HTPB推进剂自然贮存与高温加速老化力学性能研究

研究了自然贮存和70、60、50℃加速老化下HTPB推进剂的力学性能变化规律。结果表明,2种条件下HTPB推进剂老化规律相同,表现为强度升高、伸长率降低。以最大伸长率为表征参量,结合自然贮存试验结果,得到HTPB推进剂老化性能与温度、时间的关系。     

组分对高能HTPB推进剂燃烧性能和力学性能的影响

通过调整氧化剂AP粒径与含量、键合剂及R值,研究了固体质量分数为90%的HTPB推进剂的燃烧性能和力学性能.结果表明,在HTPB推进剂能量性能得到提高的同时,推进剂的燃烧性能和力学性能也得到了较好的保证.高固体含量下HTPB推进剂的燃烧和力学性能随配方调节呈现出较为明显的规律.推进剂的燃烧性能稳定,燃速和压力指数可调,压力指数控制在0.30～0.40;分别测定了高温(60 ℃)、常温(20 ℃)和低温(-40 ℃)力学性能,高温、低温和常温下的拉伸强度一般均大于1.0 MPa,低温延伸率最高可达74.7%.     

HTPB推进剂的低温力学性能

通过低温和低温恢复常温单轴拉伸试验,考察了低温条件下HTPB推进剂力学性能的变化情况,用SEM扫描电镜观察了推进剂拉伸断面形貌,分析了所得HTPB推进剂的拉伸应力-应变曲线和力学性能特性。结果表明,在低温拉伸条件下,HTPB推进剂主要表现为基体撕裂和颗粒脆断,而在低温恢复常温拉伸条件下,主要以"脱湿"破坏为主。推进剂的低温拉伸曲线具有明显的屈服现象发生,说明推进剂的屈服现象与低温有关。推进剂在低温和低温恢复常温条件下的最大抗拉强度、弹性模量和延伸率等力学性能呈现出不同的变化规律。     

湿度对HTPB复合推进剂力学性能的影响

通过常温湿度试验,研究了HTPB复合推进剂力学性能随试验时间的变化规律.试验证明,湿度使HTPB推进剂的力学性能大幅度下降;经干燥后,其力学性能能够得到部分恢复.用扫描电镜对常温湿度试验前后推进剂的表面状态和拉伸断口进行了对比分析,结果表明,试验后推进剂表面的AP粒子形状有明显改变,拉伸断口上的AP粒子裸露面增大,粒子脱落坑表面光滑、规整.由此得出HTPB推进剂吸湿后,通过干燥方法不能使其力学性能恢复到原始状态.     

组分对高能HTPB推进剂燃烧性能和力学性能的影响

通过调整氧化剂AP粒径与含量、键合剂及R值，研究了固体质量分数为90％的HTPB推进剂的燃烧性能和力学性能。结果表明，在HTPB推进剂能量性能得到提高的同时，推进剂的燃烧性能和力学性能也得到了较好的保证。高固体含量下HTPB推进剂的燃烧和力学性能随配方调节呈现出较为明显的规律。推进剂的燃烧性能稳定，燃速和压力指数可调，压力指数控制在0．30～0．40；分别测定了高温（60℃）、常温（20℃）和低温（-40℃）力学性能，高温、低温和常温下的拉伸强度一般均大于1．0MPa，低温延伸率最高可达74．7％。     

不同温度条件下HTPB推进剂干燥恢复研究

以在30℃、RH为100%条件下湿老化5 d的丁羟(HTPB)推进剂试样为研究对象,分别进行了在10、30、50℃3种温度下的干燥恢复试验,测试了干燥恢复过程中推进剂试样的失水率和力学性能。综合分析了试验数据,得到了不同温度下干燥时初始阶段推进剂试样的失水率、抗拉强度恢复速率,以及各力学性能参量恢复度90%且伸长率比值1.2的恢复时间。对抗拉强度测试中得到的断面照片进行了对比和分析,将样品30℃干燥恢复1、4、9 d后的单向拉伸曲线绘制在一张图上进行比较寻找规律,在对试验数据和试验现象分析总结的基础上探讨了HTPB推进剂干燥恢复过程中氢键的作用规律。     

一种耐刮擦增强PA6材料的制备及其吸湿行为研究

采用熔融挤出法将PA6树脂与玻璃纤维和玻璃微珠共混挤出,制得一种耐刮擦增强PA6复合材料,并探讨该种复合材料在一定环境下(60℃,80%RH)的吸湿行为,研究材料吸湿后力学性能和材料尺寸随吸湿率的变化。结果发现:基于PA6/GB/GF制得的复合材料性能优异,该种材料吸湿后,尺寸有轻微变大,强度刚性下降,韧性显著提升。     

丁羟推进剂的热加速老化力学性能及寿命预估

用单轴拉伸试验和扯离试验测试了不同老化温度(55、65、75和85℃)下热加速老化后丁羟(HTPB)推进剂的力学性能及其粘接试件的扯离强度,用Berthlot方程预估了推进剂及其粘接试件的寿命。结果表明,HTPB推进剂的最大延伸率随老化时间的增加呈现降低趋势;老化温度越高,推进剂的最大延伸率降低幅度越大,85℃贮存30d时最大延伸率降幅为29.81%,而55℃贮存30d时最大延伸率降幅仅为4.34%;粘接试件的扯离强度随着老化时间的增加呈降低趋势,老化时间相同时,扯离强度随老化温度的升高而降低。预估HTPB推进剂和推进剂粘接试件的贮存寿命分别为9.4y和15.9y。     

湿热条件下复合固体推进剂老化特性研究

为研究HTPB(端羟基聚丁二烯)、NEPE(硝酸酯增塑聚醚)2种复合固体推进剂在湿热贮存环境中的老化机理,开展了77%相对湿度、60℃和77%相对湿度、20℃条件下的贮存老化试验,实时监测了推进剂最大抗拉强度、冲击感度、邵氏硬度、热老化过程中质量的变化规律。研究发现:2种推进剂在湿热贮存环境下,最大抗拉强度随老化时间的延长持续下降;黏合剂分解是造成2种推进剂硬度变化的主要因素,且HTPB推进剂内部黏合剂受影响更大;NEPE推进剂冲击感度随老化时间增加逐渐降低,而HTPB推进剂则存在感度值回升现象;2种推进剂在湿热环境中质量均增大,且HTPB推进剂吸湿性更强。     

改性双马树脂/碳纤维复合材料体系耐湿热性能研究

对5428/T700复合材料的吸湿率、不同吸湿条件下的玻璃化转变温度及高温湿态力学性能进行了研究。结果表明,5428/T700体系具有较低的吸湿率,经70℃去离子水水煮72 h,吸湿率为0.5%,饱和吸湿率(水煮360 h)为0.8%。而且随着复合材料吸湿量的增加,其Tg下降缓慢;5428/T700复合材料在干态170℃下的弯曲性能和层间剪切性能保持率在70%以上,在湿态150℃下的弯曲性能和层间剪切性能保持率在50%以上;5428/T700复合材料在湿态150℃下的开孔压缩强度保持率在80%以上。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

Insect antifeedant properties of anthranoids from the genusVismia

Vismiones and ferruginins, representatives of a new class of lypophilic anthranoids from the genusVismia were found to inhibit feeding in larvae of species ofSpodoptera, Heliothis, and inLocusta migratoria.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.