微波条件下淀粉基固体酸对壳聚糖的降解性能

以淀粉为原料,通过水热合成法与羟乙基磺酸、柠檬酸等反应制备了淀粉基固体酸催化剂;通过红外光谱、热重、扫描电镜、比表面积分析等对固体酸的物理化学性质进行了表征;将壳聚糖溶解在一定量的稀盐酸溶液中进行氨基的质子化,在微波辅助条件下研究了淀粉基固体酸催化剂降解壳聚糖制备D-氨基葡萄糖的性能;考察了反应时间、反应温度、微波功率、固体酸用量对壳聚糖降解性能影响。研究结果表明,当反应温度60℃、反应时间35 min、微波功率400 W、固体酸与壳聚糖质量比0.1∶1时,淀粉基固体酸降解壳聚糖制备D-氨基葡萄糖的产率达到95.3%,淀粉基固体酸催化剂在循环使用6次后仍可保持很好的反应活性。     

壳聚糖磺化改性及应用研究

以工业级壳聚糖为原料,用浓硫酸为磺化试剂,通过实验确定制备磺化壳聚糖的最佳工艺流程.证明壳聚糖磺化以后,磺酸基团存在于壳聚糖大分子链上;进一步用动态滴定法对磺化壳聚糖的磺化率进行定量检测,确定产品的平均磺化率为8.51%.最后将磺化壳聚糖应用于水处理中.     

两亲性壳寡糖衍生物的制备、表征及对疏水性染料TO的包覆

以天然高分子壳聚糖为原料,通过在壳聚糖2位—NH2上引入部分疏水性烷基,在6位-oH和2位-NH,上引入亲水性羟乙基,制得N-月桂基-O,N-羟乙基壳聚糖（LGC）两亲性衍生物,分别用FTIR、HNMR和元素分析等技术对其结构进行表征．此壳聚糖衍生物在水相中自组装形成胶柬,以芘为荧光探针研究了其自聚集行为,结果表明制得的自聚体具有较小的临界胶束浓度（CMC为1．67×10-2mg／mL）,并用此壳聚糖胶束对疏水性染料噻唑橙（TO）进行了包覆,发现包覆后染料的荧光强度显著增强．     

印花糊料羟乙基醚化度的测定

本文阐述了羟乙基化种子胶所制成的印花糊料醚化度的测定方法，并测定了五种羟乙基印花糊料的醚化度，Ｍ，ＳＰ－３０，ＰＡ－４０，ＳＰＧ，ＤＦＰＰ－１０４五种羟乙基印花糊料的醚化度分别为０．５５，０．５８，０．３４，０．３１和０．３２。同时探讨了该测定方法的置信度。     

印花糊料羟乙基醚化度的测定

本文阐述了羟乙基化种子胶所制成的印花糊料醚化度的测定方法，并测定了五种羟乙基印花糊料的醚化度。Ｍ、ＳＰ－３０、ＰＡ－４０、ＳＰＧ、ＤＦＰＰ－１０４五种羟乙基印花糊料的醚化度分别为０．５５、０．５８、０．３４、０．３１和０．３２。同时探讨了该测定方法的置信度。     

成衣无甲醛免烫整理的现状及发展

综述了无甲醛免烫整理方面的研究，分析比较了乙二醛－酰胺类整理剂、水溶热反应性聚氨酯、双羟乙基砚、天然高聚物壳聚糖、反应性的有机硅、淀粉改性物、环氧类整理剂、多羧酸化合物等无甲醛抗皱整理剂的功能以及各种整理剂存在的不足。     

低分子壳聚糖的磺化及其抗凝血活性初步研究

研究低分子壳聚糖的磺化改性及抗凝血活性.低分子壳聚糖在N,N-二甲基甲酰胺反应溶剂中与氯磺酸反应,合成低分子磺化壳聚糖.分别考察磺化反应温度、氯磺酸用量和反应时间对低分子磺化壳聚糖含硫量的影响,通过正交优化,获得最佳反应条件:反应温度70℃、氯磺酸用量3mL和反应时间4h,其最大含硫量达到8.94%.低分子磺化壳聚糖体外抗凝血活性通过活化部分凝血活酶时间(APTT)测定,结果显示其可延长APTT时间,表明是由内源性途径来影响凝血过程的;且含硫量在4.61%~8.94%范围内,低分子磺化壳聚糖抗凝血活性随含硫量的增大而增强.     

水煤浆添加剂磺化三聚氰胺——尿素—甲醛树脂的合成

给出了用于水煤浆添加剂复配的水溶性的磺化三聚氰胺－尿素－甲醛树脂的合成过程及影响因素。反应分四步进行，羟甲基化、磺化、低pH缩合、高pH重排，反应及树脂产物受pH、温度、时间、料比（氨基／甲醛，氨基／磺化剂）的影响，测定了选择样品羟甲基化物、磺化物和树脂产物的红外波谱。     

三聚氰胺系列减水剂的研究与应用

研究了三聚氰胺系列减水剂的基本合成工艺 ,考察了各种因素对羟甲基化阶段、磺化阶段、缩聚阶段的影响 ,确定了各阶段的最佳工艺条件 ,通过加入一些廉价组分制成复合型减水剂 ,使得三聚氰胺系列减水剂的生产成本大幅度降低 ,提高了产品的推广应用价值     

新型阳离子淀粉的研究

对两类新型阳离子淀粉－－阳离子羟乙基淀粉和阳离子苄基淀粉的合成方法进行了研究，通过元素分析和红外光谱对其进行了初步表征，元素分析表明，所得产物取代度小于０．２；红外光谱分析表明在阳离子淀粉中引入了羟乙基和苄基，与预基结构相符，此外，对两类新型阳离了淀粉的某些使用性能如絮凝性、破乳性进行了初步探讨，并与普通阳离子淀粉进行了比较，试验表明，阳离子羟乙基淀粉具有较好的絮凝性能；阳离子羟乙基淀粉、阳离子苄     

梯度渗透法组装仿木年轮结构壳聚糖棒材

受树木生长过程的启示，建立了一种新型的壳聚糖成型方法，以氢氧化钠梯度溶液通过膜渗透中和壳聚糖醋酸溶液，使壳聚糖原位沉析，自行组装成仿木年轮结构材料.以体积分数为2％的乙酸溶液为溶剂，配制质量分数为4％的壳聚糖溶液，然后将其注满模具，脱模后依次放入质量分数为3%、4%、5%的NaOH凝固液中凝固1 h，制备了具有仿树木年轮结构的壳聚糖棒材.通过改变凝固液中NaOH的质量分数可以调节材料中层状结构的层厚与层间距.力学性能测试表明该材料的抗弯强度高达96.8 MPa.采用梯度渗透法制备的壳聚糖棒材不仅在形态上与树木的年轮相似，而且仿木年轮结构起到了提高材料力学性能的作用，使其更适合作为骨折内固定材料.     

聚苯胺/磺化神府煤复合导电材料的合成与表征

用磺化煤作聚苯胺的掺杂剂，通过原位氧化聚合法制备磺化煤／聚苯胺复合导电材料，研究了磺化煤的量、苯胺单体浓度等反应条件对复合导电材料的影响，得出最佳反应条件，并用红外光谱分析了磺化煤对聚苯胺的掺杂作用。     

水溶性羧甲基壳聚糖制备研究

探讨以壳聚糖为原料制备甲壳素水溶性衍生物－羧甲基壳聚糖的方法。 将壳聚糖在乙醇中浸泡数小时,然后用质量分数为50％NaOH溶液碱化,制得碱化壳聚糖,把氯乙酸加入碱化壳聚糖中,在50℃搅拌4h,粗产品用乙醇溶液提纯,得到水溶性羧甲基壳聚糖,产率97．1％。     

Friction-reducing,anti-wear and self-repairing properties of sulfonated graphene

The friction reducing properties of sulfonated graphene as a lubricating additive were investigated using a four-ball machine tester with high carbon chromium bearing steels GCr15 (SAE52100) friction pairs. The microscopic morphology, elemental composition, and self-repairing properties were observed and analyzed by using scanning electronic microscopy (SEM), X-ray diffraction (XRD) and digital microscopy. The relationships among sulfonated graphene ethanol solution concentration, friction coefficient, and abrasion loss were revealed. It was found that the optimal concentration of ethanol solution with the addition of sulfonated graphene was 0.15g/mL and the coefficient of friction was only 0.105 under certain condition. Then the stable chemical properties and good anti-corrosion properties of the metal-graphene layer were further confirmed using salt spray corrosion test. In summary, sulfonated graphene can be used as a new kind of self repairing additive, and it has excellent wear-resistant and self-repairing performances.     

微波辐射下壳聚糖降解性能的研究

采用微波辐射技术对壳聚糖进行了降解，考察了微波辐射功率、辐射时间和降解时的pH值等对低相对分子质量壳聚糖制备的影响。结果表明，壳聚糖在pH值7～8，微波功率为528W(中火)，微波辐射1．5h时，可降解得到相对分子质量小于3000的低聚壳聚糖，且重复性较好，这种产品在生物医药领域具有广阔的应用前景。     

中空球形壳聚糖的制备及在固定化红酵母生产L—苯丙氨酸中的应用

报道了壳聚糖溶液注射到含有质量浓度为３０％的甲醇和质量 度为２０％的ＮａＯＨ的溶液中制成中空球形壳聚糖,经质量浓度为０．４％的戊二醛交联,固定化红酵酶生产Ｌ－苯丙氨酸,转化率为８２．４％。     

用于质子交换膜的三个苯环磺化聚芳醚的合成

合成一种含三个苯环的新型磺化聚芳醚.采用特殊单体结构的设计,在聚合物主链上引入甲基取代基对主链进行保护.用氯磺酸直接磺化方法在聚芳醚高分子侧基上引入磺酸功能基,实现了聚合物磺化结构的可控定位合成,得到了磺酸基在侧链上的磺化聚芳醚.通过核磁共振(1H-NMR)、凝胶渗透色谱(GPC)和元素分析(EA)等方法,对其结构进行表征.     

Periodontal ligament cells cultured on the tricalcium phosphate/chitosan scaffolds in vivo and in vitro

To search suitable scaffolds for periodontal tissue regeneration, different ratios of tricalcium phosphate/chitosan(TCP/chitosan) scaffolds were prepared through a freeze-drying process. Human periodontal ligament cells(HPLCs) were incubated on the scaffolds in vitro. Cells were cultured on the scaffolds, detected by scanning electron microscopy (SEM). HPLCs were analyzed by MTT assay and alkaline phosphatase(ALP) activity detection. HPLCs were seeded onto the scaffolds. Then these scaffolds with HPLCs were implanted subcutaneously into athymic mice. The state of periodontal tissue regeneration was detected after 4 weeks. As the ratio of TCP increased, TCP/chitosan scaffolds accelerated HPLCs proliferation significantly higher than the pure chitosan scaffold. HPLCs produced the cementoid tissue in vivo. The periodontal tissue regeneration engineering is able to be applied with TCP/chitosan scaffolds.     

壳聚糖的提取,纺丝及医用研究

壳聚糖是一种生物聚合物。壳聚糖纺丝可制备具有可吸收性的医用手术缝线。本研究主要探讨壳聚糖的分子结构特征及化学性能，寻求壳糖纺丝的最佳工艺条件和成纤方法，为壳聚糖的深度开发应用提供基础、数据及方法。