以镇海,埃索,SK三种90#基质沥青为原料,分别掺入多聚磷酸(PPA)、聚合物SBS两种改性剂,采用高速剪切法在室内制备多种复配改性沥青材料.通过常规指标测试、重复蠕变试验、疲劳性能分析、粘度试验,对不同掺量复合改性沥青的路用性能进行评价,从而确定改性剂的最佳掺量,并选择适用于复合改性沥青生产的基质沥青.结果表明:PPA的掺入使得改性沥青温度敏感性降低,高温性能以及抗疲劳性能显著提高;PPA的最佳掺量为1%,此时复合改性沥青的性能达到最优;适用于掺入PPA进行改性的基质沥青为SK90#最优,埃索90#次之,镇海90#最差;SK90#基质沥青掺入3.5% SBS和1%的PPA所复配的改性沥青经济效益较普通SBS改性沥青更为优异. 相似文献
2.
3.
为了探究多聚磷酸(PPA)复配SBS改性沥青组成材料对其粘弹性的影响,本文以SK90#基质沥青、SBS改性剂、抽出油、稳定剂、PPA、邻苯二甲酸二丁酯(DBP)为原材料,在正交试验设计的基础上,用高速剪切机制备了PPA复配SBS改性沥青,利用动态剪切流变仪分析了其粘弹特性.结果表明:(1)随着温度的升高,PPA复配SBS改性沥青的抗车辙因子随之降低、弹性减弱、抗永久变形能力降低,而其相位角增大、粘性增强、不可恢复变形能力提高.(2)当多聚磷酸的掺量为0.5%,复配改性沥青的其他组分选择最大掺量(均为3号水平)时提高了其粘弹性能,达到最优流变性能.(3)当PPA掺量为0.5%,SBS掺量为4%,抽出油掺量为2%,DBP为2%时,其复配改性沥青的性能最佳. 相似文献
4.
5.
6.
高性能的SBS改性沥青对于我国道路交通业的发展具有重要意义,本文将利用四组分法对来自不同产地的基质沥青进行分析,利用各个基质沥青制备SBS改性沥青,并对此改性沥青进行对比,以分析基质沥青对SBS改性沥青性能的影响,希望对业内有所帮助。 相似文献
7.
沥青与石料的黏附性大小直接影响沥青混合料的强度、稳定性、耐久性等性质。通过分子模拟计算的方法研究沥青与石料的黏附作用,计算比较沥青改性前后与石料间的黏附功,并与水煮法沥青黏附性实验结果及沥青混合料微观形貌研究结果进行比对;同时考察沥青改性剂LM-S对沥青混合料路用性能的改进效果。结果表明,采用LM-S改性后的沥青-石料体系的界面黏附功比基质沥青-石料体系提高了近26%,因而具有更好的黏附性;沥青混合料实验结果亦表明LM-S改性剂可显著提高基质沥青和SBS改性沥青混合料的高温稳定性能、低温稳定性能及水稳定性性能,其中动稳定度分别提高了162%和43%。 相似文献
8.
介绍了石油沥青的组分、结构等性质,应用红外光谱技术分析10#和100#基质沥青,得出沥青中加入改性剂SBS是一物理共混过程,没有形成新的官能团,仅在改性沥青中形成了稳定、均匀的网络结构,使改性沥青性能得以改善. 相似文献
9.
10.
以减三糠醛抽出油为相容剂,90#沥青为基质沥青,LG501S为改性剂,考察了相容剂的不同掺入量(占基质沥青质量)0,1.0%,2.0%,3.0%,4.0%,5.0%对改性沥青性能的影响,分析了增加相容剂掺入量沥青相与SBS相的形态特征。结果表明,增加相容剂掺入量后,改性沥青针入度、弹性恢复逐渐升高,软化点、针入度比逐渐降低,经过旋转薄膜烤箱(RTFOT)后,改性沥青5℃延度、5℃老化后延度逐渐增加,提高了改性沥青的延伸性能。随着相容剂掺入量的增加,改性沥青的高温抗车辙因子能力降低,低温抗裂性能提高;改性剂SBS在沥青中的粒径逐渐减小,分布律逐渐增加,使改性沥青的储存稳定性得到显著提高。 相似文献
11.
Solid solutions of diphosphates of zinc and copper and of zinc and cobalt were synthesized from mixtures of pure diphosphates at temperatures up to 1000°C. Their X-ray diffractometry patterns varied continuously from one end member to the other. Solid solutions of orthophosphates of composition Zn3−x Cox(PO4 )2, with x = 0.4–1.6, were formed at temperatures up to 950°C; all exhibited the structure of γ-Zn3 (PO4 )2. Solid solutions of orthophosphates of composition Zn3−x Cux (PO4 )2 exhibited more-complex behavior. At 1000°C and copper contents of 20–80 mol%, a phase that is related to Cu3 (PO4 )2, termed here the "ε-phase," predominated. At 850°–950°C and in the region from 20 mol% to ∼33 mol% of copper, the solid solutions (the "η-phase") adopted the structure of graftonite. At 800°–900°C and 10–15 mol% of copper, the solid solutions exhibited a new structure (the "δ-phase"), which we found to be related to the mineral sarcopside. At temperatures 950°C, the solutions that contained 5–15 mol% of copper (the "β-phase") had the structure of β-Zn3 (PO4 )2, whereas at 800°–850°C, solutions with 5 mol% of copper (the "-phase") exhibited the structure of γ-Zn3 (PO4 )2. Attempts to synthesize Cu+ ZnPO4 and Cu+ Cu2+ Zn3 (PO4 )3 were unsuccessful. 相似文献
13.
为了提高油田的生产效率,设计最佳的油气集输处理的工艺流程,更好地完成油气水分离处理的任务。对油气集输工艺技术进行优化,发挥高效油气水分离处理设备的优势,提高油气水处理的质量,保证油气集输工艺顺利实施,获得最佳的油田产量外输。 相似文献
14.
15.
建设创新型国家是我们中华民族的历史责任。“自主创新、重点突破、支撑发展、引领未来”的16字方针应当成为我们未来创新活动的指南。建设创新型国家把自主创新放在首位,并提出了引领未来的高标准要求。钢铁科技创新必须突出重点,抓住创新成果产业化这个关键,支撑起行业和国民经济的发展。 相似文献
16.
相比已经完善丰富的开采和勘探技术,油气的运输以及储存却仍然存在不足之处。我国对能源安全提出更加严格要求的同时,对区域经济的发展规划也有足够重视。因此,保障油气管道的安全则成为了我国能源安全战略的重中之重。在阐释油气管道现阶段在储运安全保障技术发展状况的基础上,分析了现存的问题及解决问题的手段,并指出未来可能使用的目标策略,为今后研究者提供一定程度上的借鉴经验。 相似文献
17.
膜的污染和劣化及其防治对策 总被引:25,自引:0,他引:25
较为系统地介绍了膜污染和劣化的定义和特点,因膜污染和劣化而造成的膜性能变化,以及如何预防、减少或清除膜污染和劣化的一些通用方法。 相似文献
18.
19.
20.
对几种印染废水处理工艺方案作了比较,结合水质条件,处理工艺等,最终选择了水解酸化+生物接触氧化法工艺处理印染废水。然后对其进行初步设计,并对重要的构筑物进行设计计算,最终出水水质达到国家排放标准。 相似文献