活性剂对3003铝合金直流A-TIG焊的影响

对3003铝合金进行直流A-T1G焊接试验,选用卤化物NaC1、CaF2和氧化物SiO2、MnO2、TiO2作为活性剂,分别研究了单一组元和多组元表面活性剂对焊接熔深、焊缝成形以及接头组织的影响.结果表明:在进行铝合金直流TIG焊时,在焊缝表面涂敷一定成分活性剂能够增加焊缝熔深,改善焊缝质量,提高焊接生产率.总体来看,除NaC1增加熔深有限外,其余活性剂普遍增加熔深1倍以上.多组元配方活性剂增加熔深效果好于单组元活性剂,其中PS5活性剂熔深增加3倍以上,且焊缝成形良好,未见裂纹、气孔、夹渣等缺陷.分别对TIG焊和A-TIG焊接头组织进行观察,A-TIG焊较TIG焊的焊缝组织明显细小,而活性剂对焊接热影响区的平均晶粒度影响不大.     

铝合金分区活性TIG焊接法研究

针对铝合金材料,提出了一种新型活性焊接方法--FZ-TIG焊(Flux Zoned TIG Welding).在传统TIG焊接前,在待焊焊道表面中心区域涂敷低熔沸点低电阻率活性剂,在两侧区域分别涂敷高熔沸点高电阻率活性剂,然后进行正常焊接,可以同时保证焊接熔深显著增加和焊缝表面成形良好.以自行研制的FZ108活性剂进行了FZ-TIG焊,并与传统TIG焊、采用FZ108作为活性剂的A-TIG焊、采用SiO2作为活性剂的FB-TIG焊进行了对比.发现在相同参数下,采用FZ-TIG焊进行焊接,焊缝熔深明显大于传统TIG焊、A-TIG焊和FB-TIG焊,达到TIG焊熔深的3倍以上,并且焊缝成形良好,焊缝组织细化,力学性能改善.     

铸钢补焊用活性剂研制

研究了表面活性剂时铸钢TIG焊的影响,在分析各单一活性剂对焊缝熔深、表面成形影响规律的基础上,利用正交试验法对多组元配方进行了研究,得出了各组元质量百分比的变化对焊缝熔深的影响规律,w(SiO2)=40%时对焊缝熔深的影响最为显著,w(TiO2)和w(Cr2O3)在小于30%时对焊缝熔深的增加作用明显,卤化物含量较小时对焊缝熔深的增加作用明显.考虑焊缝的表面成形,得到由卤化物、SiO2、TiO2、Cr2O3等组成的铸钢A-TIG焊活性剂,可使焊接熔深增加3倍,在铸钢缺陷修复时,在缺陷表面涂敷活性剂,正常焊接规范条件下,可修复10mm以内的缺陷.     

单组分活性剂对铝合金A-TIG焊焊缝的影响

针对6 mm的6061铝合金试板,选用SiO2,TiO2,Cr2O3,CaF2,BaCl2共5种单一成分活性剂进行铝合金交流A-TIG焊工艺试验,研究活性剂对A-TIG焊焊缝表面成形及宏观形貌的影响,并结合焊接过程电弧形态变化,分析熔深增加机理.结果表明,5种单一成分活性剂均可改善焊缝熔深,其中SiO2增加焊缝熔深效果最好,CaF2效果不明显;涂覆SiO2时表面成形比涂覆其它活性剂时差,其中TiO2表面成形最好;电弧进入活性剂区时无明显收缩,认为熔深增加是活性剂的引入导致导电通道电阻变化引起的电弧热输入增加的结果.     

活性剂对镁合金交流A-TIG焊的影响

分别以单质Te,Ti和Si,氧化物SiO2,TiO2和V2O5,卤化物MnCl2,CdCl2和ZnF2作为表面活性剂进行了镁合金交流A-TIG焊,研究了活性剂对焊缝成形和组织的影响规律.Te粉,ZnF2和CdCl2都能明显增加熔深,其中Te粉使熔深达到传统TIG焊的1.6倍,焊缝深宽比达到0.43.Ti粉对焊缝熔深熔宽几乎没有影响.V2O5,SiO2,TiO2,MnCl2和Si粉都使得焊缝熔深熔宽减小.在三种明显增加熔深的活性剂中,Te粉和ZnF2都使得焊缝组织晶粒细化,而CdCl2使得焊缝组织晶粒略有粗化.结果表明,活性剂增加镁合金ATIG焊熔深主要与活性剂粒子和电子复合导致电弧收缩有关.     

SiO2增加铝合金交流A-TIG焊熔深的机理

采用单组元活性剂进行铝合金交流A-TIG(Activating flux TIG)焊时,SiO2增加熔深最明显,对其增加熔深的机理进行了研究.进行正散焦真空电子束焊试验,SiO2对焊缝成形几乎没有影响;进行系列直流正接A-TIG焊试验,研究了活性剂对电弧的影响,发现SiO2使得氧化膜厚度增加,电弧极性区收缩,弧柱区扩展,电弧电压升高;进行氦气保护交流A-TIG焊试验,发现SiO2使活性剂或金属蒸发的区域变窄且蒸发量变小,熔池表面凹陷,并且在焊接过程中SiO2涂层始终存在于熔池表面,只在熔池凹陷中央区域出现很窄的裂缝,蒸气主要集中在电弧中下部.认为电弧极性区收缩和热输入增加是SiO2增加铝合金交流A-TIG焊熔深的主要机理.     

表面活性剂对钛合金A-TIG焊熔深的影响

采用卤化物（CaF2，ZnF2，MnCl2）、氧化物（SiO2，TiO2，V2O5）和单质Te作为表面活性剂进行钛合金A—TIG焊，研究了表面活性剂对焊接熔深的影响规律。结果表明：3种卤化物都能增加焊接熔深，其中MnCl2使得焊接熔深达到传统TIG焊的2倍以上：3种氧化物对焊缝成形几乎没有影响；Te能明显增加焊接熔深，减小焊缝熔宽。认为电弧收缩是卤化物但不是Te增加钛合金A—TIG焊熔深的主要机理。     

活性剂对镁合金直流正接A-TIG焊熔深的影响

分别以单质Te,Ti和Si,氧化物SiO2,TiO2和V2O5,卤化物MnCl2,CdCl2和ZnF2作为表面活性剂进行了镁合金直流正接A-TIG焊,研究了活性剂对焊缝熔深的影响规律.Te能显著增加熔深熔宽,分别达到传统TIG焊的2.5倍和1.4倍,而Ti和Si对熔深熔宽影响较小;V2O5和SiO2都使得熔深熔宽同时增加,其中SiO2增加熔深熔宽效果最明显,分别达到传统TIG焊的2.0倍和1.6倍,而TiO2对熔深熔宽影响较小;ZnF2,CdCl2和MnCl2都使熔深熔宽显著增加,其中ZnF2的熔深熔宽增加最明显,分别达到传统TIG焊的4.0倍和1.6倍.认为活性剂增加镁合金直流正接A-TIG焊熔深主要与活性剂收缩电弧所导致的热输入增加有关.     

奥氏体304不锈钢A-TIG焊活性剂研制

A-TIG焊是一种采用活性剂来增加焊缝熔深的高效TIG焊接技术。与常规TIG焊相比,A-TIG焊具有焊接效率高、焊缝质量好及成本低等优点。本文先对各氧化物单一组元活性剂对焊缝熔深的影响进行研究,然后采用正交试验设计的方法,以获得符合熔深要求的配方,最后进一步优化活性剂配方,以满足焊缝其他性能要求,如表面成形、显微组织、铁素体含量及硬度。试验结果表明,进行A-TIG焊试验可以一次性焊透8 mm厚的304不锈钢板,同时获得外观良好的焊缝,并能满足其他性能要求。     

铸造镁合金A-TIG补焊工艺分析

文中研究了TIG、A-TIG焊接方法对铸件焊缝熔深和缺陷的影响规律,并完成模拟铸件孔洞类缺陷的补焊试验.结果表明,在TIG与A-TIG对不同尺寸孔洞愈合的试验中,在相同的焊接参数条件下,A-TIG愈合孔洞的深度明显高于TIG,且焊缝中无焊接缺陷;在相同的补焊熔深条件下,TIG焊接电流远大于A-TIG,同时出现热影响区（HAZ）组织恶化,焊接缺陷产生.分析表明,A-TIG补焊工艺性能优于TIG补焊工艺性能主要是由于活性剂与电弧、熔池的相互作用导致.     

胫骨生物陶瓷复合材料的微结构增韧机理

扫描电镜观察显示胫骨是一种由羟基磷灰石和胶原蛋白组成的自然生物陶瓷复合材料.羟基磷灰石具有层状的微结构并且平行于骨的表面排列.观察也显示这些羟基磷灰石层又是由许多羟基磷灰石片所组成,这些羟基磷灰石片具有长而薄的形状,也以平行的方式整齐排列.基于在胫骨中观察到的羟基磷灰石片的微结构特征,通过微结构模型分析及实验,研究了羟基磷灰石片平行排列微结构的最大拔出能.结果表明,羟基磷灰石片长而薄的形状以及平行排列方式增加了其最大拔出能,进而提高了骨的断裂韧性.     

Prospects of the Use of Synergetic Approach to Solution of Problems of the Science of Nanomaterials

A synergetic approach to solution of problems of self-controlled synthesis of nanostructures and creation of self-organizing nanotechnologies is considered in connection with the superproblem of creation of materials with functional properties resembling those of biosystems. __________ Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 7, pp. 55 – 61, July, 2005.     

Kinetics of the oxidation of metals — Influence of self-diffusion of metal

The importance of the self-diffusion of a metal during its oxidation by a gas is treated for the cases of nonstoichiometric oxides having either interstitial cation or cation vacancies. We have established a general relationship for the reaction rate when a mixed diffusion process occurs. From this relationship, we have shown that the pressure dependence can be different, according to whether the rate-determining process is the self-diffusion through the metal or through the product.     

Features of formation of the structure in production of blanks of disks of heat-resistant nickel alloys

Conclusions To provide a high level of mechanical properties in wrought blanks of cast ÉP741NP and ÉP962 alloys it is necessary to form controlled structures. A necklace-type structure formed in homogenizing isostatic treatment, subsequent thermomechanical working including alternation of the operations of deformation in the (+)-area and recrystallization anneals, and final heat treatment is preferable. The temperature conditions of all stages of thermomechanical working are strictly controlled, especially the final operation of deformation and heating for hardening. To eliminate hardening cracks and distortions it is necessary to use molten salts at t=600°C as quenchants. The use of multiple production operations makes it possible to significantly reduce the structural inhomogeneity related to inhertance of the original dendritic structure. However, the structure of the final semifinished product is nevertheless characterized by a difference in occurrence of the processes of polygonization and recrystallization between the former dendritic cells and the interdendritic spaces in deformation and heat treatment.To obtain structurally homogeneous blanks for gas turbine engine parts it is necessary to use basically new methods of remelting such as vacuum double electrode remelting and electron beam remelting with an intermediate vessel.Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 12, pp. 25–29, December, 1991.     

Ab-initio calculation of enthalpies of formation of intermetallic compounds and enthalpies of mixing of solid solutions

A large number of ab-initio calculations of energies of formation of intermetallic compounds have been performed in the last 15 years. The currently used methods are listed. The paper presents a review of the aluminium based compounds which have been studied. Comparisons of calculated and experimental enthalpies of formation are provided for aluminim-3d and-4d transition metal alloys at equiatomic composition. The modelling of the enthalpies of mixing of solid solutions based on a given lattice is described.     

试论洋务派教师聘任的思想

洋务派在洋务学堂的办学活动中,为了解决西学专业学科的教学困难,采用了聘请外籍教师的应急措施.他们以真才实学,合同制管理作为主导思想,并认为这种解决师资的途径只是权宜之计,并非久远.从客观上看,洋务派的教师聘任思想有深刻的历史影响.