Carbothermal reduction synthesis of high porosity and low thermal conductivity ZrC-SiC ceramics via an one-step sintering technique

In this work, porous ZrC-SiC ceramics with high porosity and low thermal conductivity were successfully prepared using zircon (ZrSiO₄) and carbon black as material precursors via a facile one-step sintering approach combining in-situ carbothermal reduction reaction (at 1600 °C for 2 h) and partial hot-pressing sintering technique (at 1900 °C for 1 h). Carbon black not only served as a reducing agent, but also performed as a pore-foaming agent for synthesizing porous ZrC-SiC ceramics. The prepared porous ZrC-SiC ceramics with homogeneous microstructure (with grain size in the 50–1000 nm range and pore size in the 0.2–4 µm range) possessed high porosity of 61.37–70.78%, relatively high compressive strength of 1.31–7.48 MPa, and low room temperature thermal conductivity of 1.48–4.90 W·m^?1K^?1. The fabricated porous ZrC-SiC ceramics with higher strength and lower thermal conductivity can be used as a promising light-weight thermal insulation material.     

Facile synthesis of MgO–Mg2SiO4 composite ceramics with high strength and low thermal conductivity

The recycling of solid waste is a win-win solution for humans and nature. For this purpose, magnesite tailings and silicon kerf waste were employed to prepare MgO–Mg₂SiO₄ composite ceramics by solid-state reaction synthesis in the present work. Then, effects of sintering temperature and raw material ratio on as-prepared ceramics were systematically studied. As-prepared ceramics showed improvement in their relative density (from 47.55%–68.12% to 90.96%–95.25%) and cold compressive strength (from 7.34–118.66 MPa to 303.39–546.65 MPa) with the increase in sintering temperature from 1300 to 1600 °C. In addition, it was found that Si promoted synthesis process of Mg₂SiO₄ phase through transient liquid phase sintering and Fe₂O₃ accelerated sintering process through activation sintering. Consequently, the presence of Mg₂SiO₄ phase effectively improved the density and strength of MgO–Mg₂SiO₄ composite ceramic, while reducing its thermal conductivity. This work provides a potential reutilization strategy for magnesite tailings, and as-prepared products are expected to be applied in fields of construction, metallurgy, and chemical industry.     

Ultra-low cost porous mullite ceramics with excellent dielectric properties and low thermal conductivity fabricated from kaolin for radome applications

Near-net-shape mullite ceramics with high porosity were prepared from ultra-low cost natural aluminosilicate mineral kaolin as raw material and polystyrene micro-sphere (PS) as pore-forming agent. Microstructure, flexural strength, thermal conductivity and dielectric properties of the ceramics were systematically researched. Results show that the porous mullite ceramics possess fibrous skeleton structure formed by a large quantity of interlocked mullite whiskers, which results in good mechanical properties and low-to-zero sintering shrinkage. Flexural strength of the porous mullite ceramics can be up to 41.01 ± 1.12 MPa, even if the porosity is as high as 62.44%. The dielectric constant and loss tangent of the porous mullite ceramics at room temperature are lower than 2.61 and 5.9 × 10⁻³, respectively. Besides, dielectric constant is very stable with the rising of temperature, and the dielectric loss can be consistently lower than 10⁻² when the temperature is not higher than 800 °C. In addition, thermal conductivity at room temperature is as low as 0.163 W/m/K when the porosity of mullite ceramics is 80.05%. The infiltration of SiO₂ aerogels (SiO₂ AGs) can further decrease the thermal conductivity to 0.075 W/m/K, while has just little effects on the dielectric properties. Excellent mechanical, thermal and dielectric properties show that the porous mullite ceramics have potential applications in radome fields. The porous mullite ceramics prepared from kaolin not only have low cost, but also can achieve near-net-shape.     

Low-temperature preparation of porous SiC ceramics using phosphoric acid as a pore-forming agent and a binder

Porous SiC ceramics combine the properties of both SiC ceramics and porous materials. Herein, we design a facile method via pressureless sintering at relatively low temperatures for the synthesis of porous SiC ceramics. In the synthesis process, phosphoric acid was used as the sintering additive that reacted with SiO₂ on the surface of SiC to form phosphates. The formed phosphates acted as a binder to connect the SiC particles. At a fixed temperature, the phosphates were partially decomposed and released a large amount of gas. This changed the pore structure of the ceramics and greatly improved their porosity. Finally, we obtained the porous SiC ceramics with high porosity and high strength. We investigate the effects of H₃PO₄ content on the phase composition, microstructure, porosity, mechanical properties and thermal expansion coefficient of the prepared porous SiC ceramics. It was shown that at the sintering temperature of 1200 °C, the highest porosity of the samples can reach 70.42% when the H₃PO₄ content is 25 wt%, and their bending strength reaches 36.11 MPa at room temperature when the H₃PO₄ content is 15 wt%. In addition, the porous SiC ceramics show good high-temperature stability with a bending strength of 42.05 MPa at 1000 °C and the thermal expansion coefficient of 3.966 × 10⁻⁶/°C.     

Effect of carbon content on electrical,thermal, and mechanical properties of porous SiC ceramics with B4C and C additives

The electrical, thermal, and mechanical properties of porous SiC ceramics with B₄C-C additives were investigated as functions of C content and sintering temperature. The electrical resistivity of porous SiC ceramics decreased with increases in C content and sintering temperature. A minimal electrical resistivity of 4.6 × 10^?2 Ω·cm was obtained in porous SiC ceramics with 1 wt% B₄C and 10 wt% C. The thermal conductivity and flexural strength increased with increasing sintering temperature and showed maxima at 4 wt% C addition when sintered at 2000 °C and 2100 °C. The thermal conductivity and flexural strength of porous SiC ceramics can be tuned independently from the porosity by controlling C content and sintering temperature. Typical electrical resistivity, thermal conductivity, and flexural strength of porous SiC ceramics with 1 wt% B₄C-4 wt% C sintered at 2100 °C were 1.3 × 10^?1 Ω·cm, 76.0 W/(m·K), and 110.3 MPa, respectively.     

Preparation of porous Y2SiO5 ceramics with relatively high compressive strength and ultra-low thermal conductivity by a TBA-based gel-casting method

Porous Y₂SiO₅ ceramics with relative high compressive strength (as high as 24.45 MPa) and ultra-low thermal conductivity (～0.08 W/m K) were successfully fabricated by a tert-butyl alcohol based gel-casting method. The formation mechanism of the 3D interconnected pores and the properties of the green body are discussed. The porosity, pore size, compressive strength and thermal conductivity could be controlled by varying the initial solid loading and the sintering temperature. When regulating the initial solid loading (from 20 to 50 wt%) and sintering temperature (from 1200 to 1500 °C), the porosity can be controlled between 47.74% and 73.93%, and the compressive strength and the thermal conductivity of porous Y₂SiO₅ ceramics varied from 3.34 to 24.45 MPa and from 0.08 to 0.55 W/m K, respectively. It should be noted that the porous Y₂SiO₅ ceramics with 30 wt% solid loading and sintering at 1400 °C had an open porosity of 61.80%, a pore size of 2.24 μm, a low room-temperature thermal conductivity of 0.17 W/m K and a relatively high compressive strength of 13.91 MPa, which make this porous Y₂SiO₅ ceramics suitable for applications in high-temperature thermal insulators.     

New multifunctional porous Yb2SiO5 ceramics prepared by freeze casting

New porous Yb₂SiO₅ ceramics were prepared by a water-based freeze casting technique using synthesized Yb₂SiO₅ powders. The prepared porous Yb₂SiO₅ ceramics exhibit multiple pore structures, including lamellar channel pores and small pores, in its skeleton. The effects of the solid content and sintering temperature on the pore structure, porosity, dielectric and mechanical properties of the porous Yb₂SiO₅ ceramics were investigated. The sample with 20 vol% solids content prepared at 1550 °C exhibited an ultra-low linear shrinkage (i.e. 4.5%), a high porosity (i.e. 79.1%), a high compressive strength (i.e. 4.9 MPa), a low dielectric constant (i.e. 2.38) and low thermal conductivity (i.e. 0.168 W/(m K)). These results indicate that porous Yb₂SiO₅ ceramics are good candidates for ultra-high temperature broadband radome structures and thermal insulator materials.     

Processing and properties of cordierite-silica bonded porous SiC ceramics

Cordierite-silica bonded porous SiC ceramics were fabricated by infiltrating a porous powder compact of SiC with cordierite sol followed by sintering at 1300–1400 °C in air. The porosity, average pore diameter and flexural strength of the ceramics varied 30–36 vol%, ~ 4–22 µm and ~ 13–38 MPa respectively with variation of sintering temperature and SiC particle sizes. In the final ceramics SiC particles were bonded by the oxidation-derived SiO₂ and sol-gel derived cordierite. The corrosion behaviour of sintered SiC ceramics was studied in acidic and alkaline medium. The porous SiC ceramics were observed to exhibit better corrosion resistance in acid solution.     

Low thermal conductivity in porous SiC–SiO2–Al2O3–TiO2 ceramics induced by multiphase thermal resistance

The introduction of multiple heterogeneous interfaces in a ceramic is an efficient way to increase its thermal resistance. Novel porous SiC–SiO₂–Al₂O₃–TiO₂ (SSAT) ceramics were fabricated to achieve multiple heterogeneous interfaces by sintering equal volumes of SiC, SiO₂, Al₂O₃, and TiO₂ compacted powders with polysiloxane as a bonding phase and carbon as a template at 600 °C in air. The porosity could be controlled between 66% and 74% by adjusting the amounts of polysiloxane and the carbon template. The lowest thermal conductivity (0.059 W/(m·K) at 74% porosity) obtained in this study is an order of magnitude lower than those (0.2–1.3 W/(m·K)) of porous monolithic SiC, SiO₂, Al₂O₃, and TiO₂ ceramics at an equivalent porosity. The typical specific compressive strength value of the porous SSAT ceramics at 74% porosity was 3.2 MPa cm³/g.     

Processing and properties of silica-bonded porous nano-SiC ceramics with extremely low thermal conductivity

Silica-bonded porous nano-SiC ceramics with extremely low thermal conductivity were prepared by sintering nano-SiC powder-carbon black template compacts at 600–1200 °C for 2 h in air. The microstructure of the silica-bonded porous nano-SiC ceramics consisted of SiC core/silica shell particles, a silica bonding phase, and hierarchical (meso/macro) pores. The porosity and thermal conductivity of the silica-bonded porous nano-SiC ceramics can be controlled in the ranges of 8.5–70.2 % and 0.057–2.575 Wm⁻¹ K⁻¹, respectively, by adjusting both, the sintering temperature and template content. Silica-bonded porous nano-SiC ceramics with extremely low thermal conductivity (0.057 Wm⁻¹ K⁻¹) were developed at a very low processing temperature (600 °C). The typical porosity, average pore size, compressive strength, and specific compressive strength of the porous nano-SiC ceramics were ∼70 %, 50 nm, 2.5 MPa, and 2.7 MPa·cm³/g, respectively. The silica-bonded porous nano-SiC ceramics were thermally stable up to 1000 °C in both air and argon atmospheres.     

Preparation and pore-forming mechanism of MgO–Al2O3–CaO-based porous ceramics using phosphorus tailings

A simple strategy for preparing MgO–Al₂O₃–CaO-based porous ceramics (MACPC) with high strength and ultralow thermal conductivity has been proposed in this work based on the raw material of phosphorus tailings. The effects of phosphorus tailings content, carbon black addition and heat treatment temperature on the properties of MACPC were studied, and their pore-forming mechanism during sintering was revealed. The results showed that the main phase composition of MACPC was magnesia alumina spinel and calcium aluminate after sintering at 1225 °C. Furthermore, the MACPC exhibited excellent comprehensive properties when 60 wt% phosphorus tailings and 40 wt% alumina were added, whose apparent porosity was 62.8%, cold compressive strength was 14.8 MPa, and the thermal conductivity was 0.106 W/(m·K) at 800 °C. The synchronously enhanced strength and thermal insulation properties of MACPC were related to the formation of uniformly distributed micropores (<2 μm) and passages in the matrix, which originated from the decomposition of phosphorus tailings and the burnt out of carbon black during the sintering process. The preparation of MACPC with high temperature resistance and excellent mechanical and thermal insulation properties with the raw material of phosphorus tailings provided an effective method for the high-value utilization of phosphorus tailings.     

Porous ceramics with near-zero shrinkage and low thermal conductivity from hazardous secondary aluminum dross

Herein, a simple, versatile, and low-cost approach has been proposed to realize the green utilization of secondary aluminum dross, the hazardous solid waste, namely directly sintering dry-pressed green bodies from secondary aluminum dross to fabricate porous ceramics according to high-temperature foaming process spontaneously without adding spare foaming agents. Aluminum nitride (AlN) in secondary aluminum dross was employed to realize high-temperature foaming due to its oxidation, which makes traditional AlN and salts removal process needless. Moreover, near-zero shrinkage or even expansion during sintering of porous ceramics have occurred because in-situ foaming process together with the oxidation of Al particles well offset the sintering shrinkage. After sintering at 1400°C for 2 h, porous ceramics composed of α-Al₂O₃ and spinel phases with open porosity of 37.91%, sintering expansion rate of 1.13%, flexural strength of 45.67 MPa, and thermal conductivity of 0.97 W/(m·K) have been prepared. Cenospheres as pore-forming agents have been added to further improve the porosity, and alumina-based porous ceramics with open porosity of 28.39%–43.20% and flexural strength of 15.80–52.48 MPa have been obtained. This effective solution for recycling secondary aluminum dross could supply high-performance porous ceramics, which is expected to be applied in the fields of light-weight structural components and thermal insulations.     

Controllable preparation of porous ZrB2–SiC ceramics via using KCl space holders

In this work, a novel and facile technique based on using KCl as space holders, along with partial sintering (at 1900 °C for 30 min), was explored to prepare porous ZrB₂–SiC ceramics with controllable pore structure, tunable compressive strength and thermal conductivity. The as-prepared porous ZrB₂–SiC samples possess high porosity of 45–67%, low average pore size of 3–7 μm, high compressive strength of 32–106 MPa, and low room temperature thermal conductivity of 13–34 W m⁻¹ K⁻¹. The porosity, pore structure, compressive strength and thermal conductivity of porous ZrB₂–SiC ceramics can be tuned simply by changing KCl content and its particle size. The effect of porosity and pore structure on the thermal conductivity of as-prepared porous ZrB₂–SiC ceramics was examined and found to be consistent with the classical model for porous materials. The poring mechanism of porous ZrB₂–SiC samples via adding pore-forming agent combined with partial sintering was also preliminary illustrated.     

A novel strategy for synthesizing porous ZrB2-SiC ceramics via boro/carbothermal reaction process templated pore-forming approach

In this work, pure ZrB₂-SiC composite powders were obtained using ZrO₂, SiO₂, B₄C and carbon black as raw materials via a boro/carbothermal reduction (BCTR) reaction process at 1500 °C for 2 h in vacuum condition. Based on this finding, porous ZrB₂-SiC ceramics were in-situ synthesized via a novel and facile boro/carbothermal reaction process templated pore-forming (BCTR-TPF) method. The phase composition, linear shrinkage, and pore size distribution were also methodically studied. Results show that the porous ZrB₂-SiC ceramics with controllable porosity of 67–78%, compressive strength of 0.2–9.8 MPa and thermal conductivity of 1.9–7.0 W·m⁻¹K⁻¹ can be fabricated by varying of ZrO₂ and B₄C particle sizes. The formation of ZrB₂ grains was controlled via solid-solid and solid-liquid-solid growth mechanisms, the growth process of SiC grains was mainly regulated by solid-solid, vapor-vapor and vapor-solid growth mechanisms during the overall synthesis process. Finally, the pore-forming mechanism of porous samples prepared via the BCTR-TPF method was gases combined with template pore-forming mechanism, i.e., B₄C and carbon black acted as pore-forming templates, and gaseous products generated in the BCTR reaction were also applied as gas pore-forming agent.     

Synthesis and characterization of porous Y2SiO5 with low linear shrinkage,high porosity and high strength

The emerging porous Y₂SiO₅ ceramic is regarded as a promising candidate of thermal insulator owing to its very low thermal conductivity. However, recent works on porous Y₂SiO₅ are confronted with severe problems such as large linear shrinkage (18.51–20.8%), low porosity (47.74–62%) and low strength (24.45–16.51 MPa) at high sintering temperatures (1450–1500 °C). In this work, highly porous Y₂SiO₅ ceramic with low shrinkage and excellent high-temperature strength was fabricated by in-situ foam-gelcasting method at 1550 °C. The as-prepared sample has unique multiple pore structures, low linear shrinkages of 6.3–4.5%, controllable high porosities of 60.7–88.4%, high compressive strengths of 38.2–0.90 MPa, and low thermal conductivities of 0.126–0.513 W/(m K) (porosity: 87.1–60.2%). The effects of relative density on relative strength, as well as porosity on thermal conductivity were quantitatively discussed. The present results indicate that porous Y₂SiO₅ is the potential high-temperature thermal insulation material of light weight, low thermal conductivity, and high strength.     

Effects of porosity on electrical and thermal conductivities of porous SiC ceramics

The effects of porosity on the electrical and thermal conductivities of porous SiC ceramics, containing Y₂O₃–AlN additives, were investigated. The porosity of the porous SiC ceramic could be controlled in the range of 28–64 % by adjusting the sacrificial template (polymer microbead) content (0–30 wt%) and sintering temperature (1800–2000 °C). Both electrical and thermal conductivities of the porous SiC ceramics decreased, from 7.7 to 1.7 Ω⁻¹ cm⁻¹ and from 37.9 to 5.8 W/(m·K), respectively, with the increase in porosity from 30 to 63 %. The porous SiC ceramic with a coarser microstructure exhibited higher electrical and thermal conductivities than those of the ceramic with a finer microstructure at the equivalent porosity because of the smaller number of grain boundaries per unit volume. The decoupling of the electrical conductivity from the thermal conductivity was possible to some extent by adjusting the sintering temperature, i.e., microstructure, of the porous SiC ceramic.     

Investigating the effect of SPRM on mechanical strength and thermal conductivity of highly porous alumina ceramics

For recycling waste refractory materials in metallurgical industry, porous alumina ceramics were prepared via pore forming agent method from α-Al₂O₃ powder and slide plate renewable material. Effects of slide plate renewable material (SPRM) on densification, mechanical strength, thermal conductivity, phase composition and microstructure of the porous alumina ceramics were investigated. The results showed that SPRM effectively affected physical and thermal properties of the porous ceramics. With the increase of SPRM, apparent porosity of the ceramic materials firstly increased and then decreased, which brought an opposite change for the bulk density and thermal conductivity values, whereas the bending strength didn’t decrease obviously. The optimum sample A2 with 50 wt% SPRM introducing sintered at 1500 °C obtained the best properties. The water absorption, apparent porosity, bulk density, bending strength and thermal conductivity of the sample were 31.7%, 62.8%, 1.71 g/cm³, 47.1 ± 3.7 MPa and 1.73 W/m K, respectively. XRD analysis indicated that a small quantity of silicon carbide and graphite in SPRM have been oxidized to SiO₂ during the firing process, resulting in rising the porous microstructures. SEM micrographs illustrated that rod-like mullite grains combined with plate-like corundum grains to endow the samples with high bending strength. This study was intended to confirm the preparation of porous alumina ceramics with high porosity, good mechanical properties and low thermal conductivity by using SPRM as pore forming additive.     

Low sintering shrinkage porous mullite ceramics with high strength and low thermal conductivity via foam-gelcasting

Excessive sintering shrinkage leads to severe deformation and cracking, affecting the microstructure and properties of porous ceramics. Therefore, reducing sintering shrinkage and achieving near-net-size forming is one of the effective ways to prepare high-performance porous ceramics. Herein, low-shrinkage porous mullite ceramics were prepared by foam-gelcasting using kyanite as raw material and aluminum fluoride (AlF₃) as additive, through volume expansion from phase transition and gas generated from the reaction. The effects of AlF₃ content on the shrinkage, porosity, compressive strength, and thermal conductivity of mullite-based porous ceramics were investigated. The results showed that with the increase of content, the sintering shrinkage decreased, the porosity increased, and mullite whiskers were produced. Porous mullite ceramics with 30 wt% AlF₃ content exhibited a whisker structure with the lowest shrinkage of 3.5%, porosity of 85.2%, compressive strength of 3.06 ± 0.51 MPa, and thermal conductivity of 0.23 W/(m·K) at room temperature. The temperature difference between the front and back sides of the sample reached 710°C under high temperature fire resistance test. The low sintering shrinkage preparation process effectively reduces the subsequent processing cost, which is significant for the preparation of high-performance porous ceramics.     

High interfacial thermal resistance induced low thermal conductivity in porous SiC-SiO2 composites with hierarchical porosity

The incorporation of a thermally insulating secondary phase can significantly increase the interfacial thermal resistance attributed to its low intrinsic thermal conductivity and the creation of multiple phonon scattering interfaces between adjacent SiC particles. The newly developed porous SiC-33 wt% SiO₂ composites with SiO₂ as a thermally insulating secondary phase exhibited a very low thermal conductivity (0.047 Wm⁻¹ K⁻¹, 72.4 % porous), which is an order of magnitude lower than the previously reported lowest thermal conductivity (0.14 Wm⁻¹ K⁻¹, 76.3 % porous) for powder processed porous SiC ceramics and is even lower than the thermal conductivity (0.060 Wm⁻¹ K⁻¹, 87.9% porous) of SiO₂ aerogel. The porous SiC-(16–73 wt%) SiO₂ composites processed from nano β-SiC and a 40 wt% carbon template exhibited a hierarchical (meso-/macro-porous) pore structure that transformed to a trimodal (micro-/meso-/macro-porous) porous structure when polysiloxane was added and sintering was performed at 600–1000 °C in air.     

Electrical,thermal, and mechanical properties of porous silicon carbide ceramics with a boron carbide additive

The effects of the boron carbide (B₄C) content and sintering atmosphere on the electrical, thermal, and mechanical properties of porous silicon carbide (SiC) ceramics were investigated in the porosity range of 58.3%–70.3%. The electrical resistivities of the nitrogen-sintered porous SiC ceramics (∼10^–1 Ω·cm) were two orders of magnitude lower than those of argon-sintered porous SiC ceramics (∼10¹ Ω·cm). Both the thermal conductivities (3.3–19.8 W·m^–1·K^–1) and flexural strengths (8.1–32.9 MPa) of the argon- and nitrogen-sintered porous SiC ceramics increased as the B₄C content increased, owing to the decreased porosity and increased necking area between SiC grains. The electrical resistivity of the porous SiC ceramics was primarily controlled by the sintering atmosphere owing to the N-doping from the nitrogen atmosphere, and secondarily by the B₄C content, owing to the B-doping from the B₄C. In contrast, the thermal conductivity and flexural strength were dependent on both the porosity and necking area, as influenced by both the sintering atmosphere and B₄C content. These results suggest that it is possible to decouple the electrical resistivity from the thermal conductivity by judicious selection of the B₄C content and sintering atmosphere.