载银沸石抗菌剂的性能及其对纸张性能的影响

研究了自制的载银沸石抗菌剂对大肠杆菌的抗菌性能,及其浆内添加应用时对纸张白度、强度等物理性能的影响。抗菌实验表明:载银沸石抗菌剂对大肠杆菌(ATCC8739)的MIC和MBC分别为5×10-8g/ml和1×10-7g/ml;在较低用量下对强度影响可以忽略,白度略微降低,能够同时满足抗菌与纸张性能的需要。     

载银抗菌沸石对涂布抗菌纸性能的影响

研究了载银抗菌沸石在纸张表面涂布中的应用及其用量对涂布抗菌纸性能的影响,采用电子探针微区分析(EPMA)和原子力显微镜(AFM)对涂布抗菌纸表面涂层结构进行分析。结果表明,载银抗菌沸石可使纸张具有非常好的抗菌效果且对纸张色调、色差、印刷适性及表面微观结构没有明显影响,但白度略微降低。     

鞋用缓释型载银沸石抗菌剂的制备与抗菌性能初探

详细分析了液相离子交换制备方法中AgNO3 溶液的浓度、反应温度、pH值等反应条件对载银沸石含银量的影响,利用抑菌圈试验法分析了载银沸石抗菌剂对大肠杆菌和金黄色葡萄球菌的抗菌性能     

杉木地板的抗菌特性研究

通过抑菌圈法比较了5种纳米抗菌剂的抗菌性能,优选出载银磷酸锆为效果较好的抗菌剂。通过分散度法,优选出六偏磷酸钠为效果较好的分散剂,并确定其最佳的加入量为纳米抗菌剂质量分数的1%。对杉木地板基材表面进行抗菌处理,通过贴膜法检测抗菌性能发现:当载银磷酸锆抗菌剂在涂料和MF中的加入量分别为1%和0.6%时,制备的抗菌杉木地板基材的抗菌率≥90%,有抗菌作用;当加入量分别为1.5%～2%和0.8%～1%时,抗菌杉木地板基材的抗菌率≥99%,有强抗菌作用。     

载银甲壳素纤维的制备与抗菌性能研究

将羟基功能化纳米银应用于载银甲壳素纤维的制备,利用分光光度法研究了甲壳素纤维对羟基功能化纳米银的吸附性能和吸附机理;测试了不同银含量载银甲壳素纤维的抗菌性能;采用扫描电镜(SEM)和光电子能谱(XPS)对载银甲壳素纤维的微观形貌和元素成分进行了分析。研究结果表明,甲壳素纤维对羟基功能化纳米银具有较高的吸附能力,最高吸附量可达3 390 mg/kg;纳米银颗粒在甲壳素纤维表面分布均匀,且未被氧化;另外,抗菌测试结果表明载银甲壳素纤维具有优异的抗菌性能,当银含量达到1 000 mg/kg时,其对E.coli和S.aureus的抑菌率均可达99%以上。     

银系纤维及其抗菌性能的研究进展

银系纤维在抗菌性能方面具有抗菌效果好、性能持久的特点。文章综述银系纤维的制造方法、抗菌机理、安全性方面的研究现状,指出了适合银系纤维抗菌性能评价的测试方法,同时也对银含量与抗菌性能的关系,影响银系纤维抗菌持久性的因素进行了探讨。已有成果表明银系纤维产品是一种安全、高效、持久的抗菌产品,具有良好的市场前景。     

载银沸石在鞋材抗菌整理中的应用

采用不同的分散时间、不同的分散剂用量和pH值,对载银沸石抗菌剂的分散性进行了较系统的探讨,利用Zeta电位、黏度、沉降法以及扫描电子显微镜对分散情况进行表征.同时,对分散体系进行了应用实验和抗菌检测.结果表明,分散时间、分散剂用量和pH值都是影响载银沸石分散效果的重要因素;经整理后的抗菌鞋里对大肠杆菌和金黄色葡萄球菌的杀菌率均达100%.     

钼酸银抗菌纸的制备及其抗菌性能

制备钼酸银抗菌纸,并对其抗菌性能进行研究。抗菌剂采用表面喷涂和浆内填加两种方式与纸浆纤维结合;选择大肠杆菌、黑曲霉菌、金黄色葡萄球菌三种代表性菌种检测其抗菌性能。研究结果表明:钼酸银抗菌纸对以上三种菌种均具有一定的抑制效果,对金黄色葡萄球菌的抗菌效果最为明显;随钼酸银浓度升高,抗菌效果增强;随时间延长,对霉菌抗菌效果减弱,但对大肠杆菌、金黄色葡萄球菌抗菌效果下降不明显。     

载银活性炭纤维的制备及应用性能

以粘胶纤维、烷基化环糊精和硝酸银为原料,采用原位还原法制备载银粘胶纤维,再经炭化、活化制备了银含量约为2 200 mg/kg的载银活性炭纤维。结果表明,该载银活性炭纤维具有优异的抗菌性能,对白念珠菌（ATCC10231）、金黄葡萄球菌（ATCC6538）的抗菌率达到99%以上;具有优异的抗菌耐久性能,超声波清洗50次后,载银活性炭纤维的银含量未见明显下降;体外细胞毒性检测结果表明,载银活性炭纤维体外细胞毒性为1级,无明显的细胞毒性,体现了优异的生物安全性能。     

壳聚糖载银抗菌纱的制备及性能初探

涤纶丝广泛用于抗菌纱和织物的制备。近年来,许多抗菌物质逐渐商业化,替代抗菌物质已成为抗菌纱加工研究的重要目的。大多数抗菌物质是通过直接浸泡或涂层的方式加载在抗菌纱上的。研究旨在通过二浸二压的纺织品整理工艺,将壳聚糖载银溶液固定到涤纶纱线上。通过扫描电子显微镜分析了纱线涂层前后结构的变化,并测试了其对金黄色葡萄球菌和大肠埃希菌的抗菌性能。试验结果表明,经壳聚糖载银溶液涂层处理的涤纶纱线均具有较好的抗菌性能,且试样R-3具有更优的抗菌效果。     

负载银纳米簇功能纸的制备及其抗菌性能研究

银纳米簇具有优越的荧光发射及抗菌活性,如将其负载在纸上,可赋予纸发光及抗菌性能。本研究通过在漂白硫酸盐桉木浆上接枝聚丙烯酸,然后利用光诱导还原银离子的方法在纸浆上原位合成银纳米簇,最后抄造成纸张,实现银纳米簇在纸上的负载。在合成银纳米簇过程中,修饰到纤维素上的羧酸根起到了螯合剂、模板剂和还原剂等三重作用。荧光光谱分析表明,制得的负载银纳米簇纸浆具有荧光发射性能,其最优激发波长为355 nm,发射波长为555 nm,且成纸后的荧光发射性得以保留。负载银纳米簇后纸张白度略有降低,当负载银纳米簇纸浆含量为10%时,纸张抗张指数最优为39.3 N·m/g。抑菌实验表明,所得纸张具有良好的抗菌性能,其抗菌圈直径为14mm。     

纸张涂料流变性能的研究方法

介绍了用于分析纸张涂料流变性能的研究方法，涂料的静态流动性能和动态粘弹性分别可以用表观粘度和动态粘弹参数等物理量进行表征，并通过实验说明了测量方法和评价标准。结合表观粘度与模量参数，能够准确地衡量纸张涂料的流变性能。     

PLA基纳米结构银薄膜的抗菌性能

在低温条件下,利用磁控溅射技术,在聚乳酸非织造布表面沉积不同厚度的纳米结构银薄膜,研究PLA基纳米结构银薄膜厚度对样品抗菌性能的影响。采用振荡烧瓶法测试样品的抗菌性能,利用原子力显微镜(AFM)分析纳米结构银薄膜表面形态及粒径,应用EDX分析薄膜表面的元素分布。结果表明:随着薄膜厚度的增大,样品抗菌性能提高;溅射时间延长,薄膜厚度增大,膜层的致密性改善,单位面积上的银含量增加,膜层表面积增大,银离子释放几率增大,是提高抗菌性能的主要原因;当纳米结构银薄膜厚度为1 nm时,对大肠杆菌和金黄色葡萄球菌的抑菌率均达到100%。     

新型流变改性剂改善高固含量涂料的流变性

高固含量涂料有很多优点,但提高涂料固含量会因涂料流变性恶化而导致运行方面问题,传统的碱性膨润流变剂不利于改善高固含量涂料的流变性。新型流变剂克服了传统流变剂的缺点,在高固含量涂料上表现出超低的高剪切黏度,流变问题得到改善,具有很好的应用前景。     

Preparation of Ultrafine Starch Particle and its Application in Paper Coating

Despite its biodegradability, adequate cohesive strength and comparatively low cost, the use of cooked starch as a paper coating binder is limited due to its high viscosity and serious negative impact on the gloss. Starch-based bio-latex with size in the nanometer or sub-micrometer range has been developed recently to overcome these shortcomings. In this study, ultrafine starch particle (UFSP) was prepared by mechanical milling using a DYNO mill in combination with light chemical pretreatment. Model coating colors containing different dosages of UFSP were applied to base paper and the properties of the coated papers were evaluated. The results showed that the UFSP was disc-shaped with a median particle diameter of 167 nm. Water retention capacity of the coating colors was improved considerably with the addition of UFSP, i.e., the water retention value decreased by nearly 40% when styrene-butadiene latex was replaced by UFSP at a dosage of 3 pph (per hundred parts of pigment). The high shear rate viscosities of the coating colors containing no more than 2 pph of USFP were similar to that of the control coating color at shear strain rate higher than 2000 s1. The properties and performances of the coated papers were comparable to the control coated paper with single synthesized latex binder. The gloss and the print gloss of paper samples with or without USFP were 59.7% and 58.2%, 79.0% and 78.8%, respectively. Surface strength of paper samples with or without USFP were 0.96 and 0.90 m/s, respectively, while the ink absorptivity values were 34% and 33%. This study demonstrates a promising approach to obtain sub-micrometer sized starch for paper coating.     

单一胶粘剂对涂料流变性的影响

对常用的氧化淀粉、羧基丁苯胶乳和聚乙烯醇在不同的添加量情况下配成的涂料进行了系统的研究,结果表明涂料都呈剪切稀化特性,通过对实验结果进行多次分析,认为用修改的幂律方程表达很理想。     

涂布合成纸喷墨打印性能的研究

通过对合成纸进行表面处理,增强涂料在纸张表面的附着力。实验采用单层涂布与双层涂布,并对涂布后的合成纸进行打印性能的评价。单层涂布样张中用sMA表面处理后,色密度随胶黏剂用量的增加而上升,而用PVA表面处理后,色密度随胶黏剂用量增加先上升后下降;灰阶在50％～90％范围内再现性最佳,而在90％-100％范围再现性较差;单层涂布纸样中两种样张差别不大,且都要优于双层涂布纸样的阶调再现性。     

紫苏叶保鲜纸袋的研制及其基本性能分析

为延长紫苏鲜叶货架期,保证叶片在贮藏及零售时的贮藏品质,本研究采用新研制涂膜保鲜纸袋对紫苏叶片进行包装处理。试验所用复合涂布液由壳聚糖、D-异抗坏血酸钠、茶多酚及氯化钙按照一定比例溶于乙酸水溶液配制而成,通过单因素及正交试验考察保鲜纸袋复合涂布液中不同组分浓度对紫苏叶感官品质、V_C含量及失重率的影响,确定复合涂布液最佳组分浓度配比:壳聚糖浓度2.0%、D-异抗坏血酸钠浓度2.4%、茶多酚浓度0.25%、氯化钙浓度0.6%。通过物理、化学及抑菌性能分析表明,当涂布量为30 g/m2时,复合涂布液在纸张表面形成均匀涂层,具有较强抑菌能力,且涂料渗入纸张纤维间隙内部,使得纸张重量、厚度、伸长率、水分含量皆有所提升,水蒸气透过系数下降,抗张强度及润湿性能略有下降,符合紫苏叶片包装要求,本研究预计将在果蔬包装领域具有广阔发展前景。     

彩色喷墨打印纸涂料的流变性能研究

探讨了SiO2、PVA、固色剂、辅助胶黏剂和润滑剂等对彩色喷墨打印纸涂料流变性能的影响。结果表明,SiO2分散液浓度高时,SiO2粒子间的作用增强;PVA与涂料组分形成的网络结构强度比较差;固色剂与涂料组分形成不可逆、强度高的网络结构;辅助胶黏剂具有分散剂的作用,可在一定程度上弱化涂料结构的强度;润滑剂能够提高涂料的流动性能。     

颜料涂布对再生箱纸板性能的影响

研究了GCC、高岭土及其混合颜料对涂布再生箱纸板光学性能、油墨吸收性和机械强度的影响,并在此基础上优化了涂料配方。研究结果表明：涂布箱纸板的白度不仅依赖于颜料自身的白度,而且取决于颜料的遮盖性能。在一次涂布中,高岭土和GCC的混合比例为60：40时,涂布箱纸板的白度最高。预涂及面涂涂料中GCC含量增加均可提高二次涂布箱纸板的油墨吸收性。在涂料中加入OBA可显著提高涂布箱纸板的白度。另外,经涂布加工后,箱纸板的横向耐折次数及横向环压指数均有所增加。