热处理对TC4钛合金电子束焊接件组织性能的影响

对分别处于退火和固溶时效态的TC4钛合金进行电子束焊接,焊后采用不同的热处理工艺,利用光学显微镜(OM)及X射线衍射(XRD)的方法对这两种TC4焊接件的微观组织及相组成进行了分析,并进行力学性能试验.结果表明,两组试件母材组织均为α相和β相转变组织的机械混合物,但状态和分布不同;退火态试件的热影响区为粗而短的针状α相和少量初生α相,焊缝为单一板条α'马氏体,粗大且分布均匀,属于典型的网篮状组织,而固溶态试件热影响区中的针状α马氏体细小且分布不均;焊缝主要为粗大原始β晶粒内针状回火α'马氏体及晶界α相.这两组试件的抗拉强度及冲击韧度均高于母材,但退火态试件抗拉强度高于固溶态试件,冲击韧度略低于后者.     

低温固溶及时效处理对TC4合金棒材组织及力学性能的影响

研究了TC4钛合金棒材经650和700℃固溶处理及时效处理后的组织和性能变化。结果表明:对热加工态的TC4钛合金进行650℃的固溶热处理,材料的显微组织和拉伸性能变化不大。经过700℃固溶热处理,TC4钛合金棒材强度明显降低,屈服强度相对于热加工态降低77 MPa,且屈/强比明显低于普通退火。时效热处理后,合金的强度显著提高,400℃时效后抗拉强度达到1020 MPa,相对于热加工态提高53 MPa。显微组织分析表明,热加工后的TC4棒材显微组织由初生α相、次生α相以及残余β相组成。热处理过程中,残余β相中针状α相的溶解与重新析出是影响合金拉伸性能变化的主要原因。     

锻态TC25G钛合金棒材的显微组织和织构

利用光学显微镜(OM)和电子背散射技术(EBSD)研究α+β型TC25G钛合金大规格棒材不同位置的显微组织和晶体取向。结果表明:锻态TC25G棒材不同位置组织和织构不同;表面位置和1/2R位置为双态组织,棒材中心为等轴状初生α相、棒状α板条和β转变组织;棒材表面为α相0001//AD和1120/1010//AD的弱织构,1/2R位置处为1120//AD的弱织构,中心位置形成2022织构;适当增加β单相区的锻造变形量,细化原始β晶粒并通过控制α+β两相区的终锻温度,降低坯料的温度梯度,提高坯料应变场的均匀性,可提高棒材组织和晶体取向分布的均匀性。     

EBSD技术在钛合金板材研究中的应用

采用ZEISS ULTRA 55热场发射扫描电镜测试了不同工艺条件下的TC2钛合金板材中α和β相含量、分布、织构、取向差和晶粒大小等。结果表明:A板材α相含量多于B板材;A板材以(1010)的柱面织构为主,而B板材以(0002)的基面织构为主;A板材晶粒小于B板材。     

TC16钛合金板材冷轧工艺及组织性能研究

进行了TC16钛合金板材多道次冷轧试制,利用光学显微镜、扫描电镜和X射线衍射等手段研究了变形量对冷轧板材微观组织与力学性能的影响。结果表明:α+β两相TC16钛合金板材冷轧加工是可行的,其极限冷变形量达到79%,冷轧板材表面无裂纹。大幅度冷轧变形后,TC16钛合金组织为分布均匀的纤维状结构,且存在极少量未充分变形的α晶粒,并伴有应变诱导的α″马氏体相产生;抗拉强度和显微硬度均得到较大程度的提高,发生明显的冷形变强化。     

AgCu28合金的织构组织与力学性能

用X射线衍射法研究AgCu28合金的轧制变形织构组织和退火织构组织,对它们的延伸率和抗拉强度进行测试。结果表明,当AgCu28合金轧制变形量为95%时,Ag和Cu的主要变形织构是{110}112Brass织构;在H2气氛下经650℃,1.5h退火后,AgCu28的退火织构与变形织构相同;加工态AgCu28合金沿横向(TD)和轧制方向(RD)的抗拉强度分别为750和680MPa,退火态AgCu28合金沿TD和RD的抗拉强度分别是374和327MPa;退火态沿TD和RD的延伸率都约为12%。这表明在两元共晶合金中两相晶粒相互影响导致它们的变形织构与退火织构一致、晶粒显著细化、再结晶温度明显提高、抗拉强度显著提高并存在各向异性。     

钛合金激光填药芯焊丝接头组织性能

通过激光填丝焊接方法并采用自主开发设计的钛合金药芯焊丝,进行TC4钛合金板的焊接,对获得的焊接接头进行850℃保温2 h后随炉冷却退火工艺处理,并与焊态焊接接头的组织性能进行比对分析,结果表明,热处理态焊接接头焊缝中由α_p相、α_s相集束及点状分布的残留β相构成,没有发现焊态焊缝中的α’马氏体组织;热处理态焊接接头强度降低但断后伸长率和常温冲击韧性增加;热处理态焊接接头拉伸断口由大量撕裂唇包围,韧窝深且均匀,呈微孔聚合韧性断裂.通过XRD测试发现焊态焊缝中主要由α’马氏体组成,还有少量极弱的多角度α相衍射峰,而热处理态焊缝中α相衍射峰中心角度位置与焊态焊缝中α’马氏体一致,另外还发现了较为明显且尖锐的β相(110)衍射峰.     

退火温度对TC18钛合金组织及织构演变规律的影响

随着钛合金锻件的大型化,锻造过程中应力场、温度场不均匀问题更加突出,锻件局部形成锋锐织构的可能性大大增加,易对产品的可靠性及安全性造成危害。本文利用EBSD技术,对比了工业生产的大规格TC18钛合金棒材不同位置中心及表层的组织及织构差异,通过观察两者在不同保温温度下α相及β相的组织及织构特征,研究退火后组织及织构演变规律。结果表明：在两相区,β相主要发生回复,部分α相发生再结晶,β相晶粒尺寸及织构基本不发生变化。接近相变点时,大尺寸回复态β晶粒易于利用尺寸优势吞并其他晶粒;部分α相,特别是晶界处取向接近的片层α相,易于通过合并发生晶粒长大;特殊取向的α相更易发生相变,相变的α相不会形成新的β晶核。在单相区,β相发生再结晶及晶粒长大,且无择尤现象,β相织构明显减弱。     

TC4钛合金小规格棒材连续轧制工艺研究

研究了不同连续轧制温度对TC4钛合金组织和力学性能的影响。结果表明,TC4钛合金相同道次加工,α+β两相区加工较β区加工棒材组织更细小弥散;两种轧制温度的棒材性能均符合GB/T 13810标准要求,两相区轧制较β区轧制抗拉强度高80~90 MPa,塑性变化不大。     

TC17(α + β)/TC17(β)钛合金线性摩擦焊接头相组成及织构分析

利用电子背散射衍射技术对TC17(α+β)/TC17(β)钛合金线性摩擦焊接头测试并分析,对接头各区域进行相鉴定和织构分析.结果表明,与母材相比,焊态接头两侧热力影响区α相减少,β相增多.由于焊缝区冷却迅速快,焊态焊缝处发生动态再结晶,生成了大量的亚稳定β相晶粒. TC17(β)侧母材及热力影响区的织构分布密度比TC17(α+β)侧强,且焊态焊缝区产生(5 4 6)[■]织构,轧面与(1 1 1)近似平行.经过610℃热处理后,焊缝区亚稳定β相发生分解,形成细小的次生α相和β相.与焊态焊缝相比,热处理后焊缝区晶体稍有转动,焊缝区织构强度较焊态有较大增强,形成(5 5 7)[■]织构.热处理前后的焊缝区晶体取向都存在着ND方向与[1 1 1]靠近,轧面与(111)接近平行的择优取向.     

Extracting dimensional information from steel reinforcing bars in concrete using neural networks trained on data from an inductive sensor

A new method is presented for extracting dimensional information from steel bars using images generated by an inductive sensor. The technique is based on the application of two feedforward backpropagation neural networks; one to estimate bar depth and the other to estimate bar diameter. Both of the networks have been trained on a set of data that consists of the peak parameters of six different bars scanned at 41 different bar depths. These input and target data must be pre-processed to obtain a good network generalisation. By testing the two networks with a completely different set of data, accurate performance has been obtained. Real, two-dimensional scan data have then been applied to both of the networks and the bar dimensional parameters have been extracted successfully. The advantage of the neural network method for extracting information is that it continues to operate reliably for very deep bars, for which the signal strength is severely attenuated and manifests a poor signal-to-noise ratio. Depth and diameter measurements have been obtained for bars located down to 58 mm, with errors that satisfy the requirements of the BS 1881 standard. At a depth of 40 mm, these measurements yield an error of ±4%, and this decreases as the depth reduces; in other words, the extracted bar diameter is within the requirements of the DIN 488 standard.     

30Cr3MoV钢热压缩流变应力行为研究

利用Gleeble-3500进行热模拟压缩实验,对低合金钢30Cr3MoV在1173～1473 K变形温度以及0.1-10 s(-1)应变速率条件下的高温流变应力行为进行了研究.通过对真应力-真应变曲线进行分析得到该材料的形变激活能、流变应力本构方程以及峰值应变和峰值应力与变形温度、应变速率之间的关系方程.     

Thickness measurement of non-magnetic plates using multi-frequency eddy current sensors

A robust feature in multi-frequency eddy current (MEC) testing has been found that can be directly linked to the thickness of the plate under test. It is shown mathematically that the peak frequency of the imaginary part of the inductance change when an air-cored coil is placed next to a non-magnetic metallic plate is inversely proportional to the thickness of the plate for a given material. Experimental results indicate that this relationship also holds for a ferrite-cored U-shaped coil. In addition, this peak frequency has been shown to be relatively independent of lift-off variations. Use of this new feature provides a fast and accurate method to gauge the thickness of plates. Measurements made for a sample air-cored and ferrite U-cored coil next to copper and aluminium plates of various thicknesses verified the proposed method.     

普通快走丝线切割机间隙电压取样电路浅析

介绍了传统的间隙电压取样电路，指出了它存在的问题，简述了取样电路的发展方向。     

缺陷深度脉冲热像检测新方法

介绍脉冲热像检测中由峰值时间求缺陷深度的方法，对热传导性能好的材料，从红外热像时间序列难以捕捉到峰值时间。为此提出了一个既能避开峰值时间又能被红外热像仪探测和记录的新参数，从而达到测量缺陷深度的目的。     

非正弦交变励磁电流峰值与试件磁化关系的讨论

论述了磁粉探伤中,当用可控硅产生非正弦交变(50 Hz)电流励磁时,磁化的效果仍取决于励磁电流的峰值。     

中频低压脉冲电流对纯铝凝固组织的影响

通过调整脉冲电流峰值和脉冲频率，研究了中频低压脉冲电流对纯铝凝固组织的影响。试验结果表明：中频低压脉冲电流可使纯铝的凝固组织由柱状晶转变为等轴晶，电流峰值在500～6000A、脉冲频率在100～1000Hz范围内，随着脉冲电流峰值和脉冲频率的提高，等轴晶不断细化，等轴晶晶区面积增大。     

脉冲电流对亚共晶Al-Si合金凝固组织的影响

采用自制的脉冲电源,通过调节脉冲电流峰值,研究了脉冲电流峰值对亚共晶Al-Si合金凝固组织的影响。结果表明:随着脉冲电流峰值的增大,合金的的宏观组织愈加细化;微观组织中,先析出相α-Al枝晶形态趋于向等轴晶转变,而共晶Si组织逐渐粗化。     

脉冲电流对亚共晶A-Si合金凝固组织的影响

采用自制的脉冲电源，通过调节脉冲电流峰值，研究了脉冲电流峰值对亚共晶Al-Si合金凝固组织的影响。结果表明；随着脉冲电流峰值的增大，合金的的宏观组织愈加细化；微观组织中，先析出相α-Al枝晶形态趋于向等轴晶转变，而共晶Si组织逐渐粗化。     

基于巴克豪森效应的钢轨表面应力研究

基于巴克豪森噪声(MBN)检测原理,研究了60 kg/m钢轨的巴克豪森信号与压应力的变化关系。介绍了MBN检测系统的设计与实行方案和在应力检测方面的应用。在材料的弹性范围内,MBN平均值、均方根和振铃数都随着压应力的增大而减小,其变化率依次递增。MBN峰值时间随着压应力的增大而增大。MBN信号与温度呈线性关系,可用来检测不同温度下的钢轨应力值。