Green preparation of vanadium carbide through one-step molten salt electrolysis

Vanadium carbide (VC) as excellent ceramic and functional material is usually prepared by carbothermal reduction of V₂O₅ which must be extracted from a typical V slag by complex processes. Pollutants, such as ammonia-nitrogen wastewater, NH₃ and CO₂ are inevitably discharged. A novel and green method for VC preparation was proposed by one-step co-electrolysis of soluble NaVO₃ and CO₂ in molten salt. It was found that VC with high purity was easily obtained by reducing electrolysis temperature and CO₂ flow rate to 600 °C and 10 mL min⁻¹ at 3.0 V. Besides VC with particles and layered stacking structure in products, a small amount of carbon and oxygen elements existed. The atomic percentage contents of C, V, and O elements in VC were about 50.0%, 44.5% and 3.8%, respectively. During electrolysis, CO₃²⁻ and VO₃⁻ was reduced at about −0.55 V (vs. Ag/AgCl) and −1.38 V (vs. Ag/AgCl), respectively. CO₃²⁻ ions were more easily reduced than VO₃⁻, and was firstly reduced to CO₂²⁻ and then converted to C. Then, VC was prepared by two routes from CO₂ and NaVO₃. One route is that VO₃⁻ ions are firstly electroreduced to VO₂⁻ ions and then are further electroreduced to VC with C. Another route is that VO₃⁻ ions are electroreduced to V which in-situ reacted with C to VC. Both VO₃⁻ and CO₃²⁻ ions are electroreduced by two-step process. In final, VC is in-situ deposited on cathode. It provides a novel and green way to prepare VC and also achieves the high value-added utilization of vanadium slag and CO₂.     

Stem Photosynthesis—A Key Element of Grass Pea (Lathyrus sativus L.) Acclimatisation to Salinity

Grass pea (Lathyrus sativus) is a leguminous plant of outstanding tolerance to abiotic stress. The aim of the presented study was to describe the mechanism of grass pea (Lathyrus sativus L.) photosynthetic apparatus acclimatisation strategies to salinity stress. The seedlings were cultivated in a hydroponic system in media containing various concentrations of NaCl (0, 50, and 100 mM), imitating none, moderate, and severe salinity, respectively, for three weeks. In order to characterise the function and structure of the photosynthetic apparatus, Chl a fluorescence, gas exchange measurements, proteome analysis, and Fourier-transform infrared spectroscopy (FT-IR) analysis were done inter alia. Significant differences in the response of the leaf and stem photosynthetic apparatus to severe salt stress were observed. Leaves became the place of harmful ion (Na⁺) accumulation, and the efficiency of their carboxylation decreased sharply. In turn, in stems, the reconstruction of the photosynthetic apparatus (antenna and photosystem complexes) activated alternative electron transport pathways, leading to effective ATP synthesis, which is required for the efficient translocation of Na⁺ to leaves. These changes enabled efficient stem carboxylation and made them the main source of assimilates. The observed changes indicate the high plasticity of grass pea photosynthetic apparatus, providing an effective mechanism of tolerance to salinity stress.     

Structural Aspects of P2-Type Na0.67Mn0.6Ni0.2Li0.2O2 (MNL) Stabilization by Lithium Defects as a Cathode Material for Sodium-Ion Batteries

A known strategy for improving the properties of layered oxide electrodes in sodium-ion batteries is the partial substitution of transition metals by Li. Herein, the role of Li as a defect and its impact on sodium storage in P2-Na_0.67Mn_0.6Ni_0.2Li_0.2O₂ is discussed. In tandem with electrochemical studies, the electronic and atomic structure are studied using solid-state NMR, operando XRD, and density functional theory (DFT). For the as-synthesized material, Li is located in comparable amounts within the sodium and the transition metal oxide (TMO) layers. Desodiation leads to a redistribution of Li ions within the crystal lattice. During charging, Li ions from the Na layer first migrate to the TMO layer before reversing their course at low Na contents. There is little change in the lattice parameters during charging/discharging, indicating stabilization of the P2 structure. This leads to a solid-solution type storage mechanism (sloping voltage profile) and hence excellent cycle life with a capacity of 110 mAh g^-1 after 100 cycles. In contrast, the Li-free compositions Na_0.67Mn_0.6Ni_0.4O₂ and Na_0.67Mn_0.8Ni_0.2O₂ show phase transitions and a stair-case voltage profile. The capacity is found to originate from mainly Ni³⁺/Ni⁴⁺ and O^2-/O^2-δ redox processes by DFT, although a small contribution from Mn⁴⁺/Mn⁵⁺ to the capacity cannot be excluded.     

Current advances concerning the most cited metal ions doped bioceramics and silicate-based bioactive glasses for bone tissue engineering

Studies related to biomaterials that stimulate the repair of living tissue have increased considerably, improving the quality of many people's lives that require surgery due to traumatic accidents, bone diseases, bone defects, and reconstructions. Among these biomaterials, bioceramics and bioactive glasses (BGs) have proved to be suitable for coating materials, cement, scaffolds, and nanoparticles, once they present good biocompatibility and degradability, able to generate osteoconduction on the surrounding tissue. However, the role of biomaterials in hard tissue engineering is not restricted to a structural replacement or for guiding tissue regeneration. Nowadays, it is expected that biomaterials develop a multifunctional role when implanted, orchestrating the process of tissue regeneration and providing to the body the capacity to heal itself. In this way, the incorporation of specific metal ions in bioceramics and BGs structure, including magnesium, silver, strontium, lithium, copper, iron, zinc, cobalt, and manganese are currently receiving enhanced interest as biomaterials for biomedical applications. When an ion is incorporated into the bioceramic structure, a new category of material is created, which has several unique properties that overcome the disadvantages of primitive material and favors its use in different biomedical applications. The doping can enhance handling properties, angiogenic and osteogenic performance, and antimicrobial activity. Therefore, this review aims to summarize the effect of selected metal ion dopants into bioceramics and silicate-based BGs in bone tissue engineering. Furthermore, new applications for doped bioceramics and BGs are highlighted, including cancer treatment and drug delivery.     

低分子量聚丙烯酸钾的合成及其应用

采用水溶液聚合法制备了低分子量聚丙烯酸钾（PAAK），并作为新型消焰剂加入单基发射药中。通过火焰原子吸收光谱法测试了PAAK中钾的含量；用乌氏黏度计测定了特性黏度；采用DSC法研究不同pH值的PAAK与硝化棉（NC）的相容性；利用充氮氧弹法对添加PAAK、硝酸钾KNO₃、硫酸钾K₂SO₄的单基发射药的燃烧残渣进行了对比研究。结果表明，合成的PAAK中，钾的质量分数为15.21%，相对分子量在3 000左右，有利于和NC均匀混合，且在中性或微碱性（pH＝7.0~7.5）的情况与NC相容性良好。与传统的KNO₃、K₂SO₄消焰剂相比，PAAK能够和NC均匀混合，制备均质透明的单基发射药；PAAK发射药的燃烧残渣最少，占发射药质量的0.18%。     

Impact of gypsum on flotation of scheelite and fluorite using sodium oleate as collector

ABSTRACT

In this study, effect of calcium and gypsum on scheelite and fluorite was investigated using sodium oleate as collector. Micro-flotation and contact angle results showed that the adsorption of calcium could inhibit the hydrophobicity of scheelite and fluorite. Moreover, sulfate could enhance the inhibition. FT-IR results showed that calcium could be priori precipitated into calcium oleate and adsorb on mineral surface. The adsorption of calcium could increase the scheelite potential to IEP, while it showed limited effect on fluorite potential. However, the interaction of calcium on scheelite and fluorite in gypsum solution was more complex than that in calcium solution.     

Revealing Electrical-Poling-Induced Polarization Potential in Hybrid Perovskite Photodetectors

Despite recent rapid advances in metal halide perovskites for use in optoelectronics, the fundamental understanding of the electrical-poling-induced ion migration, accounting for many unusual attributes and thus performance in perovskite-based devices, remain comparatively elusive. Herein, the electrical-poling-promoted polarization potential is reported for rendering hybrid organic–inorganic perovskite photodetectors with high photocurrent and fast response time, displaying a tenfold enhancement in the photocurrent and a twofold decrease in the response time after an external electric field poling. First, a robust meniscus-assisted solution-printing strategy is employed to facilitate the oriented perovskite crystals over a large area. Subsequently, the electrical poling invokes the ion migration within perovskite crystals, thus inducing a polarization potential, as substantiated by the surface potential change assessed by Kelvin probe force microscopy. Such electrical-poling-induced polarization potential is responsible for the markedly enhanced photocurrent and largely shortened response time. This work presents new insights into the electrical-poling-triggered ion migration and, in turn, polarization potential as well as into the implication of the latter for optoelectronic devices with greater performance. As such, the utilization of ion-migration-produced polarization potential may represent an important endeavor toward a wide range of high-performance perovskite-based photodetectors, solar cells, transistors, scintillators, etc.     

High-resolution FIB-TEM-STEM structural characterization of grain boundaries in the high dielectric constant perovskite CaCu3Ti4O12

In this work, the grain boundaries composition of the polycrystalline CaCu₃Ti₄O₁₂ (CCTO) was investigated. A Focused Ion Beam (FIB)/lift-out technique was used to prepare site-specific thin samples of the grain boundaries interface of CCTO ceramics. Scanning transmission electron microscopy (STEM) coupled with energy dispersive X-ray spectrometry (EDXS) and Electron Energy Loss Spectroscopy (EELS) systems were used to characterize the composition and nanostructure of the grain and grain boundaries region. It is known that during conventional sintering, discontinuous grain growth occurs and a Cu-rich phase appears at grain boundaries. This Cu-rich phase may affect the final dielectric properties of CCTO but its structure and chemical composition remained unknown. For the first time, this high-resolution FIB-TEM-STEM study of CCTO interfacial region highlights the composition of the phases segregated at grain boundaries namely CuO, Cu₂O and the metastable phase Cu₃TiO_4.