiation occurred easily at pro-eutectoid ferrite when the joint was subjected to tensile. Tensile strength and impact toughness were promoted with increasing acicular ferrite. Tensile strength of the joint fabricated using MK·G60-1 wire was close to that of base metal. And tensile samples fractured at location of the fusion zone, which had lower toughness and thus became the weak region in the joint. Impact absorbing energy was the highest in the heat affected zone. Fibrous region in fracture surfaces of impact specimens was characterized as transgranular fracture with the mechanism of micro-void coalescence. Acicular ferrite microstructure region corresponded to relatively large dimples while boundary ferrite microstructure corresponded to small dimples.     

车用TRIP590钢光纤激光焊接接头组织与性能研究

为了促进先进高强钢激光焊接技术的发展,采用光纤激光器对1.5mm厚的TRIP590钢板进行焊接,对焊接接头的微观组织、硬度以及拉伸性能进行了研究,分析了焊接速度对组织、性能的影响。结果表明:焊缝组织主要为板条状马氏体,热影响区可分为完全淬火区和不完全淬火区。焊接接头硬度分布不均匀,在热影响区或焊缝处硬度最高。随着焊接速度提高,热影响区马氏体含量增多,贝氏体含量减少,热影响区和焊缝组织变得细小。焊接速度为3~5m/min时,拉伸试样均断裂在母材,断后延伸率均超过30%,随着焊接速度提高,断后延伸率也有所提高,强塑积(PSE)均在20000MPa%以上,拉伸变形过程中相变诱发效应显著,大部分残余奥氏体转变为马氏体,在提高材料塑性的同时也提高了强度,实现了高强度和高塑性的统一。     

热输入对Inconel 617镍基高温合金激光焊接接头显微组织与力学性能的影响EI北大核心

采用两种热输入不同的焊接工艺参数对3 mm壁厚的Inconel 617镍基高温合金进行激光焊接。通过光学显微镜和扫描电子显微镜对焊接接头显微组织进行观察分析,并测试了焊接接头在室温(25℃)及高温(900℃)下的拉伸性能。结果表明:激光焊接热输入对Inconel 617焊接接头显微组织及力学性能影响明显。在高热输入(200 J/mm)条件下,焊缝正面宽度3.88 mm,熔化区中部晶粒尺寸粗大,取向杂乱,树枝晶二次枝晶间距较大(6.71μm),枝晶间碳化物颗粒尺寸较为粗大,枝晶间Mo,Cr等合金元素的凝固偏析较为严重。焊接接头热影响区宽度约0.29 mm,在晶界和晶内形成了γ+碳化物共晶组织,这是由于焊接升温过程中,热影响区内球状碳化物颗粒与周边奥氏体发生组分液化,并在焊后凝固过程中形成共晶。低热输入(90 J/mm)工艺参数获得的焊缝正面宽度为2.28 mm,焊缝呈沿熔合线母材外延生长并沿热流方向定向凝固形成的柱状晶形态。焊缝中部树枝晶二次枝晶间距较小(2.26μm),枝晶间碳化物颗粒尺寸细小,热影响区宽度约0.15 mm。室温(25℃)拉伸测试表明:高热输入下获得的焊接接头由于焊缝中固溶元素偏析造成的局部组织弱化,从焊缝中部破坏,强度与伸长率有所降低,低热输入条件下获得的焊接接头从母材破坏。而高温实验条件下(900℃),母材晶界发生弱化导致所有试样均从母材破坏。     

热成形淬火对QP1180/22MnB5激光拼焊板组织与性能的影响

目的 对QP1180和22MnB5激光拼焊板进行热成形试验,以解决超高强钢板材焊后的软化问题。方法 选择QP1180和22MnB5异种高强钢作为母材进行激光自熔焊,对焊后的激光拼焊板进行热成形试验,通过体式显微镜、扫描电子显微镜、液压拉伸试验机和维氏硬度计等手段,分析热成形前后激光拼焊板微观组织和力学性能的变化。结果 与焊态拉伸试样相比,热成形试样抗拉强度提高了135%,断后伸长率降低了55%,拉伸试样都在22MnB5母材处断裂,均为塑性断裂。在热成形后,对焊接接头进行组织分析,发现QP1180母材区马氏体含量增加,22MnB5母材区和临界热影响区组织由珠光体和铁素体转变为马氏体,焊接接头热影响区各亚区的组织均转变为大小不同的板条马氏体。硬度测试结果表明,焊态试样焊接接头的QP1180临界区存在软化现象,硬度值最低为335HV,22MnB5侧硬度值由母材处向焊缝升高,母材硬度最低为170HV;而在热成形后,QP1180临界区软化现象消失,硬度值趋于平缓,22MnB5母材处硬度比焊态试样硬度高了2倍。结论 与焊态试样相比,经热成形后激光拼焊板的焊后软化问题得到了解决。     

X70大变形管环焊接头及断裂机制研究

目的基于应变设计大变形管线环焊接头热影响区的软化问题,解决制约管线安装质量和服役寿命等难题。方法通过显微硬度测试、微观组织分析,研究了X70大变形管接头热影响区的软化原因,并利用数字相关法研究了焊接接头拉伸过程中的断裂机制,还对焊接接头热影响区进行了激光增强探索。结果 X70焊接接头热影响区粗晶区的最大硬度损失达HV0.239;软化区最大应变达到37%以上;经过热影响区激光重熔后,X70钢焊接接头抗拉强度可提高10%以上,断裂位置均位于母材。结论 X70焊接接头热影响区粗晶区存在明显的软化;拉伸过程中在软化区出现了明显的应变集中,是X70焊接接头断裂于近缝区的主要原因;焊接接头热影响区粗晶区粗大的粒状贝氏体和铁素体导致了焊接接头热影响区的软化。     

不锈钢激光点焊接头组织和力学性能研究

目的 改善SUS301L–HT不锈钢激光点焊焊接性能。方法 以2 mm SUS301L–HT不锈钢为母材进行激光点焊试验,并分析焊接接头的金相组织、硬度、拉伸性能以及断口形貌等。结果 焊点表面无损坏、压痕均匀、无较大焊接变形,表面无飞溅、母材颜色无明显变化。焊核区的微观组织主要是柱状晶,柱状晶依附于未熔化母材晶粒向焊核中心生长。母材硬度最高,约为309HV;焊核中心附近区域硬度适中,约为255HV,热影响区硬度最小,不到220HV。点焊接头断裂形式多为纽扣式断裂且发生在热影响区。结论 不锈钢激光点焊整体质量较好,可用于轨道列车车体加工。     

U75V轨道钢线性摩擦焊工艺研究

目的 提高及改善目前轨道连接与修复的质量。方法 采用线性摩擦焊（LFW）的方法,对高碳轨道钢（U71Mn）在不同参数下进行了焊接试验,并对其微观组织和力学性能进行了表征。结果 焊接参数对接头质量起着决定性的作用。根据焊后接头的微观组织差异,可将其分为4个部分：焊缝中心区（WCZ）、热力影响区（TMAZ）、热影响区（HAZ）和母材（BM）。BM为珠光体和上贝氏体的混合组织,TMAZ由珠光体和少量马氏体组成。在WCZ中,由于受到的热力耦合作用的增强和更高的冷却速率,该区域马氏体含量进一步增加。在拉伸试验中,所有试样均在WCZ处发生断裂,接头的最大抗拉强度达到BM强度的86.6%。此外,WCZ中存在大量马氏体,在增加焊缝显微硬度的同时也降低了焊缝的冲击韧性。结论 采用LFW的方法可以得到焊接质量优良的轨道钢接头。