Influences of poling condition and sintering temperature on piezoelectric properties of (Na0.5Bi0.5)1 − xBaxTiO3 ceramics

The structure, ferroelectric characteristics and piezoelectric properties of (Na_0.5Bi_0.5)_1 − xBa_xTiO₃ (x = 0.04, 0.06, 0.10) ceramics prepared by conventional solid state method were investigated. The influences of poling condition and sintering temperature on the piezoelectric properties of the ceramics were examined. The piezoelectric properties of the ceramics highly depend on poling field and temperature, while no remarkable effect of poling time on the piezoelectric properties was found in the range of 5-25 min. Compared with (Na_0.5Bi_0.5)_0.96Ba_0.04TiO₃ and (Na_0.5Bi_0.5)_0.90Ba_0.10TiO₃, the piezoelectric properties of (Na_0.5Bi_0.5)_0.94Ba_0.06TiO₃ are more sensitive to poling temperature due to the relatively low depolarization temperature. Moderate increase of sintering temperature improved the poling process and piezoelectric properties due to the development of microstructural densification and crystal structure. With respect to sintering behavior and piezoelectric properties, a sintering temperature range of 1130-1160 °C was ascertained for (Na_0.5Bi_0.5)_0.90Ba_0.10TiO₃.     

Dielectric, ferroelectric and piezoelectric properties of Bi0.5Na0.5TiO3-(Ba0.7Ca0.3)TiO3 ceramics at morphotropic phase boundary composition

(1 − x)Bi_0.5Na_0.5TiO₃-x(Ba_0.7Ca_0.3)TiO₃ (BNT-xBCT, 0 ≤ x ≤ 0.15) solid solutions have been synthesized by a conventional solid state sintering method for obtaining a morphotropic phase boundary (MPB) with good piezoelectric properties. X-ray diffraction patterns reveal that a MPB of rhombohedral and tetragonal phases is formed at compositions 0.09 ≤ x ≤ 0.12. Addition of BCT into BNT greatly lowered coercive field E_c without degrading remanent polarization P_r. The specimen with x = 0.09 has the good piezoelectric properties: d₃₃ = 125 pC/N and k_p = 0.33. A modified Curie-Weiss law was used to fit the dielectric constant of BNT-xBCT ceramics, and a frequency dispersion was observed during the phase transitions from antiferroelectric to paraelectric in specimens with x exceeding 0.06.     

Influence of sintering temperature on piezoelectric properties of (K0.5Na0.5)NbO3-LiNbO3 lead-free piezoelectric ceramics

Lead-free piezoelectric ceramics (1 − x)(K_0.5Na_0.5)NbO₃-xLiNbO₃ have been synthesized by traditional ceramics process without cold-isostatic pressing. The effect of the content of LiNbO₃ and the sintering temperature on the phase structure, the microstructure and piezoelectric properties of (1 − x)(K_0.5Na_0.5)NbO₃-xLiNbO₃ ceramics were investigated. The result shows that the phase structure transforms from the orthorhombic phase to tetragonal phase with the increase of the content of LiNbO₃, and the orthorhombic and tetragonal phase co-exist in (K_0.5Na_0.5)NbO₃-LiNbO₃ ceramics when the content of LiNbO₃ is about 0.06 mol. The sintering temperature of (1 − x)(K_0.5Na_0.5)NbO₃-xLiNbO₃ decreases with the increase of the content of LiNbO₃. The optimum composition for (1 − x)(K_0.5Na_0.5)NbO₃-xLiNbO₃ ceramics is 0.94(K_0.5Na_0.5)NbO₃-0.06LiNbO₃. The optimum sintering temperature of 0.94(K_0.5Na_0.5)NbO₃-0.06LiNbO₃ ceramics is 1080 °C. Piezoelectric properties of 0.94 (K_0.5Na_0.5)NbO₃-0.06LiNbO₃ ceramics under the optimum sintering temperature are piezoelectric constant d₃₃ of 215 pC/N, planar electromechanical coupling factor k_p of 0.41, thickness electromechanical coupling factor k_t of 0.48, the mechanical quality factor Q_m of 80, the dielectric constant of 530 and the Curie temperature T_c = 450 °C, respectively. The results indicate that 0.94(K_0.5Na_0.5)NbO₃-0.06LiNbO₃ piezoelectric ceramics is a promising candidate for lead-free piezoelectric ceramics.     

The synthesis of lead-free ferroelectric Bi0.5Na0.5TiO3-Bi0.5K0.5TiO3 thin films by sol-gel method

(1 − x)Bi_0.5Na_0.5TiO₃-xBi_0.5K_0.5TiO₃ [BNT-BKT-100x] thin films have been successfully deposited on Pt/Ti/SiO₂/Si substrates by a sol-gel process together with rapid thermal annealing. A morphotropic phase boundary (MPB) between Bi_0.5Na_0.5TiO₃ and Bi_0.5K_0.5TiO₃ was determined around x ∼ 0.15. Near the MPB, the film exhibits the largest grain size, the highest ε value (360) and the largest P_r value (13.8 μC/cm²). The BNT-BKT thin film system is expected to be a new and promising candidate for lead-free piezoelectric applications.     

Morphotropic phase boundary and piezoelectric properties of (Bi1/2Na1/2)1 − x(Bi1/2K1/2)xTiO3-0.03(Na0.5K0.5)NbO3 ferroelectric ceramics

Lead-free piezoelectric ceramics, (Bi_1/2Na_1/2)_1 − x(Bi_1/2K_1/2)_xTiO₃-0.03(Na_0.5K_0.5)NbO₃ (x = 0.10-0.40) were synthesized by conventional solid-state sintering. A morphotropic phase boundary (MPB) between rhombohedral and tetragonal phases was confirmed. Two dielectric anomalies can be observed, showing diffused phase transition behavior. There is no shift of the dielectric maximum temperature with frequency due to the contribution of space charge at high temperatures, similar to pure (Bi_1/2Na_1/2)TiO₃. The materials near MPB show a strong compositional dependence with the optimal properties of a d₃₃ of 167 pC/N, a k_p of 35.5%, a P_r of 27.6 μC/cm² and a E_c of 27.9 kV/cm, suitable for future application.     

Electrical and luminescence properties of Er-doped Bi0.5Na0.5TiO3 ceramics

The influences of Er content on the dielectric and photoluminescence performances of Bi_0.5Na_0.5TiO₃-xEr (x = 0, 0.005, 0.01, 0.015, 0.02, 0.03) ceramics have been investigated. The results show that Bi_0.5Na_0.5TiO₃-xEr ceramics with x = 0.01 Er have maximum values of photoluminescence and piezoelectric properties. A bright green emission at 550 nm and enhanced piezoelectric response are achieved in the ceramic Bi_0.5Na_0.5TiO₃-0.01Er at room temperature. Furthermore, the photoluminescence performance of the ceramics is significantly enhanced by electric poling.     

Structure and ferroelectric properties in (K0.5Bi0.5)TiO3-BiScO3-PbTiO3 piezoelectric ceramic system

(K_0.5Bi_0.5)TiO₃-BiScO₃-PbTiO₃ ceramics were synthesized by conventional solid-state method. A morphotropic phase boundary (MPB) was confirmed with the aid of structural analysis. Two dielectric anomalous peaks were observed, the one around dielectric maximum temperature (T_m) due to phase transformation from ferroelectric to paraelectric while the second one could be ascribed to space charges. Furthermore, the existence of space charges also resulted in the independence of T_m with frequency at low lead composition. A new high temperature piezoelectric ceramic, 0.30(K_0.5Bi_0.5)TiO₃-0.30BiScO₃-0.40PbTiO₃ close to MPB exhibited excellent electrical properties with T_m of 384 °C, d₃₃ of 247 pC/N, k_p of 38.9%, P_r of 19.41 μC/cm², and E_c of 2.25 kV/mm, indicative of a candidate for high temperature application.     

Giant strain in Nb-doped Bi0.5(Na0.82K0.18)0.5TiO3 lead-free electromechanical ceramics

The effect of Nb substitution on the crystal structure, ferroelectric, and electric field induced strain properties of Bi_0.5(Na₈₂K_0.18)_0.5TiO₃ (BNKT) ceramics has been investigated. The coexistence of rhombohedral and tetragonal phases was found in undoped BNKT ceramics, however, Nb doping induced a phase transition to a pseudocubic phase with high electrostriction coefficients. When 3 mol% Nb was substituted on Ti ions, the electric field induced strain was markedly enhanced up to S_max/E_max = 641 pm/V, which is higher than those previously reported on non-textured lead-free electromechanical ceramics.     

Piezoelectric and dielectric properties of K0.5Na0.5NbO3-LiSbO3-BiScO3 lead-free piezoceramics

(1 − x) (0.95K_0.5Na_0.5NbO₃-0.05LiSbO₃)-xBiScO₃ lead-free piezoceramics have been fabricated by an ordinary pressure-less sintering process. The relationship between the BS content, phase structure, density, and piezoelectric properties and their temperature stability was discussed particularly. All compositions show a main perovskite structure, showing room-temperature symmetries of orthorhombic at x = 0, of tetragonal at 0.002 ≤ x ≤ 0.01. When 0.002 ≤ x ≤ 0.008, the ceramics have excellent electrical properties of d₃₃ = 265-305 pC/N, k_p = 45-54%, ?_r = 1346-1638, Curie temperature T_c = 315-370 °C and depolarizing temperature T_d = 315-365 °C, comparable to that of other KNN-based piezoceramics. The results indicate that the ceramics are promising lead-free piezoelectric materials.     

Tantalum influence on physical properties of (K0.5Na0.5)(Nb1−xTax)O3 ceramics

Lead-free (K_0.5Na_0.5)(Nb_1−xTa_x)O₃ ceramics with x = 0.00-0.30 were prepared by the solid-state reaction technique. The effects of Ta on microstructure, crystallographic structure, phase transition and piezoelectric properties have been investigated. It has been shown that the substitution of Ta decreases Curie temperature T_C and orthorhombic-tetragonal phase transition temperature T_O-T, while increasing the rhombohedral-orthorhombic phase transition temperature T_R-O. In addition, piezoelectric activity is enhanced with the increase of Ta content. The ceramics with x = 0.30 have the high value of piezoelectric coefficient d₃₃ = 205 pC/N. Moreover, k_p shows little temperature dependence between −75° C and 75 °C, and d₃₃ exhibits very good thermal stability over the range from −196 °C to 75 °C in the aging test.     

Fabrication of lead-free (Na0.82K0.18)0.5Bi0.5TiO3 piezoelectric nanofiber by electrospinning

(Na_0.82K_0.18)_0.5Bi_0.5TiO₃ nanofibers were synthesized by sol-gel process and electrospinning. Scanning electron microscopy was used to verify that the diameters and lengths are in the range of 150-600 nm and several hundreds of micrometer. Perovskite structure and grain size (20-70 nm) were verified by X-ray diffraction and transmission electron microscopy. The high effective piezoelectric coefficient d₃₃ (96 pm/V) was measured by scanning force microscopy. It may be attributed to easily tilting the polar vector of domain for an electric field and the increase in the number of possible spontaneous polarization direction near the rhombohedral-tetragonal morphotropic phase boundary. The research shows that there are potentional applications for (Na_0.82K_0.18)_0.5Bi_0.5TiO₃ nanofiber in nanoscale lead-free piezoelectric devices.     

Dielectric and piezoelectric properties of Y2O3 doped (Bi0.5Na0.5)0.94Ba0.06TiO3 lead-free piezoelectric ceramics

Y₂O₃ doped lead-free piezoelectric ceramics (Bi_0.5Na_0.5)_0.94Ba_0.06TiO₃ (0-0.7 wt%) were synthesized by the conventional solid state reaction method, and the effect of Y₂O₃ addition on the structure and electrical properties was investigated. X-ray diffraction shows that Y₂O₃ diffuses into the lattice of (Bi_0.5Na_0.5)_0.94Ba_0.06TiO₃ to form a solid solution with a pure perovskite structure. The temperature dependence of dielectric constant of Y₂O₃ doped samples under various frequencies indicates obvious relaxor characteristics different from typical relaxor ferroelectric and the mechanism of the relaxor behavior was discussed. The optimum piezoelectric properties of piezoelectric constant d₃₃ = 137 pC/N and the electromechanical coupling factor k_p = 0.30 are obtained at 0.5% and 0.1% Y₂O₃ addition, respectively.     

Effects of CuO doping on the electrical properties of 0.98K0.5Na0.5NbO3-0.02BiScO3 lead-free piezoelectric ceramics

CuO-doped 0.98K_0.5Na_0.5NbO₃-0.02BiScO₃ (0.98KNN-0.02BS-xCu) lead-free piezoelectric ceramics have been fabricated by ordinary sintering technique. The effects of CuO doping on the dielectric, piezoelectric, and ferroelectric properties of the ceramics were mainly investigated. X-ray diffraction reveals that the samples at doping levels of x ≤ 0.01 possess a pure tetragonal perovskite structure. The specimen doped with 1 mol% CuO exhibits enhanced electrical properties (d₃₃ ~ 207 pC/N, k_p ~ 0.421, and k_t = 0.424) and relatively high mechanical quality factor (Q_m = 288). These results indicate that the 0.98KNN-0.02BS-0.01Cu ceramic is a promising candidate for lead-free piezoelectric ceramics for applications such as piezoelectric actuators, harmonic oscillator and so on.     

Ferroelectric properties of lithia-doped (Bi0.95Na0.75K0.20)0.5Ba0.05TiO3 ceramics

Lead-free piezoelectric (Bi_0.95Na_0.75K_0.20−xLi_x)_0.5Ba_0.05TiO₃ ceramics have been prepared by conventional process for different lithium substitutions. The SEM images show that the ceramics are well sintered at 1428 K. Dielectric and ferroelectric measurements have been performed. With the increasing of lithium substitution, the Curie temperature of the (Bi_0.95Na_0.75K_0.20−xLi_x)_0.5Ba_0.05TiO₃ ceramics shifts from 570 K to 620 K, but the maximum value of the dielectric constant decreases from 6700 to 4700 correspondingly. A relatively larger remanent polarization of 36.8 μC/cm² has been found in the x = 0.05 sample. The coercive field decreases as the lithium substitution amount increases. An optimized d₃₃ = 194 × 10^− 12 C/N and a relative dielectric constant ε_r = 1510 have been obtained in (Bi_0.95Na_0.75K_0.15Li_0.05)_0.5Ba_0.05TiO₃.     

Synthesis and characterization of (Na0.85K0.15)0.5Bi0.5TiO3 ceramics by different methods

The (Na_0.85K_0.15)_0.5Bi_0.5TiO₃ (BNKT) powders were synthesized by solid-state method, sol-gel method and stearic acid method. Microstructure, piezoelectric and dielectric properties of the ceramics were investigated. Attempts had been made to understand the reaction processes by using thermo gravimetric (TG) and differential scanning calorimetry (DSC). The BNKT powders have a perovskite structure with average crystallite sizes of 168 nm, 85 nm and 79 nm, corresponding to the solid-state method, the sol-gel method and the stearic acid method, respectively. The ceramics derived from the powder synthesized by sol-gel method presents the most homogeneous microstructure and largest grain size (5-7 μm). The effects of average crystallite size on microstructures and electric properties of the BNKT ceramics were investigated. Both the piezoelectric properties and dielectric properties were enhanced with the increase of grain size.     

Enhanced multiferroic properties and tunable magnetic behavior in multiferroic BiFeO3-Bi0.5Na0.5TiO3 solid solutions

A series of multiferroic (1−x)BiFeO₃−x(Bi_0.5Na_0.5)TiO₃ (BF-BNT) (x = 0 − 0.6) solid solution ceramics were prepared by a sol-gel method. The XRD results show that increasing BNT content induce a gradual phase transformation from rhombohedral to pseudocubic structure near x = 0.4. Compared with pure BiFeO₃, superior multiferroic properties are obtained for x = 0.3 with remnant polarization P_r = 1.49 μC/cm² and saturated magnetization M_s = 0.51 emu/g. Importantly, the paramagnetic (PM) to ferromagnetic (FM) transition is observed for the solutions, and the Curie temperature (T_C) can be tuned by varying the content of BNT. This observed FM ordering is discussed in terms of the possible existence of the long-range superexchange interaction of Fe³⁺-O-Ti-O-Fe³⁺ in the chemically ordered regions.     

Mixed cation effect in xR2O-(40 − x)Na2O-50B2O3-10Bi2O3 (R = Li, K) glasses

Mass density, glass transition temperature and ionic conductivity are measured in xLi₂O-(40 − x)Na₂O-50B₂O₃-10Bi₂O₃ and xK₂O-(40 − x)Na₂O-50B₂O₃-10Bi₂O₃ glass systems with 0 ≤ x ≤ 40 mol%. The strength of the mixed alkali effect in T_g, dc electrical conductivity and activation energy has been determined in each glass system. The magnitudes of the mixed alkali effect in T_g for the mixed Li/Na glass system are much smaller than those in the mixed K/Na glasses. The impact of mixed alkali effect on dc electrical conductivity in mixed Li/Na glass system is more pronounced than in the K/Na glass system. The results are explained based on dynamic structure model.     

SmAlO3-modified (K0.5Na0.5)0.95Li0.05Sb0.05Nb0.95O3 lead-free ceramics with a wide sintering temperature range

Lead-free ceramics (1 − x)(K_0.5Na_0.5)_0.95Li_0.05Sb_0.05Nb_0.95O₃-xSmAlO₃ (KNLNS-xSA) were prepared by conventional sintering technique. The phase structure, dielectric and piezoelectric properties of the ceramics were investigated. All compositions show a main perovskite structure, exhibiting room-temperature symmetries of tetragonal at x ≤ 0.0075, of pseudo-cubic at x = 0.0100. The Curie temperature of KNLNS-xSA ceramics decreases with increasing SmAlO₃ content. Moreover, the addition of SmAlO₃ can effectively broaden the sintering temperature range of the ceramics. The KNLNS-xSA ceramic with x = 0.0050 has an excellent electrical behavior of piezoelectric coefficient d₃₃ = 226 pC/N, planar mode electromechanical coupling coefficient k_p = 38%, dielectric loss tan δ = 3.0%, mechanical quality factor Q_m = 60, and Curie temperature T_C = 327 °C, suggesting that this material could be a promising lead-free piezoelectric candidate for piezoelectric applications.     

Effect of BiFeO3 additions on the dielectric and piezoelectric properties of (K0.44Na0.52Li0.04)(Nb0.84Ta0.1Sb0.06)O3 ceramics

(1 − x) (K_0.44Na_0.52Li_0.04)(Nb_0.84Ta_0.1Sb_0.06)O₃ − x BiFeO₃ (x = 0, 0.002, 0.004, 0.006, 0.008, 0.01) lead-free piezoelectric ceramics were prepared by the conventional ceramic processing. The compositional dependence of the phase structure and the electrical properties of the ceramics were studied. A morphotropic phase boundary between the orthorhombic and tetragonal phases was identified in the composition range of 0.004 < x < 0.006. The ceramics near the morphotropic phase boundary exhibit a strong compositional dependence and enhanced piezoelectric properties. The ceramics with 0.6 mol.% BiFeO₃ exhibit good electrical properties (d₃₃ ∼ 246 pC/N, k_p ∼ 43%, T_c ∼ 285 °C, ?_r ∼ 1871, and tan δ ∼ 1.96%). These results show that the (1 − x) (K_0.44Na_0.52Li_0.04)(Nb_0.84Ta_0.1Sb_0.06)O₃ − x BiFeO₃ ceramic is a promising lead-free piezoelectric material for applications in different devices.     

Effect of Pb(Fe1/2Nb1/2)O3 modification on dielectric and piezoelectric properties of Pb(Mg1/3Nb2/3)O3-PbZr0.52Ti0.48O3 ceramics

10 mol% Pb(Fe_1/2Nb_1/2)O₃ (PFN) modified Pb(Mg_1/3Nb_2/3)O₃-PbZr_0.52Ti_0.48O₃ (PMN-PZT) relaxor ferroelectric ceramics with compositions of (0.9 − x)PMN-0.1PFN-xPZT (x = 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8 and 0.9) were prepared. X-ray diffraction investigations indicated that as-prepared ceramics were of pure perovskite phase and the sample with composition of x = 0.8 was close to morphotropic phase boundary (MPB) between rhombohedral and tetragonal phase. Dielectric properties of the as-prepared ceramics were measured, and the Curie temperature (T_c) increased sharply with increasing PZT content and could be higher than 300 °C around morphotropic phase boundary (MPB) area. At 1 kHz, the sample with composition of x = 0.1 had the largest room temperature dielectric constant ?_r = 3519 and maximum dielectric constant ?_m = 20,475 at T_m, while the sample with composition of x = 0.3 possessed the maximum dielectric relaxor factor of γ = 1.94. The largest d₃₃ = 318 pC/N could be obtained from as-prepared ceramics at x = 0.9. The maximum remnant polarization (P_r = 28.3 μC/cm²) was obtained from as-prepared ceramics at x = 0.4.