电镀工艺条件对铁-镍-铬合金镀层成分和硬度的影响

在由FeSO4·7H2O、NiSO4·6H2O、NiCl2·6H2O、CrCl3·6H2O组成的镀液中,采用直流电沉积方法制备Fe-Ni-Cr合金镀层。研究了pH、电流密度、温度和镀液主盐的浓度对镀层成分和硬度的影响,并对镀层的表面形貌和晶体结构进行了分析。实验结果表明:镀层的硬度随着镀层中铁和铬的含量的增加而增大;控制pH为2.0,阴极电流密度为14A/dm2,温度为30℃,镀液主盐的浓度适量,可以得到Cr含量接近6%、Fe含量为54%、硬度高达70(HR30T)光亮镀层。     

工艺条件对电沉积Ni-金刚石复合镀层性能的影响

研究了温度、电流密度、pH等工艺条件对镍-金刚石复合镀层性能的影响。实验表明,在金刚石含量为40 g/L的瓦特镀镍液中,当电流密度为1.5 A/dm2、温度为40℃、pH为3.8时,在45#钢上可获得性能较好的镍-金刚石复合镀层,且沉积速率适中。镀层中金刚石微粒含量为11%~13%(质量分数),镀层硬度为2100 MPa左右,耐磨性能较好。     

Ni-Fe-SiC复合镀层的制备及性能研究

用电沉积的方法在含NiSO4及FeSO4的电解质溶液中制备了Ni-Fe-SiC复合镀层.通过正交试验,研究了Fe2 与Ni2 的浓度比、温度、pH和电流密度对镀层中SiC质量分数的影响,讨论了镀液中SiC含量与镀层显微硬度的关系,确定了最佳工艺条件为:c(Fe2 )/c(Ni2 )=0.09,镀液温度55 ℃,pH=3.0,电流密度1.8 A/dm2.在最佳工艺条件下所获得的复合镀层,显微硬度达650～850 HV,结合力和耐蚀性均良好.     

Ni-W纳米晶合金电沉积工艺条件的研究

纳米晶材料与常规晶体材料相比有许多优良的性能 ,已受到广泛关注。本文采用电沉积方法获得了Ni W纳米晶合金镀层。研究了镀液中钨酸钠含量、温度、pH值及电流密度对沉积速度的影响。测定了镀层的显微硬度 ,并用X -射线衍射仪对其微观结构进行了观察。结果表明 ,影响沉积速度最大的因素为pH值 ,其次是电流密度 ;镀层显微硬度最高可达 6 70 .3HV。通过正交试验得出适宜工艺条件范围为 :Na2 WO4·2H2 O 1 0～ 30g/L ,电流密度 1 0～1 5A/dm2 ,温度 6 0～ 70℃ ,pH值 6～ 7。     

工艺参数对RE-Ni-Fe-P-PTFE复合镀层中PTFE含量的影响

在铜片上电沉积得到了RE–Ni–Fe–P–PTFE复合镀层,探讨了温度、pH、搅拌速率及电流密度对镀层中PTFE含量的影响。结果表明,在温度为55°C,pH为2~3,电流密度10A/dm2及中等强度搅拌的条件下,可获得PTFE质量分数7.6%的RE–Ni–Fe–P–PTFE复合镀层。随着镀层中PTFE含量的增大,镀层的摩擦因数不断降低,其润滑性得到提高。     

氟硼酸盐体系电沉积因瓦合金箔的工艺研究

在含有O.75 mol/L Ni(BF4)2.6H2O,0.05～0.25 mol/ LFe(BF4)2,0.5 moI/L H3803,30 g/L NaBF4和0.5/L糖精的镀液中,以316L不锈钢作为旋转阴极,电沉积制备了因瓦合金箔.讨论了镀液中亚铁离子含量、阴极旋转速率、温度、pH、电流密度等5个因素对合金箔中铁含量及阴极电流效率的影响,确定了最佳工艺条件为:Fe2+浓度0.15 moI/L,温度45～55℃,pH 2.5～3.0,电流密度18～25 A/dm2,阴极旋转速率600～900 r/min.所得合金箔光亮致密,柔韧性好,其Fe含量稳定在62%～66%,达到了因瓦合金的组分要求.     

(Ni-W)-纳米Si3N4复合电镀工艺的研究

研究了(Ni-W)-纳米Si3N4复合镀层的共沉积条件,考察了电流密度、温度和时间等操作条件对镀层沉积速率和显微硬度的影响.结果表明,随着电流密度提高,复合镀层的沉积速率和硬度不断增加,但当电流密度达到16 A/dm2,镀层的硬度下降;合适的镀液温度为75℃左右,沉积时间约60 min.     

平均电流密度对脉冲镀镍钨合金微观形貌和性能的影响

在硫酸镍15g/L,钨酸钠30g/L,柠檬酸35g/L,烷基有机添加剂1.5g/L,pH为7,温度65°C的条件下,研究了平均电流密度对脉冲镀镍钨合金镀层的外观、结合力、显微硬度、沉积速率、镀层中钨含量及表面微观形貌的影响。结果发现,随着平均电流密度的增大,镀层中钨含量增加,镀层硬度先增大而后趋于恒值。过高和过低的平均电流密度都会引起镀层缺陷,最佳的平均电流密度为5～8A/dm2。     

电流密度对喷射电沉积钴–磷合金镀层的影响

采用喷射电沉积法在45钢棒表面制备Co-P合金镀层。镀液组成和工艺参数为:CoSO_4·7H_2O 200 g/L,H_3PO_4 50g/L,H_3BO_3 30 g/L,NaCl 25 g/L,pH=1.0,温度50℃,喷头移动速率1.2 mm/s,电流密度10~70A/dm~2。研究了电流密度对Co-P合金镀层的表面形貌、相结构、显微硬度和耐磨性的影响。结果表明:在10~70A/dm~2电流密度范围内,随电流密度从10A/dm~2增大到70 A/dm~2,Co-P合金镀层的厚度变化不大,晶粒细化,显微硬度升高,耐磨性改善,但电流密度高于40A/dm~2时所得镀层的表面平整度下降。     

铝基体复合电沉积镍–碳纳米管复合镀层

采用电沉积法在铝基体上制备了镍–碳纳米管复合镀层,探讨了镀液中碳纳米管含量、电流密度、搅拌速率、温度、电镀时间等因素对镀层碳纳米管含量和厚度的影响,得出制备镍–碳纳米管复合镀层的适宜工艺条件为:碳纳米管质量浓度4 g/L,电流密度8 A/dm2,搅拌速率440 r/min,温度40°C,沉积时间40 min。采用扫描电镜和X射线衍射仪对镀层表面形貌和成分进行分析,通过电化学测试比较了不同镀层在不同腐蚀介质中的耐腐蚀性。与纯镍镀层相比,镍–碳纳米管复合镀层的晶粒尺寸更小,表面更粗糙,耐腐蚀性更好。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

Insect antifeedant properties of anthranoids from the genusVismia

Vismiones and ferruginins, representatives of a new class of lypophilic anthranoids from the genusVismia were found to inhibit feeding in larvae of species ofSpodoptera, Heliothis, and inLocusta migratoria.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.