碳纤维表面化学镀铜工艺的优化

以甲醛为还原剂对碳纤维表面进行化学镀铜,利用正交实验对碳纤维化学镀铜工艺进行了优化,研究了施镀时间与镀层厚度及导电性之间的关系,确定了较理想的化学镀铜工艺。结果表明,采用优化后的碳纤维化学镀铜工艺制得的镀铜碳纤维镀覆均匀,光泽性好,镀层结合力强,导电性能显著提高。     

碳纤维布化学镀铜工艺的研究

采用以甲醛为还原剂的化学镀铜液,用硝酸银作活化剂,在碳纤维布表面沉积出连续、均匀、有光泽的化学镀铜层。研究了不同前处理工艺对碳纤维布化学镀铜的影响。采用扫描电子显微镜表征了化学镀铜层的表面形貌,并用数字电压表测试了碳纤维布化学镀铜前后的导电性。     

激光活化参数对塑料表面通过化学镀铜制备电子线路的影响

先将10 g/L CuSO_4·5H_2O+30 g/L NaH_2PO_2·H_2O活化液均匀涂覆于ABS基体表面,再采用激光活化工艺在基体表面得到具有催化活性的电子线路图形,最后通过化学镀铜得到电子线路。研究了激光功率、光斑直径和扫描速率对电子线路上铜层覆盖率的影响。表征了化学镀铜层的表面形貌、相结构、可焊性和结合力。当激光功率为2.0 W,光斑直径为0.2 mm,扫描速率为12 mm/s时,线路的活化效果最佳,化学镀铜后线路边缘整齐,铜层覆盖率为100%,电阻率为3.6μ?·cm,可焊性和结合力良好。     

碳纤维表面化学镀Ni-Co-Fe-P工艺研究

介绍了碳纤维表面化学镀Ni-Fe-Co-P的工艺流程,探讨了碳纤维的去胶方法.通过正交实验法优化了化学镀Ni-Fe-Co-P的配方和工艺条件,观察了碳纤维的表面形貌,测试了镀层的结合力,研究了碳纤维增重率与时间和温度的关系.结果表明,在400℃灼烧30min,可去胶完全.本工艺得到的镀层均匀致密,结合力好.     

硝酸银在聚酰亚胺薄膜表面化学镀铜中作用

硝酸银在化学镀的过程中常作为催化剂,实验研究发现,硝酸银在聚酰亚胺薄膜表面化学镀铜时,不仅起到催化剂的作用,还有增加聚酰亚胺薄膜和化学镀铜层结合力的作用。实验采用Na OH溶液对聚酰亚胺表面进行改性,利用不同浓度的硝酸银溶液进行活化,将吸附在聚酰亚胺薄膜表面Ag+还原,进行化学镀铜。使用红外光谱仪对聚酰亚胺的表面结构进行表征和分析,利用3M胶带粘贴法测试镀铜层与聚酰亚胺薄膜的结合力,利用X-射线衍射、扫描电子显微镜表征铜镀层结构及表面微观形貌。结果表明,当硝酸银在一定浓度范围内变化时,硝酸银浓度对化学镀铜层质量和化学镀铜沉积速度无明显影响,但对镀铜层与聚酰亚胺薄膜的结合力影响很大。     

哈工大研制出用于塑料基体化学镀铜前处理的离子金属涂料

全国涂料工业信息中心消息,哈尔滨工业大学研制出一种用于塑料基体化学镀铜前处理的离子金属涂料技术。该项目涉及一种塑料基体表面处理所用涂料及利用其进行表面处理的方法,可以解决现有的采用涂料涂覆法使塑料工件表面具有催化活性的方法的化学镀铜的启镀困难、铜层与涂料层的结合力低及涂料层的均匀性差的技术问题。     

碳纤维的表面化学镀及其在青铜器纹样中的应用研究

为了将碳纤维应用于青铜器纹样中,采用化学镀的方法在碳纤维表面制备了化学镀镍层和化学镀铜层,研究了碳纤维表面预处理、化学镀镍和化学镀铜对碳纤维表面形貌和力学性能的影响.结果表明,热脱脂处理后碳纤维表面粗糙度增加,凹槽数量增多且深度相对商业碳纤维有所加深;粗化处理后碳纤维表面凹槽模糊化,表面粗糙度增加的同时凹槽棱角有所钝化...     

聚酰亚胺塑料表面激光诱导活化化学镀铜

以硫酸铜和次磷酸钠为主要成分配制活化液,并将其均匀涂在改性后的聚酰亚胺基体表面。通过激光诱导使基体活化,施镀后得到平整、致密的化学镀铜层。研究了不同改性工艺对激光诱导活化化学镀铜效果的影响。采用接触角测量仪分析了不同改性工艺条件下基体的亲水性,并通过扫描电镜观察改性前后和激光诱导活化前后基体的表面形貌。结果表明:飞秒激光刻蚀改性后的基体具有良好的亲水性,其表面形成的刻蚀孔洞为激光诱导活化后生成的铜微粒提供了吸附场所,施镀后得到结合力良好的化学镀铜层。     

"考本"液在钢铁上直接化学镀铜

指出了普通镀铜工艺的缺点通过对铜原子结构的分析,提出了得到良好结合力的化学镀铜层的可能性,进而给出了使用“考本”液在钢铁上直接化学镀铜的工艺。该工艺操作简单、安全性好、成本低,得到的镀层与钢铁基体结合力好,表面可以达到镜面光泽。     

氧化铝陶瓷表面化学镀铜无钯活化新工艺

研究了一种氧化铝陶瓷化学镀铜无钯活化新工艺。将基体放入CuSO_4和NaH_2PO_2的混合溶液中进行超声波浸润,然后通过热处理实现基体表面的无钯活化。通过正交试验,确定了活化的最佳工艺条件为:CuSO_4 20 g/L,NaH_2PO_2 80 g/L,超声波浸润时间2 min,活化温度145℃,活化时间10 min。此时镀层覆盖率达到100.0%。经高温活化后,基体表面附着一层均匀的、平均直径为40 nm的铜微粒。施镀后,化学镀铜层完全覆盖基板,组织均匀,结合力良好。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

Insect antifeedant properties of anthranoids from the genusVismia

Vismiones and ferruginins, representatives of a new class of lypophilic anthranoids from the genusVismia were found to inhibit feeding in larvae of species ofSpodoptera, Heliothis, and inLocusta migratoria.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.