利用XRD分析高温下淮南煤灰矿物质变化

利用X射线衍射分析四种淮南煤在不同温度下煤灰矿物组成变化。结果表明：淮南煤中主要晶体矿物有高岭石、石英、方解石、黄铁矿等,高岭石类矿物含量越高,煤灰熔点越高;方解石和黄铁矿含量越高,煤灰熔点越低。煤灰中主要晶体矿物有石英、硬石膏、赤铁矿等,硬石膏和赤铁矿含量越大煤灰熔点越低。随着温度的升高,煤灰中石英、硬石膏、赤铁矿等结晶矿物含量逐渐减少,生成新的矿物质,莫来石的生成是导致淮南煤灰熔点高的主要原因,钙长石起到降低煤灰灰熔点的作用。     

脱水褐煤中矿物质对复吸性能的影响

利用XRF、低温灰化+XRD及FTIR分析胜利高灰褐煤中矿物质组成及特性,在30℃不同相对环境湿度条件下,考察了脱水褐煤的复吸性能,研究了矿物含量对脱水褐煤复吸性能的影响.结果表明:胜利褐煤中矿物有石英、高岭石、白云母、石膏、正长石和赤铁矿等,其中石英和高岭石含量最高,分别占矿物总量的38.1%和28.4%;脱水褐煤的复吸性能受到环境湿度和矿物含量的影响,同一相对湿度下煤样的复吸率随着矿物含量的升高而降低;煤中矿物表面基团吸附水分子的能力较有机含氧官能团弱.     

煤与单一矿物质在摩擦电选过程中的分离

摩擦电选能够有效分选粒度小于74μm的微粉煤,为了探索煤中矿物质在摩擦电选过程中的分离规律,将净煤(ρ1.3g/cm3)与煤中常见伴生矿物质如石英、高岭土、黄铁矿、方解石等分别按照一定比例混合,进行摩擦电选研究,并对各组精煤产品进行了X射线荧光光谱分析.试验结果表明:4种矿物质都可以通过摩擦电选方法有效脱除,方解石、石英、黄铁矿和高岭土的脱除率可分别达74.871%,82.608%,96.169%,94.986%.     

弱还原性气氛条件下CaO对高灰熔点煤灰熔融性影响的研究

选取CaO为助熔剂,分别与2种煤灰样进行不同比例的混合,在弱还原性气氛条件下对煤灰熔融性进行研究.结果表明,CaO作为助熔剂可有效降低煤灰熔融温度.这是由于助熔剂的加入改变了煤灰化学成分中的酸性氧化物与碱性氧化物的比例,以及煤中矿物质在高温下与CaO发生反应最终形成低熔点共熔物,从而使得煤灰熔融温度下降.     

燃烧炉内煤中矿物质行为研究

采用马弗炉和四角燃烧炉对煤中矿物质在加热过程中组分和含量变化利用Ｘ－射线衍射进行分析。结果表明,在燃烧炉内煤灰矿物质行为与在马弗炉内加热煤灰的矿物质行为基本一致;煤灰矿物质行为与原煤中矿物组成及含量关系较大。     

我国若干煤中矿物质的研究

本文采用低温灰化仪分离了我国１８个煤样中的矿物质，用Ｘ射线衍射法对它们进行鉴定。根据煤灰化学成分分析结果，参照矿物标准成分推算各矿物相在煤灰中的含量。本文还总结了我国煤中矿物质的特征，并初步探讨了煤中矿物质组成与沉积环境之间的关系。     

基于矿物晶体结构的铝土矿细菌浸矿机制研究

采用环状芽孢杆菌CGMCC12对5种含不同结构硅酸盐矿物的铝土矿样进行了生物脱硅研究.选用铝土矿中常见的橄榄石、高岭石、钾长石及河南铝土矿作为细菌溶蚀作用对象,采用电镜及XRD衍射技术,研究细菌对它们的分解作用差异.结果表明:浸矿12d,细菌对橄榄石、高岭石及石英型铝土矿脱硅作用显著,铝硅比(A/S)分别从7.12,6.11,2.89提高到16.15,11.61,13.56,而对钾长石型铝土矿及河南铝土矿脱硅效果较差,A/S分别从3.69和4.90仅提高到4.64和7.30;细菌对试验用硅酸盐矿物的溶蚀破坏作用由易至难依次为橄榄石、高岭石、钾长石;在细菌作用下,橄榄石向水镁石与石英转化,钾长石向伊利石转化,高岭石向水铝石与石英转化;多种矿物同时存在的情况下,细菌对不同晶体结构的硅酸盐矿物的分解有一定的选择性,对较易分解的矿物破坏作用较快,细菌会优先选择分解含Fe,Ca等生命元素的赤铁矿与方解石等矿物.     

两种煤配煤降低淮南煤高灰熔融性温度的研究

通过两两配煤的方法,对高灰熔融性淮南煤与4种灰熔融性温度较低煤进行配加,可以显著降低淮南煤的高灰熔融性温度,基本符合Texaco气化炉液态排渣要求。配煤灰熔融性温度的变化不是两种单煤灰熔融性温度简单的加和关系,而是非线形的关系,这与灰熔融过程中结晶矿物形成的种类不同有关。通过X-衍射分析,初步探讨灰熔融性机理。     

遂昌萤石矿的工艺矿物学及其浮选性能

为了高效利用浙江遂昌萤石矿资源,基于工艺矿物学对浮选性能研究的重要性,研究了矿石的主要化学成分、矿物组成及嵌布特征,并探讨了矿物的浮选行为.结果表明,遂昌矿区横坑坪矿和坑口矿两种矿石的结构类型基本一致,脉石矿物主要为石英,其次为长石、绢云母、方解石、高岭石等.两种矿石的主要区别在于,横坑坪矿样中方解石含量较高,达5.4%,且嵌布关系较为复杂.方解石与萤石的可浮性相近,直接导致横坑坪矿样的选别难度相对较大.浮选试验结果与矿石工艺矿物学研究结果一致.     

渤南断阶带沙四上亚段储层成岩演化研究

渤南断阶带沙四上亚段发育广泛的低孔低渗碎屑岩储层.综合铸体薄片分析、扫描电镜观察和黏土矿物X衍射分析等手段,总结储层发育的成岩作用类型及特征、所属成岩阶段和成岩演化序列;结合地层埋藏史、热演化史和烃类充注史提出储层阶段性时空演化过程和成岩-成藏耦合关系.结果表明:储层中成岩A1期次生孔隙形成时间与烃源岩主生排烃期、有效圈闭形成时间具较好的耦合关系,构成油气成藏的各项条件;渤南断阶带东部和西部因埋深和原始组成物质差异造成储层成岩特征和成岩-成藏过程的差异.根据储层自生矿物间接触关系判定成岩作用顺序为草莓状黄铁矿胶结→石英次生加大/长石岩屑溶蚀→石英弱溶蚀/方解石胶结/长石弱胶结→方解石溶蚀→铁方解石胶结→晚期黄铁矿胶结.相伴随的黏土矿物演化是由成岩早期的伊蒙混层、伊利石和高岭石矿物组合到成岩中后期的伊利石、高岭石、伊蒙混层和绿泥石矿物组合,对应质量分数变化为伊蒙混层减少约30%、伊利石增加约40%、高岭石减少约20%和绿泥石增加约20%.渤南断阶带东部和西部储层埋深差异约400m同时石英质量分数相差约10%.由此造成两者分别处于中成岩A期和B期的成岩阶段进而造成储层物性、油气储集能力和成藏过程的差异.     

The Mineral Transformation of Huainan Coal Ashes in Reducing Atmospheres

By using the advanced instrumentation of a Computer Controlled Scanning Electron Microscope （CCSEM）, X-ray diffraction （XRD） and X-ray fluorescence （XRF）, the ash composition and the mineral components of six typical Huainan coals of different origins were studied. The transformation of mineral matter at high temperatures was tracked by XRD in reducing conditions. The quartz phase decreased sharply and the anorthite content tended to increase at first and then decreased with increasing temperatures. The formed mullite phase reached a maximum at 1250 ℃ but showed a tendency of slow decline when the temperature was over 1250 ℃. The mullite formed in the heating process was the main reason of the high ash melting temperature of Huainan coals. Differences in peak intensity of mullite and anorthite reflected differences in phase concentration of the quenched slag fractions, which contributed to the differences in ash melting temperatures. The differences in the location of an mnorphous hump maximum indicated differences of glass types which may affect ash melting temperatures. For Huainan coal samples with relatively high ash melting tempera- tures, the intensity of the diffraction lines for mullite under reducing condition is high while for the samples with relatively low ash melting temperature the intensity for anorthite is high.     

淮南电厂粉煤灰的物质组成特征及其评价

利用XRF、XRD和ICP-MS等方法,对淮南电厂采集的20个粉煤灰样品的化学成分、矿物成分和微量元素的含量进行测试分析,并在分析的基础上,对淮南电厂粉煤灰中有害元素进行环境影响评价,并结合当前粉煤灰的利用情况,提出了合理的资源化利用途径。     

淮南煤焦结构及其高温气化反应性研究

采用FTIR、TG／DTA和比表面分析对淮南煤焦进行研究,考察了成焦条件对淮南煤焦的物理、化学结构及其CO2气化反应性的影响。结果表明,随着热解温度的升高,煤焦中的碳含量增加、氢含量降低、孔容减小,煤焦与CO2的气化反应性降低;在热解温度相同的备件下,与快速热解煤焦相比,慢速热解煤焦的碳含量较高、氢含量较低、孔容和比表面积较小、与CO2的气化反应性较低。     

煤灰助熔剂对灰熔点影响的研究

采用ＣａＯ，Ｆｅ２Ｏ３以及石灰石、硫酸渣助熔剂按不同比例与煤灰混合，对助熔剂对煤灰熔点的影响进行试验研究．结果表明，在还原性气氛下，添加适量ＣａＯ和Ｆｅ２Ｏ３可使煤灰熔点下降，当ＣａＯ添加率超过４０％时反使灰熔点急剧上升；石灰石、硫酸渣中起助熔作用的成分是其中的ＣａＯ和Ｆｅ２Ｏ３，其助熔行为与分析纯ＣａＯ和Ｆｅ２Ｏ３基本一致．     

秸秆燃料特性对炉内结渣的影响分析

秸秆锅炉在运行中,由于燃料所含碱金属成分较高,较易引起受热面的结渣沉积,影响锅炉的安全运行.结合秸秆锅炉燃烧特点和秸秆燃料特性,并根据工程实际,就秸秆燃料燃烧过程中的结渣机理、结渣部位,以及结渣特性的评判方法进行分析.此外,得出了生物质灰熔融的特性曲线,以及碱金属所占灰成分比重.     

水泥搅拌饱和黄土强度特性试验研究

通过试验对水泥、粉煤灰与饱和黄土搅拌后的强度增长特性进行研究,探讨水泥搅拌饱和黄土强度与二灰(水泥、粉煤灰掺合料)掺入比、养护龄期的关系.试验结果表明:二灰掺入比越大,强度越高,当二灰掺入比从12%增加到20%,龄期90 d,水泥搅拌饱和黄土强度平均增长1.90倍;龄期为90 d、二灰掺入比为12%和20%的水泥搅拌饱和黄土的强度分别是原状土强度的40倍和80倍;水泥搅拌饱和黄土强度随龄期增加而增大,养护龄期与强度总体上呈fcu,90∶fcu,28∶fcu,7=1∶0.38∶0.17的比例关系.     

生物塑料聚（3HB-co-4HB）／玉米淀粉共混材料的制备与性能

以聚4-羟基丁酸酯摩尔分数为7．3％的聚（3-羟基丁酸酯-co—4-羟基丁酸酯）和玉米淀粉为原料,通过挤出熔融共混和注塑成型制备了P（3HB-co-4HB）／玉米淀粉共混材料．借用差示扫描量热仪（DSC）、热失重分析仪（TGA）和电子拉力机等考察了玉米淀粉含量对共混材料熔点、结晶度、热分解温度、耐水性及力学性能的影响．结果表明：随玉米淀粉含量增加,共混体系的结晶度减小,熔融温度降低,熔限变宽且出现明显的双峰;玉米淀粉含量为30份的共混材料热分解温度较纯P（3HB—co-4HB）-7.3略有降低,缺口冲击强度和断裂伸长率分别在淀粉含量为10份和20份达最佳,其值分别为4．95kJ／m^2和33．15％,较纯P（3HB—co-4HB）-7.3分别提高14.3％和147．76％．拉伸强度和弯曲强度则随玉米淀粉含量增加逐渐下降．     

聚丁二酸丁二醇酯（PBS）交联改性研究

采用化学方法对聚丁二酸丁二醇酯（PBS）进行交联改性,交联剂为过氧化苯甲酰（BPO）．研究了交联剂添加量对交联体系性能的影响．采用溶胀法、差示扫描量热法、X射线衍射、平板流变仪等手段对交联后PBS的凝胶含量、结晶和熔融行为、动态流变性能进行了研究．结果表明：随着BPO添加量的增加,交联PBS的凝胶含量升高,复数黏度、储能模量和损耗模量均显著增大;结晶度和熔点降低,但结晶温度有所提高．