基于Abaqus的双裂纹不同间距对裂纹扩展速率的研究

扩展有限元法是近年经过大量运用的,在传统有限元的范围中求解不连续问题一种有效计算方法,它是基于单位分解的思想,在计算不连续问题时加入跳跃函数。以ABAQUS为平台,基于扩展有限元方法 (XFEM),以含双穿透型裂纹的有限宽板受横向拉伸载荷为力学模型,建立相应的裂纹尖端应力的有限元模型,研究焊接接头区域不同间距双裂纹相互作用对裂纹扩展速率的影响。结果表明:双裂纹间距的的大小并没有对裂纹的扩展速率产生影响。     

异种铁素体耐热钢接头界面组织及其影响

综述了铁素体与铁素体异种金属焊缝（dissimilar metal welds，DMWs）接头界面组织及其影响。结果表明，在焊后热处理或运行温度下的铁素体钢DMWs接头的不均匀界面组织中，通常会形成脱碳层和增碳层。在铁素体钢DMWs焊接接头界面组织影响因素中，焊缝金属的化学成分有重要影响；焊后热处理规范（温度和时间）、工作温度下运行时间的影响较为突出；焊接工艺参数的影响亦不可忽略。异种钢接头界面处近缝区裂纹的产生，以及接头的蠕变强度随Larson Miller 参数增大而下降等不利影响，均为异种钢界面碳迁移行为所导致。焊缝成分控制法是接头界面组织控制或改善的必要条件，而脱碳层部位转移法能有效防止裂纹发生，亦是接头安全运行的重要工艺措施之一。     

Performance evaluation of structural concrete using controlled quality coarse and fine recycled concrete aggregate

This paper presents the fresh, mechanical, and durability performance, of a structural concrete mix classified as C-1, by the Canadian Standards Association (CSA) made with controlled quality Recycled Concrete Aggregate (RCA). Five mixes with water-to-cementing material (w/cm) ratio of 0.40 were produced with various RCA contents and tested against two 0% RCA control mixes made with General Use (GU) cement, and General Use Limestone cement (GUL). The RCA contents in the mixes were 10%, 20%, and 30% by coarse aggregate volume replacement, as well as 10% and 20% fine and coarse (granular) aggregate volume replacement. All evaluated mixes met the specifications from the CSA for fresh, mechanical, and durability properties. The coarse RCA mixes performed better than the granular RCA mixes in terms of flexural and splitting tensile strengths, linear drying shrinkage, water sorptivity, and rapid chloride-ion permeability, where the test results were significantly affected by the ultra fines present in the granular RCA.     

Behavior of 316L stainless steel containing corrosion pits under cyclic loading

The environmental performance of 316L grade stainless steel, in the form of tensile specimens containing a single corrosion pit with various aspect ratios, under cyclic loading in aerated chloride solutions is investigated in this study. Results from environmental tests were compared and contrasted with those obtained using finite element analysis (FEA). Fractography of the failed specimens obtained from experiments revealed that fatigue crack initiation took place at the base of the shallow pit. The crack initiation shifted towards the shoulder and the mouth of the pit for pits of increasing depth. This process is well predicted by FEA, as the strain contour maps show that strain is the highest around the centric strip of the pit. However, for shallow pits, local strain is uniformly distributed around that strip but begins to concentrate more towards the shoulder and the mouth region for increasingly deep pits.     

Stress distribution in thick-walled cylinder due to non-uniform radial pressure on the example of reinforcement corrosion in concrete

This paper presents an analytical solution to the non-uniform pressure on thick-walled cylinder. The formulation is based on the linear elasticity theory (plain strain) and stress function method. As an example, the proposed solution is used to model the stress distribution due to non-uniform steel reinforcement corrosion in concrete. The model is formulated considering different scenarios of corrosion pressure distribution. It is validated against the finite element model for different cases of non-uniform pressure distributions. The results show that the corrosion-induced cracks are likely to start just beyond the anodic zone. This is confirmed by the experimental tests on concrete cylinder exposed to non-uniform accelerated corrosion of steel reinforcement. The model can be effectively used to calculate the distribution of corrosion-induced stresses in concrete.     

Effect of steel slag on 3D concrete printing of geopolymer with quaternary binders

A new type of 3D-printable ‘one-part’ geopolymer was synthesized with fly ash (FA), granulated blast furnace slag (GBFS), steel slag (SS) and flue gas desulfurization gypsum (FGD). The effects of SS content (0–40%) on the rheological properties, 3D-printability, mechanical anisotropy and reaction kinetics of geopolymer were investigated. The yield stress and plastic viscosity monotonically decreased with the increasing SS content. Contrarily, the geopolymer with 10% of SS presented better extrudability, buildability and mechanical strength than those with 0, 20%, 30% and 40% of SS. This was mainly attributed to the conflicting influence of SS on geopolymerization, of which the OH^? produced by hydration of SS raised the alkalinity of the reaction system and accelerated the dissolution of SiO₄^4? and AlO₄^5?, while the low reactivity prohibited the following polymerization process. Furthermore, the 3D-printed geopolymer presented more compact microstructure and less mechanical anisotropy thanks to the crosslinking of morphologically complementary products, including N(C)-A-S-H, C–S–H, AFt and CH, formed via synergistic reaction of FA-GBFS-SS-FGD system.     

混凝土结构的压电声波检测分析

本文介绍了混凝土结构的压电体波和表面波检测的主要进展,对两种压电声波检测的优缺点进行了总结。体波检测设备一般埋入混凝土内部,需要选择合理的检测部位,检测结果较为精确;声表面波检测无需选择特定的部位,但是检测深度有限。在实际检测工作过程中,可以联合两种方法相互验证。     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

Investigation on the effectiveness of the repair method 8.3 “Corrosion protection by increasing the electrical resistivity” in chloride-containing concrete Part 2: Chloride redistribution in concrete after application of a system sealing surface protective coating

This DFG-funded research project aimed to gain a better understanding of the mechanisms of the W-Cl repair principle within the framework of fundamental investigations, to contribute to the creation of the necessary basis for a broader application of the repair principle in practice. The focus was on the development of a model to describe the chloride redistribution after the application of a system sealing surface protective coating. On the basis of Fick's second law of diffusion, a mathematical model with a self-contained analytical solution was developed, with the help of which the chloride redistribution after application of a system sealing surface protective coating can be calculated under the idealized assumption of complete water saturation of the concrete. Furthermore, the influence of the dehydration of the concrete, expected as a result of the application of the repair principle W-Cl, on the chloride redistribution was investigated. On the basis of laboratory tests and numerical simulations, material-specific reduction functions were developed to quantify the relationship between the chloride diffusion coefficient and the ambient humidity.