Novel core-shell-like Ni-supported hierarchical beta zeolite catalysts on bioethanol steam reforming

Hierarchical-Beta zeolites have been hydrothermally synthesized by adding a new gemini organic surfactant. The used gemini surfactant play the role of a “pore-forming agents” on the mesoscale, on the same time, providing alkaline environment for the system. With this hierarchical Beta zeolite as the core support, we successfully prepared a shell layer of Ni-containing (22 wt%) petal-like core-shell-like catalyst and applied it to bioethanol steam reforming. At the reaction temperature of 350 °C–550 °C, the conversion rate of ethanol and the selectivity of hydrogen were always above 85% and 70%. After reaction of 100 h on stream at 400 °C, there were not obvious inactivation could be observed on NiNPs/OH-MBeta catalyst.     

Cd-ZSM-5沸石催化剂的制备、表征和芳构化催化性能

采用离子交换、浸渍和混合三种方法制备镉改性ZSM-5沸石催化剂,考察了改性方法和镉含量对催化剂的表面酸性和Cd状态以及芳构化性能的影响。结果表明,加入镉降低了B酸性,Cd~(2+)与沸石结合形成了L_(1612)酸中心,其生成量取决于改性方法和Cd含量,并与芳构化活性提高有直接关系。     

乙二胺在沸石分子筛上的TPD研究

以程序升温脱附(TPD)为主要试验手段,对乙二胺在5种不同沸石分子筛上的吸附、脱附行为进行了研究。结果表明,沸石分子筛对乙二胺有着较强的吸附作用,但不同的沸石分子筛对乙二胺的吸附能力受其结构和表面酸性特征的影响而有所不同;适用于交联条件的有效吸附部位为一与沸石分子筛表面酸性有关的弱化学吸附位;乙二胺从不同沸石分子筛表面脱附的动力学与晶内扩散有关,其表观脱附活化能分别为:69.9kJ/mol(5A)、78.3kJ/mol(13X)、22.4kJ/mol(菱沸石)、37.5kJ/m0l(NaY)、44.7kJ/mol(ZSM-5)。     

NaY晶化母液制备硅铝胶的技术探讨

在导向剂法合成Y型分子筛的工艺下，晶化母液中SiO₂的含量为50～55g/l,Na₂O含量为20～25g/l，相当于模数为1.65～2.58的稀水玻璃，将晶化母液分离处理后，在晶化母液中加入一定量的硫酸铝溶液使硅沉淀,经过滤和水洗后即可制备出合格的硅铝胶，以便进行重新利用。     

沸石加氢处理催化剂的制备方法

考察了渣油加氢处理催化剂制备过程中引入一种低硅铝比沸石的情况，它不仅提高催化剂的酸性，而且由于引入的分子筛孔径集中，最终使催化剂具有集中的孔分布，弥补了制备高活性催化剂采用混捏法的不足，制备出来的催化剂性能更优异。     

均匀设计法优化苯一步羟基化制苯酚工艺参数

在单因素研究的基础上 ,用均匀设计法对苯一步羟基化制苯酚的反应条件进行了整体优化。在反应温度 75℃ ,催化剂用量 2 .2g mol,n(C6H6) n(H2 O2 ) =10∶1,H2 O2 浓度为 0 .5 2mol L的条件下 ,反应 2h ,苯的转化率可达 6.18% ,双氧水的转化率和利用率分别可达 87.4%和 89.2 %。     

A STUDY ON ACIDITY AND CATALYTIC PROPERTY OF [B] ZSM-5 CATALYST MODIFIED WITH SILICON COMPOUND BY CHEMICAL SURFACE DEPOSITION OF LIQUID-PHASE TECHNIQUE

The boron heteroatom zeolite catalyst has been modified with silicon compound by Chemical Surface Deposition of Liquid-phase (CLD) technique and the catalytic property of the modified catalyst is studied. Meanwhile, the acidity of the modified zeolite catalysts is characterized through TPD and IR technique, and the fluid adsorption method is used to determine its pore structure. The relationship between the catalytic property of the zeolite catalyst and its pore structure, its acidity has been found. The results of toluene-ethylene alkylation reaction indicate that the selectivity of p-ethyltoluene on the modified zeolite catalyst is higher than that on the zeolite catalyst before silanizated, reaching 94.14%.     

Synthesis, Characterization, and Formation Process of Na-X Zeolite from Coal Fly Ash

Using the SiO₂ and Al₂O₃ components of the amorphous phase in coal fly ash (Fa), Fa was converted to Na-X zeolites in NaOH-NaAlO₂ solutions by stirring at 35°C for 72 hr and then aging at 85°C for a given period. The molar ratio SiO₂/Al₂O₃ of the starting materials was controlled from 2.0 to 13.2. The resulting materials were characterized by various means. Increasing the SiO₂/Al₂O₃ ratio of the starting material increased the degree of crystallinity of faujasite, exhibiting a maximum at SiO₂/Al₂O₃ = 8.0. The faujasite formed was identified as Na-X zeolite with Si/Al = 1.20. The amorphous phase in Fa was dissolved during the stirring to form a precursor of zeolite, such as amorphous aluminosilicate. The Na-X zeolite was formed by aging for 24 hr, and the degree of crystallinity of this material was increased with the increasing aging period. The cation exchange capacity and specific surface area were increased with the increasing degree of crystallinity of the Na-X zeolites.     

Catalytic properties and electronic structure of copper ions in Cu-ZSM-5

The effect of ion exchange conditions, such as Si/Al ratio, precursor copper salt, pH and concentration of the solution, on the catalytic activity in SCR of NO by propane and on the electronic state of copper ions in Cu-ZSM-5 has been studied. The NO conversion in NO SCR by C₃H₈ has been found to reach a maximum value at Cu/Al ratio about 0.37–0.4 and remain constant at higher Cu/Al.

ESR and UV–vis DR spectroscopy have been used to elucidate stabilization conditions of copper ions in Cu-ZSM-5 zeolites as isolated Cu²⁺ ions, chain copper oxide structures and square-plain oxide clusters. The ability of copper ions for reduction and reoxidation in the chain structures may be responsible for the catalytic activity of Cu-ZSM-5. These transformations of copper ions are accompanied by the observation of intervalence transitions Cu²⁺–Cu⁺ and CTLM of the chain structures in the UV–vis spectra.