锌镍合金镀层耐腐蚀性的研究

锌镍合金层具有优异的耐蚀性,从全硫酸盐体系中用电沉积的方法制备了纯锌镀层和锌镍合金镀层.应用能量色散X射线分析仪检测了合金层的相对含量.通过中性盐雾试验、极化曲线、交流阻抗和腐蚀浸泡等试验方法研究了镀层的耐腐蚀性能.试验表明,含镍16%的锌镍合金镀层的腐蚀电位较纯锌镀层的腐蚀电位正移230 mV,该合金的耐盐雾性能达到1 000 h,是相同厚度纯锌镀层的4.5倍,具有优良的耐腐蚀性.     

弱酸性无铵锌镍合金电镀工艺的研究

研究了一种无铵弱酸性锌镍合金电镀工艺,并深入探讨了镀液的成分及工艺条件对镀层含镍量的影响,得到了镀层为γ相Ni5Zn21与δ相Ni3Zn22、且含镍量为13%的全光亮锌镍合金镀层,确定了电镀工艺规范.该镀层具有极好的耐高温性能及优良的耐腐蚀性.     

碱性体系电镀锌镍合金工艺中配位剂对镀层的影响

锌镍合金是目前最理想的代镉镀层,而碱性锌镍合金电镀体系则以其分散能力强、成本低等优点受到关注.以三乙醇胺或三乙烯四胺作为配位剂研究了锌镍合金的碱性电镀工艺,采用赫尔槽试验、重量及分光光度测定等方法讨论了镀液组成、配位剂添加量、电流密度、温度等因素对镀层外观及镀层镍含量的影响.结果表明:镀液中[Ni2 ]/[Zn2 ]浓度比、配位剂用量等对镀液稳定性、镀层质量及镍含量有较大的影响;在较宽的电流密度范围内获得光亮耐蚀合金镀层的最优工艺参数为[Ni2 ]/[Zn2 ]浓度比0.29,三乙醇胺或三乙烯四胺的最佳添加量50 mL/L(或30 mL/L),镀液温度30～60 ℃;锌镍合金镀层在5%NaCl溶液中的腐蚀行为表明,含镍量为13%的锌镍合金镀层的耐蚀性明显优于纯锌镀层.     

二元配合物中电镀锌镍合金的结构与抗腐蚀性

为深入了解碱性锌酸盐体系的工艺参数对锌镍合金镀层结构和耐蚀性的影响,在以四乙烯五胺(TEPA)为镍离子主络合剂、三乙醇胺(TEA)为辅助络合剂的碱性镀液中电沉积制备了锌镍合金镀层,利用电子能谱、X射线衍射、极化曲线和电化学阻抗谱等方法表征镀层的组成结构和在氯化钠溶液中的耐腐蚀性.结果表明:镀层含镍原子数分数11.54%~20.12%,为γ-Ni2Zn11+纯Zn两相结构(低含镍原子数分数时)或单一γ相结构(较高含镍原子数分数时),γ相晶粒在(600)方向上具有不同程度的择优取向性;随着镀液中镍原子数分数的提高,镀层的腐蚀电位正移,阻抗增加,耐蚀性提高;当电流密度为2 A/dm2时,镀层的腐蚀电位和电荷传递电阻最高,耐蚀性最好.     

碱性体系中电镀黑色光亮锌镍合金的研究

介绍了一种在碱性溶液中电镀黑色光亮锌－镍合金新工艺,讨论了镀液的组成、操作温度及阴极电流密度对镀层含镍量的影响。腐蚀实验结果表明,在含镍量相同的条件下,当镀层未钝化时,此黑色光亮锌－镍合金镀层的耐蚀性能是白色光亮锌－镍合金镀层的４倍。     

锌镍合金电镀工艺试验

为在复杂零件上获得含镍量基本恒定的锌镍合金镀层,试验采用碱性电镀液。结果表明,这种新型的锌镍合金电镀工艺具有光亮电流密度范围宽、镀液稳定等特点,锌镍合金镀层的耐蚀性是纯锌层的７～１０倍。锌镍合金电镀工艺试验@牛丽媛     

新型碱性锌镍合金电镀工艺

正0前言在恶劣的工况条件下,汽车、船舶、机械、电子等设备的镀锌层已不能满足高耐蚀性能的要求,锌镍合金镀层作为锌系合金层具有优异的综合性能,其应用范围也越来越广。锌镍合金镀层可从多种溶液中获取,对于非铸铁件,碱性锌酸盐体系是首选。在强碱性溶液中,适当的配位剂可以使镍离子稳定存在,并参与电极反应,从而得到镍含量相对稳定的锌镍合金镀层。但是,现有的锌镍合金电镀工艺存在镀层镍含量稳定性差、钝化处理难度大、添加剂种类过多、镀液维护难     

低合金高强度结构钢预镀镍后热镀锌的镀层组织研究

研究了含0.38%Si(质量分数)的Q345钢预镀镍后热镀锌时镀层的生长和组织形成。结果表明:预镀一薄层镍可有效抑制含Si>0.3%的低合金高强度结构钢热镀锌时生成超厚、表面灰暗的锌层,镍层越厚,锌层生长越慢。在浸锌时,镀镍层先与Zn反应生成Ni Zn合金相γ,和γ,镍层消耗完后,出现Fe Zn合金相δ和Ni Zn合金相δ2,最后Ni Zn相消失,镀层为连续的δ相和分散在η相中的块状ζ相;Ni Zn相形成连续致密的层状组织是抑制锌层快速生长的主要原因。     

锌镍合金镀液中锌镍离子浓度对镀层镍含量的影响

为了得到成分较稳定的锌镍合金镀层,考察了镀液中锌、镍离子浓度对镀层镍含量影响情况,发现镀液中锌镍离子摩尔浓度比对镀层镍含量影响最大;控制镀液中c(Ni2 )/[c(Ni2 ) c(Zn2 )]为0.15～0.17、c(Ni2 ) c(Zn2 )在0.17～0.40 mol/L范围内,能得到镍含量质量分数在13%左右的高耐蚀性锌镍合金镀层.循环伏安曲线分析表明,在合金电镀过程中,Zn2 的存在和析出会在阴极表面形成中间产物吸附膜,使镍的还原受阻,导致合金镀层的镍含量低于镀液中的c(Ni2 )/[c(Ni2 ) c(Zn2 )],锌镍合金共沉积表现为异常共沉积.     

不同铁含量的碱性Zn-Fe合金镀层在3种溶液中的耐蚀性能

含铁量低于1%(质量分数,下同)的Zn-Fe合金具有优异的耐腐蚀性能,有必要对其耐蚀性及机理做深入研究。采用动电位极化技术和交流阻抗方法(EIS)研究了未钝化的纯Zn镀层和碱性Zn-Fe合金镀层(含铁0.15%～0.89%)在0.2 mol/L Na2B4O7-H3BO3,含0.05 mol/L Cl-的0.2 mol/L Na2B4O7-H3BO3和1%NaCl溶液中的耐蚀性能,采用XRD法研究了不同镀层的晶体结构。结果表明:少量铁在锌中的存在明显影响锌的耐蚀性能,含铁0.15%～0.60%的Zn-Fe合金镀层腐蚀电阻和反应电阻都较纯Zn层的大,腐蚀电流密度较小,在一定电位范围内形成的电化学钝化膜耐Cl-点蚀的能力强;含铁量为0.29%的合金表现出了最好的耐蚀性;Zn-Fe合金镀层与碱性纯Zn镀层的晶体结构相同,都是六方密排结构,铁在Zn-Fe合金中不是以独立相而是以固溶相的形式存在。     

电镀Zn-Ni合金研究进展与应用现状

Zn-Ni合金镀层以其良好的耐蚀性、低氢脆性而成为替代锌镀层和镉镀层的优良镀层.本文介绍了电镀Zn-Ni合金的应用现状,分析对比了酸性体系和碱性体系电镀Zn-Ni合金的特点,重点概括了碱性Zn-Ni合金镀液体系中配位剂和添加剂的研究进展,并对电镀Zn-Ni合金未来的发展进行了展望.     

Electrolytic deposition and corrosion resistance of Zn-Ni coatings obtained from sulphate-chloride bath

Zn-Ni coatings were deposited under galvanostatic conditions on steel substrate (OH18N9). The influence of current density of deposition on the surface morphology, chemical and phase composition was investigated. The corrosion resistance of Zn-Ni coatings obtained at current density 10–25 mA cm⁻² are measured, and are compared with that of metallic cadmium coating. Structural investigations were performed by the X-ray diffraction (XRD) method. The surface morphology and chemical composition of deposited coatings were studied using a scanning electron microscope (JEOL JSM-6480) with EDS attachment. Studies of electrochemical corrosion resistance were carried out in the 5% NaCl, using potentiodynamic and electrochemical impedance spectroscopy (EIS) methods. On the ground of these research, the possibility of deposition of Zn-Ni coatings contained 24–26% at. Ni was exhibited. It was stated, that surface morphology, chemical and phase composition of these coatings are practically independent on current density of deposition. On the basis of electrochemical investigations it was found that corrosion resistance of these Zn-Ni coatings is also independent of current density. These coatings are more corrosion resistant in 5% NaCl solution than metallic cadmium. It was suggested that the Zn-Ni coating may be used as a substitute for toxic cadmium.     

Influence of thermal treatment on the corrosion resistance of electrolytic Zn-Ni coatings

This study was undertaken in order to obtain and characterize the corrosion resistance of Zn-Ni coating. The process was carried out under galvanostatic conditions (j = 50 mA·cm^?2) chosen on the ground of an analysis of the deposition process in the Hull’s cell. The Zn-Ni coatings were deposited on austenitic (OH18N9) steel substrate from the ammonia bath. Thermal treatment of Zn-Ni coating was carried out in argon atmosphere. Structural investigations were conducted by X-ray diffraction method. Surface morphology of the obtained coatings was determined using a scanning electron microscope (JEOL JSM-6480) with EDS attachment. The electrochemical corrosion resistance of the prepared Zn-Ni coatings, austenitic (OH18N9) and (St3S) steels, was defined. The studies of electrochemical corrosion resistance were carried out in 5 % NaCl, using potentiodynamic and electrochemical impedance spectroscopy (EIS) methods. Examinations of localized corrosion resistance were conducted using scanning vibrating electrode technique (SVET). On the grounds of these investigations it was found that Zn-Ni coating after thermal treatment was more corrosion resistant than the Zn-Ni coating before thermal treatment. The relatively good corrosion resistance of Zn-Ni coatings is not as high as the resistance of (OH18N9) steel substrate, but higher compared to (St3S) steel. Therefore, the Zn-Ni coatings may be regarded as a protective coating for St3S steel.     

镁合金浸锌合金溶液中金属离子对浸锌层的影响

镁合金电镀或化学镀之前一般均需要进行浸锌处理,浸锌层的质量直接影响到镀层和基体间的结合力,也关系到镀层的耐蚀性等.为提高镀层的结合力与耐蚀性,采用扫描电子显微镜(SEM)、能谱仪(EDS)、塔菲尔极化曲线等方法,对比研究了一元Zn,二元Zn-Fe,Zn-Ni,Zn-Co,Zn-Cu以及三元Zn-Ni-Fe等浸锌工艺在AZ91D镁合金上获得的浸锌层,并详细分析了各种金属离子对浸锌层形成过程的影响.结果表明:Ni2+的加入既能提高镀层的覆盖率,又能使镀层结合力提高;Fe3+的加入可以细化浸锌层的晶粒;Cu2+的加入可以提高镀层的覆盖率,使浸锌铜镀层的覆盖率达到了99.1%;Co2+对镀层的性能有不好的影响,既降低了镀层的覆盖度,又降低了镀层的结合力.     

碱性镀液中电镀光亮Zn-Ni合金

为使Zn-Ni合金镀层中Ni含量更稳定,镀层耐蚀性更好,以碱性锌酸盐为基础镀液,加入多胺聚合物（ETA）和酒石酸（C4H606）配位剂、苄基嗡盐辅助剂和多胺合成缩聚物光亮剂进行光亮Zn-Ni合金电镀。研究了2种配位剂对Zn-Ni合金共沉积、Zn-Ni合金镀层电化学行为的影响;运用小槽（1000,2000,5000mL）...     

热浸镀锌合金的研究现状以及发展趋势

热浸镀锌液中添加合金元素,将对镀层厚度、显微组织、耐蚀性和外观质量等产生重要的影响.本文重点介绍了含有Ni、Mg、Ti、Mn、Bi 5种合金镀层技术,探讨了这几种合金元素对热浸镀层组织、性能的影响,并展望了其发展趋势.     

热浸镀锌合金镀层的研究进展

热浸镀锌液中添加合金元素,将对镀层厚度、显微组织、耐蚀性和外观质量等产生重要的影响.重点介绍了含有镍、镬、钛、锰、铋的5种合金镀层技术,探讨了这几种合金元素对热浸镀层组织、性能的影响,并展望了其前景.     

双向脉冲快速电沉积非晶态Ni-P/Al_2O_3复合镀层

采用双向脉冲电沉积法制备出高P非晶态Ni-P/Al_2O_3复合镀层,利用扫描电镜(SEM)和能谱分析(EDS)方法考察镀层的微观形貌和化学组成,采用X射线衍射技术(XRD)表征镀层的相结构,并通过分析金属镀层和复合镀层的电化学测试结果,评价不同种类镀层的耐腐蚀能力。结果表明:与直流电沉积法相比,双向脉冲电沉积法可将镀层中的P含量提高至12.06%(质量分数),有利于非晶态Ni-P合金镀层的形成。采用双向脉冲法制备的Ni-P/Al_2O_3复合镀层比直流电沉积法制备的Ni-P/Al_2O_3复合镀层更平整、结晶更致密。脉冲电沉积法制备的非晶态Ni-P合金镀层具有更好的耐蚀性,而且复合微粒Al_2O_3的加入,对进一步提高非晶态Ni-P合金镀层的耐蚀性有积极作用。     

Zn-Ni合金电镀的研究进展

综述了Zn-Ni合金电镀的工艺特点、沉积机理、镀层耐蚀性机理等的研究现状,分析了Zn-Ni合金镀液体系特性和钝化特性,提出了Zn-Ni合金电镀今后的研究方向,以期为Zn-Ni合金电镀的研究和生产提供参考.     

有机多膦酸盐电镀锌镍合金的研究

研究了用有机多膦酸盐（HEDP）作络合剂,ZNP作添加剂电镀光亮锌镍合金,探讨了络合剂、氯化物含量、[Zn^2＋]/[Ni^2＋]比、阳极电流密度、温度、辅助络合剂对合金中镍含量的影响,测定了合金镀层中物相组成及镀液稳定性,通过筛选得出最佳最镀光亮锌镍合金的镀液组成及工艺条件,并讨论了锌镍合金的异常共沉积机理。