陶瓷表面装饰墨水的制备研究

采用分散剂NNO与聚羧酸类化合物作为分散剂,以水为介质,通过砂磨分散研制无机颜料墨水,研究了该混合分散剂的比例,添加剂及含固量对无机颜料墨水性能的影响,经测试,所制墨水的粒径、粘度、表面张力等指标完全符合喷墨打印墨水的要求,其中黑色墨水的着色剂含量可达20%,打印于陶瓷上,经煅烧显色正常.     

借助流变曲线优化中性墨水配方

润湿剂、分散剂、树脂种类与添加量直接影响颜料型中性墨水体系中颜料粒子的分散、稳定与触变体系的构建。分别考察了不同添加量的分散剂BYK-191所制备的墨水色浆以及不同添加量的苯丙树脂M101和润湿剂4187所制备的中性墨水的流变行为,并借助激光粒度仪、光学显微镜、表面张力仪对颜料的分散粒径、微观成像、临界胶束浓度进行了分析,首次将流变仪用于中性墨水配方优化。结果表明,当墨水中添加质量分数2.0%分散剂BYK-191、质量分数4.0%苯丙树脂M101和质量分数2.5%润湿剂4187时,既保证了中性墨水触变体系的良好建立,又实现了颜料的超细分散与长期稳定。     

反相微乳液法制备高溶度ZrO2陶瓷墨水(Ⅱ)

对喷墨打印成型用ZrO2陶瓷墨水的反相微乳液制备法进行了研究.采用已经优化的Triton x-100/正己醇/环己烷/水反相微乳液体系, 以氧氯化锆溶液和氨水溶液分别替代水, 获得了澄清的微乳液, 再将它们均匀混合反应制得了均匀分散、微粒尺寸7～8 nm、稳定存在的ZrO2陶瓷墨水.针对喷射打印墨水的理化性能要求, 考察了所制备的ZrO2陶瓷墨水的理化性能(流变性能、表面张力、电导率、稳定性等), 并对性能改善进行了探讨.所制两个陶瓷墨水当pH＜8时, 电导率分别为20 mS/m和35 mS/m, 表面张力分别为21.6 mN/m和34.3 mN/m左右, 粘度为25 mPa*s和32 mPa*s, 且无剪切增稠效应.这些结果说明所制陶瓷墨水的性能指标基本满足非连续式打印机要求.从透光率测试结果表明所制陶瓷墨水属反相微乳液.     

丙烯酸树脂类水性颜料型记号墨水的制备与稳定性研究

通过测试接触角和表面张力优选了表面活性剂和助溶剂,测试墨水附着性优选了附着力促进剂。配制由色浆、丙烯酸树脂、表面活性剂、附着力促进剂等助剂组成的水性墨水,用红外光谱和热重分析对树脂和树脂-附着力促进剂进行表征,测试墨水经高温和低温存放前后的黏度、微观、pH、粒径D50、表面张力等性能变化,最后测试了优选墨水的书写效果。结果表明,表面活性剂OP-10在该墨水体系中降低表面张力的效果最明显,乙醇润湿性最好;附着力促进剂的效果与其分子结构和添加量有关,过量的附着力促进剂易导致墨水稳定性下降,主要体现在微观、黏度、粒径的变化;优选墨水书写效果良好。     

超细涂料色浆的制备及其稳定性研究

涂料色浆的着色强度和色牢度等性能除了与颜料分子的化学结构、分散性密切相关外,还与涂料色浆微观颗粒的大小与分布有关。颜料粒径越小,其着色强度、光泽和遮盖力越好,因此,超细涂料色浆的制备得到了人们越来越多的关注。本课题研究了超细涂料色浆的制备方法,讨论了分散剂结构及用量、超声波处理时间、超声波处理功率对颜料分散效果的影响,分析表征了所制备涂料色浆的稳定性。研究结果表明分散剂FPE对颜料的分散效果较好,其较佳工艺为:颜料含量15%,分散剂用量占颜料用量的20%,超声波处理时间30 min,处理功率800 W,所制备的超细涂料色浆的粒径可达到150.9 nm,其离心稳定性达93.27%。稳定性实验表明所制备的涂料色浆具有良好的对温度、pH和电解质的稳定性。     

水性红色色淀颜料的改性研究

采用含有磺酸基及乙氧基团的偶氮染料衍生物对C.I.颜料红57∶1和C.I.颜料红49∶1进行改性。考察了3种偶氮染料衍生物对颜料色光、着色强度、光泽度、粘度及分散稳定性的影响。结果表明：改性后的C.I.颜料红57∶1和C.I.颜料红49∶1具有更高的着色强度和光泽度,应用于水性体系均具有较低的粘度和较好的分散稳定性。     

喷打用蓝色陶瓷表面装饰墨水的制备与性能

制备了一种与传统陶瓷表面装饰的新技术(连续式喷墨打印法)配套的新型墨水——蓝色陶瓷表面装饰墨水。它以陶瓷颜料为基本着色料,用溶胶—凝胶法制备,以连续式喷墨打印墨水的质量标准为参照标准。经测试,所制墨水的电导率、表面张力、粘度等理化性能完全符合喷墨打印墨水的要求,适用喷墨打印法陶瓷装饰工艺的需要。研究了分散剂、粘接剂、pH值、固含量等工艺因素对该墨水性能的影响。该墨水制成时为草绿色,经煅烧,各组分反应生成颜料,显现蓝色。     

溶剂／颜料型喷墨油墨的制备及其性能的研究

利用物理分散手段制备了具有稳定分散性的溶剂/颜料型彩色数字打样用喷墨油墨样品,探讨了分散方法对颜料粒子分散性的影响以及油墨组分对其粘度、表面张力、电导率等性能的影响。研究结果表明,混合溶剂体系的表面张力可以通过各溶剂组分表面张力的算术平均数预测,快干溶剂和慢干溶剂分别影响喷墨油墨的初干性和彻干性,样品油墨的色域范围能够达到数字打样颜色再现的要求。     

在微压电打印机上墨水物化参数对打印性能和图像质量的影响

研究了在微压电型打印机上,墨水的物化参数对打印性能和图像质量的影响,通过墨水不同的参数对比,比如粘度,含氧量,溶剂化作用等,与上机打印表现建立联系,找出影响打印稳定性能和图像质量的规律。通过上机对比打印流畅性和打印稳定性,说明粘度,含氧量必须要在打印机正常工作要求的范围内,才可以保证打印机能持续稳定的喷射。适合的溶剂化作用,粘度和表面张力等参数可以使墨水在介质上具有很高的图像质量。     

水性涂料用非离子型聚氨酯分散剂

通过引入带有强吸附作用的锚基基团和具有较好亲水性的聚合物链段,自行开发了具有润湿和分散作用的非离子型水性聚氨酯分散剂。结合不同表面能的颜料对其进行分散试验,并给予粘度、外观、流动性及稳定性的性能评价,指出颜料与分散剂之间通过范德华力结合在一起,通过亲水链段提供的熵斥力达到有效稳定的水性涂料分散体系。     

Preparation and characterization of waterborne ceramic ink with submicron-sized praseodymium-doped zirconium silicate pigment by water-based diblock polymer dispersants

Two diblock polymer dispersants (i.e., PMAA-b-AMPS and PSSS-b-GMA) were synthesized and used as water-based dispersants for dispersion and stabilization of waterborne ceramic ink with submicron-sized praseodymium-doped zirconium silicate (Pr-ZrSiO₄) pigment. The color property, dispersion, and stability of the pigment particles in aqueous suspension were determined by colorimetry, laser particle size analysis, and sedimentation test. The adsorption mechanism of carbon chains of dispersants on the particle surface was analyzed by Fourier transform infrared spectroscopy, thermogravimetric analysis, X-ray photoelectron spectroscopy and electrokinetic potential measurement. Also, the viscosity, surface tension and stability of waterborne ceramic ink with the pigment particles were measured by rheometry, surface tension analysis and standing settlement. The results show that the submicron-sized pigment particles in waterborne ceramic ink show optimum dispersibility and stability at 5 wt% addition of diblock polymer dispersants PMAA-b-AMPS and PSSS-b-GMA mixed in a mass ratio of 9:1. This could be since the mixed dispersants provide the more interparticle electrostatic repulsion and steric hindrance energies due to the proper adsorption on the particle surfaces. It is indicated that adding 20 wt% of diethylene glycol monobutyl ether into the waterborne ceramic ink can effectively enhance the viscosity and reduce the surface tension, thus satisfying the applied requirements in inkjet printing. In addition, the jettability of waterborne ceramic ink on a simulated ceramic green body was also evaluated based on semi-empirical analysis.     

溶剂颜料型喷墨油墨粘度的研究

为了研究溶剂颜料型喷墨油墨的粘度,利用自行设计的YM—I型研磨机研磨分散制备油墨样品,测试了各油墨样品的粘度,探讨了分散剂、树脂、颜料、溶剂对溶剂颜料型喷墨油墨粘度的影响。     

水性油墨分散技术研究进展

结合国内外研究现状,对水性油墨的分散稳定机制、影响分散性的主要因素进行了综述分析,分析表明:颜料自身的可润湿性、粒径及粒径分布、树脂的特性、油墨的黏度及p H值都与水性油墨的分散性密切相关。在此基础上,阐述了提升分散性及分散稳定性的主要途径,包括对颜料进行表面改性处理、使用表面活性剂或超分散剂、设计颜料表面形貌及进行颜料预分散。并提出:随着国家产业调整的进一步深入,环保型水性油墨必将逐步取代传统溶剂型油墨,进一步提升水性油墨的质量已是当务之急。     

喷墨打印材料的制备及颜料用量对其性能的影响

为改善已有喷墨材料的吸墨性能,用SiO2@Al13核壳结构材料作为颜料制备吸墨材料;利用黏度杯、色差仪等进行测试,从涂料黏度、涂布量、涂布打印效果及色差四个方面,讨论了颜料用量对吸墨材料的影响。结果表明,颜料用量对吸墨材料性能影响显著,颜料的增加,利于材料吸墨,但不宜过高。颜料比例为75％时,材料性能优异。     

新型油溶性喷墨打印机墨水的研究

研制出一种新型油溶性喷墨打印机墨水。通过测定不同树脂的不同浓度丁酮溶液的性能，制备出具有最佳综合性能的打印机墨水。墨水溶液粘度、表面张力及耐溶剂性能、粘附性能均较佳。     

丙烯酸酯单体结构对UV油墨的流变性和分散性的影响

油墨的印刷适性与其流变学性能和分散性密切相关,UV单体是影响油墨的流变学性能和分散性的主要因素。本论文使用不同UV单体研制了UV丝印油墨,重点探讨了TMPTA、EO3-TMPTA、PO3-TMPTA三种单体的结构对研制的UV丝印油墨的粘度、触变性、动态粘弹性和油墨细度的影响。     

耐高温硅酮油墨的研制

以聚硅氧烷为主体材料，配以钛白粉和其它助剂制成硅酮油墨，并研究了增粘剂添加量、催化剂用量对其耐冷热冲击性、耐热性、耐溶剂性的影响     

永固红F5R电泳液及其微胶囊的研究

采用十八胺对永固红FSR化学修饰,以Span-80为稳定剂,四氯乙烯为分散介质,使用正交设计方法优化电泳液组成和工艺条件,制备了分散性和稳定性良好的电泳液。使用红外光谱、紫外光谱、激光光散射和光学显微镜技术对永固红FSR电泳液进行了表征。以此电泳液为囊芯,脲甲醛树脂为壁材,制备一种红色电子墨水微胶囊,形貌规则球形,表面光滑,囊壁结构致密,包覆率达81％,囊芯含量为78％。永固红F5R电泳液及其微胶囊具有明显的电场响应行为,可以作为柔板显示器的功能材料。