从锂离子二次电池正极废料—铝钴膜中回收钴的工艺研究

根据锂离子二次电池正极废料－铝钴膜原料中LiCoO2的性质,提出了LiCoO2在硫酸、双氧水体系中的分解反应为：2LiCoO2 3H2SO4 H2O2→Li2SO4 2CoSO4 4H2O O2↑确定从中回收铝、钴的工艺流程为：碱浸→酸溶→净化→沉钴。碱浸液中的铝用硫酸中和制取化学纯氢氧化铝,回收率94．84％;钴以草酸钴的形式回收,产品质量达到赣州钴钨有限责任公司的草酸钴产品标准,直收率95．75％。每处理1t铝钴膜废料可获纯利4．56万元。     

制酸烧渣综合回收铜钴实验

利用沸腾焙烧得到的硫铁矿制酸烧渣为原料,进行了酸浸、铜萃取、除铁、沉钴、尾渣氰化等综合回收铜钴实验研究。实验结果表明,采用沸腾焙烧—酸浸—萃取—除铁沉钴工艺可得到合格的铁精粉;酸浸铜浸出率为70.08%,钴浸出率为60.07%;铜萃取率93.6%,反萃率93.8%;萃余液除铁率大于99.9%,沉钴率大于98.9%。     

钴渣处理新工艺研究与生产实践

前言Foreword我公司应用碱浸工艺处理含钴物料进行七水硫酸钴产品的生产,同时产出钴渣。为了回收钴渣中的钴金属,特进行了工艺试验研究。试验中发现,采用原碱浸工艺处理钴渣时,钴回收率低,不到50%,且产品七水硫酸钴杂质超标,质量不合格。于是进行了处理钴渣的新工艺研究,开发出了直接酸浸—中和除铝—钠钴分离—酸溶净化—蒸发结晶工艺,并成功应用于生产,取得了良好的经济效益。本文主要对新工艺的试验研究结果进行了阐述及理论探讨,同时对原生产工艺及新工艺应用于生产的情况进行了介绍。含钴物料碱浸工艺流程简介A brief account of alka…     

从钴渣中浸出钴、锌、镉试验研究

研究了采用水洗—焙烧—还原酸浸工艺从A药剂钴渣中高效回收钴等有价金属,考察了焙烧温度、浸出时间、浸出温度、硫酸浓度、还原剂用量等对有价金属浸出率的影响。结果表明:钴渣在液固体积质量比5/1、常温下搅拌水洗1 h,然后在500℃下焙烧2 h,最后在80℃下用质量浓度80 g/L硫酸、10 g/L亚硫酸钠浸出1 h,钴浸出率在90%以上,锌浸出率在96%以上,镉浸出率大于99%,浸出液中的有价金属可高效回收。     

氢氧化钠碱浸钴钼废催化剂综合回收研究

采用氢氧化钠碱浸、硫酸酸化分步沉淀法从废催化剂中回收Mo,Al,Bi,Co,Ni等有色金属。首先对废催化剂进行氢氧化钠一、二次碱浸,使氧化钼和氧化铝生成可溶性的盐与氧化铋、氧化钴、氧化镍分离,然后通过分段沉淀使钼和铝分离,制备钼酸铵和硫酸铝。其次对碱浸富集氧化铋、氧化钴和氧化镍渣,利用氢氧化物溶度积不同,采用分步沉淀―酸溶萃取法使钴、铋、镍得到有效分离。试验结果表明:球磨时间30 min、催化剂粒度小于74μm、氢氧化钠的加量为金属Mo和Al理论耗量的1.2倍、液固比选取4∶1、浸出温度90℃时,一次碱浸钼的浸出率可达96.25%,一次碱浸渣再次碱浸率可达99.50%。碱浸富集金属混合渣采用加热酸浸、氧化除铁,将滤液的pH控制在2左右使铋以氢氧化铋沉淀分离,控制pH为9.5,使镍、钴以氢氧化物形式沉淀,然后酸溶、萃取使钴镍分离。整个回收工艺中,钼和铝的总回收率分别为94.56%和96.89%。     

从废高温镍钴合金中浸出镍和钴的试验研究

研究了采用"苏打焙烧-碱浸出铝、钼-氯气浸出钴、镍、铁等-TBP萃取除铁-中和水解除铬-P204萃取除微量杂质-N235萃取分离镍、钴"工艺处理废高温镍钴合金,重点考察了从废镍钴合金中浸出镍和钴,讨论了苏打焙烧温度和碱浓度对铝、钼浸出率的影响,碱浸渣氯气浸出电位、浸出时间、废合金粒度、添加剂的加入等因素对镍、钴浸出率的影响.试验确定了从废高温镍钴合金中浸出镍、钴的工艺优化条件.综合条件下,镍、钴平均浸出率分别为99.30%和97.67%,浸出渣中镍、钴质量分数平均为0.51%和0.44%.     

钴白合金的常压浸出工艺研究

采用氧化酸浸方法研究了高硅钴白合金的铜钴提取过程,考查了不同酸浸体系、氧化剂用量、H2SO4/HCl的摩尔比、液固比、浸出温度和浸出时间等因素对铜、钴浸出率的影响.结果表明：以硫酸和盐酸的混合液为浸出剂,当浸出温度为70℃、浸出时间为2 h、n（H2SO4）∶n（HCl）为8∶2、初始酸度为5 mol/L且其过量系数为1.2、以氯酸钠为氧化剂且其过量系数为1.4时,合金中钴、铁、铜的浸出率均可达99%以上,且无氯化亚铜沉淀产生,无硅胶产生,浸出浆的过滤性能良好.     

某氧化铜钴矿酸浸试验研究

针对刚果（金）某氧化铜钴矿进行了搅拌酸浸、搅拌还原-酸浸和淋滤还原-酸浸对比试验研究,确定了搅拌还原-酸浸是处理这种氧化铜钴矿的最佳方法,不但浸出速度快,而且浸出效果好,铜浸出率达到93．88％,钴浸出率达到95．2％;同时证明了采用堆浸（淋滤还原-酸浸）也是处理这种矿石的另一条重要的途径,也可得到理想的指标。     

某湿法炼锌净化钴渣选择性浸出回收锌与钴

采用选择性浸出—酸浸—萃取工艺回收某湿法炼锌企业产生的净化钴渣中的锌、钴。合适的选择性浸出条件为:净化钴渣粒度<0.530mm、浸出过程pH≥3.5、浸出终点pH=4.5、浸出时间3h、浸出液固比4∶1、浸出过程不加热(30℃),在此条件下锌浸出率超过95%、钴浸出率仅为6.24%。选择性浸出后锌主要进入浸出液,可返回至湿法炼锌工序回收利用;钴主要留存在选择性浸出渣中,继续经过酸浸溶出、P204萃取除杂后也可被回收利用。     

含金银铜硫精矿综合回收试验研究

以某含金银铜复杂硫精矿为研究对象,进行了沸腾炉焙烧—酸浸—氰化浸出联合流程研究,考察了焙烧、烧渣除杂及金、银浸出等作业条件。结果表明:采用沸腾炉焙烧—酸浸—氰化浸出联合流程,可综合回收各有价元素;在最佳工艺条件下,焙烧硫回收率97.57%,酸浸铜浸出率66.45%、硫浸出率88.28%、砷浸出率50.70%,氰化浸出金浸出率89.61%、银浸出率43.74%;酸浸渣金品位5.10 g/t、银品位20.53 g/t、铁品位65.58%,试验指标较好;酸浸液可进一步回收有价元素。     

Studies on Processing of an Alnico Scrap

This paper presents the results of research and development work on processing of alnico scrap, a secondary resource of nickel and cobalt, generated during the manufacturing of alnico magnets. The scrap contains 8–10% nickel, 10–12% cobalt, 32–50% of iron, 8–10% aluminium, 2% copper and remaining silica. Various processes such as acid leaching, aqueous chlorine leaching, salt roasting and cupric chloride leaching were studied in detail. Of these cupric chloride leaching was found to be most effective with respect to recovery and purity. It has been possible to obtain pure nickel and cobalt salts by cupric chloride leaching of the scrap, solvent extraction and precipitation of the salts. The overall recovery by the above process was almost 99%.     

Studies on Processing of an Alnico Scrap

Abstract

This paper presents the results of research and development work on processing of alnico scrap, a secondary resource of nickel and cobalt, generated during the manufacturing of alnico magnets. The scrap contains 8-10% nickel, 10-12% cobalt, 32-50% of iron, 8-10% aluminium, 2% copper and remaining silica. Various processes such as acid leaching, aqueous chlorine leaching, salt roasting and cupric chloride leaching were studied in detail. Of these cupric chloride leaching was found to be most effective with respect to recovery and purity. It has been possible to obtain pure nickel and cobalt salts by cupric chloride leaching of the scrap, solvent extraction and precipitation of the salts. The overall recovery by the above process was almost 99%.     

镍精矿加压酸浸新工艺研究

研究了金川镍精矿加压一步全浸镍、钴、铜新工艺,浸出液中和除铜后萃取分离镍钴,镍、钴、铜的浸出率可分别达到99.5%、98%和98%以上。该工艺与硫酸选择性浸出相比具有金属浸出率高、分离彻底、易分别回收等优点。     

过硫酸铵氧化沉淀法富集净化钴渣中钴的试验研究

某公司生产初期采用α-亚硝基-β-萘酚除钴工艺回收湿法炼锌净化钴渣中的钴,存在药剂消耗量大、钴渣含钴低、生产亏损的问题,后采用过硫酸铵氧化沉淀法富集钴,形成了一种钴的富集倍数高,成本低、流程短、易操作、环保的净化渣回收钴的实用方法。该方法分三个阶段:酸浸阶段包括稀酸选择性浸出和逆流酸性浸出,在较优工艺参数下,钴的浸出率达到95.8%;氧化除铁阶段在较优工艺参数下,滤液Fe含量小于80 mg/L;氧化沉钴阶段可得到含钴20%,锌18%~20%的沉钴渣,将沉钴渣用酸性水洗涤后,可得到含锌小于10%、含钴大于30%的富钴渣,可作为钴精矿销售。该工艺可为从湿法炼锌净化渣综合回收有价金属、富集钴提供参考。     

砷烟灰浸出液的制备及用于砷盐净化除钴试验研究

以某厂砷烟灰为原料,开展了砷烟灰浸出液的制备试验,然后以制备得到的砷烟灰浸出液作砷盐净化除钴的活化剂,开展了净化除钴条件、净化除钴综合条件及三氧化二砷作活化剂净化除钴对比和除钴优化条件等一系列试验研究。试验结果表明:采用砷烟灰制备砷烟灰浸出液及浸出液用于砷盐净化除钴工艺是切实可行的,不仅砷烟灰中的砷得到利用,同时,砷烟灰中铅、银、锑等有价金属与砷得以有效分离。     

高压酸浸法从镍红土矿中回收镍钴

采用高压酸浸法从Ramu镍红土矿中回收镍钴。详细介绍了矿浆处理、高压酸浸、循环浸出及矿浆中和、CCD逆流洗涤、中和除铁铝、氢氧化镍钴沉淀、深海填埋工艺(DSTP)等流程,并分析了工艺出现的问题及改进措施。全流程镍回收率～96%,钴回收率～94%。     

锂离子电池正极废料中钴和锂的回收

开展了锂离子二次电池正极废旧材料中钴和锂的回收研究。采用"碱浸除铝-硫酸体系还原浸出-P204萃取"的化学浸取、溶剂萃取法,可使钴和锂得到有效回收。铝的总去除率在98%以上,钴和锂的浸出率大于98%,体系钴的总收率在94%以上;控制P204萃取平衡体系水相的pH值在5.7左右,相比3:2,可得到良好的萃取分离效果。     

某铜钴矿的硫酸还原浸出研究

研究了刚果(金)某铜钴矿的硫酸还原浸出。结果表明,在矿样粒度为-0.074mm占90%、终点pH为1.5、SO2用量为理论量的1.5倍(4kg/t)、浸出温度80℃、浸出时间120min、液固比4∶1的条件下,铜、钴浸出率分别达到了93.35%和90.13%。在此基础上进行了模拟堆浸的柱浸试验,柱浸采用先浸铜再还原浸钴的分步浸出方式,铜浸出率达72%,钴浸出率为66%。     

赞比亚某铜钴矿金属回收试验研究

赞比亚地区铜钴矿资源品位较低,铜钴赋存状态复杂,浸出和回收技术不成熟。某冶炼厂对此地区铜钴矿采用"浸出-萃取-净化-沉钴"工艺生产粗制氢氧化钴,浸出工段在生产过程中水量过剩,在净化工段前,萃余液中钴难以富集,造成资源浪费。本文采用酸浸还原-Lix984萃取-HBL110萃取工艺对此铜钴矿进行了试验,取得了满意效果:采用还原剂双氧水与亚硫酸钠联合法进行酸浸还原,钴、铜浸出率分别为98.27%、98.59%;采用萃取剂Lix984萃取回收铜,三级逆流萃取铜萃取率为99.13%,钴的萃取率为7.12%,实现了铜和钴分离的目的;萃铜后的萃余液主要含Co和Fe,采用双氧水对萃余液预处理,再采用萃取剂HBL110萃取钴,钴的萃取率达到99%以上,除铁率也从64.37%提升至86.15%。