矿物掺合料对自密实混凝土抗氯离子渗透性的影响

耐久性是自密实混凝土（SCC）的重要性质。本文应用电通量法研究了掺粉煤灰、矿渣的SCC抗氯离子渗透性能,通过对单掺和复掺时SCC电通大小的分析发现：粉煤灰和矿渣都能改善SCC的抗氯离子渗透性能,矿渣提高SCC的抗氯离子渗透性能要优于粉煤灰,二者复掺对SCC抗氯离子渗透的复合叠加效应并不明显。其机理是粉煤灰和矿渣提高水泥石密实性,强化混凝土界面过渡区,粉煤灰、矿渣物理化学吸附作用能固结Cl-,降低Cl-渗透性。SCC中掺入掺合料能减少离析、避免泌水,达到自密实效果,粉煤灰对混凝土流动增大的作用效果要优于磨细矿渣的效果。掺合料复掺对自密实混凝土强度具有复合叠加效应,混凝土28 d强度等级可提高1～2级。     

不同矿物掺合料对RPC抗氯离子渗透性的研究

为研究不同矿物细掺合料对活性粉末混凝土氯离子渗透系数的影响,采用NEL法比较硅灰和粉煤灰双掺、硅灰和石英粉双掺、硅灰和粉煤灰及石英粉互掺、硅灰和硅微粉双掺共4组RPC不同的抗氯离子系数。研究结果表明:氯离子渗透系数随养护龄期的增加而减小;随着养护温度的提高而减小;当在同一养护条件下,粉煤灰的掺入对氯离子扩散系数影响不大;石英粉和硅微粉的掺入会提高氯离子渗透系数,复掺石英粉和粉煤灰能降低氯离子渗透系数。     

掺合料混凝土抗硫酸盐性能及评价方法

研究了硅灰、矿渣微粉和粉煤灰三种常用矿物掺合料对混凝土抗硫酸盐腐蚀能力的影响。试验结果表明:三种矿物掺合料均可改善混凝土的抗硫酸盐腐蚀能力,作用效率由高至低依次为:硅灰>矿渣>粉煤灰;掺合料混凝土中砂浆膨胀值发展与混凝土硫酸盐腐蚀程度有良好相关性,采用混凝土中砂浆的膨胀值和抗压强度比两项指标能较准确的评价混凝土抗硫酸盐腐蚀的能力。     

大掺量混合材高性能混凝土的制备及强度特性

在固定用水量为130 kg/m3下,研究了粉煤灰、磨细矿渣和硅灰对水泥替代量为30%、50%、70%,水胶比为0.33的高性能混凝土的制备。探讨了粉煤灰、硅灰和矿渣对新拌混凝土流动性和抗压强度的影响。在低水胶比情况下,粉煤灰、磨细矿渣和硅灰大掺量复掺,可制备得到工作性良好、早期强度满足要求和后期强度有极好发展的高性能混凝土;在高效减水剂的作用下,在大掺量混合材混凝土中以硅灰、磨细矿渣取代部分粉煤灰,可以有效提高大掺量混凝土的早期强度,进一步改善新拌混凝土的工作性。     

矿物功能材料对混凝土氯离子渗透性的影响

在单因素影响方案的基础上 ,研究了多种磨细工业废渣及天然矿物材料的不同组合与叠加对混凝土氯离子渗透性的影响。通过试验研究和理论分析证实了硅灰与偏高岭土、粉煤灰、矿渣之间存在着“超复合叠加效应”,为合理选择矿物功能材料的种类及掺配方式 ,特别是偏高岭土的合理应用提供了技术思路 ,实现了矿物功能材料在提高混凝土抗氯离子渗透性方面的性能优化与降低成本的双重效用     

轻集料混凝土的抗渗性能研究

利用快速氯离子渗透试验和溶液气压法研究了粉煤灰、矿渣和硅灰三种矿物掺合料对轻集料混凝土抗渗性能的影响.结果表明,掺合料的加入能够显著提高轻集料混凝土的抗渗性能;利用SEM、孔结构试验探讨了掺合料提高轻集料混凝土抗渗性的作用机理,研究结果为深入开展高性能轻集料混凝土的研究提供了参考.     

复合矿物质超细粉对水泥石自收缩影响效应

为了探讨复合矿物质超细粉对水泥石自收缩的影响规律,将硅灰与粉煤灰、磨细矿渣与粉煤灰2种复合掺合料分别加入水泥浆体中,通过改变粉煤灰与硅灰的质量比、粉煤灰与磨细矿渣的质量比。测量其自收缩量,发现粉煤灰能抑制自收缩,磨细矿渣和硅灰促进自收缩,当粉煤灰与硅灰或磨细矿渣复配时.抑制自收缩的作用和硅灰与粉煤灰的质量比或硅灰与磨细矿渣的质量比显著相关.     

纤维碱矿渣混凝土抗氯离子渗透性能研究

制备碱矿渣和普通硅酸盐水泥两种系列的混凝土,对比分析聚丙烯纤维及粉煤灰对这两种体系混凝土渗透性能的影响规律,结果表明:随着龄期的延长,氯离子渗透系数均呈降低的趋势,单掺纤维或粉煤灰并不能提高碱矿渣混凝土的抗氯离子渗透能力;粉煤灰与纤维复掺后,碱矿渣混凝土的抗氯离子渗透能力仍低于纯碱矿渣混凝土,即二者复掺亦不能提高碱矿渣混凝土的抗氯离子渗透能力。     

胶凝材料组成对混凝土TSA硫酸盐侵蚀的影响

研究不同水泥品种、矿物掺合料对混凝土抗TSA侵蚀性能的影响规律,采用掺30%石灰石粉填料的胶砂件,测试各砂浆在5±1℃的2%MgSO4溶液中浸泡1年后的外观破损与强度损失情况,通过X-射线衍射仪分析各砂浆的矿物成分.结果表明:不同品种水泥的抗TSA侵蚀能力由高到低依次为:硫铝酸盐水泥 硅酸盐水泥复合>硫铝酸盐水泥>抗硫酸盐水泥>普硅水泥.掺硅灰和矿渣细粉均能明显改善混凝土抗TSA侵蚀性能,且矿渣粉掺量越大效果越明显.由于粉煤灰活性低,掺量较少时可在一定程度上减缓TSA侵蚀过程,但掺量过多时反而产生不利影响.     

大掺量矿物掺合料混凝土的干燥收缩与数学模型

本文研究了矿物掺合料和膨胀剂对混凝土干燥收缩的影响。结果表明．在低水胶比等量取代55％水泥的情况下,单掺矿渣时混凝土的干燥收缩值最小,双掺矿渣和粉煤灰时混凝土干燥收缩值略有增加,复合掺加硅灰时将显著增大混凝土的干燥收缩,复合掺加膨胀剂有利于降低干燥收缩值。此外,建立了大掺量矿物掺合料混凝土干燥收缩的复合指数函数模型,该模型与实测值非常吻合。     

Influence of Mineral Admixtures on the Permeability of Lightweight Aggregate Concrete

The permeability of lightweight aggregate concrete was studied. Some efforts were taken to increase the resistarwe of lightweight aggregate concrete (LC) to water penetration by using the mineral admixtures of fiy ash, granulated blast furmwe slag or silica fume. Accelerated chloride penetrability test and liquid atmosphere press method were used to study the anti-permeability, of lightweight aggregate concrete. The experimental results show that fly ash, granulated blast furnace slag and silica fume can decrease the permeability of lightweight aggregate concrete, but the effect of granulated blast furnace slag is poor. According to the SEM and pore structure analyzing results, an interface self- reinforcing effect model was presented and the reinforced mechanism of mineral mixture on LC was discussed according to the model described by authors.     

Effect of glass powder on chloride ion transport and alkali-aggregate reaction expansion of lightweight aggregate concrete

The effects of glass powder on the strength development, chloride permeability and potential alkali-aggregate reaction expansion of lightweight aggregate concrete were investigated. Ground blast furnace slag, coal fly ash and silica fume were used as reference materials. The replacement of cement with 25% glass powder slightly decreases the strengthes at 7 and 28 d, but shows no effect on 90 d’s. Silica fume is very effective in improving both the strength and chloride penetration resistance, while ground glass powder is much more effective than blast furnace slag and fly ash in improving chloride penetration resistance of the concrete. When expanded shale or clay is used as coarse aggregate, the concrete containing glass powder does not exhibit deleterious expansion even if alkali-reactive sand is used as fine aggregate of the concrete.     

掺合料、早强剂对冻融混凝土Cl^-扩散系数的影响

目的研究粉煤灰、矿粉、掺硫酸钠粉煤灰、掺硫酸钠矿粉混凝土冻融循环后Cl^-扩散系数,解决混凝土冻融循环后的内部结构损伤问题．方法采用慢冻法冻融、NEL法测试冻融循环后混凝土Cl^-扩散系数．结果掺入粉煤灰的质量分数低于30％时,掺入矿粉的质量分数低于40％时,经100次冻融循环后混凝土Cl^-扩散系数均低于基准混凝土．经冻融循环后,掺硫酸钠矿物掺合料的混凝土在一定的矿物掺合料掺量范围内,混凝土Cl^-扩散系数低于基准混凝土．经冻融循环后,掺硫酸钠矿物掺合料的混凝土Cl^-扩散系数高于未掺硫酸钠的矿物掺合料混凝土．结论掺粉煤灰混凝土、掺矿粉混凝土的抗冻性好坏取决于矿物掺合料掺量范围．掺硫酸钠粉煤灰混凝土、掺硫酸钠矿粉混凝土,在一定矿物掺合料的掺量范围内,混凝土抗冻性好于基准混凝土．但是硫酸钠的加入使得混凝土抗冻性比未掺硫酸钠混凝土抗冻性差．     

聚丙烯纤维混凝土抗压强度与收缩性能时变规律研究

为了提高混凝土强度与改善混凝土的收缩性能,在混凝土中掺入聚丙烯纤维、硅灰及粉煤灰等掺合料,采用平行组对比试验,研究了掺合料对混凝土抗压强度和干燥收缩性能的影响规律,得到了相应的回归公式.结果表明,单掺粉煤灰的混凝土3,7,28 d抗压强度明显低于基准组,56 d抗压强度与基准组相差不大;复掺粉煤灰和硅灰混凝土的早期和后期抗压强度较单掺粉煤灰混凝土有不同程度的提高;聚丙烯纤维、粉煤灰和硅灰复掺可以显著抑制混凝土干燥收缩,且混凝土龄期与收缩率符合对数函数关系.     

矿物掺和料和再生骨料对混凝土的收缩性能的影响

研究了再生粗、细骨料取代量、矿物掺和料等因素对再生混凝土收缩性能的影响.结果表明：高品质再生细骨料混凝土的后期收缩值高于天然骨料混凝土,且随着再生细骨料取代量的增加而增大;高品质再生粗骨料混凝土的收缩值接近天然骨料混凝土;粉煤灰和普通矿粉相比能够很好的降低再生混凝土的早期和后期收缩值,超细矿粉和硅灰都能减少再生混凝土的后期收缩值,但硅灰增加了再生混凝土的早期收缩值.     

二次高温养护对高强混凝土抗Cl^-渗透性的影响

利用氯离子快速渗透法（RCM）研究了普通蒸汽养护后（80℃,0.1 MPa）再进行压蒸（180℃,1 MPa）养护,即二次高温养护,对不同胶凝材料体系的高强混凝土抗Cl-渗透性的影响。结果表明：对于纯水泥混凝土,与标养相比,＂蒸养-压蒸＂养护使混凝土抗Cl-渗透性能劣化。掺入粉煤灰、矿粉以及硅灰以等比例取代水泥时,＂蒸养-压蒸＂都较为充分地激发了上述混合材的火山灰活性,但不同掺合料对＂蒸养-压蒸＂后高强混凝土抗Cl-渗透性能影响差别较大。XRD和SEM研究表明上述结果的产生与高温下水化产物的种类和分布有关。