热处理工艺对Q245R钢板组织和性能的影响

通过进行显微组织观察和拉伸、冲击、硬度等力学性能试验,研究了不同加热温度、保温时间、冷却方式的热处理工艺对Q245R钢板组织和性能的影响。结果表明:加热温度与冷却方式对Q245R钢板性能影响较大,加热到Ac1以上保温后空冷可适当降低钢板硬度和强度、提高钢板韧性,并且随着保温时间的延长,可使钢板强度和硬度下降;加热到Ac1以上保温后水冷,加热温度越高,水冷后获得钢板的强度、硬度也越高,韧性则越低。     

Q345R受火后力学性能及组织的变化

通过对Q345R材料在不同受火温度、保温时长及冷却方式条件下进行热处理来模拟其受火损伤的热暴露试验,进一步评定材料的力学性能及相应的微观组织。研究表明:在20℃～649℃受火温度下,材料力学性能均满足要求,732℃～816℃受火温度下,与空冷条件下相比,水冷对其力学性能影响较大;受火温度低于649℃时,材料组织为铁素体+珠光体,高于649℃时,金相组织明显发生变化,水冷下晶粒度与空冷条件下相比较为不均匀;热处理温度不高于649℃时,材料无明显脱碳现象,在816℃时材料表面脱碳层最大深度约0.20 mm;随着受火温度的升高,热处理后表面颜色呈红褐色、灰褐色、暗红、亮红色变化。     

热处理工艺对AFA耐热钢组织和力学性能的影响

为考察热处理工艺对AFA耐热钢组织和力学性能的影响,本文利用光学显微镜、扫描电镜、X射线衍射等技术,研究了新型含铝奥氏体耐热钢(AFA)在不同保温温度和冷却方式下的组织演变规律及力学性能的变化。结果表明:加热温度和冷却方式对试样的显微组织均产生影响。随着保温温度的升高,晶粒的平均尺寸逐渐增大。在1150和1200℃保温冷却后,空冷试样的晶粒尺寸略大于炉冷试样。不同温度下保温冷却后,析出相在晶内和晶界均有分布,晶内析出相形状变为圆形或颗粒状,晶界处变为长条状,但种类并未发生改变。析出相的平均尺寸随着保温温度的升高而增大。在1200℃下炉冷后,析出相的平均尺寸、面密度和晶界覆盖率均高于空冷,此时炉冷试样的硬度值达到170 HV,高于空冷,但抗拉强度和延伸率较低,分别为680 MPa和13.04%。     

超细晶6061铝合金的搅拌摩擦制备和性能

对6061铝合金进行常规空冷和强制水冷的搅拌摩擦加工(FSP)并研究其微观组织和力学性能,结果表明：FSP 6061铝合金的加工区均为细小等轴的超细晶组织,晶内位错密度较低、高角晶界的比例均高于70%;采用强制水冷,可将FSP 6061铝合金的平均晶粒尺寸细化到200 nm。FSP 6061铝合金中的析出相主要为球状或短棒状,采用强制水冷使析出相的长大受到明显抑制并使部分固溶元素不能及时析出,使析出相的尺寸与间距明显减小。与常规空冷相比,在强制水冷条件下FSP制备的6061铝合金具有更高的细晶强化和沉淀强化效果,其抗拉强度高达505 MPa,比峰时效态6061铝合金母材提高了55%。     

热处理工艺参数对超高强度钢性能的影响

目的 研究热处理工艺参数对BR1500HS超高强度钢的微观组织、拉伸断口以及力学性能的影响,并且研究保温时间和加热温度对淬火后的硬度、抗拉强度、微观组织以及伸长率等的影响规律.方法 将BR1500HS加热到一定温度,并保温使得试样充分奥氏体化,随后在水中冷却,并测试冷却后的材料力学性能.此外,将克立金模型引入用于近似加热温度、保温时间与硬度、抗拉强度、伸长率之间的关系,用NSGA-Ⅱ多目标遗传算法优化代理模型.结果 当保温时间一定时,硬度随着加热时间的增加先增加后减小、抗拉强度先增加后减小最后趋于平稳;当加热温度一定时,硬度随保温时间的增加先增加后减小.当加热温度不同时,抗拉强度随保温时间的变化规律不同;当加热温度在950℃以下时,随着保温时间的增加而增加;当加热温度在950～1000℃时,随着保温时间的增加先增加后减小.结论 采用实验和代理模型的优化结果的误差较小,对BR1500HS超高强度钢的热处理工艺具有一定的指导作用.     

热处理工艺对Ti6246钛合金组织与力学性能的影响

研究了热处理温度和冷却方式对Ti6246合金显微组织、相组成以及室温拉伸性能的影响。结果表明:固溶热处理后合金的相组成主要与冷却方式有关。在β单相区及(α+β)两相区固溶后水冷,β相均转化为α′′马氏体和少量亚稳β相。空冷组织中的β相转变为含有少量次生α相的β转变组织,随着热处理温度的提高次生α相的含量逐渐增加,尺寸也逐渐增大。时效后组织中的亚稳相发生分解,析出细小的次生α相。固溶后水冷试样的拉伸曲线上出现"双屈服"现象,且随着固溶温度的提高合金第一屈服点逐渐升高。水淬和空冷合金试样在595℃/8 h时效后其室温拉伸强度提高,延伸率及断面收缩率降低,水淬试样室温拉伸性能的变化更大。固溶后空冷且在595℃时效处理的合金,其室温拉伸性能可达到较好的强塑性匹配。     

Ti-6Al-4V合金厚板固溶时效热处理工艺的正交试验优化

通过在热处理参数选择过程中引入正交试验,确定了固溶温度、冷却方式、时效温度和时效时间4个影响因素,并采用L16(4⁴)正交表4因素、4水平的16组热处理工艺进行试验对工艺进行优化。结果表明:在该试验条件下,各因素对板材横、纵向室温强度影响从大到小的顺序为冷却方式、时效温度、时效时间、固溶温度,对室温塑性基本没有影响;固溶后的冷却方式对板材室温拉伸性能的影响最大,随着冷却速率的增大,板材的横、纵向抗拉强度和屈服强度都大幅度提高,断后伸长率和断面收缩率的波动较小;时效温度对板材室温拉伸性能的影响次之,随着时效温度的升高,板材横、纵向抗拉强度均呈下降趋势,断后伸长率基本保持不变,而屈服强度和断面收缩率呈先略微上升后基本保持不变的趋势,并在时效温度为550℃左右达到最大值。在该试验条件下,Ti-6Al-4V合金热轧厚板最优的固溶时效热处理工艺为900~960℃/1.5 h,水冷+550℃/4~6 h,空冷。     

钢/铝薄板热无铆连接接头力学性能研究

目的 针对目前车用高强钢和高强度铝合金板料在无铆连接工艺上出现的成形接头效果不佳及接头强度难以满足实际工况等问题,提出一种钢/铝异种材料热无铆塑性连接工艺,以有效提高22MnB5高强钢与7050铝合金铆接接头性能。方法 通过软件Abaqus建立钢/铝异种材料无铆塑性连接有限元模型,对塑性连接接头尺寸特性进行分析;进一步通过仿真分析研究高强钢初始铆接温度对接头截面颈厚与自锁值的影响,并采用拉伸试验研究铝板在不同初始温度下及成形接头在不同冷却方式下对无铆塑性连接接头性能的影响。结果 将有限元仿真分析结果与试验的金相图进行了对比研究,得出二者成形接头的尺寸基本吻合,并产生了有效的机械自锁,证明了仿真模型的准确性。随后,经仿真分析确定,钢加热至700 ℃时,接头颈厚值与自锁值均最大,分别为0.402、0.357 mm,该成形温度下接头特征尺寸最佳。最后,通过试验分析发现,常温铆接、阀冷、室冷、水冷的拉力峰值分别为2.076 3、5.314 0、2.411 1、2.024 0 kN。由此可得,热处理后接头的抗剪切强度较常温铆接提高了28.5%,在3种冷却方式处理下,阀冷的接头强度最佳,水冷的接头强度最差。结论 通过对比分析,确定了22MnB5钢加热至700 ℃且铝仅经热传导并采用阀冷时进行无铆塑性连接的接头强度最佳。     

大口径厚壁12Cr1MoVG钢制高压锅炉管硬度偏高原因分析及热处理工艺优化

某大口径厚壁12Cr1MoVG钢制高压锅炉管硬度偏高,采用硬度测试、力学性能试验、金相检验等方法对硬度偏高问题进行了分析。结果表明:热处理后的钢管组织不均匀,导致钢管的力学性能不均匀,部分区域硬度不符合设计要求。根据电站机组特点,设计了正火后旋转内淋外喷冷却、正火后直接水冷和正火后"预冷+水冷+空冷"3种热处理工艺方案,最终通过选用"预冷+水冷+空冷"工艺,将回火温度和预冷时间控制在合理范围,使钢管硬度符合设计要求。     

6061-T6铝合金多道搭接FSP腐蚀性能

将6061-T6铝合金进行空冷、水冷的多道搭接搅拌摩擦加工(multi-pass FSP),用金相显微镜、扫描电镜、透射电镜、浸泡腐蚀试验和电化学腐蚀等手段表征了核区材料的腐蚀性能。结果表明:母材经这两种冷却方式的FSP改性后,核区的晶粒明显细化,腐蚀性能有显著的提高;与母材相比,核区的腐蚀电压较高,腐蚀电流密度较小,阻抗较大;空冷FSP的核区材料比水冷的腐蚀性能更好。     

Estimation of Parameters of Universal Distribution of Moments of Failure of Products

A method is proposed for estimating the parameters of a mixture of exponential and Weibull distributions for which the accuracy of preliminary estimates obtained by graphical analysis is refined in accordance with the criterion of maximum likelihood. The efficiency of the proposed method is supported by the results of statistical modeling.     

Assessment of intakes of mixtures of radionuclides

Australia has several uranium mines and a large number of mineral sand mines, with associated processing facilities. Exposures resulting from these mining and processing operations usually involve intakes of mixtures of radionuclides. This work describes the development of a suite of first order, linear compartment models, based on the ICRP Publication 66 respiratory tract model, and an analytical solution to the decay equations, for assessing the consequences of such intakes. The computer programs based on these models directly compute excretion, organ retention and organ and whole-body doses for intakes of either single radionuclides or any mixture of radionuclides belonging to the same radioactive decay chain. The intake can be via inhalation, ingestion or injection, and can be acute, chronic or of limited duration. The starting concentration and degree of secular (dis)equilibrium can be specified for each radionuclide. No assumptions need to be made about the relative magnitudes of the radioactive half-lives of the different nuclides.     

卧式金属罐容量的测量结果不确定度

本文根据多年的实践检定经验 ,参照JJF1 0 59- 1 999《测量不确定度评定与表示》以及《测量不确定度表达 1 0讲》 ,对卧式金属罐容量的测量结果不确定度进行了评定。     

盐酸浓度不确定度的评估

通过对盐酸浓度标定的过程分析，找出影响结果的各个分量，进行不确定度的评定，按照计量技术规范给出标准的表示法。     

Evaluation of optical properties of highly scattering media by moments of distributions of times of flight of photons

A novel method for the determination of the optical properties of tissue from time-domain measurements is presented. The data analysis is based on the evaluation of the first moment and the second centralized moment, i.e., the mean time of flight and the variance of the measured distribution of times of flight (DTOF) of photons injected by short (picosecond) laser pulses. Analytical expressions are derived for calculation of absorption and of reduced scattering coefficients from these moments by application of diffusion theory for infinite and semi-infinite homogeneous media. The proposed method was tested on experimental data obtained with phantoms, and results for absorption and reduced scattering coefficients obtained by the proposed method are compared with those obtained by fitting of the same data with analytical solutions of the diffusion equation. Furthermore, the accuracy of the moment analysis was investigated for a range of integration limits of the DTOF. The moment analysis may serve as a comparatively fast method for evaluating optical properties with sufficient accuracy and can be used, e.g., for on-line monitoring of optical properties of biological tissue.     

Analysis of anisotropy of properties on the basis of studies of texture of coarse-grained ingots of thermoelectric materials

An analysis of anisotropy of the properties of a Bi₂Se_0.3Te_2.7 solid solution was carried out using construction of demonstrative surfaces for thermoelectric effectiveness and thermal expansion coefficients. It is shown that the texture is an important factor forming anisotropy of properties and technological fitness of ingots for manufacturing modules. Anisotropy of properties based on the studies of the ingot textures obtained using the float-zone method and Bridgman method (growing thermoelectric plates in a flat cavity) was studied.