Nd:YAG激光+脉冲MAG电弧复合热源规范参数对平板堆焊焊缝表面成形的影响

利用余高-熔宽比表示焊缝表面铺展性并与焊缝余高一起作为参数来评价复合热源平板堆焊焊缝的表面成形,通过试验研究了Nd：YAG激光＋脉冲MAG复合热源堆焊过程中焊接规范参数对复合热源平板堆焊焊缝表面成形的影响并分析了激光对复合热源堆焊焊缝表面成形的影响.研究结果表明,在电弧功率变化过程中,随着激光功率的增大,其对平板堆焊焊缝表面成形的影响也逐渐增大;焊接速度变化过程中,激光束能量的加入不仅改善堆焊焊缝表面成形还极大地提高了焊接速度;而在光丝间距和离焦量变化过程中,激光束对复合热源平板堆焊焊缝表面成形的影响很小.     

工艺参数对304不锈钢脉冲Nd∶YAG激光/TIG电弧复合焊焊缝成形的影响

研究了304不锈钢脉冲Nd:YAG激光TIG电弧复合热源焊接工艺参数对焊缝成形的影响.结果表明,脉冲Nd:YAG激光/TIG电弧复合焊焊缝横截面面积大于单一激光焊焊缝横截面面积与单一TIG焊焊缝横截面面积之和,具有协同效应;激光功率增大时,复合焊焊缝熔深和熔宽均增大,复合焊焊缝横截面面积增大,复合热源热效率也增大;离焦...     

激光/等离子电弧复合热源能量参数对钛合金焊缝成形的影响

在对钛合金激光/等离子电弧复合焊与单一激光焊的焊缝成形进行比较的基础上,研究了激光在复合等离子电弧后主要焊接工艺参数对焊缝成形的影响.结果表明,随激光功率增大和焊接速度降低,复合焊与单一激光焊焊缝的横截面形貌均由钉形向近X形转变.与单一激光焊相比,复合焊焊缝的余高和咬边较大.激光/等离子电弧"协同效应"随激光功率和焊接速度变化而不同,从而影响复合焊焊缝的熔宽和熔宽比.随焊接电流从零增大到60 A,焊缝熔宽略有增大,而焊缝熔宽比基本保持不变.     

激光-GMAW复合焊接电弧热源形式对焊接过程参数及焊缝形态的影响

激光-脉冲GMAW复合焊接和激光-连续GMAW复合焊接两种热源形式在复合焊接中使用范围广,应用前景好.系统研究这两种热源形式和脉冲GMAW焊接以及连续GMAW焊接在焊接过程中的电参数变化特征及焊缝的形状尺寸.结果表明,激光-脉冲GMAW复合焊接中电参数平稳,焊接过程稳定,可有效地促进熔滴过渡,并且获得的焊缝尺寸较理想,熔深大、余高小,但激光功率3000W的复合焊接短路时电参数波动性增大.     

GMAW脉冲电弧对Nd:YAG激光能量的吸收

揭示了激光-电弧复合热源焊接过程中GMAW电弧对Nd∶YAG激光的吸收作用,对深入分析激光和电弧的耦合机制具有重要意义.通过保持脉冲GMAW电弧正常态,Nd∶YAG激光水平逐层、逐点扫描穿过脉冲电弧区域的试验方式,获得了Nd∶YAG激光穿过脉冲GMAW电弧后的能量损失情况.结果表明,波长为1.064μm的Nd∶YAG激光穿过保护气成分为Ar/CO2=80/20的脉冲GMAW电弧的任何区域都几乎不损失能量,波长为1.064μm的Nd∶YAG激光穿过不同电流强度的脉冲GMAW电弧也几乎不损失能量.     

铝合金激光-电弧双面焊接头特征分析

采用激光-电弧双面焊工艺进行铝合金焊接试验，发现该工艺不仅可以获得稳定可靠的焊接过程与美观的焊缝成形，还可以有效地增加接头熔深和降低焊接成本。主要研究了焊接参数对双面焊接头特征的影响。结果表明，激光功率增加时，双面焊两侧的熔宽都以同样的趋势增大；焊接电流增大时，电弧侧熔宽的增加趋势明显大于激光侧；增加激光功率或提高焊接电流都会引起焊缝最小熔宽的增大，且焊缝最小熔宽的深度也发生一定的变化。随焊接速度的提高，激光侧的深宽比增加，而电弧侧的深宽比减小。     

铝锂合金YAG-MIG复合焊焊缝成形特征

基于铝锂合金激光电弧复合焊焊缝成形特征的分析,对5A90铝锂合金YAG-MIG复合焊接工艺展开研究.固定选取合理的焊接位置条件下,讨论了激光功率、焊接速度、焊接电流和热源作用间距等主要焊接工艺参数对焊缝成形的影响规律.结果表明,两热源间距在0～6mm之间时有较好的复合效应;激光功率的增加对增大焊缝熔深和背面熔宽起主导作用;焊缝正、背面熔宽随着焊接速度的提高均明显减小,熔深亦有减小趋势;焊接电流加大时,焊缝熔深和熔宽显著增大.     

基于逐步回归法研究激光复合焊接工艺参数对焊缝的影响

采用CO2激光-TIG复合焊接3 mm厚的不锈钢板,基于多元线性回归方法,研究了焊接工艺参数对焊缝熔宽及塔深的影响.试验结果表明,对激光-电弧复合焊焊缝熔深影响程度从大到小的焊接工艺参数依次为:激光功率、焊接速度、TIG焊焊接电流和热源间距,其中前2项的影响最为突出;对熔宽影响的焊接程度从大到小的焊接工艺参数依次为:焊接速度、TIG焊焊接电流、热源问距和激光功率,并分别给出了回归教学模型.     

Nd:YAG激光+CMT电弧复合热源横焊工艺参数对焊缝成形的影响

以304不锈钢为对象,借助焊缝成形参数来评价YAG激光+CMT电弧复合热源横焊焊缝的成形特征,研究了Nd:YAG激光+CMT复合热源横焊过程中焊接工艺参数对焊缝成形的影响.结果表明,在CMT电弧焊接中加入激光可以改善横焊焊缝成形;在激光能量和焊接电流一定时,光丝间距存在一个最佳匹配,使得Nd:YAG激光+CMT复合热源横焊焊缝成形良好;与其它复合热源焊接相对比激光功率对熔深影响较大,对横焊焊缝成形的影响程度与焊接电流有关;焊接速度对横焊焊缝成形影响显著;离焦量对横焊焊缝成形影响较小;电弧功率对横焊焊缝的偏离度影响显著.     

低功率YAG激光-MAG电弧复合焊接不锈钢

以0Cr18Ni9Ti不锈钢钢板为试验材料,研究了低功率脉冲YAG激光-脉冲MAG电弧复合热源和单脉冲MAG焊接不锈钢.结果表明,低功率脉冲YAG激光-脉冲MAG电弧复合热源同样具有大功率激光-电弧复合焊接才有的增加熔深、提高焊接速度、稳定焊接过程等优点;低功率脉冲YAG激光的加入改变了电弧形态,电弧根部被吸引和压缩现象显著,提高了能量利用率;与单脉冲MAG堆焊相比,在相同焊接速度下复合焊最大能增加熔深1.3倍,在相同熔深下复合焊的焊接速度可以提高50%;复合焊焊缝的晶粒较单MAG焊缝中的晶粒细小,其焊缝抗拉强度比单MAG的好,断裂属于延性断裂.     

Correlation between laser-wire distance and Nd：YAG laser ＋ P-GMA hybrid welding heat input parameters

In laser+P-GMA hybrid welding,laser-wire distance is an important parameter to describe the distance from laser spot to the center of the pulsed gas metal arc.The experiments results show that the optimal laser-wire distance with the deepest weld penetration increases with welding current and laser power being increased and decreases with welding speed being increased.Welding current,laser power and welding speed determine the hybrid welding heat input in laser+arc hybrid welding process,so there is a correlation between the optimal laser-wire distance and the hybrid heat input welding parameters for the deepest weld penetration: the optimal laser-wire distance increases with the heat input being increased.The positive correlation between the optimal laser-wire distance and the hybrid welding heat input is induced by the characteristics of the limited influence of P-GMA welding process on laser transmission and the dependence of weld penetration of hybrid welding on laser power.     

YAG激光与脉冲MIG复合焊接

研究了YAG(掺钕钇铝石榴石 ,Nd 3:Y3Al5O1 2 )激光与脉冲MIG电弧复合焊接铝合金的新工艺 ,设计制造了复合焊接机头 ,探讨了各种规范参数对焊缝成形的影响规律及激光与电弧的复合作用。结果表明 ,在比较宽的参数范围内YAG激光 -脉冲MIG复合焊接铝合金焊缝成形美观 ,无气孔等缺陷 ,熔深与激光单独焊比增加 4倍 ,与脉冲MIG焊接比增加 1倍以上 ,焊速显著提高 ,是一种理想的焊接工艺。     

YAG/MAG激光电弧复合焊工艺研究

利用YAG激光焊头和MAG焊枪旁轴复合进行了1Cr18Ni9Ti不镑钢的激光电弧复合焊工艺研究。研究表明：影响复合焊过程的主要工艺参数有激光功率、焊接速度、焊接电流、电弧电压、激光焦点位1、两热源的间距和相对于焊接方向的排列方式等；在一定的焊接工艺条件下所研究的YAG／MAG复合焊具有协同效应。电弧参数测试也表明，当激光与电弧复合的协同效应存在时，复合焊电流高于电弧焊，而电弧电压降低；若电弧采用过大的焊接电流与激光复合，尤其是在较低的焊接速度时，复合焊过程体现不出协同效应．复合焊熔深反而低于激光焊熔深。复合焊激光焦点位置变化对电弧稳定性和熔宽影响小，但获得最大熔深的焦点位王不同于激光焊。激光前置焊比激光后置焊获得的熔深大，两种条件下均在两热源闻距为0.5mm时熔深最大。     

Nd:YAG激光+CMT电弧复合热源横焊工艺参数对焊缝形貌的影响

以304不锈钢为对象,借助横焊焊缝横断面图像来分析Nd:YAG激光+CMT电弧复合热源横焊焊缝横断面的成形特征,研究了Nd:YAG激光+CMT电弧复合热源横焊过程中焊接工艺参数对焊缝横断面形貌的影响.结果表明,在Nd:YAG激光+CMT电弧复合热源横焊中,焊接工艺参数对横焊焊缝横断面形貌的影响显著;Nd:YAG激光加入CMT电弧焊中明显提高了复合焊缝以及复合焊中CMT焊缝的熔深;采取适当的焊接工艺参数(小的光丝间距、大的激光功率、小的焊接速度、适合的离焦量以及小的或大的CMT功率)可以避免熔池机械式叠加和焊缝横断面错位现象,使得焊缝成形良好.     

焊接参数对铝合金激光——MIG电弧复合焊缝熔深的影响

以5A06(LF6)铝合金为研究对象,研究了铝合金激光-MIG电弧复合焊(HYBRID焊)时焊接参数的变化对焊缝熔深的影响规律,并将焊接参数的变化对激光-MIG电弧复合焊、MIG电弧焊、激光焊的焊缝熔深的影响进行了综合比较分析.结果表明,若以等效于激光焊熔深的MIG电弧功率为分界线,可以把MIG电弧的功率分成高、低能量两个区,当激光与低能量电弧区的电弧复合时,激光对焊缝的熔深起主导作用,HYBRID焊的熔深大于该区的MIG电弧焊;当激光与高能量电弧区的电弧复合时,电弧对焊缝的熔深起主导作用,HYBRID焊缝主要体现为MIG焊缝的特点,加入激光的优势主要体现在增加焊接速度方面,即高速焊时也可获得良好的焊缝成形.     

激光+GMAW复合热源焊接过程热-力耦合数值分析

从宏观的焊接热过程出发,根据激光+GMAW复合热源焊接的特点,提出了适用于复合热源焊接的“双椭球体＋峰值递增圆柱体”组合式体积热源分布模式;建立了激光+GMAW复合热源焊接过程的有限元模型,数值计算了焊接温度场和焊缝横截面的形状尺寸,计算结果与试验结果吻合良好,证明了组合式体积热源模型的合理性和适用性. 采用焊接温度场的计算结果,进一步对复合热源焊接和GMAW的焊接变形和残余应力进行了数值模拟和对比分析. 结果表明,在焊缝熔深基本相同的情况下,复合热源焊接的焊接热输入、焊缝熔宽、焊接变形和高应力区域范围等均比GMAW小. 研究结果印证了激光+GMAW复合热源焊接工艺的优越性,并为焊接工艺参数的优化提供了基础理论数据.