Maskless Preparation of Spatially-Resolved Plasmonic Nanoparticles on Polydimethylsiloxane via In Situ Fluoride-Assisted Synthesis

Here, a fluoride-assisted route for the controlled in-situ synthesis of metal nanoparticles (NPs) (i.e., AgNPs, AuNPs) on polydimethylsiloxane (PDMS) is reported. The size and coverage of the NPs on the PDMS surface are modulated with time and over space during the synthetic process, leveraging the improved yield (10×) and faster kinetics (100×) of NP formation in the presence of F⁻ ions, compared to fluoride-free approaches. This enables the maskless preparation of both linear and step gradients and patterns of NPs in 1D and 2D on the PDMS surface. As an application in flexible plasmonics/photonics, continuous and step-wise spatial modulations of the plasmonic features of PDMS slabs with 1D and 2D AgNP gradients on the surface are demonstrated. An excellent spatially resolved tuning of key optical parameters, namely, optical density from zero to 5 and extinction ratio up to 100 dB, is achieved with AgNP gradients prepared in AgF solution for 12 minutes; the performance are comparable to those of commercial dielectric/interference filters. When used as a rejection filter in optical fluorescence microscopy, the AgNP-PDMS slabs are able to reject the excitation laser at 405 nm and retain the green fluorescence of microbeads (100 µm) used as test cases.     

Progressive NO2 Sensors with Rapid Alarm and Persistent Memory-Type Responses for Wide-Range Sensing Using Antimony Triselenide Nanoflakes

Antimony triselenide (Sb₂Se₃) nanoflake-based nitrogen dioxide (NO₂) sensors exhibit a progressive bifunctional gas-sensing performance, with a rapid alarm for hazardous highly concentrated gases, and an advanced memory-type function for low-concentration (<1 ppm) monitoring repeated under potentially fatal exposure. Rectangular and cuboid shaped Sb₂Se₃ nanoflakes, comprising van der Waals planes with large surface areas and covalent bond planes with small areas, can rapidly detect a wide range of NO₂ gas concentrations from 0.1 to 100 ppm. These Sb₂Se₃ nanoflakes are found to be suitable for physisorption-based gas sensing owing to their anisotropic quasi-2D crystal structure with extremely enlarged van der Waals planes, where they are humidity-insensitive and consequently exhibit an extremely stable baseline current. The Sb₂Se₃ nanoflake sensor exhibits a room-temperature/low-voltage operation, which is noticeable owing to its low energy consumption and rapid response even under a NO₂ gas flow of only 1 ppm. As a result, the Sb₂Se₃ nanoflake sensor is suitable for the development of a rapid alarm system. Furthermore, the persistent gas-sensing conductivity of the sensor with a slow decaying current can enable the development of a progressive memory-type sensor that retains the previous signal under irregular gas injection at low concentrations.     

福建某低品位金矿新型浸金剂浸金试验

福建某斑岩型金矿品位低、规模大,金主要以自然金形式存在,可见金的粒度较粗,为高效利用该低品位金矿,开展新型浸金剂金蝉全泥浸出试验和柱浸试验,结果表明：全泥浸出在磨矿细度为-0.074 mm占80%、矿浆浓度25%、加石灰调pH 值11.0左右、初始金蝉浓度为500 mg/L和过程中控制金蝉浓度不小于300 mg/L条件下浸出20 h,金的浸出率为93.43%,金蝉耗量为1.02 kg/t；柱浸在矿石粒度为-30 mm条件下喷淋浸出23天,金累计浸出率和金蝉累计耗量分别为86.54%和1.22 kg/t。     

中国首例缓倾铋铜金矿脉--曙光(小西南岔)铜金矿床研究新进展

据现场深入研究，结合多年生产实践，首次系统地描述了小西南岔矿床北山矿段缓倾斜铋铜金支矿脉的地质产状、规模、铜和金品位、自然铋与自然金的交生关系。在此基础上，进一步阐述了缓倾铋铜金矿脉对理论、应用研究及矿山确保铜和金入选品位的重要意义。     

Recovery of gold cyanide using inherently conducting polymers

Removal of gold from basic solutions containing [Au(CN)₂]^? has been demonstrated using the inherently conducting polymer polypyrrole. Polymers containing sulfonated aromatic dopants have been found to display a significant ability to remove gold from such solutions. Experiments performed in solutions containing both gold and copper cyanide complexes indicate that the recovery process is not highly selective. However, the polypyrroles used display significantly faster rates of gold recovery than activated carbon. © 2003 Society of Chemical Industry     

镍层耐硝酸腐蚀性测试——一种简单的预先探测ENIG镍层“黑盘”现象的测试方法

随着更加精细的SMT、BGA等表面贴装技术的运用,化学沉镍金(ENIG)作为线路板最终表面处理得到了越来越广泛的应用,同时可怕的“黑盘”现象也随之更广泛地“流行”起来,直接导致贴装后元器件焊接点不规则接触不良。为了贯彻执行最好的流程控制和采取有效的预防措施,了解这种焊接失败的产生机理是非常重要的,及早的观测到可能发生“黑盘”现象的迹象变得同样关键。本文介绍了一种简单的预先探测ENIG镍层“黑盘”现象的测试方法-镍层耐硝酸腐蚀性测试,这种测试可以用于作为一种常规的测试方法监测一般化学沉镍溶液在有效使用寿命范围内新鲜沉积的镍层的质量。利用Weibull概率统计分析在不同的金属置换周期(MTO)下镍层的可靠性能表现。结合试验结果得出了一个镍层耐硝酸腐蚀性的判定标准。     

Inhibition of acid rock drainage from uranium ore waste using a conventional neutralization and precipitation treatment

Glass columns (length 50 cm, i.d. 4 cm) containing 900 g of uranium ore waste were subjected to a three-step process: (1) acid drainage generation, (2) neutralization and precipitation treatment and, again, (3) acid drainage generation. In the first acid generation step, lasting about one year, different variables (pyrite addition, inoculation and irrigation solution) were tested by measuring effluent pH, redox potential, total iron and sulphate. Conditions of acid generation were satisfactorily reproduced, reaching stable pH values around 2.0 that were determined mainly by pyrite addition and the type of irrigation solution used (distilled water or ferrous sulphate). The neutralization and precipitation treatment consisted of alternating irrigations of a neutralizing solution (CaO saturated plus NaOH) and a precipitating solution (ferric sulphate saturated). This treatment caused accumulation of basic iron sulphate and iron oxide precipitates according to SEM studies. After this treatment, the barrier effect created by the reaction products was checked, using irrigation solutions similar to the first step. The effluents collected showed higher pH and lower redox potential, total iron and sulphate values than those observed before the treatment, evidencing inhibition of acid drainage generation.