磨料有序排布电镀砂轮的制备及其把持力研究

为解决电镀砂轮磨削加工中容屑空间不足的问题，采用点胶微粘接的方法制备了磨料有序排布的电镀砂轮，分析了磨料粘接效果和镀层力学性能。通过SEM分析了磨料/镀层/导电胶的结合界面，并进行了干磨削试验。研究结果表明，直径约为磨料粒径40%的胶点可粘接住磨料，单个胶点上粘接多颗磨料的占比小于6%；双脉冲电镀工艺制备的镀层显微硬度大于500HV，表层残余应力小于100MPa，磨料/镀层/导电胶之间的界面贴合紧密，无明显缺陷；砂轮在磨削时没有出现磨料脱落现象。     

Study on the non-uniform contact during ELID groove grinding

This paper introduces the potential feasibility that ELID (electrolytic in-process dressing) grinding replaces superfinishing in bearing manufacturing, but ELID grinding will bring new challenges. Different regions present distinguish surface profile due to the non-uniform contact in ELID groove grinding. However, few reports explaining the non-uniform contact are available. This article explores the mechanisms of the non-uniform contact during ELID groove grinding. Experiments on the non-uniform contact between bearing raceway and grinding wheel have been carried out under different conditions. The results show that non-uniform contact exists in ELID groove grinding process and it exerts influence on the profile of the raceway surface. Non-uniform contact influences the Rsk and Rku value all the time, but it influences the Ra value occasionally. Improvement strategies of eliminating the non-uniform contact are also discussed based on the experimental study.     

超细粉在内循环流化床中的流态化特性

在内径120 mm的半圆柱形内循环流化床中,以平均粒径387 nm的Ti O2为原料,考察了单独通入流化气、射流气和同时通入流化气和射流气三种流化方式下超细粉的流化特性以及射流气速对超细粉聚团尺寸的影响。结果表明:同时通入流化气和射流气时,流化气能促进粉体循环,消除环隙死区;高速射流能有效破碎聚团,显著减小聚团尺寸,从而使超细粉在环隙区与导流管之间形成稳定循环,小聚团在环隙区实现平稳流态化。随着射流气速的增大,聚团尺寸减小,粒度分布变窄,在射流气速分别为60,90,120,150 m/s的条件下,聚团平均直径分别为194,158,147,135μm。     

郴州某复杂硫化铅锌矿阶段磨浮试验研究

针对郴州某复杂硫化铅锌矿资源的性质特点,采用铅快速浮选后尾矿再磨再选的阶磨阶选工艺,较好地实现了铅锌的高效浮选回收。研究了磨矿方式、捕收剂和调整剂种类及用量等因素对该矿石浮选的影响,确定了最佳浮选条件,通过小型闭路浮选试验,得到了铅品位60.05%、回收率89.63%的铅精矿和锌品位47.01%、回收率88.14%的锌精矿。     

纳米级BaAl_2O_4微粉的制备和性质

分别用溶胶 -凝胶法、低温固相反应法 ,制得了纳米级BaAl2 O4微粉 ,用电镜观察了其形貌和粒径的大小 ,用X-射线衍射仪进行了物相分析 ,测定了其纯度与晶型 ,讨论了制备方法与粒度大小的相互影响     

电沉积法制备铜分散电极

研究了电沉积制备铜分散电极的方法,通过对阴极极化曲线的测试,考察了电流密度及不同冲击电流方式对铜粉粒度的影响。结果表明:适当的电流密度、合适的分散剂、间歇式的电流是得到较细铜粉的条件。同时对铜分散电极的电化学性质进行初步测试,结果表明铜粉细化以后,铜分散差电池的电动势值有所上升。     

Simulation of Strength Distribution in Ground Ceramics by Incorporating Residual Stress Effect

Strength of ground ceramics may be affected by residual stress as well as surface flaws induced by grinding. Strength prediction for ground ceramics is convenient for mechanical design of ceramic components. In this article, a numerical procedure based on fracture mechanics was proposed to estimate strength distribution of ground ceramics by considering grinding-induced residual stress. Bending strength and residual stress of ground ceramics were measured for three grinding-conditions. By comparison of simulated results with experimental ones, it was revealed that strength characteristics in experiments were well simulated by using the proposed procedure.     

FeBP非晶态合金超细微粒的合成及其对PH3分解的催化作用

用化学还原法合成了FeBP非晶态合金超细微粒，用电感耦合等离子体光谱（ICP）、X射线粉末衍射（XRD）、透射电子显微镜（TEM）和差热分析（DSC）等手段对其进行了物性表征，并用微型催化反应装置考察了其对PH3分解的催化作用，结果表明，非晶态合金FeBP对PH3的分解具有良好的催化作用，能使PH3的分解温度从800℃以上降到500℃左右。490℃时分解率超过90％，540℃时达100％。     

成形磨削中砂轮修整精度的研究

成形磨削一般采用金刚石笔来修整所需要的砂轮形状，金刚石笔在安装中的位置误差将影响被加工工件的精度，本文对此误差的大小进行了分析。     

超微粒子的量子阻尼振动理论

根据SU(1,1)Lie代数,建立超微粒子的量子阻尼振动理论,得到超微粒子量子阻尼振动系统的能级和波函数。