Microstructure development and thixoextrusion of magnesium alloy prepared by repetitive upsetting-extrusion

Thixoextrusion involves processing alloys with a spheroidal microstructure in the semi-solid state. Before thixoextrusion, repetitive upsetting-extrusion (RUE) is introduced into the strain induced metal activation (SIMA) process to predeform AZ80 magnesium alloy. Microstructure evolution of RUE formed AZ80 magnesium alloy during partial remelting is studied at temperatures for times. Tensile mechanical properties of thixoextruded components are determined and compared with those of AZ80 magnesium alloy thixoextruded from starting material produced by casting. The results show that with increasing number of RUE passes solid grain size decreases and the rate of liquation is improved. Prolonged holding time results in grain coarsening and the improvement of degree of spheroidization. The variation of the solid grains with holding time obeys the Lifshitz, Slyozov and Wagner law. Increasing the heating temperature is favorable for the formation of spheroidal solid grains. The tensile properties for AZ80 magnesium alloy thixoextruded from starting material produced by RUE are better than those of AZ80 magnesium alloy thixoextruded from starting material produced by casting.     

Microstructure and tensile properties of AM50A magnesium alloy prepared by recrystallisation and partial melting process

Prior to thixoextrusion, the microstructural evolution of semi-solid AM50A magnesium alloy prepared by the recrystallisation and partial remelting (RAP) route was investigated. The effect of compressive ratio on microstructure of semi-solid AM50A magnesium alloy was studied. Furthermore, tensile properties of thixoextruded components were determined. The results showed that the occurrence of recrystallised grains was closely associated with the location of the first liquid formed above the solidus. With prolonging holding time, deformed microstructure was penetrated, causing fragmentation, which resulted in the decrease of average grain size. Moreover, prolonging holding time was favorable for the improvement of the degree of spheroidization due to the increase in the amount of liquid. With the increase in compressive ratio, the size of solid grain decreased, the degree of spheroidization was improved during partial remelting, and the tensile properties of thixoextruded AM50A components were improved. The tensile properties for AM50A magnesium alloy thixoextruded from starting material produced by the RAP route were better than those of the same alloy produced by die-casting and thixomolding.     

脉冲电场下制备AZ91D镁合金部分重熔过程的组织演变

研究利用低压脉冲电场技术制备的AZ91D镁合金在部分重熔过程中的组织演变,考察加热温度和保温时间对不同脉冲电压制备的AZ91D合金初生相形态和尺寸的影响。结果表明:经低压脉冲电场处理后,将AZ91D镁合金进行部分重熔可得到非枝晶的半固态合金,随坯料制备的脉冲电压增加,重熔时初生相变得圆整且尺寸减小,但制备坯料的脉冲电压过高,重熔时初生相尺寸有所增加;脉冲电场处理后的AZ91D镁合金坯料经适当的部分重熔处理可获得具备触变过程所需要的组织状态。     

Microstructural evolution and tensile mechanical properties of thixoformed AZ91D magnesium alloy with the addition of yttrium

The microstructure evolution of AZ91D magnesium alloy in the semi-solid state has been proposed or reported in previous literature. However, no detailed investigation has been conducted regarding the relationship between the microstructure and tensile mechanical properties of the thixoformed AZ91D magnesium alloy. In this paper, the microstructure of AZ91D alloy with the addition of yttrium was produced by the semi-solid thermal transformation (SSTT) route and the strain-induced melt activation (SIMA) route, respectively. Isothermal holding experiments investigated grain coarsening and the degree of spheroidization as a function of holding time in the semi-solid state. The SSTT route and the SIMA route were used to obtain the semi-solid feedstock for thixoforming. The results show that solid particles of the SSTT alloy are spheroidized to some extent but the previous irregular shape is still obvious in some of them. While the SIMA alloy exhibits ideal, fine microstructure, in which completely spheroidized solid particles contain little entrapped liquid. The microstructure of the SSTT alloy is less spheroidized compared with the SIMA alloy under the similar isothermal holding condition. As the holding time increases, the mean solid particle size of the SSTT alloy decreases initially, then increases, while the mean solid particle size of the SIMA alloy increases monotonously at 560 °C. Compared with the SSTT alloy, the SIMA alloy obtains finer grains under the similar isothermal holding condition. The mechanical properties of the thixoformed AZ91D alloy with the addition of yttrium produced by the SIMA route are better than those of the thixoformed alloy produced by the SSTT route. The ultimate tensile strength, yield strength and elongation for the thixoformed alloy produced by the SIMA route are 303.1 MPa, 147.6 MPa and 13.27%, respectively. The tensile properties for the AZ91D alloy with the addition of yttrium thixoformed from starting material produced by the SIMA route are better than those of the AZ91D alloy with the addition of yttrium thixoformed from starting material produced by the SSTT route.     

挤压铸造制备半固态AZ61镁合金的组织演变及力学性能(英文)

采用挤压铸造后直接二次重熔的方法制备半固态AZ61镁合金。首先通过挤压铸造预成形铸态AZ61镁合金,以获得细小的枝晶;然后在半固态区间进行二次重熔,细小的枝晶演变成球状晶,完全球化的晶粒被液相均匀包裹。研究结果表明:通过挤压铸造预成形的铸态AZ61镁合金与传统铸造预成形的铸态AZ61镁合金相比,在相同的二次重熔条件下,挤压铸造预成形的铸态AZ61镁合金获得更细小的半固态组织。此外,挤压铸造加上二次重熔触变成形的AZ61镁合金,力学性能优于传统铸造后二次重熔触变成形的AZ61镁合金。     

SSTT和RAP方法得到的ZK60镁合金的组织变化和力学性能

研究了分别由半固态热成形方法（SSTT）和部分重熔再结晶方法（RAP）得到的 ZK60镁合金在一定温度下显微组织随等温时间的变化和触变成形试样的力学性能。结果表明,合并长大机制在SSTT合金的组织变化中占主导地位,熟化机制在RAP 合金的组织变化中起主要作用。在相同的等温条件下,与SSTT方法相比,RAP方法可以得到更细小的半固态显微组织,RAP合金组织比SSTT合金组织更圆整。由SSTT方法和RAP方法得到的ZK60镁合金触变成形后均得到了较理想的成形件,触变成形工艺提高了材料的力学性能。与 SSTT 合金相比, RAP合金具有更优越的力学性能。     

Preparation of semi-solid billet of magnesium alloy and its thixoforming

Preparation of semi-solid billet of magnesium alloy and thixoforming was investigated by applying equal channel angularextrusion to magnesium alloy.The results show that mechanical properties of AZ91D alloy at room temperature,such as yieldstrength(YS),ultimate tensile strength(UTS)and elongation,are enhanced greatly by four-pass equal channel angularextrusion(ECAE)at 573 K and microstructure of AZ91D alloy is refined to the average grain size of 20μm.Through using ECAE asstrain induced step in SIMA and completing melt activated step by semi-solid isothermal treatment,semi-solid billet with finespheroidal grains of 25μm can be prepared successfully.Compared with common SIMA,thixoformed satellite angle framecomponents using semi-solid billet prepared by new SIMA have higher mechanical properties at room temperature and hightemperature of 373 K.     

流变压铸成形镁合金AZ91D的显微组织与性能

采用双螺杆机械搅拌法制备半固态镁合金浆料,对比研究了液态压铸与半固态流变压铸成形镁合金AZ91D的组织与性能,探讨了半固态成形镁合金铸件的热处理强化机制.试验结果表明,流变压铸成形铸件与液态压铸成形铸件在铸态时的力学性能相当;由于半固态成形减轻了铸件内部气孔、偏析等铸造缺陷,因而T4和T6热处理均明显地提高了半固态成形镁合金铸件的力学性能.研究还得出,液态压铸成形镁合金铸件经过固溶处理之后,其抗拉强度和伸长率也有所提高,但是,时效处理明显地恶化了铸件的力学性能.     

半固态重熔加热工艺对镁合金组织与耐蚀性能的影响

详细研究了半固态重熔加热工艺参数对AZ91D镁合金半固态组织演变及其耐蚀性的影响.结果表明:AZ91D镁合金在液固双相区进行重熔处理时,合金中低熔点共晶组织首先发生熔化并隔离α-Mg树枝晶,其后被隔离的粗大α-Mg树枝晶逐步演化成为类球晶甚至发生合并长大现象.不同半固态重熔加热工艺参数对组织演化过程影响明显.     

直流电流作用下AZ91D镁合金半固态等温处理过程中的组织演变

考察了直流电流密度、等温温度及等温时间对AZ91D镁合金半固态组织的影响，对电流影响组织演变的机理进行了探讨．实验结果表明：当等温温度和等温时间一定时，随着电流密度的增加，初生相变得圆整，初生相的尺寸有所减小．但电流密度过高时，初生相尺寸有所增加．直流电流可以加速半固态等温处理的组织演化过程，明显改善枝晶球化效果．直流电流增加扩散激活能，增大溶质原子的扩散系数，促进溶质原子的扩散，从而加速半固态等温过程的组织演化；直流电流作用下的电迁移效应、Joule热效应和Peltier效应都将促进枝晶的熔断和球化．     

超声处理半固态AZ91D组织分布规律研究

研究镁合金AZ91D在半固态下经超声处理后其微观组织的分布规律,进而研究半固态浆料形成细晶和非枝晶组织的机理。在不同的超声功率下,取一定的超声引入温度和超声持续时间,将镁合金AZ91D熔体试样在半固态状态下进行超声处理,获得了试样不同位置处的半固态微观组织。结果表明,在同一超声功率下,超声处理试样的不同位置所引起的晶粒形态和大小有很大差别,在不同功率下,相同取样位置的微观组织也有很大不同。     

流变铸轧AZ91D镁合金半固态组织演变特点

采用旋转管浇注法制得AZ91D镁合金半固态浆料,在水平双辊铸轧机上进行了流变铸轧试验研究,对铸轧前后组织的特点进行了分析比较.结果表明,铸轧可使初晶更加圆整,620 ℃浇注温度下,静置时间短,铸轧对初晶圆整化效果更加显著;铸轧后初晶尺寸略微减小,分布更加均匀;铸轧后薄板面上的初晶晶粒密度低于半固态浆料的晶粒密度,620 ℃浇注温度下,铸轧后晶粒密度显著下降.     

Microstructures of AZ91D alloy solidified during electromagnetic stirring

With the help of an electromagnetic stirring device self-made and alloy melt quenching technology, the effect of electromagnetic stirring parameters on the microstructures of semi-solid AZ91D alloy was mainly studied at the stirring frequency of 200 Hz. The experimental results show that when the stirring power rises, the primary α-Mg rosettes in the semi-solid melt will bear stronger man-made temperature fluctuation and the root remehing effect of the dendritic arms is promoted so that the spherical primary α-Mg grains become much more and rounder. If the stirring frequency is 200 Hz, the ideal semi-solid microstructure of AZ91D magnesium alloy can be obtained when the stirring power is increased to 6.0 kW. If the stirring frequency is 200 Hz and the stirring power is 6.0 kW, it is found that the lower cooling rate is favorable for the spherical primary α-Mg grains to be developed during the electromagnetic stirring stage. If the AZ91D magnesium alloy billet prepared during electromagnetic stirring at the stirring frequency of 200 Hz and the stirring power of 6.0 kW is reheated to the solidus and liquidus temperature region,the primary α-Mg grain‘s shape will get more spherical, so it is very advantageous to the semi-solid thixoforming process     

Sr对AZ91D镁合金半固态等温热处理后的组织的影响

通过对等温热处理温度和时间等工艺参数的控制，研究了变质剂Sr对AZ91D镁合金半固态等温热处理后组织的影响。结果表明，随着等温时间的延长，未变质处理的合金组织将由树枝晶变成近球状组织，而经Sr变质处理的合金组织将由树枝晶变成细小的球状组织，都将逐渐合并长大。等温热处理过程中，树枝晶经历了熔断、粒状化、球化和粗化。     

Preparation of AZ91D magnesium alloy semi-solid billet by new strain induced melt activated method

1 Introduction AZ91D magnesium alloy has received more attention due to its high specific strength, specific rigidity and good dimensional stability and so on[1]. Thixoforming is one of the best methods with regard to forming AZ91D magnesium alloy compone…     

Mg-Al系镁合金半固态坯料制备及触变挤压研究

采用拉伸试验机、金相显微镜和等径道角挤压等试验方法对Mg-Al系镁合金半固态坯料制备及触变挤压过程进行了研究.结果表明,等径道角挤压工艺对Mg-Al系镁合金有很好的应变诱导效果.经过等径道角挤压的Mg-Al系镁合金力学性能高,晶粒细小.等径道角挤压+等温处理方法制备的Mg-Al系镁合金半固态坯的微观组织晶粒细小,球化程度高,微观组织非常均匀.生产的AZ61、AZ80、AZ91D和AM60镁合金角框零件的微观组织细小,抗拉强度分别达到306.8、308.3、299.8、321.6MPa.伸长率分别达到21.6%、28.4%、14.6%和29.6%.     

添加0.5%富铈混合稀土AZ91D镁合金半固态组织的形成

半固态浆料的固相颗粒尺寸、形态和分布主要取决于熔化过程中液相的形成与演化过程。采用添加0.5%富铈混合稀土来改善AZ91D镁合金的铸态组织,研究在半固态等温热处理中的组织演变以及非枝晶组织制备与控制的机理。结果表明:稀土合金化处理可促进初生相在等温热处理过程中由枝晶向粒状晶的转变,可获得更加细小、均匀的球状固相颗粒,并且其粗化速度较慢。半固态等温热处理过程中,整个系统处于熔化和结晶的动态平衡,铸态组织中枝晶根部高溶质浓度区或系统的温度、浓度起伏是固相颗粒内液相形成的内在和外在条件。     

Structure evolution of AZ61 magnesium alloy in SIMA process

The effect of prior compressive deformation, isothermal temperature and holding time on the structure of AZ61 magnesium alloy fabricated by strain-induced melt activation(SIMA) processing was investigated. The specimens were subjected under deformation ratios of 0%, 22% and 40% and various heat treatment time and temperature regions. The results indicate that the ideal technological parameters of semi-solid AZ61 alloy produced with non-dendrites are recommended as 22% (prior compressive deformation), 595℃ (heat treatment temperature) and 40 min(time). The as-cast AZ61 magnesium alloy isn‘t fit for semi-solid forming.     

Effect of heat treatment on microstructure and properties of semi-solid squeeze casting AZ91D

Semi-solid AZ91D magnesium alloy billets were prepared by near-liquidus heat holding. Semi-solid squeeze casting was conducted at 575, 585 and 595 ℃, respectively, with 1 mm·s~(-1) squeeze speed. The semisolid squeeze casting AZ91D samples were heat treated by T4(solution at 415 ℃ for 24 h) and T6(solution at 415 ℃ for 24 h + 220 ℃ for 8 h) processes, respectively. The microstructure and mechanical properties of the alloy in different states were investigated by means of OM, SEM and tensile testing machine. The results show that compared to as-cast alloy, the grain size of the semi-solid squeezed AZ91D decreased significantly, and with the increase of semi-solid squeeze temperature, the grain size of AZ91D increased. The grains of the alloy were refined by T4 treatment, and further refined by T6 treatment. T6 treatment greatly improved the tensile strength, elongation, and hardness, but did not significantly improve yield strength. After 575 ℃ squeeze casting and T6 treatment, the ultimate tensile strength(UTS) reached 285 MPa, the elongation reached 13.36%, and the hardness also reached the maximum(106.8 HV), but the yield strength(YS) was only 180 MPa. During the process of semi-solid squeeze casting and heat treatment, the matrix grain was refined and a large number of precipitated and secondary precipitated phases of Mg_(17)Al_(12) appeared. Both the average size of matrix grain and secondary precipitated phase decreased, while the volume fraction of secondary precipitated phase increased. All these resulted in high tensile strength, elongation and hardness.     

触变模锻成形工艺对镁合金成形件力学性能的影响

采用半固态等温热处理法、近液相线模锻法和等通道角挤压法制备AZ91D—Y镁合金半固态坯料。分别将3种状态的坯料加热到半固态温度区间进行二次重熔后,进行了触变模锻成形。结果表明,在半固态温度为560℃,模锻压力为200MPa的条件下,半固态等温热处理法、近液相线模锻法和等通道角挤压法制备坯料分别保温30,20,15min后触变模锻获得最佳力学性能;随着坯料加热温度的升高,触变模锻成形件力学性能呈现先上升后下降的趋势;增加成形压力有利于触变模锻成形件力学性能的提高;在相同成形条件下,等通道角挤压法制备坯料触变模锻后的力学性能最好,近液相线模锻法次之,半固态等温热处理法较差。