造孔剂法制备多孔生物玻璃陶瓷的工艺研究

通过造孔剂法,以溶胶-凝胶法制备的生物玻璃58S和熔融法制备的生物玻璃45S5为原料,以NH4 HCO3与淀粉的混合物为造孔剂制备生物玻璃陶瓷.利用XRD和SEM等材料分析测试手段研究了烧成温度、造孔剂添加量、成型压力及45S5的用量对多孔材料显微结构、表面形貌、抗折强度的影响.结果表明:在成型压力20 MPa,造孔剂含量60％,烧成温度800℃及45S5的加入量10％的工艺参数下,制备出抗折强度达到4.5 MPa,孔隙率达到68.74％的珊瑚状结构的多孔生物玻璃陶瓷材料.     

烧成制度对干法造粒制备轻质陶瓷砖性能的影响

以抛光废渣、高铝泥、恒峰砂、力鸿砂、黑滑石为原料,采用干法造粒工艺,在1 100℃~1 200℃,保温时间为10~30min条件下,制备轻质陶瓷砖,并研究了烧成制度对轻质陶瓷砖性能的影响。结果表明:随着烧成温度的升高,轻质陶瓷砖线膨胀率逐渐升高;吸水率呈先升高再降低而后升高的趋势,在1 170℃时达到最低值;抗折强度和容重随着烧成温度的升高逐渐降低。随着保温时间的延长,试样容重和抗折强度逐渐降低,但变化不明显。烧成温度为1 160℃,保温时间为15min时,制备的轻质陶瓷砖抗折强度为6.3MPa,吸水率为2.3%,闭气孔率为71.2%,容重为0.64g/cm3。     

利用废旧CRT屏制备泡沫玻璃的工艺与性质研究

本文主要以废旧阴极射线管(CRT屏)为主要原料,利用烧结法制备出的泡沫玻璃是一种高性能无机建筑保温材料.配合料被预先压制成板块状,然后在发泡温度下进行烧成.研究了发泡剂碳粉的含量、发泡温度和发泡时间与其结构,及密度和抗折强度等性能的关系.研究分析表明,随碳粉含量和发泡温度的升高,泡沫玻璃的密度和抗折强度均呈现先降低后升高的趋势.在碳粉含量和发泡温度相同的条件下,发泡时间过短发泡不充分,气孔过小且分布不均匀,发泡时间过长会使部分气孔连通,产生超大不规则气孔,影响其力学性能.最佳生产工艺为:碳粉添加量0.5％,发泡温度850℃,发泡时间30 min.此时泡沫玻璃的密度为0.298 g/m3,抗折强度为3.4 MPa.     

烧成工艺对堇青石-莫来石窑具材料性能的影响

以堇青石、莫来石、高岭土和氧化铝微粉为原料制备堇青石-莫来石窑具材料,研究了烧成温度、保温时间对堇青石-莫来石窑具材料的常温性能、高温抗折强度和抗热震性的影响。并通过XRD分析了试样烧成后的物相变化,通过SEM观察了试样的显微结构。结果表明:随烧成温度从1340℃提高到1400℃,试样的线膨胀率增加,显气孔率增加,常温抗折、常温耐压强度和高温抗折强度增大,但1370℃烧成后的试样的抗热震性最好;对1370℃烧成的试样,随保温时间从3 h延长到5 h,试样的常温性能、高温抗折强度及抗热震性都有所降低。综合分析,在1370℃下保温3 h烧成的试样性能较为优良。     

冷却工艺对CaO-Al2O3-SiO2系微晶玻璃强度及热膨胀性能的影响

将某一固定组成的CaO-Al2O3-SiO2系玻璃烧结到一定温度后,采用不同的冷却工艺得到若干试样。通过X衍射分析、抗折强度和热膨胀系数的测定,研究了冷却温度制度对CaO-Al2O3-SiO2系微晶玻璃强度及热膨胀性能的影响。研究发现随着微晶玻璃的起始冷却温度逐渐升高,试样的抗折强度逐渐提高,热膨胀系数逐渐减小。     

Al2O3多孔陶瓷的制备和性能研究

采用乙基纤维素为成孔剂制备了Al2O3多孔陶瓷,探讨了工艺参数对其性能的影响。研究结果表明,造孔剂含量、球磨时间及烧结温度均对多孔陶瓷的气孔率和抗折强度有影响。烧结温度的升高使得气孔率降低,但变化不明显,抗折强度明显提高。随造孔剂含量的升高,使得气孔率逐渐上升,超过20％后变化趋于平稳。随着球磨时间的增加,试样呈现气孔率下降和抗折强度升高的趋势。以烧结温度为1580℃,造孔剂含量20％;球磨时间为2．5h的条件下,可获得高显气孔率、抗折强度较高的舢203多孔陶瓷。     

低温Li_2O-ZnO-B_2O_3-Al_2O_3-SiO_2玻璃结合剂的研究

采用传统熔体冷却法制备了Li_2O-ZnO-B_2O_3-Al_2O_3-SiO_2玻璃,分析了玻璃的特征温度、探讨了与刚玉磨料的热膨胀匹配性,研究了烧成温度和保温时间对玻璃为结合剂的刚玉砂轮试样抗弯强度的影响,并对玻璃结合剂的高温析晶稳定性进行了分析。结果表明,以Li_2O-ZnO-B_2O_3-Al_2O_3-SiO_2玻璃具有较低的流动温度和与刚玉磨料相匹配的热膨胀率,以其为结合剂制备刚玉砂轮磨具适宜的烧成温度为750℃-790℃,保温时间以1-2 h为佳,所制备砂轮的抗弯强度可达45 MPa。该体系玻璃结合剂烧成时保温时间不宜过长,当保温时间达到8 h时将导致Li_(2.4)Mg_(0.8)SiO_4晶体的析出,从而降低磨具的强度。     

废旧建筑玻璃制备泡沫玻璃的研究

利用废旧建筑玻璃为原料,以碳酸钙为发泡剂、硼酸为助溶剂,采用模压成型、高温发泡工艺成功制备出了泡沫玻璃,研究了发泡剂含量与发泡温度对泡沫玻璃的体积膨胀率、体积密度、气孔率、抗折强度等性能的影响.结果 表明:在800 ～840℃的发泡温度范围内,随发泡剂含量的增加,泡沫玻璃的体积膨胀率与气孔率先增大后降低,而体积密度和抗折强度先降低后增大,在发泡剂含量为3％,发泡温度在820℃时,泡沫玻璃综合性能良好,其体积膨胀率达476％,体积密度为0.21 g/cm3,气孔率达87.26％,抗折强度为(1.38 ±+0.15) MPa,孔径介于1.7 ～2.2 mm之间.     

多孔微晶玻璃的研制及性能

以废玻璃为主要原料,用V2O5作为成核剂,再加入其它辅助原料制备了多孔微晶玻璃,研究了发泡温度、保温时间等因素对多孔微晶玻璃泡径及性能的影响。结果表明,发泡温度越高,泡径越大,制品密度越小,最佳发泡温度为725℃;保温时间越长,泡径越大,当在725℃保温25min时,析出的晶体有SiO2、Al2SiO5及Na2Ca2(SiO3)3,平均泡径为2.039mm,密度为0.65g.cm-3,热膨胀系数为115.6×10-7℃-1,抗压强度为7.31MPa,抗折强度为5.83MPa。     

微晶泡沫玻璃的制备及力学性能研究

以废旧阴极射线管为主要原料,SiC为发泡剂,采用烧结法制备了微晶泡沫玻璃。通过DTA,XRD,SEM等分析手段,研究了发泡剂用量,升温速率,降温速率,保温时间对试样力学性能的影响。结果表明,所制备的微晶泡沫玻璃的主晶相为Pb,次晶相为Pb3O4,Al6Si2O13,抗压强度为6.28MPa,抗折强度为2.1MPa。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

Insect antifeedant properties of anthranoids from the genusVismia

Vismiones and ferruginins, representatives of a new class of lypophilic anthranoids from the genusVismia were found to inhibit feeding in larvae of species ofSpodoptera, Heliothis, and inLocusta migratoria.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.