2024高强铝合金腐蚀小裂纹行为研究

本文研究了2024-T62高强铝合金在带有腐蚀预损伤的基础上的腐蚀小裂纹行为。小裂纹试验采用单边缺口拉伸试样（SENT）,在试样半圆形缺口根部预制直径大小为100～300μm的单腐蚀坑,然后在3．5％NaCl溶液中进行疲劳小裂纹试验。采用QUESTAR长焦距显微镜与摄像机相结合的QUESTAR—CCD监测腐蚀小裂纹的萌生及扩展情况。试验结果表明,小裂纹绝大多数萌生在缺口根部腐蚀坑位置,并呈半椭圆形的表面裂纹;该材料在R=0.06恒幅载荷下,小裂纹效应不明显;对应可观测到的最小裂纹长度为6～60μm,裂纹起始寿命约占疲劳寿命的15％～25％。     

5CrMnMo钢的热疲劳裂纹研究SCIEI

通过自制Coffin型及自约束型热疲劳试验机研究了5CrMnMc钢经不同热处理后的热疲劳行为。利用扫描电镜、透射电镜等揭示了热疲劳裂纹萌生及其扩展。结果表明,淬火态的5CrMnMo钢绝大多数热疲劳裂纹优先在晶界处萌生;淬回火态的试样裂纹主要萌生于碳化物与基体的脱开处,或形成晶界裂纹;无论是淬火或淬回火态的试样其热疲劳裂纹主要沿着碳化物与基体脱开处及晶界裂纹桥接而扩展。     

QT400球墨铸铁的热疲劳行为

采用V形缺口试样,通过上限温度为500~900 ℃的热疲劳试验研究了QT400球墨铸铁的热疲劳行为,并对不同上限温度下材料热疲劳裂纹的萌生与扩展以及试样的显微组织与硬度等进行了分析。结果表明,热疲劳裂纹主要从试样的V形缺口底部萌生,上限温度越高,裂纹萌生越早,萌生后扩展速率也越快,其热疲劳寿命越低;随着上限温度的升高,试验后试样基体的硬度逐渐增加,上限温度由700℃上升到800℃时,试样硬度快速上升;热疲劳试验过程中的氧化腐蚀、球墨形态以及组织变化等为球墨铸铁QT400的热疲劳破坏的主要影响因素。     

A356合金原位拉伸裂纹萌生与扩展行为分析

采用扫描电镜原位拉伸观察了电解低钛A356合金铸态下裂纹萌生与扩展特征。结果表明:铸态A356合金裂纹优先萌生于二次枝晶臂间薄弱的共晶体区、大块的共晶硅相处;裂纹的扩展主要是微裂纹易沿着共晶体与基体界面扩展,合金组织中的共晶硅相对裂纹的扩展有一定的阻碍作用,当裂纹与共晶硅颗粒相遇时,扩展方向发生偏离而转向裂纹尖端前沿处有共晶体区开裂、共晶硅相发生断裂、或与基体界面发生分离的更薄弱区。     

TiAl合金750℃下疲劳小裂纹行为研究

研究Ti-46Al-4Nb-1.8Cr-0.2Ta合金在高温下小裂纹的萌生和扩展行为。选用光滑板材试样在原位试验机上进行750 ℃、应力比R=0.1、频率为4 Hz的疲劳试验,并使用扫描电镜对裂纹微观形貌进行观察。结果表明:片层组织TiAl合金的疲劳裂纹最易在片层团界萌生,疲劳过程中伴随较大的微观塑性变形,并在片层团界及片层间萌生大量裂纹,疲劳裂纹扩展试样半圆形缺口根部与水平方向呈45°的应力集中区域最易萌生裂纹,主裂纹通过疲劳过程中产生的片层团界裂纹、片层间裂纹合并而成,并沿与载荷方向垂直的方向扩展。在疲劳裂纹扩展后期,裂纹为穿层扩展断裂。     

喷射沉积Al-Si/SiCp制动盘材料的热疲劳微裂纹扩展行为

采用V形缺口试样,研究喷射沉积Al-Si/SiCp复合材料制动盘在25(450 ℃热循环下的热疲劳行为.通过金相显微镜和扫描电镜观察了复合材料的组织和热疲劳裂纹形貌,研究热疲劳裂纹形成与扩展机制.结果表明:热疲劳主裂纹主要从V形缺口处萌生;在同样的热循环次数下,热处理前的试样要比热处理后的试样先出现裂纹,且裂纹扩展的速率较快;裂纹绕过Si颗粒向前扩展以及裂纹穿过Si颗粒向前扩展是裂纹与Si颗粒相互作用的主要机制;SiC颗粒与热疲劳裂纹有明显的交互作用.因此,改善Si相的形态和分布以及加强Al/SiC颗粒间的界面结合有利于提高热疲劳裂纹扩展的抗力.     

球墨铸铁热疲劳裂纹萌生和扩展行为研究

以球墨铸铁QT400-15为研究对象,研究上限温度在600~900℃范围内时其热疲劳裂纹的萌生和扩展行为。结果表明,热疲劳裂纹主要是在石墨与基体交界处或交界处附近萌生,氧化对裂纹的萌生和扩展起辅助作用。主裂纹从人工缺口出发,通过环形裂纹带、楔形或者条形裂纹与沿线裸露或者浅埋石墨连接,从而形成长裂纹。石墨的不圆整以及线性排列、上限温度超过共析转变温度均加速裂纹的萌生和扩展。     

2397合金高周疲劳性能及裂纹萌生扩展行为

研究了2397-T87铝锂合金的高周疲劳性能及裂纹萌生扩展行为。结果表明:在应力比R=0.1时,2397-T87铝锂合金L方向、LT方向和ST方向光滑试样(K_t=1.0)的疲劳寿命极限分别约为192,243和151 MPa;缺口试样(K_t=3.0)的疲劳寿命极限分别约为72,78和70 MPa。其疲劳裂纹主要萌生于试样表面,以及氧化物、夹杂等脱落形成的空洞,Al(CuFeMn)第二相杂质粒子。驻留滑移带(PSB)和晶粒取向对其疲劳裂纹早期扩展有重要影响。     

7449合金高周疲劳及裂纹萌生行为

研究7449-T7951合金的高周疲劳及裂纹萌生行为。在室温下,采用光滑及缺口试样进行疲劳寿命测试,应力比(R)分别为0.5和1.0。采用金相显微镜、扫描电镜及透射电镜对该合金的微观组织及疲劳试样断口进行分析,以揭示其疲劳裂纹萌生机理与合金微观组织之间的关系。结果表明:7449-T7951合金具有优异的疲劳性能;应力比为0.5和1.0时,光滑试样的疲劳寿命极限(σN)分别为349和134 MPa,而缺口试样的σN(缺口系数Kt=3.0)分别为138和70 MPa。其裂纹萌生行为受合金中粗大第二相、析出相、晶界和位错(滑移带)的共同影响。     

一种Al-Cu-Mg-Zr合金的疲劳裂纹扩展行为研究

研究热处理状态、应力比和试样取向等对含Zr的Al-Cu-Mg系铝合金疲劳裂纹扩展行为的影响.结果表明,T3、T4两种热处理状态试样的疲劳裂纹扩展速率没有明显差别;L-T方向和T-L方向的试样也有大致相同的疲劳裂纹扩展速率;应力比R对疲劳裂纹扩展行为有明显影响,高应力比下的疲劳裂纹扩展速率明显快于低应力比条件下的扩展速率,并且高应力比下的疲劳裂纹扩展在较小的△K值下进入快速扩展阶段,并很快断裂.在较低的△K水平下应力比的影响与裂纹闭合效应有关.     

SHORT FATIGUE CRACK PARAMETER BASED ON THE TOTAL CRACK AREA

1. Introduction The initiation and propagation behavior of short cracks occupies a significant fraction of the fatigue life of unflawed material[13]. For this reason an understanding of the basic characteristics of short cracks in a smooth specimen is very important. There have been some studies concerned with the multiplication of cracks during fatigue in carbon steels[3~1 and a stainless steel1~J. In particular Goto reported that there is a continuous formation of microcracks during the en…     

Cu双晶的循环形变行为与疲劳裂纹萌生：Ⅱ.疲劳裂纹萌生与早期扩展

用扫描电镜观察了受应变疲劳载荷作用的Ｃｕ双晶物的表面形貌，发现晶界是疲劳形变双晶是有利的裂纺萌生地点，在滑移带撞击晶界的地方，特别是在几条粗滑移带共同撞击晶界的地方观察到许多疲劳微裂纹；并且发现与平行晶界双晶相比，垂直晶界双晶有有利于疲劳裂纹沿晶界作早期扩展。     

BEHAVIOR OF SHORT FATIGUE CRACKS AT BLUNT NOTCHESIN A MEDIUM CARBON STEEL

1.IntroductionTheinitiati0nandpropagation0ffatiguec=acksatn0tchesareofgreatpracticalim-portancesincethemaj0rity0ffatiguefailuresinengineeringc0mponentsandstructuresoccurduetol0calstressconcentrationsatnotches.Thefatiguelifeisusuallyseparatedintotwoparts:0neportion0flifespentincrackinitiationandtheotherp0rti0nspentinpropagati0n.However,t0talfatiguelifecannotbeevaluatedbecausetherearepresentlyn0proceduresf0revaluatingthecrackinitiati0nlength.Crackinitiati0nisusuallydefinedasthepr0cessesofl0calpl…     

CYCLIC DEFORMATION OF COARSE GRAINED POLYCRYSTALLINE PURE Al——Ⅱ.FRACTURE SURFACE MORPHOLOGY

SEM photos for very coarse grained and high ductile polycrystalline pure Al show followingcharacteristics:A few fracture sources are concentrated,the crack propagates in fan-shapenear them,and the fatigue striations are cyclic cleavage facets.Each striation consists of awide cleavage facet and a narrow cleavage stage.Those stages often blunt due to plasticdeformation.The fatigue striations are clear and continual,and distribute over whole zone ofstage Ⅱ crack propagation.Two kinds of fatigue striations form in different levels,areconjoined by a“twisted baked piece of pastry”band.The secondary crack along the fatiguestriations was observed frequently.Some of them have already developed into secondarymacrocracks and secondary fatigue striations were found clearly on secondary fracture sur-face.The fracture surface can be divided into two parts,initiation and propagation zone of thecrack,however,no statical-fracture zone was observed.The mechanism to form striationswas preliminarily discussed.     

THE CHARACTERISTICS OF SHORT CRACKS AND EQUIVALENT PARAMETER OF FATIGUE DAMAGE

1. IntroductionThe initiation and propagation behavior of short cracks occupy a sigllificant fractionof the fatigue life of unflawed ..ie.ialll--3]. FOr this reason all understanding of the basiccharacteristics of short cracks in a smooth specimen is very importallt. There have beensome studies concerned with the multiplication of cracks dllring fatiglle ill carbon steels[3--4]and a stainless steeds]. In particular Goto reported that there is a colltilluous formationof microcracks during the …     

疲劳寿命预测方法综述

综述了疲劳裂纹形成寿命和疲劳裂纹扩展寿命的预测方法,评述了各种不同预测方法的基本假设、估算步骤和特点,并对疲劳寿命预测方法进一步的发展方向作了展望。     

Fatigue crack retardation by silicon carbide powder paste infiltration under different cyclic stress conditions*

Fatigue crack retardation with infiltrated SiC paste into a crack is examined in low carbon structural steel. Two different sizes of SiC powders, whose average diameters are 15 and 53 μm, are used. The SiC powder mixed with oil is infiltrated into a through thickness fatigue crack from the crack mouth. Fatigue crack growth retardation is examined by the ΔK increasing test of R = 0.1, comparing with the base plate property, where ΔK is stress intensity factor range and R is stress ratio. Crack growth is retarded just after infiltrating SiC paste into the crack mouth, and the deceleration of crack growth rate to 1/50 of the base plate appears in the maximum. It is revealed that this crack retardation behaviour results from the crack closure induced by the wedge effect of the SiC particle into a crack. The crack retardation effect is investigated with several combinations of SiC particle size and cyclic stress conditions. The crack growth rate, da/dn and stress intensity factor, K_cl for the crack closure depend on both the maximum stress intensity factor, K_max, and the stress ratio, R. While the better retardation effect can appear in the higher K_max and the higher R ratio, it disappears in the R ratio over 0.7. The SiC paste with 15 μm powder brings the crack retardation effect in the wider cyclic stress condition more stable than in the SiC paste with 53 μm powder.     

海洋柔性立管用钢的疲劳断裂行为

采用GPS100高频疲劳试验机研究了海洋柔性立管用钢在温轧工艺下的疲劳断裂行为。结果表明,海洋柔性立管用钢疲劳寿命随加载应力幅的升高而不断下降;疲劳裂纹产生于试样表面,裂纹源区可见变形带及河流花样,裂纹扩展区存在大量二次裂纹,瞬断区疲劳裂纹呈韧性断裂特征。在疲劳裂纹扩展过程中,裂纹的扩展能力因大角度晶界的铁素体和高强度贝氏体的相互作用而受到限制,同时在晶界处形成的二次裂纹同样可减缓扩展速率,达到提高疲劳寿命的效果。     

CYCLIC DEFORMATION OF COARSE GRAINED POLYCRYSTALLINE PURE Al Ⅱ. FRACTURE SURFACE MORPHOLOGY

对粗晶纯Al多晶体的疲劳断口进行了扫描电镜分析,在应变控制循环形变下,晶粒粗大而延性很好的金属的疲劳断口具有某些特征:断裂源少而集中,断裂源附近裂纹呈扇形扩展,疲劳条纹为循环解理刻面,每一条纹由较宽的解理刻面和窄的解理台阶两部分组成,台阶往往由于塑性形变而钝化;在裂纹扩展第Ⅱ阶段的疲劳条纹清晰、连续,布满裂纹扩展第Ⅱ阶段的整个区域,不同水平面形成的条纹间以“麻花形”的条带连接;多处观察到沿条纹形成的二次微裂纹,有些已发展成二次宏观裂纹,并有二次疲劳条纹;在断口上可观察到解理小舌台;断口上无最后拉断的静断区,对疲劳条纹的形成机制进行了初步的探讨。     

粗晶纯Al多晶材料的循环形变——Ⅱ.断口形貌

对粗晶纯Al多晶体的疲劳断口进行了扫描电镜分析,在应变控制循环形变下,晶粒粗大而延性很好的金属的疲劳断口具有某些特征:断裂源少而集中,断裂源附近裂纹呈扇形扩展,疲劳条纹为循环解理刻面,每一条纹由较宽的解理刻面和窄的解理台阶两部分组成,台阶往往由于塑性形变而钝化;在裂纹扩展第Ⅱ阶段的疲劳条纹清晰、连续,布满裂纹扩展第Ⅱ阶段的整个区域,不同水平面形成的条纹间以“麻花形”的条带连接;多处观察到沿条纹形成的二次微裂纹,有些已发展成二次宏观裂纹,并有二次疲劳条纹;在断口上可观察到解理小舌台;断口上无最后拉断的静断区,对疲劳条纹的形成机制进行了初步的探讨。