采用正交试验结合中性盐雾试验和极化曲线测定等方法,研究了热镀锌钢板表面的硅烷膜在制备过程中的硅烷体积分数、水解溶剂中甲醇体积分数、水解时间、水解温度、溶液pH值、浸涂时间等因素对硅烷膜耐蚀性能的影响,并确定了最佳成膜工艺,讨论了硅烷膜作用机理。结果表明:最佳成膜工艺为硅烷体积分数7%、溶液pH值4、水解溶剂中甲醇体积分数10%、水解温度40℃、水解时间6 h、浸涂时间120 s,采用该工艺制备硅烷膜可明显推迟热镀锌钢板出现白锈的时间;硅烷膜同时也抑制了热镀锌钢板在腐蚀过程中阳极和阴极的反应,显著改善了热镀锌钢板的耐蚀性能。     

磨粒固化气囊光整技术及试验研究

针对模具激光强化表面高硬度、高耐磨性以及局域硬度差异等问题,提出了一种磨粒固化气囊光整加工新技术,以期实现模具激光强化表面的高效精密自动化光整加工.该技术将处于游离态的磨粒通过高分子粘结剂固化于橡胶基体表层,使磨粒群获得更稳定的支撑,形成了更有效和平稳的切削效果.根据磨粒固化气囊的性能要求,从材料特性着手,确定出通过酸性硅酮密封胶将磨粒直接固化在丁苯橡胶基体表面,以制得磨粒固化气囊的工艺方法;借助机器人辅助加工平台,对制得的不同粘结层厚度的磨粒固化气囊进行了光整试验研究.研究结果表明:通过控制磨粒固化气囊的均匀性,加强复合层的粘结效果,可以降低工件表面粗糙度,提高加工效率,为模具高效光整加工奠定了坚实的基础.     

粘结固体润滑膜的摩擦学特性研究

采用2种不同的固体润滑粉末(石墨和二硫化钼)分别与溶剂、粘结树脂组合制得粘结固体润滑剂,涂敷于钢板表面成膜,然后对得到的粘结固体润滑膜的润滑性能、物理化学性能和耐磨性能进行了测试。结果表明:粘结固体润滑剂中的固体粉末含量越多、颗粒越细,润滑膜的润滑性能越好,但固体粉末含量的增加影响了润滑膜的干燥时间,附着力、柔韧性和耐冲击性能也变差;只有当润滑剂中加入了适量固体粉末后,得到的润滑膜的减磨效果最佳。     

高能喷丸镁合金表面磁控溅射铝膜的微观结构和耐腐蚀性能

对AZ91D镁合金基体表面进行不同时间(0,20,30,40min)高能喷丸(HESP)处理,再采用磁控溅射技术在HESP基体表面沉积铝膜,研究了铝膜的微观形貌与耐腐蚀性能。结果表明:HESP基体表面铝膜的表面组织均匀、致密,铝膜较厚,且随着HESP处理时间的延长,组织更加细小、均匀,铝膜厚度增大;经40min HESP处理后,铝膜与基体之间存在明显的过渡层,二者的结合力为16N,是未经HESP处理的3.2倍;与未经HESP处理的相比,HESP基体表面铝膜在NaCl溶液中的自腐蚀电流密度与在盐雾中腐蚀24h后形成的腐蚀坑深度均较小,且随着HESP处理时间的延长,自腐蚀电流密度与腐蚀坑深度均减小,铝膜的耐电化学和耐盐雾腐蚀性能显著提高。     

铝硅聚苯酯封严涂层切向载荷作用下应力分布的有限元分析

在封严涂层弹性模量试验的基础上,建立封严涂层摩擦有限元模型,对民航发动机铝硅聚苯酯封严涂层的摩擦过程进行有限元分析。分析了摩擦系数、涂层厚度和粘结层厚度等参数对涂层/粘结层/基体系统应力分布的影响。分析结果表明:在切向载荷的作用下,随着摩擦系数的增大,涂层表面、涂层与粘结层的界面以及粘结层和基体界面处的应力峰值均增大;随着涂层厚度的增大,涂层表面及两界面处的应力峰值均减小,但当涂层厚度达到一定程度后,继续增加涂层厚度对降低应力峰值的效果不明显;粘结层厚度在一定范围内的变化对涂层表面和涂层与粘结层界面处的应力变化影响不大,但随着粘结层厚度的减小,粘结层与基体界面处的应力峰值均增大。     

环保型锌铝基耐蚀涂层的制备与性能

以硅烷为粘接剂、片状锌铝粉为原料,在20钢基体上制备了无铬的环保型锌铝基耐蚀涂层,以替代传统的含铬达克罗涂层;用X射线衍射仪、扫描电子显微镜对涂层的成分和结构进行了表征,用开路电位、电化学阻抗谱测试和盐雾试验研究了涂层的电化学和耐腐蚀性能。结果表明:无铬锌铝基耐蚀涂层的耐蚀性能与达克罗涂层几近相同;硅烷偶联剂在涂层中主要起粘结作用,涂层中片状锌铝粉分布均匀,层层堆叠;涂层对基体具有牺牲阳极保护和屏蔽作用,增加涂层厚度可增强涂层的屏蔽作用。     

一种新型改性树脂固化剂的研制

研究了硅酸酯对有机胺固化剂的化学改性反应，制备了一种适用于环氧-有机硅树脂的新型固化剂，并对改性产物的结构与性能进行了研究，结果表明，此种固化剂不仅改善了环氧-有机硅树脂的室温固化性及树脂固化膜的表面疏水性，而且很大程度上提高了该种树脂对金属基体的附着强度。     

表面粘贴式FBG传感器应变传递分析

6层光纤布拉格光栅传感器由光纤、保护层、粘结层、衬底、外粘结层、基体组成,基体与光纤不直接接触,所以测量精度取决于光纤和基体之间的粘结特性。提出基体到光纤应变传递的函数模型,然后利用有限单元法验证函数模型的正确性,最后,基于该函数讨论中间层参数对平均应变传递率的影响。文中的分析结果满足FBG传感器测量精度要求。     

溅射羟基磷灰石薄膜与钛合金基体结合强度的研究

采用射频磁控溅射法，在Ti-6Al-4V合金基体上制备了羟基磷灰石(HA)及HA和TiO2复合薄膜。通过显微压入法及粘结拉伸法，定量及定性分析了涂层与基体之间的结合强度，重点探讨了涂层在热处理前后结合强度的变化规律。结果表明，几种材料膜-基结合强度均达到15～20MPa，完全满足生物涂层材料的使用性能要求。     

0Cr18Ni9Ti不锈钢表面渗锆合金层的耐腐蚀性能及抗高温氧化性能

采用双辉等离子渗金属技术在0Cr18Ni9Ti奥氏体不锈钢表面制备渗锆合金层,然后将其分别置于在0.5mol·L-1 HCl溶液、3.5%NaCl溶液、0.5mol·L-1 NaOH溶液中进行电化学腐蚀试验,另在静态空气中进行了1 000~1 150℃的高温氧化试验,研究了渗锆合金层的耐腐蚀性能及抗高温氧化性能,并与不锈钢基体进行了对比。结果表明:在三种溶液中,不锈钢基体的相对腐蚀速率分别为渗锆合金层的24.43倍、2.44倍、1.90倍,不锈钢基体表面发生了较为严重的腐蚀,而渗锆合金层只出现了局部腐蚀坑,这是因为在腐蚀过程中其表面形成了一层致密的ZrO2钝化膜;不锈钢基体和渗锆合金层的氧化质量增加曲线都基本遵从抛物线规律;在1 150℃氧化20h后,不锈钢基体表面氧化严重,而渗锆合金层的表面形貌较好,存在少量孔洞,组织相对致密。     

黏结剂组元对固体润滑涂层性能的影响

固定石墨、MoS2含量,通过改变黏结剂环氧树脂E54、酚醛环氧树脂F44的比例,设计配比几种黏结固体润滑涂层配方。基体黏结剂热失重分析试验可知,温度超过250℃以后,基体黏结剂开始缓慢分解,温度升高至300℃左右时热分解速度加快,热失重迅速增大,F44的添加可以提高E54环氧树脂的耐热性能。不同载荷条件下黏结固体润滑涂层的摩擦磨损结果表明:黏结剂组元中F44的比例过高或过低都不利于涂层承载能力的提高,当黏结剂组元中F44与E54的比例为3∶2时,黏结涂层体现了较好的摩擦学特性和最高的承载能力。     

全自动钉排涂胶机的设计

主要介绍用于建筑装璜业的钉排加工的自动涂胶机的结构设计。该涂胶机可以完成自动上料、双面刷胶、自动输送、切断的全部功能,是一个自动化程度较高的生产设备。该设备的应用可以提高生产效率、提高产品质量,减少污染,对于该行业生产水平的提高有很大的实际意义,也填补了该技术领域的缺欠。     

粘接结构的超声检测技术及其进展

粘接结构由于具有优越的性能被广泛应用于多个领域.超声检测方法能够有效地解决粘接界面粘接质量的无损检测.本文结合粘接结构自身的特点,介绍了应用于多层金属-非金属粘接结构的超声检测方法、信号分析方法及相关检测技术进展,并就多层金属-金属粘接界面的超声检测提出一点设想.     

刀具对胶粘带产品加工品质的影响

介绍了胶带由半成品到最终产品的加工方式及采用的刀具种类；分析了如何选用刀具，以及刀具的角度、宽度、安装、调整等对加工品质的影响。     

Does laser etching have an effect on application mode of a universal adhesive?—A microleakage and scanning electron microscopy evaluation

This study aimed to evaluate the microleakage of a universal adhesive's different application modes incorporated with Er,Cr:YSGG laser on Class V resin composite restorations. Sound human molar teeth (n = 30) were used for microleakage evaluations. Specimens with 60 standardized Class V cavities were divided into five groups according to the adhesive modes of universal adhesive, Adhese Universal (n = 12). Group 1‐etch‐and‐rinse mode with phosphoric acid; Group 2‐etch‐and‐rinse mode with Er,Cr:YSGG laser; Group 3‐selective‐etch mode with phosphoric acid; Group 4‐selective‐etch mode with Er,Cr:YSGG laser; Group 5‐self‐etch. After restorations were performed with a resin composite, Tetric N‐Ceram, the specimens were polished and subjected to thermocycling (10,000X). Following immersion in 0.5% basic fuschin for a day, the teeth were sectioned and the degree of microleakage was determined along the tooth‐resin composite interface using a light microscopy(40X). Five specimens from each group were examined by scanning electron microscopy. The Kruskal–Wallis, Siegel Castello, and Wilcoxon tests were used for statistical analyses (α = .05). At the enamel margins, significant differences were obtained among the groups (p < .05). Significantly higher microleakage scores were detected in Group 5 in comparison with Groups 1, 2, and 3. There were no significant differences between different adhesive strategies at the dentin margins (p > .05). While analyzing enamel and dentin microleakage scores, no statistically significant differences were observed in Groups 4 and 5 (p > .05). The laser application time and the adhesive modes of universal adhesives could affect the microleakage at the enamel margins. Different adhesive modes of universal adhesives combined with laser etching had no influence on the microleakage scores of dentin margins.     

胶层缺陷对胶接-拉铆搭接剪切接头力学性能影响研究

近年来胶接-拉铆技术在载运工具和航空航天等领域得到了广泛应用,而大型结构连接部件的制备过程会不可避免地在胶层内部产生局部缺陷,进而影响接头服役性能。以胶接-拉铆单/双搭接接头为研究对象,通过在胶层区域设置不同形式的人工缺陷,模拟胶层制备过程中产生的胶层内部缺陷,研究其对胶铆接头搭接剪切力学性能的影响规律。以6061-T6铝合金为基底制备胶接-拉铆接头试件,考虑单、双搭接试件形式,胶层内部预先放置不同厚度、面积、形状、位置的聚四氟乙烯缺陷片,对固化后的接头进行准静态拉伸破坏试验,并采用宏观观测和扫描电镜分析胶层失效表面宏观和微观样貌,从而对胶层内部缺陷对其失效模式影响机理进行评价。试验结果表明,接头主要失效模式为内聚失效,胶层中缺陷的位置、面积、厚度会对接头失效载荷以及失效强度产生不同程度影响,而缺陷的形状对接头力学性能影响不大。无缺陷的双搭接试件胶层失效载荷是单搭接试件1.62倍,单搭接试件胶层失效强度是双搭接试件1.24倍。有圆形缺陷的双搭接试件失效载荷是单搭接试件2倍,而失效强度没有受较大影响。基于现有试验结果,可以为实际结构设计中含胶层缺陷胶铆复合接头失效强度提供有效评估方法。     

反射镜无热装配中胶层厚度的计算及控制

为了实现空间遥感器反射镜无热装配,对反射镜粘接镶嵌件时胶层厚度的计算及控制胶粘厚度的方法进行了研究。首先介绍了工程中常用的计算反射镜无热装配胶层厚度的方法及胶层厚度控制工艺,主要描述了工装保证法、精密测量法和工装测量结合法,给出了各种方法的优缺点及局限性。针对目前胶粘工艺控制胶层厚度存在的问题,提出采用具有不同直径规格的空心玻璃微珠来控制胶层厚度的方法。拉伸试验验证了添加了空心玻璃微珠的光学环氧胶比纯光学环氧胶的力学性能提升了20%;利用平面反射镜粘接镶嵌件的试验表明,依靠填充空心玻璃微珠保证胶层厚度的胶粘工艺方法能够保持反射镜面形值,同时证明了胶层计算方法可以应用于空心玻璃珠的直径选择。提出的胶层厚度计算方法及玻璃微珠胶粘工艺可以实现反射镜无热装配,目前已应用于某在研项目。     

胶层固化对反射镜面形影响的仿真与试验

研究了用厚胶层进行光学零件之间的黏结操作时,胶层固化后其收缩力对反射镜面形的影响。首先,分析了胶层固化过程中胶层对光学元件产生拉应力的原理,找到了胶层固化过程中产生收缩力的主要因素。其次,建立了反射镜胶结组件的有限元模型,采用等效热变形法仿真分析了胶层收缩对反射镜面形的影响,分析发现胶层的等效线胀系数不能直接采用收缩率代替,而将材料的收缩率转换为胶层的等效线胀系数后,分析结果与试验结果吻合较好。最后,提出了减小胶层收缩对反射镜面形影响的改进方案。试验结果表明:黏胶方案改进后,胶层固化过程中的收缩力引起反射镜中心区域鼓包的PV值从0.574λ减小为0.064λ,镜面面形均方根值从0.127λ减小为0.038λ,这些结果显示胶层固化过程中产生的收缩力对反射镜面形的影响得到了显著改善。     

Comparison of microtensile bond strength and resin–dentin interfaces of two self‐adhesive flowable composite resins by using different universal adhesives: Scanning electron microscope study

The aim of this in‐vitro study was to evaluate microtensile bond strength (μTBS) of two different self‐adhesive composites (SACs) on the permanent dentin by applying five different universal adhesive systems. In this study, two different SACs [Vertise Flow (VF), Fusio Liquid Dentin (FLD)] and five different bonding systems [Clearfil Universal Bond Quick (CUB), Single Bond Universal (SBU), All Bond Universal (ABU), Prime Bond Universal (PBU), Futurabond U (FBU)] were used. A total of 22 groups were created in which SACs were applied without adhesive and with five different universal bonding agents in total‐etch (TE) and self‐etch (SE) modes. Two hundred and forty test sticks were obtained using 48 healthy human molar teeth in total with groups having 10 samples each. The μTBS test was applied to each sample in the Universal test device and the data obtained were analyzed statistically by variance analysis and Tukey HSD test. In addition, the resin–dentin interface and fractures modes in the groups were examined by SEM. Upon examining the μTBS results, the highest values were seen in the use of SBU adhesive in TE mode in VF group, while the lowest values were seen in the FLD control group. The difference between the control and experimental groups was found statistically significant (p < .05). Upon comparing the control groups with each other, it was seen that VF group had higher μTBS values than FLD group and the difference between the groups was found statistically significant (p < .05). The μTBS results and SEM images of the study showed that the use of SACs with universal adhesive systems provides a more effective bond strength.