Activation of LSCF–YSZ interface by cobalt migration during electrolysis operation in solid oxide electrolysis cells

High-temperature water electrolysis through solid oxide electrolysis cells (SOEC) will play a key role in building a hydrogen economy in the future. However, the delamination between the air electrode and the electrolyte remains a critical issue to be addressed. Previously, it was hypothesized that Co migration may improve the catalytic activity of the SrZrO₃ second phase at the LSCF-YSZ interface, eventually leading to the delamination. In this work, the LSCF-YSZ interfaces sintered at different temperatures were examined in detail. The activation behaviors of the LSCF electrodes upon application with electrolysis current were characterized under different conditions. Further, samples containing purposely added SrZrO₃ interlayer with and without cobalt were fabricated and compared. The activation process is less significant for the sample with cobalt-added SrZrO₃ interlayer than the sample with pure SrZrO₃ layer, supporting the hypothesis that Co migration may lead to the activation behavior.     

Synthesis and performance evaluation of a new drag reducer based on acrylamide/12-allyloxydodecyl acid sodium

Hydraulic fracturing with slickwater is a field-proven stimulation technology used in tight reservoirs. Because of the high pumping rate associated with slickwater fracturing, drag reduction (DR) is critical in minimizing pressure drop and the success of oilfield operations. In this paper, a new type of drag reducer (SPR) was synthesized with acrylamide and 12-allyloxydodecyl acid sodium, and its drag reduction performance was evaluated. The results showed that the new drag reducer features low molecular weight, fast-dissolving rate and low interfacial tension. The algorithm of estimating the drag reduction rate of non-Newtonian fluid SPR was proposed and validated. Empirical or semianalytical models for estimating the friction ratio (σ) or friction factor (λ or f) were used to simulate the turbulence behavior of the SPR drag reducer under different Reynolds numbers (Re). The modified Virk's correlation could accurately model the turbulent behavior of the SPR drag reducer. A unified calculation formula was established in this study for different pipe diameters.     

Synthesis and characterization of transition metal mixed oxide doped graphene embedded durable electrocatalyst for hydrogen evolution reaction

A promising electrocatalyst containing variable percentage of V₂O₅–TiO₂ mixed oxide in graphene oxide support was prepared by embedding the catalyst on Cu substrate through facile electroless Ni–Co–P plating for hydrogen evolution reaction. The solvothermal decomposition method was opted for tuning the crystalline characteristics of prepared material. The optimized mixed oxide was well characterized, active sites centres were identified and explained by X-ray diffraction, high resolution tunnelling electron microscopy, scanning electron microscopy coupled with energy dispersive X-ray and X-ray photon spectroscopy analysis. The structural and electronic characteristics of material was done by fourier transform infrared spectroscopy and the electrochemical behaviour of the prepared material was evaluated by using Tafel plot, electrochemical impedance analysis, linear sweep voltammetry, open circuit analysis and chronoamperometry measurements. The results show the enhanced catalytic activity of Ni–Co–P than pure Ni–P plate, due to synergic effect. Moreover, the prepared mixed oxide incorporated Ni–Co–P plate has a high activity towards HER with low over potential of 101 mV, low Tafel slope of 36 mVdec^?1, high exchange current density of 9.90 × 10^?2 Acm^?2.     

Reduced Claudin-12 Expression Predicts Poor Prognosis in Cervical Cancer

Background: Within the claudin (CLDN) family, CLDN12 mRNA expression is altered in various types of cancer, but its clinicopathological relevance has yet to be established due to the absence of specific antibodies (Abs) with broad applications. Methods: We generated a monoclonal Ab (mAb) against human/mouse CLDN12 and verified its specificity. By performing immunohistochemical staining and semiquantification, we evaluated the relationship between CLDN12 expression and clinicopathological parameters in tissues from 138 cases of cervical cancer. Results: Western blot and immunohistochemical analyses revealed that the established mAb selectively recognized the CLDN12 protein. Twenty six of the 138 cases (18.8%) showed low CLDN12 expression, and the disease-specific survival (DSS) and recurrence-free survival rates were significantly decreased compared with those in the high CLDN12 expression group. We also demonstrated, via univariable and multivariable analyses, that the low CLDN12 expression represents a significant prognostic factor for the DSS of cervical cancer patients (HR 3.412, p = 0.002 and HR 2.615, p = 0.029, respectively). Conclusions: It can be concluded that a reduced CLDN12 expression predicts a poor outcome for cervical cancer. The novel anti-CLDN12 mAb could be a valuable tool to evaluate the biological relevance of the CLDN12 expression in diverse cancer types and other diseases.     

Boosting the activity of FeOOH via integration of ZIF-12 and graphene to efficiently catalyze the oxygen evolution reaction

Transition metal oxyhydroxides have been used as promising electrocatalysts for water splitting however, their catalytic activity is restricted due to low surface area and poor conductivity. Herein, we report novel composite FeOOH@ZIF-12/graphene composite as electrocatalyst for water oxidation, whereby ZIF-12 provide extra surface for the FeOOH dispersion whilst graphene act as excellent electron mediator. The composite shows a low overpotential value of 291 mV to attain a current density of 10 mA cm^?2 and a low Tafel slope value of 78 mV dec^?1. The catalyst offers a maximum current density of 101 mA cm^?2, while it gives a turnover frequency (TOF) value of 0.031 s^?1 at an overpotential of 291 mV only. The excellent activity and remarkable stability of composite is attributed to highly conductive and porous support.     

Super-oleophilicity Co-doping Co2+/F-/TiO2 one-dimensional nanotubes for photocatalytic denitrification of light oil

In this study, a simple hydrothermal synthesis method was adapted for the preparation of Co-doping Co²⁺/F^-/TiO₂ nanotubes photocatalyst, and the micro-nano structure of catalysts prepared by biomimetic technology which makes the catalyst have super-oleophilicity property. Co²⁺/F^-/TiO₂ revealed improved photocatalytic performance for denitrification of light oil compared to single TiO₂ photocatalysts. The enhance of photocatalytic activity can be attributed to narrowing the band gap, increasing the light response wavelength and exposing more highly active crystal surfaces due to synergistic effects of Co²⁺ and F^? in the photocatalyst.     

Stabilizing temperature-capacitance dependence of (Sr,Pb, Bi)TiO3-Bi4Ti3O12 solutions for energy storage

(1-x)Sr_0.7Pb_0.15Bi_0.1TiO₃-xBi₄Ti₃O₁₂ ((1-x)SPBT-xBIT, x = 0-0.125) bulk ceramics were developed and calcined via the solid-state method, aimed at the application of pulsed power capacitors. The phase structures, temperature stability, hysteresis loop, and discharge properties were systematically investigated. Considering both the temperature stability and dielectric properties, 0.925SPBT-0.075BIT bulk ceramics with a capacitance variation satisfying the X7R specification were developed for pulsed power capacitors. The energy storage density was 0.252 J/cm³, and the ceramics showed high temperature stability at 80 kV/cm. The discharge current waveforms of the 0.925SPBT-0.075BIT ceramics were recorded. A high discharge power density of approximately 1.01 × 10⁸ W/kg with an 8 Ω load resistor and short discharge period of 84 ns were achieved at 50 kV/cm. The good temperature stability properties and high power density show that the 0.925SPBT-0.075BIT ceramics are well suited for pulsed power capacitors with a wide temperature range.     

Formation of ST12 phase Ge nanoparticles in ZnO thin films

In this work, we focus on the Ge nanoparticles (Ge-np) embedded ZnO multilayered thin films. Effects of reactive and nonreactive growth of ZnO layers on the rapid thermal annealing (RTA) induced formation of Ge-np have been specifically investigated. The samples were deposited by sequential r.f. and d.c. sputtering of ZnO and Ge thin film layers, respectively on Si substrates. As-prepared thin film samples have been exposed to an ex-situ RTA at 600 °C for 60 s under forming gas atmosphere. Structural characterizations have been performed by X-ray Diffraction (XRD), Raman scattering, Secondary Ion Mass Spectroscopy (SIMS), and Scanning Electron Microscopy (SEM) techniques. It has been realized that reactive or nonreactive growth of ZnO layers significantly influences the morphology of the ZnO: Ge samples, most prominently the crystal structure of Ge-np. XRD and Raman analysis have revealed that while reactive growth results in a mixture of diamond cubic (DC) and simple tetragonal (ST12) Ge-np, nonreactive growth leads to the formation of only DC Ge-np upon RTA process. Formation of ST12 Ge-np has been discussed based on structural differences due to reactive and nonreactive growth of ZnO embedding layer.