利用数值模拟开发涡轮增压器壳体铸件

介绍了汽车发动机中涡轮增压器壳体铸件的结构及技术要求,利用自动化线壳型铸造,一型2件,水平分型,采用封闭式浇注系统,浇口比为ΣF直:ΣF横:ΣF内=2:1.5:1,其中,直浇道截面面积为1 200 mm2,横浇道截面面积为900mm2,内浇道截面面积为600 mm2。热侧冒口直径为65 mm,高度为100 mm,冒口颈尺寸为23 mm×33 mm;顶冒口直径为50 mm,高度为70 mm,冒口颈尺寸为10 mm×25 mm,并在涡轮室内部圆形平面处放置尺寸为50 mm×15 mm×15 mm的随型冷铁,使生产的铸件冒口颈区域微观缩松消除。     

利用负压消失模工艺生产机架铸件

介绍了机架铸件的铸件结构及技术要求,详细阐述了其工艺设计:采用底注、开放式浇注系统,浇口比为ΣF直:ΣF横:ΣF内=1:1.32:2,其中,直浇道截面尺寸为φ90 mm,横浇道截面尺寸为60 mm×70 mm,共2道,内浇道截面尺寸为25 mm×25 mm,共20道,在铸件关键部位设计一定数量尺寸为70 mm×70 mm的集渣包,浇注温度1 420±10℃,负压度0.4 MPa,保压时间15 min。为防止模样变形,采用竹木条拉筋粘接固定模样簇及消失模易变形的部位,通过设计使用一种中空芯铁填充物,有效降低该缺陷的发生几率。最终生产的铸件各项指标均符合技术要求,废品率由原来的80%降到20%以内,已达到批量生产状态。     

运用大孔出流理论设计磨齿机床身底注式浇注系统

Y7163-10-102磨齿机床身,材质HT200,轮廓尺寸1275mm×680mm×620mm,主要壁厚20mm,最大壁厚55mm,铸件重1300kg,树脂砂型。运用大孔出流理论,设计底注式浇注系统,1个直浇道,直径φ55mm,2个横浇道,截面38mm×40mm,14个内浇道,截面29mm×8mm。浇道比为A直∶∑A横∶∑A内=1.0∶1.2∶1.4。铸件顶部放2只侧冒口,直径φ80mm。实测浇注时间80s,型腔金属液面上升速度8mm/s。生产结果表明:铸件形状完整,轮廓清晰。机加工后,铸件没有缩孔、气孔、渣孔缺陷,达到技术要求。     

球铁滑轨铸件浇注系统和冒口联合补缩工艺设计

滑轨铸件材质QT450-10,重3 020 kg,轮廓尺寸为长5 800 mm,宽550 mm,高180 mm,热节截面尺寸为180 mm×165 mm。为了防止铸件产生铸造缺陷,采用均衡凝固技术,浇注系统和冒口联合补缩工艺,沿长度方向开设10个内浇道,在浇注系统的对面一侧安置4个补缩-溢流冒口。用收缩模数法设计浇冒口尺寸:1个浇口盆,2个直浇道φ56 mm,双向横浇道44/56 mm×80 mm,内浇道40 mm×10 mm。冒口尺寸φ105/φ200 mm×160 mm,冒口颈厚15 mm,宽200 mm,长20 mm。用此工艺连续生产76件,总重230 t,铸件加工后,没有缩孔、缩松、气孔、渣孔缺陷,全部合格。证明采用均衡凝固工艺生产大型球铁铸件是可靠的。     

轮形铸铁件补缩式雨淋浇注系统的设计

采用上雨淋浇注系统生产轮形铸铁件,将直浇道、横浇道当冒口,内浇道(雨淋孔)当冒口颈,采用均衡凝固收缩模数法设计其尺寸,浇口兼作冒口,完成充填与补缩双重作用.对材质为HT250,轮廓尺寸φ600 mm×601 mm,轮缘厚61 mm,轮毂厚71 mm,轮辐厚50 mm,重920 kg的BA36050皮带轮,采用直浇道φ50 mm,横浇道50/60 mm×55 mm,内浇道(雨淋孔)φ20 mm(5只)的浇注系统.经批量生产验证,铸件无铸造缺陷,达到技术要求,工艺出品率97%,成品率大于97%.     

耐热球铁深入煤斗铸件浇口冒口工艺设计

箱体类耐热球铁深入煤斗铸件,轮廓尺寸1 920 mm×890 mm×330 mm,璧厚25 mm,材质RQTSi-5.5,重740 kg。粘土砂干型,内腔顶面分型,铸件主要在下型,浇注系统座在芯头上。采用大孔出流理论进行充填设计:1只直浇道φ69 mm,位于横浇道中间,横浇道截面44 mm/54 mm×56 mm,6只内浇道110 mm/130 mm×6 mm。在浇注系统对面设2只溢流补缩耳冒口。用均衡凝固收缩模数法设计计算冒口,直径70 mm,高100 mm。批量生产,生产结果,没有工艺缺陷,生产稳定可靠,工艺出品率93.7%。证明采用大孔出流设计浇注系统,均衡凝固收缩模数法设计耐热球铁箱体类铸件的补缩系统是可靠的。     

148电机线圈支架灰铸铁件顶注压边浇冒口工艺的设计

148线圈支架上下为圆环,由中间9个腰肋连接,最大壁厚40 mm,铸件重70 kg,材质HT 150,普通粘土砂,水平三开箱造型。运用大孔出流理论设计了顶注压边浇冒口系统。直浇道直径φ35 mm,横浇道尺寸24/28 mm×26 mm,内浇道由截面为37/39 mm×6 mm的2道内浇道和2个压边冒口形成的55 mm×5 mm的压边缝隙合成,浇道比为A直∶A横∶A内=1.0∶1.4∶1.1。用收缩模数法设计冒口,冒口直径φ55 mm、高90 mm,设1只φ30 mm的排气耳冒口。首批生产30件,经检查无缩孔、气孔、夹砂等缺陷,铸件经加工后,全部合格,表明运用大孔出流理论设计浇注系统,采用顶注压边浇冒口填充补缩工艺,生产148线圈支架铸件是可行的。     

超超临界汽轮机中压外缸铸件浇注系统的设计

介绍了中压外缸铸件的结构以及其浇注系统设计.采用半开放式浇注系统,最小截面设置在分直浇道,各组元截面积比为F直1∶F横1∶F直2∶F横2∶F内=1.2∶1.34∶1∶1.07∶ 1.24;内浇道做成宽度逐渐扩大形,开设在下型3只轴孔处.采用华铸CAE凝固模拟软件分析浇注动态过程,结果表明充型较为平稳;铸件尺寸检验和UT检测显示铸件符合客户要求.     

运用均衡凝固理论设计铸铁件升降平台的浇冒口系统

橡胶机械产品胶片机升降平台,材质HT200,重85 kg,由260/110mm×75mm圆环体与400mm×400mm×40mm方板相接组成.为防止环板交接处的收缩缺陷,采用圆环体在下、方板在上的浇注工艺.侧注式浇注系统,在浇注系统对侧安置补缩-溢流冒口.运用均衡凝固收缩模数法设计冒口尺寸,用大孔出流理论设计浇注系统.设计结果:直浇道φ35 mm,双向横浇道24/27 mm×28 mm,4道内浇道10/12 mm×34 mm,浇口截面比∑A直∶∑A横∶∑A内=1.0∶1.5∶1.6.两只冒口φ70mm×130mm,冒口颈厚7 mm,长8 mm.生产表明铸件上表面光洁,无气孔,渣孔缺陷,机加工后铸件没有缩孔、缩松缺陷,工艺出品率88.5％.证明采用均衡凝固技术设计的浇冒口系统是可靠的.     

砂型+金属型板生产铝合金电热板

1电热板生产工艺及铸造缺陷电热板是染花机用零件,材料为铸铝,尺寸510 mm×390 mm×30 mm,铸件质量13 kg,采用南京红砂造型,浇注系统采用热侧冒口,即铝液通过冒口进入型腔,在2热侧冒口之间设置直浇道、横浇道,过滤网放在直浇道与浇口杯之间。采用钟罩法精炼铝合金,精炼温度700~     

Preparation of helicopter rotor counterbalance component by means of permanent-mold casting

Copper alloy was adopted to prepare helicopter rotor counterbalance component by means of permanent-mold casting. Process parameters were determined on the basis of theory calculation and computer numerical simulation. Through controlling mould temperature, pouring temperature and speed, the defects, such as gas cavity, shrinkage porosity, cold shut, can be effectively avoided. The results show that the best process parameters for smeking are as follows： pouting temperature is 1 100 ℃, pouring time is 14 s and opened mould time is 6 min. Mixture of 90% charcoal powder and 10% fluorite were selected as covering agent and 0.01% phosphorus copper acts as oxidizer. The density of rotor counterbalance component after casting in permanent-mold is 99.91% of its theory density. Mechanical properties are as follows： σb=315 MPa, σ0.2=143 MPa, δ=25%, HB=950. The mass deviation is between -5 g and ＋5 g, the curved surface distortion is less than 0.20 mm, and the largest tolerance of sectional thickness can be controlled between -0.10 mm and ＋0.10 mm.     

球墨铸铁主传动器壳体消失模铸造工艺

介绍了用消失模工艺生产球墨铸铁主传动器壳体的工艺过程。为便于安装拆卸,铸件上下两段分开制作模具;采用阶梯式浇注系统,冒口为80mm长、50mm宽、90mm高的长方体;采用雨淋式加砂法,浇注时铸型抽成负压。试样检测结果:抗拉强度为462～487MPa,伸长率在12%～16%;基体中铁素体体积分数占95%左右,球化率达2～3级,满足铸件技术要求。     

汽车前桥的V法铸造工艺

介绍了汽车前桥的铸件结构和技术要求,详细阐述了该铸件的生产条件和铸造工艺:利用V法造型机造型,砂箱尺寸2 500 mm×1 800 mm×350/300 mm;采用开放式浇注系统,浇口比为ΣF直:ΣF横:ΣF内=1:1.75:7,最小截面积为9.6 cm2,冒口尺寸为φ80 mm;在砂箱的箱档上焊接支撑与吸气2个功能的支撑钢管,涂刷涂料前,对砂型表面的涂料进行烘干,造型时要保证型腔干净,防止中间披缝;浇注温度1 540~1 560℃,浇注时间25~30 s;保压15 min,保温缓冷1 h后开箱,浇注与造型过程真空度≥55 kPa。最终生产的铸件的表面粗糙度比树脂砂工艺生产的铸件高1~2级。     

用覆砂铁型铸造工艺生产球铁轮毂

介绍了用于QT450-10轮毂铸件的覆砂铁型铸造工艺:覆砂层厚度控制在7～10 mm,铁型壁厚20～30 mm;采用双工位覆砂造型机造型,模具温度控制在240±10℃;铸件采用边冒口补缩,浇注温度控制在1 420～1 350℃。生产结果显示:轮毂铸件表面粗糙度达到Ra12.5μm,尺寸公差等级CT7～8,工艺出品率88%,球化等级1～2级,石墨球大小6～7级,内部组织致密,产品合格率在95%以上。     

小方坯高拉速结晶器铜管温度的测量

阐明了小方坯结晶器铜管温度测量试验的方法与过程,通过在铜管内弧、外弧和侧面不同位置埋设的32支热电偶,对浇铸150 mm×150 mm过程中铜管温度进行在线检测,记录了不同工况下铜管温度随浇注时间的变化关系,分析了各种工艺参数对结晶器铜管温度分布的影响。结果表明,生产过程中结晶器铜管温度场是不稳定的,各点温度都在做非周期性、无规律的起伏变动;拉速越快,铜管四面的温度不均匀倾向越大;梅花型铜管各处温度要高于普通铜管,证明其换热效率更高,更适合高拉速的生产。     

特大型球墨铸铁钢锭模的铸造工艺

介绍了重量38t的大型钢锭模球铁件的生产工艺。采用底注式浇注系统,锭模内孔型芯采用焊接钢管芯骨,外层30mm为呋喃树脂砂层。铸件顶部延长200mm作为本体冒口,其顶面还设有4个安全小冒口。浇注后钢管芯骨内注入冷却水,对铸件下段进行强制冷却。利用球墨铸铁石墨化膨胀进行自补缩解决了铸件内部的缩孔、缩松缺陷,使生产的铸件达到质量要求。     

Preparation of big size open-cell aluminum foam board using infiltration casting

This paper presents an infiltration casting technique for manufacturing big size open-cell aluminum foam boards. The principle and key technologies of infiltration casting are also analyzed. Based on the previous practice of the small size aluminum foam production, the die for preparing big size aluminum foam boards is designed and manufactured. The experiments on aluminum boards of 300 mm × 300 mm × （20-75） mm, with the pore size ranging from 1.0 to 3.2 mm and average porosity of 60%, have been performed. The experimental results show that a reliable infiltration process depends critically on the pouring temperature of the molten AI-alloy, the preheated temperature of the mould and salt particles and vacuum. Current research explores the possibility of large-scale manufacturing and application of the aluminum foams.     

镁合金轮毂反挤压铸造成形工艺研究

介绍了采用AM60B镁合金和液态挤压铸造技术成形摩托车轮毂,对该铸件的成形工艺进行了试验并加以分析。结果表明,铸型温度为240～280℃,浇注温度为680～700℃,反挤压比压为82～100MPa,保压时间为20～25s、充型速度为0.91m/s时,反挤压铸造AM60B合金的力学性能达到:σb=218～227MPa,硬度(HBS)为66～71,δ5=9.8%～10.7%,αk=(17.5～18.7)×104J/m2。