采用阳极氧化法在Al膜上制备具有绝缘性能的壁垒型Al2O3膜,研究不同成分比例的电解液、阳极氧化电压对壁垒型Al2O3膜性能的影响.利用能量分散谱和扫描电镜观测壁垒型Al2O3膜的元素组成、表面形貌及厚度,并对其绝缘耐压性进行了测试.结果表明,所制备的Al2O3膜厚度均为纳米量级,在95％乙二醇,1.9％癸二酸铵,3.1％硼酸的电解液中,以300V恒定电压制备的壁垒型Al2O3膜拥有很好的绝缘性能,击穿场强可达5.25 Mv/cm.     

AZ91镁合金表面热浸镀Zn．4％Al-1％Sb合金层的状况及Al，Sb的作用

与其他表面处理方法相比,AZ91镁舍金表面热浸镀Zn-4％Al—1％Sb合金层工艺简单、费用低,且又能提高其耐蚀性。采用扫描电镜观察和能谱分析研究了AZ91镁合金表面热浸镀Zn-4％A1-1％Sb合金镀层。结果表明：AZ91镁合金预热温度为200℃,Zn．4％A1．1％Sb合金液温度为420℃,浸镀时间为6s时,能获得较光滑的镀层;且在AZ91镁合金和Zn-4％Al-1％sb合金中含有Mg,Zn,Sb,Al元素,其主要为Mg2Zn3,Mg3Sb2,Mg17Al12化合物,冶金结合效果良好,镀层的耐腐蚀性能明显提高;Sb元素的加入能在-定程度上减缓锌合金液与基体的反应。     

Hf对Pt改性γ’-Ni3Al单相磁控溅射层氧化行为的影响

γ＇-Ni3Al高温合金表面溅射纳米晶涂层和铂改性γ＇＋γ＇涂层的成分、结构与基体相近,涂层脆性、相容性等改善明显,但有关改性层抗高温氧化性的研究有待深入。通过磁控溅射方法在γ＇-Ni3Al基高温合金表面沉积Ni3（Al,Hf）纳米晶涂层,在溅射层表面电镀1．5μm的Pt,1150℃扩散退火1h,得到Pt＋Hf改性的γ＇-Ni3Al单相涂层,不含Hf的涂层中没有明显的浓度梯度,而含Hf涂层中则有明显的浓度梯度。通过场发射扫描电镜（EFG—SEM）、X射线衍射（XRD）、电子探针（EPMA）和能谱（EDX）分析了涂层的结构与成分,考察了Pt改性γ＇-Ni3Al单相涂层在l050oC下空气中的氧化行为。结果表明：不合Hf的涂层生成外层为NiAl2O4、内层为Al2O3的复合氧化膜,含Hf的涂层均生成单一的Al2O3膜,Hf促进了Al的选择性氧化。适当含量的Hf降低了Pt改性γ＇-Ni3Al涂层的氧化速率,但是过高含量的Hf则使得涂层的氧化速率升高。     

电解液中Ce^3＋／Ce^4＋含量对ZAlSi12Cu2Mg1微弧氧化膜特性和表面形貌的影响

用微弧氧化方法在铸造铝合金表面获得性能优良的陶瓷层对于提高其表面耐热、耐蚀及耐磨性，扩大其应用范围将具有重要意义。在微弧氧化过程中，通过控制电解液组成可以改善膜层性能。稀土金属离子化学性质活泼而且有助于普通陶瓷的烧结。研究了ZAlSi12Cu2Mg1合金在Na2SiO3电解液体系中微弧氧化时，Ce^3＋／Ce^4＋的引入对微弧氧化陶瓷层性能的影响，测定陶瓷层的厚度、硬度，用X射线衍射仪（XRD）分析其相组成，扫描电镜（SEM）观察其表面形貌，并初步探讨了Ce^3＋／Ce^4＋对陶瓷层形成机理的影响。结果表明：Ce^3＋在0．1～0．7g／L变化时，对陶瓷层的厚度和硬度影响较小，分别为165～193μm和449～935Hv。Ce^4＋在0．1～0.7g／L变化时，陶瓷层的厚度和硬度分别为126～148μm和463～1022HV。XRD分析结果显示，陶瓷层主要由α-Al2O3、γ-Al2O3、Al2SiO5和非晶相组成，加入Ce^3＋后，陶瓷层中Al2SiO5衍射强度明显降低。     

Co对电沉积Ni—P／Al2O3合金层的组织影响

研究了Co对Ni—P／Al2O3合金性能和微观结构的影响。实验采用扫描电镜（SEM）和能谱（EDs）方法对样品的组织形貌进行了表征：采用高温烧结对样件进行了硬度测定。实验结果表明：当Co含量为5．0％时,样件Al含量减少幅度不大,且P、Ni含量分别增加至11．46％和53．91％。热处理对镀层硬度性能测定,在8000C时,其硬度为822HV。     

快速凝固Al—Li合金粉末的除气作用

本文研究了真空加热除气处理对快速凝固Al—Li合金粉末表面氧化层厚度和组成,以及对合金力学性能、断口形貌的影响。试验结果表明,由于Li的存在,除气过程中,Li不断向表面迁移,形成Li_2O,还原Al_2O_3,使表面氧化层厚度增加,组成和性质发生变化。除气处理后,虽然粉末颗粒界面结合状况有较大改善,但拉伸性能变化不大,延伸率略有提高,却很不明显。界面析出相Al_3Zr影响粉末界面结合强度。     

Ti-45Al-10Nb合金的高温氧化行为

研究了Ti—45A1—10Nb(原子分数，％)合金在800-960℃在氧气和空气中的氧化行为．结果表明，该合金具有较好的高温抗氧化性能，其氧化增重速率与铁基耐热不锈钢相似或略优．与Ti—50A1合金相反，Ti-45A1-10Nb合金在空气中的氧化增重速率明显低于在纯氧中的氧化增重速率．X射线衍射与能谱分析表明，Ti-45Al一10Nb合金在氧气中的氧化产物主要有TiO2和Al2O3，但在空气中的氧化产物中有TiN相．这是降低氧化速率的主要原因，同时，合金元素Nb稳定了氧化层中的TiN相，因而提高了合金在空气中的抗氧化性能．     

NiAl及NiAl基合金的氧化

综述了近期NiAl及NiAl基合金的氧化研究成果.研究表明:在NiAl表面通常形成一层完整的Al2O3保护膜,而NiAl基合金中由于含有大量的合金化元素,使NiAl合金由单相转变为β相与其它贫铝相组成的多相结构,使得合金的氧化规律复杂化.在氧化过程中,Al2O3保护膜经历了由快速生长的不稳定相δ-Al2O3或θ-Al2O3向稳定相α-Al2O3的相变过程,不同的合金化元素对其转变速度有不同程度的影响.在氧化膜与合金之间形成的孔洞减弱了氧化膜的黏附性,加快了氧化膜的剥落速度.     

A3钢镀锌层钼酸盐钝化膜的组成和性能

使用加速腐蚀试验和X射线光电子能谱（XPS）等手段，研究了A3钢镀锌层钼酸盐钝化膜的组成和性能．结果表明，钼酸盐钝化膜膜层厚度大于35nm，钝化膜外层钼元素以Mo^3＋、Mo^6＋形式存在，主要组成为：MoO3，Mo（OH）3，Zn（OH）2，ZnO，ZnM004；钝化膜内层钼元素以Mo^3＋形式存在，主要由Mo2O3，Mo（OH）3，ZnO，ZnMo2O4组成．钝化膜表面层中的MoO4^2-具有抗氯离子等侵蚀性阴离子的破坏作用，使钝化膜具有阳离子选择性，提高镀锌钝化膜的耐蚀性能．     

一种镍基合金在900和1000℃的高温氧化行为

采用X射线衍射(XRD),扫描电镜(SEM)及能谱(EDAX)等方法,研究了Cr5.0 Co8.0 Mo0.9W5.5 Ta7.4 Al6.0 Re4.2合金在900和1 000℃的氧化行为。结果表明,氧化动力学曲线遵循氧化初期氧化增重速率较快,氧化期间氧化动力学曲线呈波浪式变化,且呈现氧化温度越高波浪式越明显的特征。在900℃氧化300 h后合金表面氧化物膜分为3层,外层为Ni O、Ni2Cr2O4、Ni2Co O4和Cr Ta O4;中间层为平直的Al2O3层,内氧化层为Al2O3,氧化期间,分布在外层的Cr Ta O4抑制基体中Al向外扩散,并抑制氧化膜的生长,使氧化速度降低。1 000℃时合金表面的氧化物膜分为2层,外层为Ni O、Ni2Cr2O4、Ni2Co O4和Cr Ta O4;内氧化层为Al2O3。在900和1 000℃氧化期间,合金均发生元素Al的内氧化和内氮化,与外氧化膜相邻的区域为元素Al的内氧化区,远离外氧化膜的基体内部形成元素Al的内氮化区,随氧化温度升高,内氧化区和内氮化区的深度增加,内氧化物和内氮化物的尺寸增大。     

涡旋压缩机吸、排气管路结构研究

对于大型商用空调而言,管路应力应变是关系到整个机组可靠性的重要因素.本文通过实验分析总结出较为适宜涡漩压缩机的吸、排气管结构.     

The status and future development of innovative optoelectronic devices based on III-nitrides on SiC and on III-antimonides

High-brightness nitride-based LEDs have been grown on SiC substrates, which offers many advantages in the production both from epitaxial, chip and device processing point of view. Optimized InGaN/GaN/GaAlN MQW structures and improved chip and package designs were developed, resulting in optical outputs that exceed 7 mW at 20 mA in a 5 mm axial lamp. InGaN oxide stripe lasers (450 μm×3.5 μm) with an emission wavelength around 420 nm were fabricated showing threshold currents of 330 mA and turn-on voltages of about 21V operated under pulse current injections at room temperature. Strained layer GaInAsSb/AlGaAsSb quantum well lasers operating near room temperature with emission wavelengths up to 2.26 μm and a cw output of 240 mW were demonstrated. Short-period InAs/GaInSb superlattices with different InAs layer widths have been used for the fabrication of photodiodes, showing responsivity spectra with cut-off wavelengths of 4.5 and 10 μm, respectively.     

纯铜表面机械沉积镍及其对组织结构和性能的影响

为了提高材料的表面性能,采用表面机械研磨处理和机械合金化相结合的方法,在纯铜表面形成一定厚度的沉积镍层。采用X射线衍射仪(XRD)和扫描电子显微镜(SEM)对试样的显微组织结构进行分析,试样的机械性能采用金相显微硬度测试仪进行测试。实验结果表明,纯铜表面经机械沉积镍处理后,表面平均晶粒尺寸达到了纳米量级;随处理时间的延长,表面硬度得到了改善。     

Studies on the effect of solvents on self-assembly of thioctic acid and Mercaptohexanol on gold

In this article we investigated the effect of solvents (CCl₄, CH₃CN, DMF, ethanol, ethanol-H₂O and H₂O) on self-assembly of Thioctic acid (TA) and Mercaptohexanol (MCH) on gold by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). Electrochemical characteristics of TA and MCH self-assembled monolayers (SAMs) formed in different solvents were evaluated by inspecting the ions permeability (interfacial capacitance C and phase angle Ф_1 Hz) and electron transfer capability (current density difference Δi and charge transfer resistance R_ct). Experimental results indicated that the ability of solvents availing the ordering of SAMs was: for TA, CCl₄ > ethanol > CH₃CN > ethanol-H₂O > DMF; for MCH, H₂O > ethanol-H₂O ≈ CCl₄ > ethanol ≈ CH₃CN > DMF. Through relating the C, Ф_1 Hz, Δi and R_ct of SAMs (TA and MCH) with parameters of solvent (polarity E_T^N, solubility parameter δ and octanol/water partition coefficients logP_ow), it was found that solvents with bigger logP_ow (smaller E_T^N and δ) availed the ordering of TA-SAMs but the effect of solvents on MCH self-assembly was complex and MCH-SAMs formed in H₂O (the biggest E_T^N, δ and the smallest logP_ow) and CCl₄ (the smallest E_T^N, δ and the biggest logP_ow) were more ordered than in other solvents.     

基于温湿度测量的室内环境调查与分析

室内空气温湿度对人体健康影响重大,为了找出导致不适居住的环境诱因,本文调查了一例典型案例,对该房间内部温湿度进行了为期一个月的测量调查,通过分析温湿度波动图、直观反映重要统计量大小的统计图和相对湿度频率分布图,了解到室内湿度偏高的现状。为了改善不良的室内环境,提出增加防潮层的建议。     

AutoCAD中圆环螺旋面的形成与绘图

根据圆柱螺旋线理论,分析了形成圆环螺旋线的要素,并运用解析几何方法建立了圆环螺旋线的参数方程.基于圆柱螺旋面和圆环螺旋线的形成原理,构建了圆环直纹螺旋面的数学模型,讨论了圆环直纹螺旋面的两种表示方法.在AutoCAD环境下,用VisualLisp语言编程,绘制了圆环螺旋线的投影图和三维立体图,并给出了圆环正螺旋面和斜螺旋面的三维CAD造型方法.     

基于SOA的企业应用框架与实现研究

针对如何整合企业应用资源,提出了基于SOA的企业应用集成架构,针对建立的集成架构,对其核心业务层的基础服务进行了设计,包括业务流程引擎、消息可靠性传输和安全管理服务．     

轮胎气压对汽车振动噪声的影响

影响汽车振动噪声的因素有设计、材料、胎压、结构、路况等,研究轮胎充气压力变化对轮胎和整车振动噪声的影响。通过实验数据和理论分析得知,轮胎刚度与固有频率随轮胎充气压力的升高而增加;悬架与汽车振动特性随轮胎充气压力的变化而有较明显改变;轮胎气压对气泵噪声也有不同程度的影响;胎压对轮胎噪声水平影响不大,而且对实验用轮胎噪声水平影响不具有规律性;胎压升高使得轮胎减振性能下降,增加整车冲击振动感,降低汽车行驶平顺性和乘坐舒适性。因此,合理的轮胎充气压力,不但可以降低和改善整车振动噪声;而且还可以提高汽车行驶平顺性与乘坐舒适性。