Mechanical properties,corrosion resistance,and rubber pad forming of cold differential speed-rolled pure titanium for bipolar plates of proton-exchange membrane fuel cells

Due to problems such as pores on surface-treated coatings, the corrosion resistance of pure titanium bipolar plates for proton-exchange membrane fuel cells can be further improved by increasing the corrosion resistance of pure titanium by using differential speed-rolling (DSR); however, these materials have not yet reached the standard requirements of bipolar plates (corrosion current density i_corr＜10³ nA·cm^?2). In this work, the corrosion resistance of pure titanium was improved by optimizing the DSR process while the strength was maintained. The best corrosion resistance of the DSR pure titanium was achieved when the roller speed ratio was 2, while i_corr was 429 nA·cm^?2 in a solution of 0.5 M H₂SO₄ and 2 mg/L HF at room temperature. The formability of the DSR pure titanium for bipolar plates was verified. The optimal holding pressure range was 6.8–7.0 kN.     

磨料有序排布电镀砂轮的制备及其把持力研究

为解决电镀砂轮磨削加工中容屑空间不足的问题，采用点胶微粘接的方法制备了磨料有序排布的电镀砂轮，分析了磨料粘接效果和镀层力学性能。通过SEM分析了磨料/镀层/导电胶的结合界面，并进行了干磨削试验。研究结果表明，直径约为磨料粒径40%的胶点可粘接住磨料，单个胶点上粘接多颗磨料的占比小于6%；双脉冲电镀工艺制备的镀层显微硬度大于500HV，表层残余应力小于100MPa，磨料/镀层/导电胶之间的界面贴合紧密，无明显缺陷；砂轮在磨削时没有出现磨料脱落现象。     

[Zr0.73(Cu0.59Ni0.41)0.27]87Al13合金过冷液相区热塑性成形研究

为探究[Zr_(0.73)(Cu_(0.59)Ni_(0.41))_(0.27)]_(87)Al_(13)非晶合金的热塑性成形性能以及绘制其对应的热加工图谱,用Gleeble3500型热模拟压缩实验机对该非晶合金进行不同参数下的热模拟压缩实验。结果表明,合金在压缩过程中变形行为由牛顿流变演变为非牛顿流变;同时,过高或过低的热加工温度均能导致合金晶化;进一步对数据分析得到该合金在不同热塑性成形参数下的功率耗散图与流变失稳图,并绘制出相应的热加工谱图,谱图分析结果表明,该合金在温度为420与430℃、应变速率为10~(-3) s~(-1)时具有较高功率耗散系数且没有失稳区域,因此,合金可选的热塑性加工参数为温度420～430℃,应变速率10~(-3) s~(-1)。     

M1080B无心外圆磨床改进

M1080B无心外圆磨床砂轮及导轮宽度较窄,磨削轴承套圈外圆时,磨削效率低,托板架调整较为繁琐、皮带打滑、磨损较为严重。针对上述问题,提出了相应的解决办法,提高了磨削效率。     

An efficient manufacturing method for I-shaped cross-sectional CFRP beam with arbitrary arrangement of carbon fiber using electro-activated resin molding

Abstract

The I-shaped cross-sectional beam of CFRP (CFRP I-beam) is usually manufactured by the continuous protrusion method. Carbon fibers can only be arranged in the longitudinal direction. The CFRP I-beam with arbitrary arrangement of carbon fiber was manufactured with applying the electro-activated deposition molding method. The carbon fiber fabric was immersed in the deposition solution and energized, epoxy resin precipitated around carbon fiber and impregnated. The resin-impregnated fabric was installed to the mold, and the CFRP I-beam was fabricated. The CFRP I-beam was subjected to three-point bending tests, and the relationship between load-deflection was simulated by finite-element analysis.     

埋地管道泄漏内封堵装置设计与研究

针对流体输送埋地管道泄漏问题,设计了一种利用管道机器人携带封堵气囊进行快速应急封堵修复的埋地管道泄漏内封堵装置。采用矩阵变换方法建立了牵引系统驱动轮过弯方程,利用MATLAB软件对过弯方程进行了验证,同时利用ADAMS软件仿真分析过弯路径与驱动轮转角对牵引系统行走速度的影响。研究结果表明:由两个串联封堵器组成的应急封堵系统可满足复杂工况下的管道泄漏封堵要求;牵引系统驱动轮在弯管内部行走时,单轮速度呈周期性变化,但三个驱动轮整体周期运动特性一致;驱动轮转角在25°~40°时,牵引系统行走速度与驱动轮转角成正比,且转角为30°时驱动效果最好。该内封堵装置的结构设计可为管道泄漏应急封堵领域装备的研发提供重要参考。     

Effect of grinding-induced cyclic heating on the hardened layer generation in the plunge grinding of a cylindrical component

This paper discusses the effects of the grinding-induced cyclic heating on the properties of the hardened layer in a plunge cylindrical grinding process on the high strength steel EN26. It was found that a multi-pass grinding brings about a uniform and continuous hardened layer along the circumference of the cylindrical workpiece. An increase of the number of grinding passes, leads to a thicker layer of hardening, a larger compressive residual stress and a deeper plastic deformation zone. Within the plastic deformation zone, the martensitic grains are refined by the thermo-mechanical loading, giving rise to a hardness of 12.5% higher than that from a conventional martensitic transformation. The coupled effects of heat accumulation and wheel wear in the multi-pass grinding are the main causes for the thickening of the hardened layer. A too small infeed per workpiece revolution would result in insufficient grinding heat, and in turn, bring about an undesirable tempered hardened layer and a reduction of its hardness.     

Bulging in incremental sheet forming of cold bonded multi-layered Cu clad sheet: Influence of forming conditions and bending

Bulge is a defect that causes geometrical inaccuracy and premature failure in the innovative incremental sheet forming (ISF) process. This study has two-fold objectives: (1) knowing the bulging behavior of a Cu clad tri-layered steel sheet as a function of forming conditions, and (2) analyzing the bending effect on bulging in an attempt to identify the associated mechanism. A series of ISF tests and bending analysis are performed to realize these objectives. From the cause-effect analysis, it is found that bulge formation in the layered sheet is sensitive to forming conditions in a way that bulging can be minimized utilizing annealed material and performing ISF with larger tool diameter and step size. The bending under tension analysis reveals that the formation of bulge is an outgrowth of bending moment that the forming tool applies on the sheet during ISF. Furthermore, the magnitude of bending moment depending upon the forming conditions varies from 0.046 to 10.24 N·m/m and causes a corresponding change in the mean bulge height from 0.07 to 0.91 mm. The bending moment governs bulging in layered sheet through a linear law. These findings lead to a conclusion that the bulge defect can be overcome by controlling the bending moment and the formula proposed can be helpful in this regards.     

东营凹陷王庄-宁海地区流体包裹体分析与流体充注研究

利用流体包裹体分析技术，系统地分析了东营凹陷王庄-宁海地区覆盖所有含油层位的流体包裹体样品。包裹体荧光观察和均一温度特征分析揭示了包裹体发育期次为5期，说明该区油藏存在5次流体充注过程；据此确定了备期烃类的成藏期次。东营组沉积时期和明化镇组沉积末期的油气运聚均在成藏后遭受大气淡水淋滤和降解作用。沙三段原油可能经历至少2期稠油化作用。荧光观察进一步证实该区主要发生2期充注、2期成藏。     

柳沟庄—窟窿山油藏储集层裂缝类型及特征

根据岩心描述、薄片观察、X－CT扫描以及钻井、测井等资料，研究了酒西盆地青西坳陷柳沟庄－窟窿山油藏裂缝性储集层的类型及特征，分析了控制裂缝发育的地质因素及裂缝对油气的控制作用，认为储集层裂缝有3种基本类型，即构造裂缝、构造熔蚀缝和饼状破裂，主要受构造应力场及构造位置等因素的控制。根据裂缝形态、充填特征及其相互关系，裂缝的形成主要有3个期次，其中喜马拉雅运动晚期形成的第三期理解缝对油气运移和聚集最有效。研究结果表明，裂缝是柳沟庄－窟窿山油藏主要的储集空间和控制油气富集的因素。