南极磷虾甲壳素纳米晶须的制备与应用

利用南极磷虾壳制备甲壳素，然后采用TEMPO氧化法将其制备成甲壳素纳米晶须，将不同添加量的甲壳素纳米晶须加入壳聚糖/鱼胶基体中，制备壳聚糖/鱼胶/甲壳素纳米晶须复合膜材料。通过扫描电镜(SEM)、透射电镜(TEM)、X射线衍射(XRD)和傅里叶红外光谱(FTIR)对甲壳素纳米晶须进行分析；通过SEM、光透射率、 XRD、热重分析(TG)对复合膜材料进行检测；通过小鼠皮下埋植实验对复合膜材料的降解性进行测试。研究结果表明，利用南极磷虾壳所制备的甲壳素纳米晶须呈针状或纤维状，平均直径为17 nm;甲壳素纳米晶须能够均匀分散在复合膜材料中，当甲壳素纳米晶须的添加量为7%时，复合膜的拉伸强度达到最大为18.37 MPa,相比于壳聚糖/鱼胶膜提高了160%,这说明纳米晶须添加到复合膜中能显著提高其机械强度。小鼠皮下降解实验表明，添加纳米晶须的复合膜降解速度变慢，第九周时，添加7%纳米晶须的膜材料降解率为66.2%。     

SF／SiO纳米复合膜的制备方法

本发明涉及一种丝素蛋白／二氧化硅纳米复合膜的制备方法．该方法采用溶胶凝胶法制备丝素蛋白／二氧化硅纳米复合溶胶，利用该发明制备丝素蛋白／二氧化硅纳米复合膜，制得的纳米复合膜中丝素蛋白和二氧化硅均匀分布，有机相与无机相间存在氢键．制备反应条件温和，而且制备条件易于控制，重复性好．     

明胶-壳聚糖/纳米SiO_2原位载药复合膜的制备及性能研究

利用明胶、壳聚糖和纳米SiO_2,制备了明胶-壳聚糖/纳米SiO_2复合膜,对复合膜的溶胀性、机械强度等进行测试。然后将明胶-壳聚糖/纳米SiO_2复合膜用于阿司匹林的原位负载,研究纳米SiO_2用量和模型药物阿司匹林用量对原位载药复合膜缓释性能的影响。结果表明,纳米SiO_2的引入能够降低复合膜在水中的溶胀性,提高复合膜的机械强度;随着纳米SiO_2用量的增加,复合膜原位负载阿司匹林的缓释效果增加;阿司匹林用量为0.5%时,明胶-壳聚糖/纳米SiO_2原位载药复合膜具有较好的缓释效果。     

纤维素磁性纳米复合膜的研究进展

目的综述了纳米Fe3O4磁性粒子的制备方法和机理,找出纤维素磁性纳米复合膜的基本复合方法。方法比较分析沉淀法、水热反应法、微乳液法、溶胶凝胶法、高温分解法等制备纳米Fe3O4磁性粒子的优缺点。结果总结了纤维素磁性纳米复合膜研究和应用进展,并为今后纤维素磁性纳米复合膜的发展提出了建议和新思路。结论采用原位复合的方法制备纤维素磁性纳米复合膜是目前的研究热点,具有显著的意义和广阔的发展前景。     

纳米TiO2/丝素复合膜的制备及其机械性能研究

为获得良好强度的纳米TiO2/丝素复合膜,在丝素蛋白溶液中添加了纳米TiO2,采用复合法,通过控制配比,pH等条件制备了不同形态的复合膜,并以普通丝素膜作对照,用AFM,EDS和IR对复合膜进行了表征,在此基础上,研究了复合膜的机械性能.实验结果表明,复合膜制备方法合理,当W(TiO2)=1/1000时,纳米TiO2以粒径50nm左右均匀分散于复合膜中,纳米TiO2的加入,促进了丝素无规卷曲构象向β-折叠构象的转化,使复合膜表现出较丝素膜更优异的机械强度.     

用电沉积法制备纳米氧化锌/海藻酸钠复合膜

以海藻酸钠为稳定剂用水热法合成纳米氧化锌,再用电沉积法制备了纳米氧化锌/海藻酸钠复合膜。测试纳米氧化锌的粒径和化学结构、观察了复合膜的形貌并测试其性能。结果表明,纳米氧化锌/海藻酸钠复合膜对大肠杆菌和金黄色葡萄球菌有良好的抗菌性能,对亚甲基蓝染料有良好的光催化降解效应。     

纳米Ni粒子/PTFE复合磁性膜的制备及表征

采用双向膜相扩散控制原位化学沉积方法,在聚四氟乙烯(PTFE)膜孔道中及膜面上原位化学沉积、生长磁性纳米Ni粒子,制得纳米Ni粒子/聚合物磁性复合膜.探讨了制备条件对复合膜磁性能的影响,并用XRD和SEM等手段对磁性复合膜的结构、组成进行了表征.结果表明,复合膜膜孔中及膜表面上均有纳米级Ni粒子生成,且膜孔中的Ni粒子对复合膜磁性能具有显著影响.     

水溶液中组装碳纳米管/硫化锌纳米晶复合膜

半导体材料ZnS在光催化领域具有重要的应用前景，如何提高其光催化能力仍是目前关键问题之一。应用碳纳米管的独特结构和性能有望调变和改善ZnS的催化功能。采用一种简便的方法在水溶液中成功组装了硫化锌／碳纳米管纳米晶颗粒（ZnS／CNTs）复合膜。TEM显示纳米复合膜以CNTs组装成席状骨架，ZnS纳米晶填充在CNTs间的缝隙或者包裹在CNTs的表面，二者之间存在良好的接触和相互作用。生成的ZnS纳米颗粒尺寸均匀、大小约为5nm。用EDS、SAED和XRD分析了复合膜的元素组成以及ZnS的晶相结构。结果显示ZnS纳米晶为闪锌矿结构。     

聚吡咯-二氧化钛自组装复合膜的制备及其光电转换性质

通过原位自组装技术制备了聚吡咯-二氧化钛纳米复合膜,利用紫外-可见光谱、红外光谱、原子力显微镜、电化学循环伏安等方法对所制备的复合膜进行了表征.与利用原位自组装技术制备的聚吡咯膜相比较,由于在复合膜中聚吡咯和TiO2纳米粒子之间的相互作用,复合膜π→π*跃迁吸收峰发生蓝移,氧化还原峰的位置向负电位方向移动.沉积在导电玻璃ITO表面的该纳米复合膜在可见光下表现出一定的光电转换性质.     

玻璃固载TiO2/纳米纤维素复合薄膜的制备及其光催化性能

将微晶纤维素溶解于NaOH-尿素的低温溶液中形成纤维素溶液,在水浴中再生形成纳米纤维素溶液.然后将纳米纤维素溶液与TiO2(P25)混合,并添加少量的钛酸正丁酯作为交联剂形成复合溶液.将制备得到的复合溶液通过流延法固载到玻璃片表面形成玻璃固载的TiO2/纳米纤维素复合膜.通过SEM、XRD表征了复合膜的形貌与结构.将玻璃固载的TiO2/纳米纤维素复合膜在紫外光下进行光催化降解甲基橙(MO)以评估复合膜的光催化性能,研究了纳米TiO2含量对复合膜光催化性能的影响,复合膜的重复使用性能以及光降解的动力学过程.结果表明:复合膜对MO的光催化降解能力可达90％以上,与纯TiO2粉末相当,并重复使用3次光催化性能基本保持不变.复合膜对甲基橙的降解动力学符合一级动力学特征.当纳米TiO2相对于纤维素的质量分数为33.3％时,光催化活性最高,动力学速率常数为0.035min-1.     

颗粒含量对含污染物油润滑条件下纳米复合电刷镀层摩擦学性能的影响

研究了电刷镀液中纳米Al₂O₃颗粒含量对复合镀层中纳米颗粒含量、镀层表面形貌、显微硬度以及摩擦学性能的影响。结果表明,随着镀液中纳米Al₂O₃颗粒含量的增加,镀层组织细化,显微硬度提高,镀层在含细沙油润滑条件下的耐磨性比不加纳米颗粒的快速镍镀层提高了80％。当镀液中Al₂O₃含量为20 g/L时,镀层具有最佳的耐磨性,进一步提高镀液中的纳米颗粒含量,镀层性能反而下降。      

Influence of nanocomposite surface coating on biofilm formation in situ

Caries and periodontitis, the most wide-spread oral diseases around the world, are caused by bacterial adherence and biofilm formation onto the natural as well as restored tooth surface. One possible way to prevent the pathogenic consequences of intraoral biofilm formation might be the modification of the tooth surface by application of an anti-adhesive coating that interferes with the bacterial attachment and subsequent bacterial accumulation. The objective of this study was to investigate the effect of an experimental, low surface free energy nano-composite coating material on biofilm formation in situ. For this purpose, an organic/inorganic nano-composite coating (NANOMER, INM, Saarbrücken, Germany) with a surface free energy of 18-20 mJ/m2 was applied to enamel as well as titanium specimens. The nano-composite coated specimens and un-coated controls were attached to removable intraoral splints and carried by volunteers over 24 h in the oral cavity. After intraoral exposure, specimens were processed for transmission electron microscopic analysis. On non-coated enamel and titanium control samples a multi-layer of adherent bacteria was found. In contrast, on nano-composite coated specimens strongly reduced biofilm formation was observed. In most areas of the surface-coated specimens only a 10-20 nm thick electron dense layer of adsorbed salivary proteins with adherent protein agglomerates of 20-80 nm diameter could be detected. In addition, detachment of the adsorbed biofilm from the nano-composite coated surfaces was evident in electron microscopic micrographs. The present investigation provides ultrastructural evidence that it is possible to cover enamel as well as titanium with a nano-composite coating revealing easy-to-clean surface properties that cause reduced biofilm formation and accelerated removal of adherent biofilms under oral conditions.     

Ni-W-SiC纳米复合电镀工艺的研究

采用一种新型的分散方法促使纳米SiC在镀液中的均匀有效分布.初步探讨了工艺参数对复合镀层的影响,着重研究阴极电流密度对Ni-W-SiC纳米复合镀层表面形貌、断面形貌、n-SiC共析量和显微硬度的影响.结果表明:在其他工艺不变的条件下,选择适当的电流密度可制备出形貌良好、成分均匀、硬度较高的纳米复合镀层.     

等离子喷涂Al_2O_3-30%TiO_2微米/纳米复合涂层的结构与耐磨性能

采用溶胶-凝胶法合成了不同粒径的Al2O3-30%(质量分数)TiO2纳米复合粉体,用喷雾干燥法对合成粉体进行喷雾造粒,造粒后的粉体通过等离子喷涂制备Al2O3/TiO2复合涂层,最后对涂层结构和性能进行了表征。涂层结构和形貌分析表明制备的涂层具有微米/纳米复合结构,初始粉体粒径对涂层的结构和致密度影响很小;涂层摩擦学性能测试表明复合涂层的磨损率随初始粉体粒径的增大而减小,初始粉体粒径为100nm左右时,复合涂层的磨损率最低。复合涂层的磨损机制为裂纹扩展导致的磨损剥落。     

纳米复合镀技术在注塑模具腔体表面处理中的应用

简要介绍了在传统复合镀技术基础上发展起来的纳米复合镀技术,其应用于注塑模具腔体表面处理的研究刚刚起步,将其与普通镍电刷镀技术相比较,叙述了注塑模具腔体表面实现纳米化的基本途径,说明了纳米复合电刷镀的优势,即增加镀层厚度与硬度,提高注塑模具腔体表面的耐磨性、耐疲劳性和耐腐蚀性,从而提高注塑模具的使用寿命。     

纳米二氧化硅复合涂料的吸水性

利用乙二醇和表面活性剂聚N-乙烯吡咯烷酮(PVP)对二氧化硅进行表面改性,制得疏水性纳米二氧化硅,粒径约39 nm。在机械搅拌和超声场的共同作用下,将改性纳米二氧化硅分散到醇酸清漆中,获得纳米二氧化硅复合涂料。采用称量法和电化学法测试了涂层的吸水性,结果表明,纳米二氧化硅的加入降低了醇酸清漆的吸水率。文中对纳米二氧化硅改性醇酸清漆吸水性改善的原因进行了分析。     

NWC—Ni纳米涂层的制备方法研究

分别用等离子喷焊法（PTS）、冷喷涂法（cs）和复合电镀法（NCP）在2Cr13不锈钢母材上制备了nWC—Ni纳米涂层，并对涂层进行了XRD分析和抗磨蚀性能测试，结果表明，CS法的涂层因与母材未达到完全冶金结合，所以不具备优良抗磨蚀性能。PTS法和NCP法所获得的涂层均能与母材牢固结合，具有优良的抗磨蚀性能，但因在PTS法过程中存在涂层质量的衰变现像，故其涂层性能仍不如NCP优。     

纳米氧化锌改性聚氨酯复合涂层的防腐性能

研究了添加不同颜基比（P／B）ZnO的聚氨酯涂料在3．5％氯化钠溶液中的电化学阻抗谱特征，提出了涂层电极在浸泡阶段对应的不同阻抗模型，结果表明，添加量为P／B=0．3的纳米复合涂层，颜料分布均匀适中，具有最佳电化学及耐盐雾性能．纳米复合涂层的抗介质渗透能力明显优于普通涂层，其原因是纳米材料独特的表面效应使其致密性有所提高，     

Two-dimensional self-organization of gold nanoparticles on supramolecular aggregates

Alkanethiol-capped gold (Au) nanoparticles, dispersed in toluene and spin-coated on atactic polystyrene films that are themselves spin-coated on fused quartz plates, self-assemble into a characteristic two-dimensional pattern-a network of the Au-thiol nano-composite separating polystyrene 'islands' of dimensions around 200 nm. This pattern changes on varying the concentration of the nanoparticles in the coating solution, evolving into the network from isolated nanoparticle clusters, and then going over to a distribution of 'pinholes' on a surface covered by the nano-composite, resembling a partially wetted surface with near-full coverage. Study of the pristine polystyrene surface reveals a pattern of low-cohesion regions separating 'islands' of polystyrene, where the latter are known to be supramolecular aggregates. It is suggested that these regions play the role of low-resistance channels to the flow of the nano-composite during spin coating.     

钛合金表面电泳沉积法制备YSZ/HAp纳米复合涂层

采用电泳沉积法在钛合金基体上制备了YSZ/HAp纳米复合涂层,用场发射扫描电镜、X射线衍射和能量散射谱对复合涂层HAp外层的表面形貌和晶相、复合涂层的断面形貌及元素组成分布进行分析研究,通过粘结-拉伸实验测定了涂层与基体的结合强度.结果表明YSZ/HAp纳米复合涂层与钛合金基体的结合强度明显高于HAp单一涂层与钛合金基体的结合强度,说明YSZ/HAp的复合缓和了HAp涂层与钛合金基体之间的热膨胀系数失配现象,改善了涂层与基体之间的结合.