双组分水性环氧防腐底漆的研制

采用水性环氧树脂作为基料,添加防锈颜填料、水性助剂以及水性环氧树脂固化剂制备了双组分水性环氧防腐底漆,研究了固化剂活泼氢当量、活泼氢和环氧基当量比、颜填料、流变助剂、防闪锈剂对涂料和涂膜性能的影响,得到了具有良好的物理机械性能和防腐性能的双组分水性环氧防腐底漆。     

水性环氧底漆在城轨车辆上应用的难点

重点介绍了城轨车辆用水性环氧底漆的涂装工艺、技术要求,探讨了水性环氧底漆防腐性能、施工工艺、配套性3个技术难点。     

铝合金用水性无铬防腐底漆的研制

针对铝合金2024-T3防腐蚀问题,通过合成自乳化环氧固化剂,采用无铬防腐颜料,开发出一款水性无铬防腐底漆。讨论了影响漆膜性能的各种因素,并与国外同类产品进行了对比实验。结果表明:本研究制备的产品在性能上超过了进口水性环氧底漆,可作为目前含Cr6+水性环氧底漆的替代品。     

钢结构重防腐涂层典型配套的水性化研究

研制开发的钢结构水性环氧防锈底漆、水性环氧富锌底漆、水性环氧防腐中间漆和水性丙烯酸聚氨酯面漆系列产品性能接近或达到行业标准(港口机械钢结构防腐涂层技术要求JT/T 733—2008)的技术要求,产品具有明显的竞争优势。     

钢结构用水性环氧防腐底漆的研制

采用水性环氧固化剂乳化固化液体环氧树脂技术路线,制备钢结构用水性双组分环氧防腐底漆。该底漆VOC含量低,气味和毒性小,涂膜附着力强,耐水、耐碱、耐盐雾性能好。其性能可以达到溶剂型环氧底漆水平,成本与溶剂型环氧底漆相当。     

水性环氧富锌底漆的研究及评价

以水性环氧树脂、固化剂、锌粉、磷铁粉、防沉剂、闪锈剂等原料合成了水性环氧富锌底漆并进行了分析讨论。表明水性环氧富锌底漆具有溶剂型环氧富锌底漆防腐性好、附着力强等基本性能,又兼具水性无机富锌底漆低VOC和安全性的优点。     

装配式钢结构水性重防腐涂层的研制

针对我国近海内陆装配式钢结构长效防腐需求,研制了与之配套的水性重防腐涂层。通过调整涂料关键材料的组成及配比,研究了其对水性环氧富锌底漆、水性环氧云铁中间漆以及水性脂肪族丙烯酸聚氨酯面漆关键性能的影响。结果表明：适量的纳米锌粉、云母氧化铁以及离子吸收剂的加入有利于提高底漆的耐腐蚀性和早期耐水性;云母氧化铁与复合磷酸锌颜料合理搭配,有助于提升中间漆的防腐性能;附着力促进剂对水性聚氨酯面漆性能提升显著。所研制的水性环氧富锌底漆、水性环氧云铁中间漆、水性脂肪族丙烯酸聚氨酯面漆及配套涂层的相关性能超过行业标准（HG/T 5176—2017）的性能指标,表明了该涂层体系可以满足 C4环境下的长效防腐要求（ >25 a）,为近海内陆装配式钢结构的表面涂装提供了技术参考。     

工程机械用水性环氧防腐底漆的制备

以水性环氧乳液/水性固化剂为成膜物质,制备了一款综合性能优异的工程机械用水性环氧防腐底漆,探讨了水性环氧乳液、防锈颜料、颜填料体积浓度(PVC)对水性环氧防腐底漆性能的影响,使用傅里叶红外光谱仪(FTIR)、扫描电镜(SEM)、电化学交流阻抗谱(EIS)等测试方法,对环氧树脂的基团结构、环氧涂层的表面形貌和涂层的腐蚀机理过程进行了表征与分析,结果表明：选用的Banco2092环氧乳液/Banco920固化剂成膜物质、防锈颜料为ZMP-1、PVC为30%时,环氧底漆的综合性能最佳,与自制水性聚氨酯面漆复配后,耐酸性达到168 h,耐碱性达到96 h,耐盐雾可达1000 h,该复合涂层的综合性能超过了行业标准HG/T 4339-2012性能要求。     

高性能水性工业防腐涂料配套体系的研究与应用

以自制高性能水性丙烯酸聚氨酯树脂(PUA)乳液为主要基料,制备了高性能水性防腐面漆,并研究了以水性环氧富锌底漆、水性环氧云铁中间漆为配套的水性工业防腐配套体系,并进行常规性能、耐化学介质、耐盐雾、耐人工老化等性能的检测分析。结果表明,以高性能水性工业防腐配套体系的防腐涂料可替代传统的溶剂型防腐涂料在相关领域的应用。     

双组份水性环氧富锌底漆制备与性能研究

以水性环氧树脂乳液为基料,改性聚酰胺固化剂,锌粉为防锈颜料,氨基偶联剂为助剂,研制了双组份水性环氧富锌防腐底漆。探讨了树脂的选择、固化剂用量、锌粉用量、硅烷偶联剂用量等对水性环氧富锌防腐底漆性能的影响。在最佳配比条件下,环氧当量∶H当量=1.2∶1,锌粉占干膜质量的75%,硅烷偶联剂为富锌涂料质量的1%时,漆膜性能优异,可应用于各种重防腐蚀领域。     

工程机械用水性环氧防锈底漆的制备

采用水性环氧树脂乳液作为基料,水性改性胺作为固化剂以及环保型助剂等配制成双组分水性环氧防锈底漆。讨论了水性环氧固化剂、活性防锈颜料、流变剂及活性稀释剂对水性环氧防锈底漆性能的影响。     

X-Ray Photoelectron Spectroscopy of the Fracture Surfaces of Iron/ Epoxy and Titanium/Epoxy Adhesive Joints

The failure path of iron/epoxy and titanium/epoxy lap joints prepared from adherends pretreated with dilute aqueous solutions of ω-aminopropyltriethoxysilane (ω-APS) and then exposed to water at 60°C for varying times was determined using X-ray photoelectron spectroscopy (XPS). Iron/epoxy lap joints prepared using T-APS primers applied at pH 8.0 and tested without exposure to water failed near the oxide/primer interface with only a small amount of adhesive left on the substrate failure surface. Iron/epoxy joints that were primed with T-APS at pH 10.4 and tested without immersion in water failed partly within the adhesive and partly near the interface. All of the iron/epoxy joints failed in the primer near the primer/oxide interface when tested after exposure to water for seven days but very little corrosion of the substrates was observed. When titanium/epoxy lap joints were tested without exposure to water, failure was partly within the adhesive and partly near the primer/oxide interface regardless of the pH at which the primer was applied. However, the failure path shifted to near the primer/oxide interface after the joints were immersed in water for seven days. It was concluded that failure of the joints after exposure to water was associated with hydrolysis within the primer rather than with extensive corrosion of the substrate.     

混凝土湿表面固化封闭底漆结合强度的研究

通过对混凝土湿表面底漆固化特点的分析,研究了不同的环氧树脂、溶剂和助剂对潮湿表面的湿态附着力的影响,表明选择合适的树脂和助剂可制备出性能优良的湿固化封闭底漆,适用于海港工程混凝土结构表面的湿固化防腐涂装。     

水性环氧防锈底漆的开发及性能研究

以水性环氧树脂乳液及水性环氧固化剂为主要成膜物质,氧化铁红与磷酸锌为防锈颜料,滑石粉和硫酸钡为填料,研制开发了一种性能优良的水性环氧防锈底漆。     

The effect of a multicomponent silane primer on the interphase structure of aluminum/epoxy adhesive joints

The structure of films formed by a multicomponent silane primer applied to an aluminum adherend and the interactions of this primer with an amine-cured epoxy adhesive were studied using X-ray photoelectron spectroscopy, reflection-absorption infrared spectroscopy, and attenuated total reflectance infrared spectroscopy. The failure in joints prepared from primed adherends occurred extremely close to the adherend surface in a region that contained much interpenetrated primer and epoxy. IR spectra showed evidence of oxidation in the primer. Fracture occurred in a region of interpenetrated primer and adhesive with higher than normal crosslink density. The primer films have a stratified structure that is retained even after curing of the adhesive.     

环氧酯底漆的研制

介绍了用环氧树脂、脂肪酸、干性油、季戊四醇、邻苯二甲酸酐制成的气干型环氧酯底漆。讨论了各种因素对树脂、涂料性能的影响。     

快干型双组分水性环氧树脂涂料的研究

采用水性环氧树脂乳液作为环氧基组分，水溶性聚酰胺作为固化剂，配制成快干型双组分水性环氧树脂防腐底漆。该涂料保持了溶剂型环氧防腐蚀涂料的强附着力和耐化学品性能，适用于对溶剂散发要求极为严格的非下水钢结构     

高性能水性环氧防腐底漆的研制

以水性环氧树脂固化体系为成膜物,以三聚磷酸铝、磷酸锌、钼酸锌为防锈颜料,以绢云母、滑石粉、沉淀硫酸钡为填料,在多种功能助剂和水的配用下,制得具有优异的附着力、防腐性、抗形变能力的水性环氧防腐底漆,适用于较难附着的不锈钢、铝合金等多种金属基材的防腐保护。